CN109776030A - The solid extraordinary slurry in copolymerization ground - Google Patents
The solid extraordinary slurry in copolymerization ground Download PDFInfo
- Publication number
- CN109776030A CN109776030A CN201711119245.6A CN201711119245A CN109776030A CN 109776030 A CN109776030 A CN 109776030A CN 201711119245 A CN201711119245 A CN 201711119245A CN 109776030 A CN109776030 A CN 109776030A
- Authority
- CN
- China
- Prior art keywords
- copolymerization
- ground
- solid
- slurry
- extraordinary
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of the present invention relates to copolymerization solid extraordinary slurry.The invention discloses it is a kind of mixed by special cement, selected aggregate and multiple additives with water after be added a kind of mobility for being formed of curing agent by force, the Self-leveling foundation material of high-ductility, compression strength, caking property, crack resistance and waterproofness with higher；It can be repaired in industry and the civilian surface of concrete buildings to have cracked, or be repaired in the industrial civil building for having damaged and not being able to satisfy design requirement；And the advantages of present invention incorporates the various patching materials in China and foreign countries, and it innovates and can be used on asphalt road, not only there is intensity and increase flexibility, product is set to attain a yet higher goal, the results showed data: water-fast, waterproof, intensity are high, flexibility is big, construction is simple, economic cost is low, utilization rate is high, not only using on cement pavement can also be in asphalt road, epoxide terrace, cement pavement, underground garage, can be used, this product is at low cost be not it is most important, most importantly fastly, can open within summer 2 hours and be open to traffic, it is fast, I will also be faster.
Description
Technical field
The present invention relates to building material technical fields, the more particularly to solid extraordinary slurry in copolymerization ground.
Background technique
Caused structural failure or building function failure is not only affecting people just due to various reasons for the world today
It often lives and causes huge economic loss, all the repairing for building of 40% or more of industrially developed country's total investment for construction
It mends and reinforces, the construction of new building is just used for less than 60%.It is badly damaged in the bridge that the U.S. has 40%, and in China 55%
The breakage on cement concrete pavement of left and right, it is clear that facility will have been damaged and replaced or build again completely, this is economically
Infeasible, solution is only repaired.
The U.S., Japan and other countries generally use the cement mortar for mixing polymer and the oil based on synthetic polymer and tar
Grey clay carries out repairing of the road surface compared with wide seam.In the U.S., mending mortar is chiefly used in bridge, deck surface and repairing work.Day
This has just been in leading position in construction industry early in the seventies, polymer modification mending mortar and resin mending mortar, applies
In the structural material of decorative cover and repairing work.American strategy develops the requirement that concrete repair and protection are answered by the committee, for branch
The strategic demand of Concrete Industry is held, Vision2020 has been set up in promotion.The purpose of Vision2020 is to improve concrete and repairing
Mend and protection working efficiency, safety and quality and determination a target, improve the design and performance of patching material, manufacture
Consistent mending mortar in performance and Practical Project out.
It can be seen that American Architecture industry has been included in industry development planning to the research of concrete repair mortar, to mending mortar
Research is quite paid attention to.Early in the sixties in last century, China has just had begun concrete and cement products repairing material
The research of material and work is applied, but since the quantity of concrete construction at that time and cement products is few, and service life is shorter,
Dosage is little, only in some applications such as concrete for hydraulic structure, bridge inspection and maintenance and cement tube factory, meanwhile, it is former by may be selected at that time
The limitation of material, kind and type are also seldom.Now, surging due to concrete construction and cement products usage quantity, and
The raising that people realize structural quality, so that the research and application of mending mortar have obtained developing on a large scale very much.Mending mortar
Using concrete destruction reparation simple from the past, develop the reinforcement and strengthening for concrete structure and cement products；Concrete
The maintenance of structure and cement products and raising durability；Newly, the crack repairing of old concrete；Concrete structure is impervious moisture-proof to be repaired
It mends；The corrosion-resistant repairing of concrete and cement products；The various aspects such as the wear-resisting repairing of road concrete.
