CN107488930A - A kind of mixed textile technique - Google Patents
A kind of mixed textile technique Download PDFInfo
- Publication number
- CN107488930A CN107488930A CN201710658925.9A CN201710658925A CN107488930A CN 107488930 A CN107488930 A CN 107488930A CN 201710658925 A CN201710658925 A CN 201710658925A CN 107488930 A CN107488930 A CN 107488930A
- Authority
- CN
- China
- Prior art keywords
- silk
- cotton fiber
- bamboo fibre
- water
- mixed textile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of mixed textile technique, following steps are included：（1）It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure bamboo fibre silk；（2）Cotton fiber silk and polyester fiber yarn are placed in water steam box, 75~85 DEG C of water temperature, steamed 70~80 minutes；（3）By step（2）Cotton fiber silk and polyester fiber yarn after processing are placed in pre-setting 12~16 hours under nature；（4）Water-jet loom is used with step（1）Maximum pressure value carries out mixed textile to cotton fiber silk, polyester fiber yarn and bamboo fibre silk；Wherein, used when water-jet loom is drawn to cotton fiber silk specification for 75 40 nozzle, used when being drawn to polyester fiber yarn specification for 75 40 nozzle, used when being drawn to bamboo fibre silk specification for 45 20 nozzle.The advantage of the invention is that：The present invention can be solved when carrying out mixed textile using cotton fiber silk and bamboo fibre silk, due to cotton fiber silk it is different from the characteristic of bamboo fibre silk and caused by be finally made into the shortcomings that quality is unsatisfactory.
Description
Technical field
The present invention relates to a kind of weaving process, and weaving cotton cloth for mixed textile is carried out using different material silk more particularly to a kind of
Technique.
Background technology
When carrying out mixed textile using different material silk, the tension force of various raw material threads and suitable processing temperature etc. are all to influence
The important parameter of end product quality, therefore need when designing textile technology to look after the characteristic of different material silk.Such as I
Using cotton fiber silk with bamboo fibre silk mixed textile into fabric when, due to cotton fiber silk and bamboo fibre silk characteristic difference it is larger,
With regard to that special process need to be used to be weaved.Specifically, bamboo fibre silk soft comfortable, good hygroscopicity, but elastic recovery capability is weak；And
Cotton fiber silk hot water resistance is good, and elastic recovery capability is good.When above-mentioned cotton fiber silk and bamboo fibre silk carried out into mixed textile in order to
The characteristic of different material silk is looked after to ensure the quality of end product, the method that this enterprise uses at present is：Utilize water-jet loom
Nozzle of the identical specification for 45-20 is used when being drawn to cotton fiber silk and bamboo fibre silk；And carrying out blending
Cotton fiber silk is put into steam box by preceding pre-processed to cotton fiber silk, is vacuumized, heated successively, vacuumized, added again
Temperature simultaneously keeps the temperature at taking-up nature sizing after 85 DEG C of steaming a period of times.But using above-mentioned traction and pretreating process
Its effect is still not fully up to expectations, and more blind still occurs in the product being finally made into.
In summary, it would be highly desirable to solve the problems, such as it is to utilize needs pair when cotton fiber silk and bamboo fibre silk progress mixed textile
Its textile technology is improved, to overcome disadvantages mentioned above.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of mixed textile technique, and it can solve utilizing cotton fiber silk
With bamboo fibre silk carry out mixed textile when, due to cotton fiber silk it is different from the characteristic of bamboo fibre silk and caused by be finally made into quality
Measure the shortcomings that unsatisfactory.
In order to solve the above technical problems, the technical scheme is that：A kind of mixed textile technique, it is characterised in that：Institute
Mixed textile technique is stated to comprise the following steps：
（1）It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure bamboo fibre silk；
（2）Cotton fiber silk and polyester fiber yarn are placed in water steam box, 75~85 DEG C of water temperature, steamed 70~80 minutes；
（3）By step（2）Cotton fiber silk and polyester fiber yarn after processing are placed in pre-setting 12~16 hours under nature；
（4）Water-jet loom is used with step（1）Maximum pressure value mixes to cotton fiber silk, polyester fiber yarn with bamboo fibre silk
Weaving；Wherein, nozzle of the specification for 75-40 is used when water-jet loom is drawn to cotton fiber silk, water-jet loom is to terylene
Nozzle of the specification for 75-40 is used when filament is drawn, specification is used when being drawn to bamboo fibre silk as 45-20
Nozzle.
Further, the step（4）In, the ratio of cotton fiber silk, polyester fiber yarn and bamboo fibre silk is 3:2:1.
