CN109704633A - A method of producing porcelain tendre - Google Patents

A method of producing porcelain tendre Download PDF

Info

Publication number
CN109704633A
CN109704633A CN201811617372.3A CN201811617372A CN109704633A CN 109704633 A CN109704633 A CN 109704633A CN 201811617372 A CN201811617372 A CN 201811617372A CN 109704633 A CN109704633 A CN 109704633A
Authority
CN
China
Prior art keywords
powder
parts
product
total volume
porcelain tendre
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811617372.3A
Other languages
Chinese (zh)
Inventor
李永国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei Shanse New Material Technology Co Ltd
Original Assignee
Hubei Shanse New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hubei Shanse New Material Technology Co Ltd filed Critical Hubei Shanse New Material Technology Co Ltd
Priority to CN201811617372.3A priority Critical patent/CN109704633A/en
Publication of CN109704633A publication Critical patent/CN109704633A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of methods for producing porcelain tendre, the following steps are included: step 1: sorting, select high-quality laterite, carclazyte and black earth, natural stone-powder and miberal powder, high molecular polymer, nano material, the primary raw material of wood fiber and multifunctional assistant as production;Step 2: ingredient mixes the laterite, carclazyte and black earth of selection, and according to 55 parts of -56 parts of progress ingredients of total volume, then by natural stone-powder and miberal powder according to 10 parts of -15 parts of progress ingredients of total volume.The method of the production porcelain tendre, the combination of the modification soil and modified inorganic powder that use can improve the weatherability of product, under the weather conditions of high temperature and low temperature, using 50 years or more reachable, make that this product reaches the bridging property between certain density, gas permeability and strand, flexibility is attained by corresponding standard, electrically heated clean energy resource improves the performance of the various aspects of device, and degree to the automation of product and effect also promote 50 or more percent.