However currently, the country such as Europe has formulated the relevant criterion of mending mortar, but there are no unified so far for the country
Test and evaluation method and standard, affect the development and market stability of mending mortar at home.
Therefore, how to provide a kind of has that construction is simple, convenient and efficient, mobility is strong, has wide range of applications, using safe
Consolidate to the copolymerization of feature the problem of extraordinary slurry is those skilled in the art's urgent need to resolve.
Summary of the invention
In view of this, the present invention provides one kind have construction is simple, convenient and efficient, mobility are strong, have wide range of applications,
Use the solid extraordinary slurry in copolymerization ground of safety feature.
To achieve the above object, the invention provides the following technical scheme:
The solid extraordinary slurry in copolymerization ground, comprising: the solid extraordinary slurry in copolymerization ground is by aluminate cement, special cement, quartz
Poly- third fiber of sand, magnesia, cellulose, VE5044N, tension, etc. various active masterbatch additives mix with water after addition solidify
Dosage form at a kind of mobility is strong, Self-leveling foundation material of high-ductility；It is characterized by further comprising: the copolymerization ground Gu Te
Kind slurry is divided into the sl-001 type packed using 20 liters of plastic barrels and using the SL-002 type of ox-hide compound paper bag packaging.
Preferably, one-storey house, building roof Specific construction technique: in a kind of above-mentioned copolymerization are directed in solid extraordinary slurry
And the reparation on cement concrete ground: (1) ground refuse is cleared up；(2) sand of dust and floating is rinsed using floor surface washing machine
Stone；(3) it is sprayed one time after dry using sl-001, making sure to keep in mind must be uniformly；(4) start to plug with molten metal special type with pouring the copolymerization after dry
Slurry, when flow coat, are closed flat using bull float, are poured completion using brokenly bubble roller and are carried out brokenly bubble processing.
Preferably, in a kind of above-mentioned copolymerization in solid extraordinary slurry, the brokenly bubble roller also waits being copolymerized at upward slope descending
Ground is pluged with molten metal in the case that extraordinary slurry less parches, and is embossed processing using the brokenly bubble roller, be can be increased antiskid function.
Preferably, it in a kind of above-mentioned copolymerization Specific construction technique: is directed to flagstone pavement in solid extraordinary slurry: (1) preparing
Good impact drill, carry out at the slabstone of loosening the punching of most depression, general every 60 centimeters make a call to one；(2) stirring copolymerization special type is pluged with molten metal
Slurry, making sure to keep in mind can not be too thick, diluter as far as possible；(3) slip casting machine is used, carrying out slip casting stone material envelope pulp is standard, without maintenance
Driving can be opened within 12 hours.
Preferably, Specific construction technique: level crossing road surface in a kind of above-mentioned copolymerization is directed to: (1) in solid extraordinary slurry
Clear up pavement garbage；(2) sandstone of dust and floating are rinsed using cleaner for road surface；(3) it is sprayed after dry using three happy sl-002
It applies one time, makes sure to keep in mind must to spray uniform (4) and starts to plug with molten metal extraordinary slurry with pouring copolymerization after dry, when flow coat is received using bull float
It is flat, completion, which is poured, using brokenly bubble roller carries out brokenly bubble processing.
It can be seen via above technical scheme that compared with prior art, the invention has the characteristics that:
1, construction is simple, convenient and efficient；Add suitable water that can form proximate freedom fluid slurry, can rapid deployment and obtain
Obtain high-flatness terrace；
2, wear-resisting, durable, economical, environmentally friendly (industrial to have a small amount of pollution, household type without)；
3, excellent mobility, the levelling ground of automatic and accurate；
4, people's walking can be gone up after 3-4 hours；Light-duty traffic can be opened after 24 hours；
5, do not increase absolute altitude, ground floor is 5-15 millimeters thin, saves material, reduces cost；
6, good caking property, smooth, not hollowing；
7, the essence for being widely used in civilian, commercial flooring is levelling；
8, harmless, radiationless；
9, speed of application is fast, and economic benefit is big, more traditional artificial levelling 5-10 times high, and in a short time i.e. for logical
Row, loading, substantially shorten the construction period；
10, ready mix product, uniform quality are stablized, and it is environmentally protective production that construction site neat and tidy, which is conducive to civilized construction,
Product；
11, resist getting damp property good, it is strong to surface layer protectiveness, it is practical, it is applied widely.
