CN108716050A - A kind of antibacterial linen-cotton blending technology - Google Patents
A kind of antibacterial linen-cotton blending technology Download PDFInfo
- Publication number
- CN108716050A CN108716050A CN201810723040.7A CN201810723040A CN108716050A CN 108716050 A CN108716050 A CN 108716050A CN 201810723040 A CN201810723040 A CN 201810723040A CN 108716050 A CN108716050 A CN 108716050A
- Authority
- CN
- China
- Prior art keywords
- fiber silk
- cotton
- cotton fiber
- silk
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antibacterial linen-cotton blending technologies, it is characterised in that:The mixed textile technique includes the following steps:(1) it is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure flaxen fiber silk;(2) cotton fiber silk is placed in water steam box, 70~75 DEG C of water temperature, is steamed 60~70 minutes;(3) by step (2), treated that cotton fiber silk is placed in a natural state pre-setting 16~18 hours;(4) water-jet loom is used to carry out mixed textile to cotton fiber silk and flaxen fiber silk with step (1) maximum pressure value;Wherein, it uses specification for the nozzle of 75-40 when water-jet loom draws cotton fiber silk, uses specification for the nozzle of 45-20 when being drawn to flaxen fiber silk;The advantage of the invention is that:The present invention can be solved when carrying out mixed textile using cotton fiber silk and flaxen fiber silk, due to cotton fiber silk it is different from the characteristic of flaxen fiber silk and caused by be finally made into the unsatisfactory disadvantage of quality.
Description
Technical field
The present invention relates to blending technology field more particularly to a kind of antibacterial linen-cotton blending technologies.
Background technology
When carrying out mixed textile using different material silk, the tension of various raw material threads and suitable processing temperature etc. are all to influence
The important parameter of end product quality, therefore need when designing textile technology to look after the characteristic of different material silk.Such as I
Using cotton fiber silk and flaxen fiber silk mixed textile at fabric when, since cotton fiber silk and the difference of flaxen fiber silk characteristic are larger,
With regard to that special process need to be used to weave.Specifically, flaxen fiber silk soft comfortable, good hygroscopicity, but elastic recovery capability is weak;And
Cotton fiber silk hot water resistance is good, and elastic recovery capability is good.When above-mentioned cotton fiber silk and flaxen fiber silk are carried out mixed textile in order to
The characteristic of different material silk is looked after to ensure the quality of end product, the method that this enterprise uses at present is:Utilize water-jet loom
The nozzle that identical specification is 45-20 is all made of when being drawn to cotton fiber silk and flaxen fiber silk;And before progress is blended
Cotton fiber silk is pre-processed, cotton fiber silk is put into steam box, is vacuumized, heated, vacuumized, heated again successively
And it keeps the temperature at 85 DEG C and steams taking-up nature sizing after a period of time.But using its effect of above-mentioned traction and pretreating process
Fruit is still not fully up to expectations, and the product being finally made into still will appear more blind.
In conclusion urgent problem to be solved is, needs pair when cotton fiber silk and flaxen fiber silk progress mixed textile are utilized
Its textile technology is improved, to overcome disadvantages mentioned above.
Invention content
The technical problem to be solved in the present invention is to provide a kind of antibacterial linen-cotton blending technology, can solve fine using cotton
When tieing up silk and flaxen fiber silk and carrying out mixed textile, due to cotton fiber silk it is different from the characteristic of flaxen fiber silk and caused by finally knit
The unsatisfactory disadvantage of final product quality.
In order to solve the above technical problems, the technical scheme is that:A kind of antibacterial linen-cotton blending technology, innovation exist
In:The mixed textile technique includes the following steps:(1) measure that flaxen fiber silk is stretchable to greatest extent can be applied it
Maximum pressure value;(2) cotton fiber silk is placed in water steam box, 70~75 DEG C of water temperature, is steamed 60~70 minutes;It (3) will be at step (2)
Cotton fiber silk after reason is placed in a natural state pre-setting 10~12 hours;(4) water-jet loom is used to be pressed so that step (1) is maximum
Force value carries out mixed textile to cotton fiber silk and flaxen fiber silk;Wherein, using rule when water-jet loom draws cotton fiber silk
Lattice are the nozzle of 75-40, use specification for the nozzle of 45-20 when being drawn to flaxen fiber silk.
