CN109778387A - A kind of silk and chiffon fabric mixed textile technique - Google Patents
A kind of silk and chiffon fabric mixed textile technique Download PDFInfo
- Publication number
- CN109778387A CN109778387A CN201711109303.7A CN201711109303A CN109778387A CN 109778387 A CN109778387 A CN 109778387A CN 201711109303 A CN201711109303 A CN 201711109303A CN 109778387 A CN109778387 A CN 109778387A
- Authority
- CN
- China
- Prior art keywords
- silk
- chiffon fabric
- pressure value
- maximum pressure
- mixed textile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of silks and chiffon fabric mixed textile technique.1) chiffon fabric is placed in water steam box it is characterized in that comprising the steps of:, 85-100 DEG C of water temperature, is steamed 80 minutes；2) chiffon fabric in step 1) is placed in a natural state pre-setting 10-20 hours；3) it is stretchable to greatest extent i.e. to the maximum pressure value that it can apply to measure silk；4) water-jet loom is used to carry out mixed textile to silk and chiffon fabric with above-mentioned maximum pressure value.It is stretchable to greatest extent i.e. to the maximum pressure value that it can apply that the present invention measures silk first, since the tensile capacity of silk is weaker than chiffon fabric, therefore the blended tension that can guarantee silk and chiffon fabric is carried out all in the range of it can bear using to the maximum pressure value that silk can apply, it is not easy to break.
Description
Technical field
The present invention relates to a kind of silks and chiffon fabric mixed textile technique.
Background technique
When carrying out mixed textile using different material silk, the tension of various raw material threads and suitable processing temperature etc. are all to influence
The important parameter of end product quality, therefore when designing textile technology need to look after the characteristic of different material silk.Utilize silkworm
When silk and chiffon fabric mixed textile are at fabric, since silk and the difference of chiffon fabric characteristic are larger, special process need to be just used
It weaves.Specifically, silk poor water resistance, chance water is easily broken and tensile capacity is weak, and stress is easily broken；And the chiffon fabric twist
Height, tensile capacity are strong.In order to look after the characteristic of different material silk to protect when above-mentioned silk and chiffon fabric are carried out mixed textile
The quality of end product is demonstrate,proved, the method that this enterprise uses at present is: drawing using water-jet loom to silk and chiffon fabric
When be all made of identical specification be 45-20 nozzle；And chiffon fabric is pre-processed chiffon i.e. before progress is blended
Fabric is put into steam box, is successively vacuumized, is heated, vacuumized, heated again and keeping the temperature at 85 DEG C of steaming a period of times
Nature sizing is taken out afterwards.But using above-mentioned traction and pretreating process, its effect is still not fully up to expectations, the production being finally made into
Product still will appear more blind.
Summary of the invention
Aiming at the problems existing in the prior art, the purpose of the present invention is to provide a kind of silks, and spinning is mixed with chiffon fabric
The technical solution of weaving process.
A kind of silk and chiffon fabric mixed textile technique, it is characterised in that comprise the steps of:
1) chiffon fabric is placed in water steam box, 85-100 DEG C of water temperature, is steamed 80 minutes；
2) chiffon fabric in step 1) is placed in a natural state pre-setting 10-20 hours；
3) it is stretchable to greatest extent i.e. to the maximum pressure value that it can apply to measure silk；
4) water-jet loom is used to carry out mixed textile to silk and chiffon fabric with above-mentioned maximum pressure value.
A kind of silk and chiffon fabric mixed textile technique, it is characterised in that the water-jet loom is to chiffon fabric
It uses specification for the nozzle of 75-40 when being drawn, uses specification for the nozzle of 45-20 when drawing to silk.
A kind of silk and chiffon fabric mixed textile technique, it is characterised in that the chiffon fabric is placed in water steam box
Water temperature is 90 DEG C when middle.
A kind of silk and chiffon fabric mixed textile technique, it is characterised in that the chiffon fabric is placed in nature shape
Pre-setting 15 hours under state.
It is stretchable to greatest extent i.e. to the maximum pressure value that it can apply that the present invention measures silk first, due to silk
Tensile capacity is weaker than chiffon fabric, therefore can guarantee silk and snow using the maximum pressure value progress that can apply to silk is blended
The tension of textile fabric is not easy to break all in the range of it can bear；Further, before carrying out mixed textile, to chiffon
Fabric is pre-processed, so that silk is more consistent with the characteristic of chiffon fabric, to be conducive to the progress of subsequent technique.
Specific embodiment
A kind of silk and chiffon fabric mixed textile technique comprising the steps of:
1) chiffon fabric is placed in water steam box, 85-100 DEG C of water temperature, is steamed 80 minutes；
2) chiffon fabric in step 1) is placed in a natural state pre-setting 10-20 hours；
3) it is stretchable to greatest extent i.e. to the maximum pressure value that it can apply to measure silk；
4) water-jet loom is used to carry out mixed textile to silk and chiffon fabric with above-mentioned maximum pressure value.
Specification is used to adopt when drawing to silk when water-jet loom draws chiffon fabric for the nozzle of 75-40
The nozzle for being 45-20 with specification.
Embodiment one
It is 90 DEG C that chiffon fabric, which is placed in water temperature when in water steam box, other to be same as above.
Embodiment two
Chiffon fabric is placed in a natural state pre-setting 15 hours, other to be same as above.
It is stretchable to greatest extent i.e. to the maximum pressure value that it can apply that the present invention measures silk first, due to silk
Tensile capacity is weaker than chiffon fabric, therefore can guarantee silk and snow using the maximum pressure value progress that can apply to silk is blended
The tension of textile fabric is not easy to break all in the range of it can bear；Further, before carrying out mixed textile, to chiffon
Fabric is pre-processed, so that silk is more consistent with the characteristic of chiffon fabric, to be conducive to the progress of subsequent technique.
Claims (2)
1. a kind of silk and chiffon fabric mixed textile technique, it is characterised in that comprise the steps of:
1) chiffon fabric is placed in water steam box, 85-100 DEG C of water temperature, is steamed 80 minutes；
2) chiffon fabric in step 1) is placed in a natural state pre-setting 10-20 hours；
3) it is stretchable to greatest extent i.e. to the maximum pressure value that it can apply to measure silk；
4) water-jet loom is used to carry out mixed textile to silk and chiffon fabric with above-mentioned maximum pressure value.
2. a kind of silk according to claim 1 and chiffon fabric mixed textile technique, it is characterised in that the water spray is knitted
It uses specification for the nozzle of 75-40 when machine draws chiffon fabric, uses specification for 45-20's when drawing to silk
Nozzle.