CN107366079A - A kind of mixed textile technique - Google Patents
A kind of mixed textile technique Download PDFInfo
- Publication number
- CN107366079A CN107366079A CN201710542928.6A CN201710542928A CN107366079A CN 107366079 A CN107366079 A CN 107366079A CN 201710542928 A CN201710542928 A CN 201710542928A CN 107366079 A CN107366079 A CN 107366079A
- Authority
- CN
- China
- Prior art keywords
- polyester filament
- mixed textile
- water
- artificial silk
- textile technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of mixed textile technique, it is related to textile technology technical field, comprises the following steps:1)It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure artificial silk;2)Polyester filament is placed in water steam box, 85 ~ 100 DEG C of water temperature, steams 45 min;3)By step 2)In polyester filament be placed under ventilating opening and divulge information, the h of pre-setting 15 ~ 25;4)Water-jet loom is used to carry out mixed textile to artificial silk and polyester filament with above-mentioned maximum pressure value.The mixed textile technique that the invention provides, scheme is complete, simple process, so that artificial silk is more consistent with the characteristic of polyester filament, so as to be advantageous to the progress of subsequent technique, every hundred meters can be significantly reduced and be made into the existing blind quantity of fabric, every hundred meters can be significantly reduced and be made into the existing blind quantity of fabric.
Description
Technical field
The present invention relates to textile technology technical field, and in particular to a kind of mixed textile technique.
Background technology
When carrying out mixed textile using different material silk, the tension force of various raw material threads and suitable processing temperature etc. are all to influence
The important parameter of end product quality, therefore need when designing textile technology to look after the characteristic of different material silk.Such as I
Using artificial silk with polyester filament mixed textile into fabric when, due to artificial silk and polyester filament characteristic difference it is larger, just need
Weaved using special process.Specifically, artificial silk poor water resistance, chance water is easily broken, and tensile capacity is weak, and stress is easily broken;
And the polyester filament twist is high, tensile capacity is strong.In order to look after difference when above-mentioned artificial silk and polyester filament are carried out into mixed textile
To ensure the quality of end product, the method that this enterprise uses at present is the characteristic of raw material thread:Using water-jet loom to artificial silk
Nozzle of the identical specification for 45-20 is used when being drawn with polyester filament;And to polyester filament before blending is carried out
Pre-processed and polyester filament is put into steam box, vacuumized, heated successively, vacuumized, heated again and protecting temperature
Hold and take out nature sizing after steaming a period of time at 85 DEG C.But using above-mentioned traction and pretreating process its effect still not to the utmost
Such as people's will, more blind still occurs in the product being finally made into.When carrying out mixed textile using different material silk, various raw materials
The tension force of silk and suitable processing temperature etc. are all the important parameters for influenceing end product quality, therefore are needed when designing textile technology
Look after the characteristic of different material silk.Such as we using artificial silk with polyester filament mixed textile into fabric when, due to people
Make silk and the difference of polyester filament characteristic is larger, need to just be weaved using special process.Specifically, artificial silk poor water resistance, meet
Water is easily broken, and tensile capacity is weak, and stress is easily broken;And the polyester filament twist is high, tensile capacity is strong.By above-mentioned artificial silk and terylene
In order to look after the characteristic of different material silk to ensure the quality of end product during long filament progress mixed textile, this enterprise uses at present
Method be:Spray of the identical specification for 45-20 is used when being drawn using water-jet loom to artificial silk and polyester filament
Mouth;And polyester filament is pre-processed before blending is carried out polyester filament is put into steam box, vacuumized successively,
Heat, vacuumize, heating again and keeping the temperature at 85 DEG C and steaming taking-up nature sizing after a period of time.But led using above-mentioned
Draw that its effect is still not fully up to expectations with pretreating process, more blind still occurs in the product being finally made into.
The content of the invention
Instant invention overcomes it is above-mentioned the shortcomings that, and provide a kind of mixed textile technique.
To achieve these goals, the present invention is to realize by the following technical solutions:The mixed textile technique, including
Following steps:
1)It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure artificial silk;
2)Polyester filament is placed in water steam box, 85 ~ 100 DEG C of water temperature, steams 45 min;
4)By step 2)In polyester filament be placed under ventilating opening and divulge information, the h of pre-setting 15 ~ 25;
4)Water-jet loom is used to carry out mixed textile to artificial silk and polyester filament with above-mentioned maximum pressure value.
Preferably, used when the water-jet loom is drawn to polyester filament specification for 45 ~ 35 nozzle.