The advantage of the invention is that：
（1）In mixed textile technique of the present invention, using cotton fiber silk, polyester fiber yarn and bamboo fibre silk carry out mixed textile it
Before, it is stretchable to greatest extent i.e. to the maximum pressure value that it can apply to measure bamboo fibre silk first, due to the bullet of bamboo fibre silk
Sexuality is weaker than cotton fiber silk, therefore can ensure cotton fiber using the maximum pressure value progress blending that can apply to bamboo fibre silk
The elastic force of silk, polyester fiber yarn and bamboo fibre silk is not easy to break all in the range of it can bear；
（2）In mixed textile technique of the present invention, before mixed textile is carried out, cotton fiber silk and polyester fiber yarn are carried out pre-
Processing so that cotton fiber silk, polyester fiber yarn are more consistent with the characteristic of bamboo fibre silk, so as to be advantageous to entering for subsequent technique
OK；
（3）In mixed textile technique of the present invention, specification is used when being drawn using water-jet loom to cotton fiber silk as 75-40
Nozzle, nozzle of the specification for 75-40 is used when being drawn to polyester fiber yarn, is used when being drawn to bamboo fibre silk
Specification is 45-20 nozzle, has looked after the different qualities of cotton fiber silk, polyester fiber yarn and bamboo fibre silk, can be obvious
Reduce every hundred meters and be made into the existing blind quantity of fabric.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Mixed textile technique of the present invention, the mixed textile technique comprise the following steps：
（1）It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure bamboo fibre silk；
（2）Cotton fiber silk and polyester fiber yarn are placed in water steam box, 75~85 DEG C of water temperature, steamed 70~80 minutes；
（3）By step（2）Cotton fiber silk and polyester fiber yarn after processing are placed in pre-setting 12~16 hours under nature；
（4）Water-jet loom is used with step（1）Maximum pressure value mixes to cotton fiber silk, polyester fiber yarn with bamboo fibre silk
Weaving；Wherein, nozzle of the specification for 75-40 is used when water-jet loom is drawn to cotton fiber silk, water-jet loom is to terylene
Nozzle of the specification for 75-40 is used when filament is drawn, specification is used when being drawn to bamboo fibre silk as 45-20
Nozzle.
As specific embodiment, more specifically embodiment is：Step（4）In, cotton fiber silk, polyester fiber yarn and bamboo
Filametntary ratio is 3:2:1.
This hair cotton fiber silk and bamboo fibre silk mixed textile technique are described in detail below by specific embodiment：
Embodiment 1
The present embodiment mixed textile technique, the mixed textile technique comprise the following steps：
（1）It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure bamboo fibre silk；
（2）Cotton fiber silk and polyester fiber yarn are placed in water steam box, 85 DEG C of water temperature, steamed 70 minutes；
（3）By step（2）Cotton fiber silk and polyester fiber yarn after processing are placed in pre-setting 16 hours under nature；
（4）Water-jet loom is used with step（1）Maximum pressure value comparative example is 3:2:1 cotton fiber silk, polyester fiber yarn and bamboo
Filament carries out mixed textile；Wherein, nozzle of the specification for 75-40 is used when water-jet loom is drawn to cotton fiber silk,
Nozzle of the specification for 45-20 is used when being drawn to bamboo fibre silk.
Embodiment 2
The present embodiment mixed textile technique, the mixed textile technique comprise the following steps：
（1）It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure bamboo fibre silk；
（2）Cotton fiber silk and polyester fiber yarn are placed in water steam box, 75 DEG C of water temperature, steamed 80 minutes；
（3）By step（2）Cotton fiber silk and polyester fiber yarn after processing are placed in pre-setting 12 hours under nature；
（4）Water-jet loom is used with step（1）Maximum pressure value comparative example is 3:2:1 cotton fiber silk, polyester fiber yarn and bamboo
Filament carries out mixed textile；Wherein, nozzle of the specification for 75-40 is used when water-jet loom is drawn to cotton fiber silk,
Nozzle of the specification for 45-20 is used when being drawn to bamboo fibre silk.
Embodiment 3
The present embodiment mixed textile technique, the mixed textile technique comprise the following steps：
（1）It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure bamboo fibre silk；
（2）Cotton fiber silk and polyester fiber yarn are placed in water steam box, 80 DEG C of water temperature, steamed 75 minutes；
（3）By step（2）Cotton fiber silk and polyester fiber yarn after processing are placed in pre-setting 14 hours under nature；
（4）Water-jet loom is used with step（1）Maximum pressure value comparative example is 3:2:1 cotton fiber silk, polyester fiber yarn and bamboo
Filament carries out mixed textile；Wherein, nozzle of the specification for 75-40 is used when water-jet loom is drawn to cotton fiber silk,
Nozzle of the specification for 45-20 is used when being drawn to bamboo fibre silk.
Described in comprehensive embodiment 1-3, relative to the existing mixed textile technique of this enterprise, the technique after being improved using the present invention
Every hundred meters can significantly be reduced it is made into product and the quantity of blind occur, specifically, every hundred meters is made into product and can go out before improvement
Existing 40 or so blind, and 2 even less blinds generally only occur after improving.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The skill of the industry
For art personnel it should be appreciated that the present invention is not limited to the above embodiments, described in above-described embodiment and specification is explanation
The principle of the present invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these
Changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and
Its equivalent thereof.
Claims (2)
- A kind of 1. mixed textile technique, it is characterised in that：The mixed textile technique comprises the following steps：（1）It is stretchable to greatest extent i.e. to maximum pressure value that it can apply to measure bamboo fibre silk；（2）Cotton fiber silk and polyester fiber yarn are placed in water steam box, 75~85 DEG C of water temperature, steamed 70~80 minutes；（3）By step（2）Cotton fiber silk and polyester fiber yarn after processing are placed in pre-setting 12~16 hours under nature；（4）Water-jet loom is used with step（1）Maximum pressure value mixes to cotton fiber silk, polyester fiber yarn with bamboo fibre silk Weaving；Wherein, nozzle of the specification for 75-40 is used when water-jet loom is drawn to cotton fiber silk, water-jet loom is to terylene Nozzle of the specification for 75-40 is used when filament is drawn, specification is used when being drawn to bamboo fibre silk as 45-20 Nozzle.
- 2. cotton fiber silk according to claim 1 and bamboo fibre silk mixed textile technique, it is characterised in that：The step （4）In, the ratio of cotton fiber silk, polyester fiber yarn and bamboo fibre silk is 3:2:1.