Further, in the step (4), the ratio of cotton fiber silk and flaxen fiber silk is 4:1.
The advantage of the invention is that:
1)It is first before carrying out mixed textile using cotton fiber silk and flaxen fiber silk in woven fibrous silk blend technique of the present invention
It is stretchable to greatest extent i.e. to the maximum pressure value that it can apply first to measure flaxen fiber silk, due to the elastic energy of flaxen fiber silk
Power is weaker than cotton fiber silk, therefore can ensure cotton fiber silk using the maximum pressure value progress that can apply to flaxen fiber silk is blended
It is not easy to break with the elastic force of flaxen fiber silk all in the range of it can bear;
2)In woven fibrous silk blend technique of the present invention, before carrying out mixed textile, cotton fiber silk is pre-processed,
So that cotton fiber silk is more consistent with the characteristic of flaxen fiber silk, to be conducive to the progress of subsequent technique;
3)In woven fibrous silk blend technique of the present invention, used when being drawn to cotton fiber silk using water-jet loom specification for
The nozzle of 75-40 uses specification for the nozzle of 45-20 when being drawn to flaxen fiber silk, and it is fine with fiber crops to have looked after cotton fiber silk
The different characteristics for tieing up silk, can significantly reduce every hundred meters and be made into the existing blind quantity of fabric.
Specific implementation mode
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among the embodiment described range.
Embodiment 1:
A kind of antibacterial linen-cotton blending technology, the mixed textile technique include the following steps:(1) it is stretchable to measure flaxen fiber silk
The maximum pressure value that it can be applied to greatest extent;(2) cotton fiber silk is placed in water steam box, 70 DEG C of water temperature, is steamed 60 minutes;
(3) by step (2), treated that cotton fiber silk is placed in a natural state pre-setting 12 hours;(4) use water-jet loom with step
(1) maximum pressure value carries out mixed textile to cotton fiber silk and flaxen fiber silk;Wherein, water-jet loom draws cotton fiber silk
Shi Caiyong specifications be 75 nozzle, used when being drawn to flaxen fiber silk specification for 45 nozzle.
In step (4), the ratio of cotton fiber silk and flaxen fiber silk is 4:1.
Embodiment 2:
A kind of antibacterial linen-cotton blending technology, innovation are:The mixed textile technique includes the following steps:(1) numb fibre is measured
The stretchable maximum pressure value that it can be applied to greatest extent of dimension silk;(2) cotton fiber silk is placed in water steam box, water temperature 75
DEG C, it steams 70 minutes;(3) by step (2), treated that cotton fiber silk is placed in a natural state pre-setting 10 hours;(4) using spray
Water loom carries out mixed textile with step (1) maximum pressure value to cotton fiber silk and flaxen fiber silk;Wherein, water-jet loom is to cotton
Used when filament is drawn specification for 40 nozzle, used when being drawn to flaxen fiber silk specification for 20 nozzle.
In step (4), the ratio of cotton fiber silk and flaxen fiber silk is 4:1.
It should be understood by those skilled in the art that the present invention is not limited to the above embodiments, above-described embodiment and explanation
Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also has
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
It is defined by the appending claims and its equivalent thereof.
Claims (2)
1. a kind of antibacterial linen-cotton blending technology, it is characterised in that:The mixed textile technique includes the following steps:(1) fiber crops are measured
The stretchable maximum pressure value that it can be applied to greatest extent of filament;(2) cotton fiber silk is placed in water steam box, water temperature
It 70~75 DEG C, steams 60~70 minutes;(3) by step (2), treated that cotton fiber silk is placed in a natural state pre-setting 10~12
Hour;(4) water-jet loom is used to carry out mixed textile to cotton fiber silk and flaxen fiber silk with step (1) maximum pressure value;Its
In, water-jet loom uses specification for the nozzle of 75-40 when being drawn to cotton fiber silk, is used when being drawn to flaxen fiber silk
Specification is the nozzle of 45-20.
2. a kind of antibacterial linen-cotton blending technology according to claim 1, it is characterised in that:In the step (4), cotton fiber
The ratio of silk and flaxen fiber silk is 4:1.