It is furthermore preferred that the water-jet loom used when being drawn to polyester filament specification for 40 nozzle.
Preferably, it is described use when being drawn to artificial silk specification for 35 ~ 15 nozzle.
It is furthermore preferred that it is described use when being drawn to artificial silk specification for 25 nozzle.
Preferably, it is 90 DEG C that the polyester filament, which is placed in water temperature when in water steam box,.
It is furthermore preferred that the polyester filament is placed in the h of pre-setting 12 under nature.
The beneficial effects of the invention are as follows:Scheme is complete, simple process so that the characteristic of artificial silk and polyester filament more phase
Symbol, so as to be advantageous to the progress of subsequent technique, can significantly reduce every hundred meters and be made into the existing blind quantity of fabric, can be obvious
Reduce every hundred meters and be made into the existing blind quantity of fabric.
Embodiment
Embodiment 1
A kind of mixed textile technique, comprises the following steps:
1)It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure artificial silk;
2)Polyester filament is placed in water steam box, 85 ~ 100 DEG C of water temperature, steams 45 min;
3)By step 2)In polyester filament be placed under ventilating opening and divulge information, the h of pre-setting 15 ~ 25;
4)Water-jet loom is used to carry out mixed textile to artificial silk and polyester filament with above-mentioned maximum pressure value.
Wherein, specification is used to be drawn for 45 nozzle to artificial silk when water-jet loom is drawn to polyester filament
Shi Caiyong specifications are 35 nozzle, and it is 90 DEG C that polyester filament, which is placed in water temperature when in water steam box, and polyester filament is placed under nature
The h of pre-setting 12.
Embodiment 2
A kind of mixed textile technique, comprises the following steps:
1)It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure artificial silk;
2)Polyester filament is placed in water steam box, 85 ~ 100 DEG C of water temperature, steams 45 min;
3)By step 2)In polyester filament be placed under ventilating opening and divulge information, the h of pre-setting 15 ~ 25;
4)Water-jet loom is used to carry out mixed textile to artificial silk and polyester filament with above-mentioned maximum pressure value.
Wherein, specification is used to be drawn for 40 nozzle to artificial silk when water-jet loom is drawn to polyester filament
Shi Caiyong specifications are 25 nozzle, and it is 90 DEG C that polyester filament, which is placed in water temperature when in water steam box, and polyester filament is placed under nature
The h of pre-setting 12.
Embodiment 3
A kind of mixed textile technique, comprises the following steps:
1)It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure artificial silk;
2)Polyester filament is placed in water steam box, 85 ~ 100 DEG C of water temperature, steams 45 min;
3)By step 2)In polyester filament be placed under ventilating opening and divulge information, the h of pre-setting 15 ~ 25;
4)Water-jet loom is used to carry out mixed textile to artificial silk and polyester filament with above-mentioned maximum pressure value.
Wherein, specification is used to be drawn for 35 nozzle to artificial silk when water-jet loom is drawn to polyester filament
Shi Caiyong specifications are 15 nozzle, and it is 90 DEG C that polyester filament, which is placed in water temperature when in water steam box, and polyester filament is placed under nature
The h of pre-setting 12.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (7)
1. a kind of mixed textile technique, it is characterised in that comprise the following steps:
1)It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure artificial silk;
2)Polyester filament is placed in water steam box, 85 ~ 100 DEG C of water temperature, steams 45 min;
3)By step 2)In polyester filament be placed under ventilating opening and divulge information, the h of pre-setting 15 ~ 25;
4)Water-jet loom is used to carry out mixed textile to artificial silk and polyester filament with above-mentioned maximum pressure value.
2. the mixed textile technique according to claim 1, it is characterised in that the water-jet loom is carried out to polyester filament
Used during traction specification for 45 ~ 35 nozzle.
3. the mixed textile technique according to claim 1, it is characterised in that the water-jet loom is carried out to polyester filament
Used during traction specification for 40 nozzle.
4. the mixed textile technique according to claim 1, it is characterised in that described to use when being drawn to artificial silk
Specification is 35 ~ 15 nozzle.
5. the mixed textile technique according to claim 1, it is characterised in that described to use when being drawn to artificial silk
Specification is 25 nozzle.
6. the mixed textile technique according to claim 1, it is characterised in that when the polyester filament is placed in water steam box
Water temperature is 90 DEG C.
7. the mixed textile technique according to claim 1, it is characterised in that the polyester filament is placed under nature
The h of pre-setting 12.