CN109776810A - 一种高分子乳化剂的制备方法 - Google Patents
一种高分子乳化剂的制备方法 Download PDFInfo
- Publication number
- CN109776810A CN109776810A CN201711102937.XA CN201711102937A CN109776810A CN 109776810 A CN109776810 A CN 109776810A CN 201711102937 A CN201711102937 A CN 201711102937A CN 109776810 A CN109776810 A CN 109776810A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- macromolecule emulsifier
- fatty alcohol
- polyoxyethylene ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明属于化工助剂加工领域,具体涉及一种高分子乳化剂。一种高分子乳化剂及其制备方法,包括如下步骤:1)、将聚异丁烯丁二酸酐20‑40份,脂肪醇聚氧乙烯醚20‑40份在20‑30摄氏度450nm光照下进行酯化反应;2)、将得到的聚异丁烯丁二酸脂肪醇聚氧乙烯醚酯的在200‑300摄氏度下与15‑25份过硫酸铵和20‑40份的氢氧化钠进行反应得到初步乳化剂;3)、将步骤2)中得到的初步乳化剂中加入交联剂和消泡剂。本发明所产品性质稳定,而且反应条件简单,能耗较少,绿色环保。
Description
技术领域
本发明属于化工助剂加工领域,具体涉及一种高分子乳化剂的制备方法。
背景技术
乳化剂一般分为3种:传统的小分子乳化剂、反应型乳化剂和高分子乳化剂。传统的小分子乳化剂会带入最终的产品,在乳液成膜的过程迁移到膜的表面,降低涂膜的光泽度和耐水性能。反应型乳化剂虽然能避免或克服小分子乳化剂的缺陷,却在一定程度上增大了乳液的黏度和粒径,使得体系的稳定性降低。由于高分子乳化剂的结构和水性上光油的结构基本相同,从而极大地提高了高分子乳化剂与水性上光油的相容性,降低了乳液粒径,增大了成膜光泽度。
发明内容
本发明研究开发了一种高分子乳化剂,目的在于:提供一种绿色环保的软化剂。
本发技术方案:
一种高分子乳化剂的制备方法,包括如下步骤:
1)、将聚异丁烯丁二酸酐20-40份,脂肪醇聚氧乙烯醚20-40份在20-30摄氏度450nm光
照下进行酯化反应;
2)、将得到的聚异丁烯丁二酸脂肪醇聚氧乙烯醚酯的在200-300摄氏度下与15-25份过硫
酸铵和20-40份的氢氧化钠进行反应得到初步乳化剂;
3)、将步骤2)中得到的初步乳化剂中加入交联剂和消泡剂。
优选的,所述步骤1)中聚异丁烯丁二酸酐为30份,脂肪醇聚氧乙烯醚30份。
优选的,所述步骤2)中过硫酸铵为20份,氢氧化钠为30份。
优选的,所述步骤3)中交联剂主要成分为三亚乙基四胺、二甲胺基丙胺及二乙胺基丙胺任意一项及其组合物。
优选的,所述步骤3)中消泡剂主要成分为有机硅氧烷。
本发明的有益效果是:
本发明所产品性质稳定,而且反应条件简单,能耗较少,绿色环保,原料来源充足,具有生产成本低,操作弹性大,生产工艺比较容易实现等特点。
具体实施方式
下面结合实施例对本发明进行进一步描述。
实施例一:
一种高分子乳化剂的制备方法,包括如下步骤:
1)、将聚异丁烯丁二酸酐20份,脂肪醇聚氧乙烯醚20份在20摄氏度450nm光照下进行
酯化反应;
2)、将得到的聚异丁烯丁二酸脂肪醇聚氧乙烯醚酯的在200摄氏度下与15份过硫酸铵和20份的氢氧化钠进行反应得到初步乳化剂;
3)、将步骤2)中得到的初步乳化剂中加入交联剂和有机硅氧烷消泡剂。
实施例二:
一种高分子乳化剂的制备方法,包括如下步骤:
1)、将聚异丁烯丁二酸酐40份,脂肪醇聚氧乙烯醚40份在30摄氏度450nm光照下进行
酯化反应;
2)、将得到的聚异丁烯丁二酸脂肪醇聚氧乙烯醚酯的在300摄氏度下与25份过硫酸铵和40份的氢氧化钠进行反应得到初步乳化剂;
3)、将步骤2)中得到的初步乳化剂中加入交联剂和有机硅氧烷消泡剂。
实施例三:
一种高分子乳化剂的制备方法,包括如下步骤:
1)、将聚异丁烯丁二酸酐30份,脂肪醇聚氧乙烯醚30份在25摄氏度450nm光照下进行
酯化反应;
2)、将得到的聚异丁烯丁二酸脂肪醇聚氧乙烯醚酯的在250摄氏度下与18份过硫酸铵和20份的氢氧化钠进行反应得到初步乳化剂;
3)、将步骤2)中得到的初步乳化剂中加入交联剂和有机硅氧烷消泡剂。
各实施例中交联剂主要成分为三亚乙基四胺、二甲胺基丙胺及二乙胺基丙胺任意一项或其组合物。
Claims (5)
1.一种高分子乳化剂的制备方法,其特征在于,包括如下步骤:
1)、将聚异丁烯丁二酸酐20-40份,脂肪醇聚氧乙烯醚20-40份在20-30摄氏度450nm光照下进行酯化反应;
2)、将得到的聚异丁烯丁二酸脂肪醇聚氧乙烯醚酯的在200-300摄氏度下与15-25份过硫酸铵和20-40份的氢氧化钠进行反应得到初步乳化剂;
3)、将步骤2)中得到的初步乳化剂中加入交联剂和消泡剂。
2.根据权利要求1所述的一种高分子乳化剂的制备方法,其特征在于:所述步骤1)中聚异丁烯丁二酸酐为30份,脂肪醇聚氧乙烯醚30份。
3.根据权利要求1所述的一种高分子乳化剂的制备方法,其特征在于:所述步骤2)中过硫酸铵为20份,氢氧化钠为30份。
4.根据权利要求1所述的一种高分子乳化剂的制备方法,其特征在于:所述步骤3)中交联剂主要成分为三亚乙基四胺、二甲胺基丙胺及二乙胺基丙胺任意一项及其组合物。
5.根据权利要求1所述的一种高分子乳化剂的制备方法,其特征在于:所述步骤3)中消泡剂主要成分为有机硅氧烷。