Specific embodiment
Below in conjunction in the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
The embodiment of the invention discloses a kind of with construction is simple, convenient and efficient, mobility is strong, has wide range of applications, makes
With the copolymerization of safety feature solid extraordinary slurry.
With please referring to a kind of copolymerization disclosed by the invention solid extraordinary slurry, specifically includes:
The solid extraordinary slurry in copolymerization ground is by aluminate cement, special cement, quartz sand, magnesia, cellulose, VE5044N, anti-
Draw poly- third fiber, etc. various active masterbatch additives mix with water after be added a kind of mobility of curing agent formation by force, high-ductility
Self-leveling foundation material；It is packed it is characterized by further comprising: the solid extraordinary slurry in copolymerization ground is divided into using 20 liters of plastic barrels
Sl-001 type and using ox-hide compound paper bag packaging SL-002 type.
The present invention can be used as following purposes:
1, as ground reparation, concrete dusting, uneven, epoxide terrace, polyurethane floor, PVC roll material, sheet material,
The high flat surfaces of the veneer materials such as rubber floor covering, solid wooden floor board, adamantine plate.
2, be the paving of modern hospital mute dustproof terrace PVC roll material must with flat surfaces material.
3, the basal planes such as food factory, drug factory, the toilet of precise electronic factory, dustless terrace, hardening terrace, antistatic terrace
Layer.
4, the polyurethane elastic terrace foundation base in kindergarten, tennis court etc..
5, as industrial premises acid and alkali-resistance terrace, abrasion-proof terrace foundation base.
6, robot track surface layer.
7, the flat surfaces of household terrace finishing.
8, the one leveling of various wide area spaces.As airport hall, grand hotel, hypermarket, department store, conference hall,
High smooth terrace can be rapidly completed in exhibition center, big office, parking lot etc..
In order to further optimize the above technical scheme, it is mixed that one-storey house, building roof and cement Specific construction technique: are directed to
The reparation in solidifying soil face: (1) ground refuse is cleared up；(2) sandstone of dust and floating are rinsed using floor surface washing machine；(3) to dry
It is sprayed one time using sl-001 afterwards, making sure to keep in mind must be uniformly；(4) start to plug with molten metal extraordinary slurry, flow coat with pouring the copolymerization after dry
When be closed flat using bull float, pour completion using brokenly bubble roller carry out brokenly bubble processing.
In order to further optimize the above technical scheme, brokenly bubble roller also waits pluging with molten metal extraordinary slurry with being copolymerized not at upward slope descending
In the case where parching very much, it is embossed processing using the brokenly bubble roller, can be increased antiskid function.
In order to further optimize the above technical scheme, it Specific construction technique: is directed to asphalt road road surface: (1) clearing up road surface rubbish
Rubbish；(2) sandstone of dust and floating are rinsed using cleaner for road surface；(3) it is sprayed one time, is made sure to keep in mind necessary using sl-002 after dry
Uniformly；(4) start to plug with molten metal extraordinary slurry with pouring copolymerization after dry, when flow coat is closed flat using bull float, is poured completion and is used brokenly bubble
Roller carries out brokenly bubble processing.
In order to further optimize the above technical scheme, Specific construction technique: be directed to flagstone pavement: (1) be ready to impact drill,
Carry out at the slabstone of loosening the punching of most depression, general every 60 centimeters make a call to one；(2) extraordinary slurry is pluged with molten metal to stirring copolymerization, made sure to keep in mind
Can not be too thick, it is diluter as far as possible；(3) slip casting machine is used, carrying out slip casting stone material envelope pulp is standard, can be opened without conserving 12 hours
Clearance vehicle.
