CN109750490A - 一种基于化纤成型段的皮层导电化处理方法 - Google Patents
一种基于化纤成型段的皮层导电化处理方法 Download PDFInfo
- Publication number
- CN109750490A CN109750490A CN201811503565.6A CN201811503565A CN109750490A CN 109750490 A CN109750490 A CN 109750490A CN 201811503565 A CN201811503565 A CN 201811503565A CN 109750490 A CN109750490 A CN 109750490A
- Authority
- CN
- China
- Prior art keywords
- chemical fibre
- carbon nanotube
- chemical
- fibre
- cortex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种基于化纤成型段的皮层导电化处理方法，其主要步骤为：a、在化纤喷丝板下方极近的位置形成碳纳米管气凝胶，b、将刚附着碳纳米管的化纤进行声波处理，c、将经过碳纳米管气凝胶和声波处理后的化纤牵伸；本发明对增强化纤导电性性效果好且性能稳定，而且用料少，方法简单，控制方便。
Description
技术领域
本发明涉及一种基于化纤成型段的皮层导电化处理方法，属于纺织材料导电处理技术领域。
背景技术
化纤是化学纤维的简称，是用天然的或人工合成的高分子物质为原料、经过化学或物理方法加工而制得的纤维的统称。在生产化纤的过程中，化纤特别容易受到静电干扰，而静电在生产过程中又是无处不在，这样就特别容易导致化纤的起毛，还会吸附尘埃形成污垢，电荷的吸引或排斥还会加大加工的难度。静电摩擦还容易起火，起火后没有及时的救火可能造成重大的安全事故。因此，需要对化纤进行防静电处理，改善化纤的抗静电性能，提高化纤的品质。
中国实用新型专利CN201720578385提供了一种化纤防静电处理装置，将抗静电药剂均匀涂抹在化纤上，从而降低化纤表面电阻，防静电高效持久，消除化纤表面吸尘问题，该种装置虽能增强化纤的导电性，但是存在浪费现象且药剂只存在于化纤表面，产生了成本较高和性能稳定性较差的问题。
中国发明专利CN201510963821提供了一种碳纳米管分散方法，可以在节省碳纳米管用料的前提下，将化纤与碳纳米管结合，使化纤具有良好的导电性。
声波会引起化纤振动，从而使碳纳米管与化纤的结合更加紧密。
牵伸可以使残留在每根纤维内部的横向联系有可能被彻底消除，为牢固地建立有规律的首尾衔接关系创造条件，有助于碳纳米管在化纤表面形成导电网络，增强化纤的导电性。
发明内容
本发明的目的在于针对上述问题，提供一种可以高效快捷地增强化纤导电性的基于化纤成型段的皮层导电化处理方法。
本发明为实现上述目的，采用以下技术方案：
a、在化纤喷丝板下方极近的位置形成碳纳米管气凝胶；
b、将刚附着碳纳米管的化纤进行声波处理；
c、将经过碳纳米管气凝胶和声波处理后的化纤牵伸。
本发明所述步骤a中形成碳纳米管气凝胶的方法为碳纳米管气相分散。
本发明所述步骤b中的声波处理所使用的声源环绕化学纤维一圈。
本发明所述声源等角度分布。
本发明所述声源的数量为1-100。
本发明所述声源与化学纤维的距离为0.1-10m。
本发明所述声源的频率为0-10GHz。
本发明所述步骤c中化纤的牵伸倍数为1-400。
本发明所述化纤的牵伸速度为0-10m/s。
本发明的有益效果是，提供了一种简便高效地增强化纤导电性的基于化纤成型段的皮层导电化处理方法。本发明对增强化纤导电性性效果好且性能稳定，而且用料少，方法简单，控制方便。
附图说明
图1是本发明的流程图。
具体实施方式
下面结合附图对本发明进一步说明具体的实施方法：
如附图所示，本发明提供了一种基于化纤成型段的皮层导电化处理方法。所述基于化纤成型段的皮层导电化处理方法包括步骤：
首先，使化纤喷丝板喷丝。其次，将三个声源环绕一圈等角度地安装在化纤喷丝板下方0.1米处，使声源与化纤的距离为0.1m。然后，利用中国发明专利CN201510963821提供的一种碳纳米管分散方法在化纤喷丝板下方0.05米处形成碳纳米管气凝胶。同时，打开声源开关，调整声源频率为25000Hz，将刚附着碳纳米管的化纤进行声波处理。同时，对经过碳纳米管气凝胶和声波处理后的化纤以0.1m/s的速度牵伸，使牵伸倍数约为200。由此，可以得到具有良好导电性的化纤。
Claims (1)
1.一种基于化纤成型段的皮层导电化处理方法，其特征在于包括以下内容：
a、在化纤喷丝板下方极近的位置形成碳纳米管气凝胶，
b、将刚附着碳纳米管的化纤进行声波处理，
c、将经过碳纳米管气凝胶和声波处理后的化纤牵伸；
步骤a中喷丝板下方极近的位置为0.01-0.1m，
步骤a中形成碳纳米管气凝胶的方法为碳纳米管气相分散，
步骤b中的声波处理所使用的声源环绕化学纤维一圈，
所述声源等角度分布，
所述声源的数量为1-100，
所述声源与化学纤维的距离为0.1-10m，
所述声源的频率为0-10GHz，
步骤c中化纤的牵伸倍数为1-400,
所述化纤的牵伸速度为0-10m/s。