In order to further optimize the above technical scheme, it Specific construction technique: is directed to level crossing road surface: (1) clearing up road surface
Rubbish；(2) sandstone of dust and floating are rinsed using cleaner for road surface；(3) it is sprayed one time, is cut using three happy sl-002 after dry
Note must spray uniform (4) and start to plug with molten metal extraordinary slurry with pouring copolymerization after dry, and when flow coat is closed flat using bull float, pour completion
Brokenly bubble processing is carried out using brokenly bubble roller.
In order to further optimize the above technical scheme,
Each embodiment in this specification is described in a progressive manner, the highlights of each of the examples are with other
The difference of embodiment, the same or similar parts in each embodiment may refer to each other.For device disclosed in embodiment
For, since it is corresponded to the methods disclosed in the examples, so being described relatively simple, related place is said referring to method part
It is bright.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (6)
1. the solid extraordinary slurry in copolymerization ground, comprising: the solid special type slurry in copolymerization ground by aluminate cement, special cement, quartz sand,
Poly- third fiber of magnesia, cellulose, VE5044N, tension, etc. various active masterbatch additives mix with water after addition solidify dosage form
At a kind of mobility is strong, Self-leveling foundation material of high-ductility；It is characterized by further comprising: the solid spoelalty pulp in copolymerization ground
Material is divided into the sl-001 type packed using 20 liters of plastic barrels and using the SL-002 type of ox-hide compound paper bag packaging.
2. the solid extraordinary slurry in copolymerization according to claim 1 ground, which is characterized in that Specific construction technique: be directed to one-storey house,
The reparation on building roof and cement concrete ground: (1) ground refuse is cleared up；(2) using floor surface washing machine rinse dust and
The sandstone of floating；(3) it is sprayed one time after dry using sl-001, making sure to keep in mind must be uniformly；(4) start to pour the copolymerization after dry
Extraordinary slurry is pluged with molten metal on ground, and when flow coat is closed flat using bull float, is poured completion using brokenly bubble roller and is carried out brokenly bubble processing.
3. the solid extraordinary slurry in copolymerization ground according to claim 2, which is characterized in that the brokenly bubble roller is also in upward slope descending
Place wait be copolymerized is pluged with molten metal in the case that extraordinary slurry less parches, and is embossed processing using the brokenly bubble roller, be can be increased anti-
Sliding function.
4. the solid extraordinary slurry in copolymerization ground according to claim 1, which is characterized in that Specific construction technique: be directed to asphalt road
Road surface: (1) pavement garbage is cleared up；(2) sandstone of dust and floating are rinsed using cleaner for road surface；(3) sl- is used after dry
002 spraying one time, making sure to keep in mind must be uniformly；(4) start to plug with molten metal extraordinary slurry with pouring copolymerization after dry, when flow coat is received using bull float
It is flat, completion, which is poured, using brokenly bubble roller carries out brokenly bubble processing.
5. the solid extraordinary slurry in copolymerization ground according to claim 1, which is characterized in that Specific construction technique: be directed to flagstone path
Face: (1) get out impact drill, carry out at the slabstone of loosening the punching of most depression, general every 60 centimeters make a call to one；(2) stirring is total
Extraordinary slurry is pluged with molten metal poly-ly, and making sure to keep in mind can not be too thick, diluter as far as possible；(3) slip casting machine is used, carrying out slip casting stone material envelope pulp is mark
Standard can open driving without conserving 12 hours.
6. the solid extraordinary slurry in copolymerization ground according to claim 1, which is characterized in that Specific construction technique: be directed to railway road
Mouth road surface: (1) pavement garbage is cleared up；(2) sandstone of dust and floating are rinsed using cleaner for road surface；(3) three are used after dry
Happy sl-002 is sprayed one time, and uniform (4) must be sprayed by, which making sure to keep in mind, starts to plug with molten metal extraordinary slurry with pouring copolymerization after dry, and when flow coat uses
Bull float is closed flat, and is poured completion using brokenly bubble roller and is carried out brokenly bubble processing.