Description

A method of producing porcelain tendre
Technical field
The present invention relates to porcelain tendre technical field, specially a kind of method for producing porcelain tendre.
Background technique
Porcelain tendre is not real porcelain, nor ceramic tile, it is a kind of novel building decoration materials.Based on modified soil Raw material is wanted, there is building decoration face flexible with one kind made of special temperature control moulding system molding, baking, cross-linking radiation Material.Since at the beginning of being born, it has the appearance of ceramic tile, therefore is commonly called as porcelain tendre, later, with the development of technology, Ke Yifa Open up imitation stone, leather texture imitation, imitation wood etc., all to imagine, porcelain tendre can all be realized.
Novel wall material on the market, similar kind at present, inside the raw material used or some not environmentally Ingredient will appear after use: there are many quality and asks in the phenomenon that aging is too fast, waterproofness is poor, anti-alkali after construction, in engineering Topic.
Summary of the invention
The purpose of the present invention is to provide a kind of methods for producing porcelain tendre, to solve mentioned above in the background art ask Topic.
To achieve the above object, the invention provides the following technical scheme: a kind of method for producing porcelain tendre, including following step It is rapid:
Step 1: sorting selects high-quality laterite, carclazyte and black earth, natural stone-powder and miberal powder, high molecular polymer, nanometer The primary raw material of material, wood fiber and multifunctional assistant as production;
Step 2: ingredient mixes the laterite, carclazyte and black earth of selection, and according to 55 parts -56 parts of total volume Ingredient is carried out, then by high molecular polymer, receives natural stone-powder and miberal powder according to 10 parts of -15 parts of progress ingredients of total volume Rice material is according to 15 parts -25 parts of total volume, by wood fiber according to 2 parts of -4 parts of progress ingredients of total volume, by multifunctional assistant According to 0.5 part of -2 parts of progress ingredient of total volume;
Step 3: the mixture and natural stone-powder and miberal powder of laterite, carclazyte and black earth that ingredient is completed pass through multiple work Modified soil and modified inorganic powder is made in sequence;
Step 4: manufactured modified soil and modified inorganic powder are sufficiently mixed;
Step 5: wood fibre and multifunctional assistant is added in the mixture of modified soil and modified inorganic powder, then Wet stirring is carried out, realization is modified again;
Step 6: addition high molecular polymer, nano material to step 5 product in, then carry out again mixing stir It mixes;
Step 7: it matches the product mixed and launches from feed inlet to temperature control device, first pass through irradiation and the curve of equipment Temperature, the reticular structure and the most suitable range hole of tension for investigating molecule, can reach the best gas permeability of finished product, watertightness is passing through After excessively high low-temperature heat, product can generate the characteristic of self-crosslinking, and molecular chain structure will form netted, and have more this product Specific flexibility is best, adjusts using low temperature, cooling finished product out.
Preferably, the laterite is generally in maroon, have high-moisture percentage, low-density and intensity is higher, compressibility is lower The soil of characteristic, the carclazyte are canescence particle powder, have biggish specific surface area and Kong Rong, have special adsorption capacity And ion-exchange performance, there are stronger decoloring ability and activity, and the rear stability that decolourizes can be good, the black earth is with strong swollen The clayey soil of contracting and disturbance characteristic.
Preferably, the natural stone-powder be natural magnesium salt monoclinic system mineral admant by it is selected, by modern production The powder that is formed after technique processing grinding, main component are aqueous carbonic acid calcium, the miberal powder refer to by mined ore into Obtained feed powder after row crushing and processing.
Preferably, that be natural reproducible timber process the wood fibre by chemical treatment, Mechanical Method is organic Wadding fibrous substance.
Preferably, the multifunctional assistant is AMP-95 type auxiliary agent.
Compared with prior art, the beneficial effects of the present invention are: the method for the production porcelain tendre, the modification soil used and change Property inorganic powder combination can improve the weatherability of product, and under the weather conditions of high temperature and low temperature, using 50 years reachable More than, the nano material and plant fiber used can be such that this product reaches between certain density, gas permeability and strand Bridging property, flexibility be attained by corresponding standard, electrically heated clean energy resource improves the performance of the various aspects of device, and And degree to the automation of product and effect also promote 50 or more percent.
Detailed description of the invention
Fig. 1 is flow diagram of the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other Embodiment shall fall within the protection scope of the present invention.
Referring to Fig. 1, a kind of embodiment provided by the invention: a method of producing porcelain tendre, it is characterised in that: including with Lower step:
Step 1: sorting selects high-quality laterite, carclazyte and black earth, natural stone-powder and miberal powder, high molecular polymer, nanometer The primary raw material of material, wood fiber and multifunctional assistant as production;
Step 2: ingredient mixes the laterite, carclazyte and black earth of selection, and according to 55 parts -56 parts of total volume Ingredient is carried out, then by high molecular polymer, receives natural stone-powder and miberal powder according to 10 parts of -15 parts of progress ingredients of total volume Rice material is according to 15 parts -25 parts of total volume, by wood fiber according to 2 parts of -4 parts of progress ingredients of total volume, by multifunctional assistant According to 0.5 part of -2 parts of progress ingredient of total volume;
Step 3: the mixture and natural stone-powder and miberal powder of laterite, carclazyte and black earth that ingredient is completed pass through multiple work Modified soil and modified inorganic powder is made in sequence;
Step 4: manufactured modified soil and modified inorganic powder are sufficiently mixed;
Step 5: wood fibre and multifunctional assistant is added in the mixture of modified soil and modified inorganic powder, then Wet stirring is carried out, realization is modified again;
Step 6: addition high molecular polymer, nano material to step 5 product in, then carry out again mixing stir It mixes;
Step 7: it matches the product mixed and launches from feed inlet to temperature control device, first pass through irradiation and the curve of equipment Temperature, the reticular structure and the most suitable range hole of tension for investigating molecule, can reach the best gas permeability of finished product, watertightness is passing through After excessively high low-temperature heat, product can generate the characteristic of self-crosslinking, and molecular chain structure will form netted, and have more this product Specific flexibility is best, adjusts using low temperature, it is cooling go out finished product, laterite has high-moisture percentage, low close generally in maroon Degree and intensity is higher, soil of the lower characteristic of compressibility, carclazyte is canescence particle powder, has biggish specific surface area and hole Hold, there is special adsorption capacity and ion-exchange performance, there is stronger decoloring ability and activity, and the rear stability energy that decolourizes Good, black earth is the clayey soil for having strong breathing and disturbing characteristic, and natural stone-powder is natural magnesium salt monoclinic system mineral Admant by it is selected, by modern production process processing grinding after the powder that is formed, main component is aqueous carbonic acid calcium, and miberal powder refers to By obtained feed powder after mined ore progress crushing and processing, wood fibre is that natural reproducible timber passes through at chemistry Organic wadding fibrous substance that reason, Mechanical Method are processed, multifunctional assistant are AMP-95 type auxiliary agent.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.

Claims (5)

1. a kind of method for producing porcelain tendre, it is characterised in that: the following steps are included:
Step 1: sorting selects high-quality laterite, carclazyte and black earth, natural stone-powder and miberal powder, high molecular polymer, nano material, The primary raw material of wood fiber and multifunctional assistant as production;
Step 2: ingredient mixes the laterite, carclazyte and black earth of selection, and according to 55 parts of -56 parts of progress of total volume Ingredient, then by natural stone-powder and miberal powder according to 10 parts of -15 parts of progress ingredients of total volume, by high molecular polymer, nanometer material Material is according to 15 parts -25 parts of total volume, by wood fiber according to 2 parts of -4 parts of progress ingredients of total volume, by multifunctional assistant according to 0.5 part of -2 parts of progress ingredient of total volume;
Step 3: the mixture and natural stone-powder and miberal powder of laterite, carclazyte and black earth that ingredient is completed pass through multiple process system At modified soil and modified inorganic powder;
Step 4: manufactured modified soil and modified inorganic powder are sufficiently mixed;
Step 5: wood fibre and multifunctional assistant is added in the mixture of modified soil and modified inorganic powder, then carries out Wet stirring, realization are modified again;
Step 6: addition high molecular polymer, nano material to step 5 product in, be then mixed again;
Step 7: it matches the product mixed and launches from feed inlet to temperature control device, first pass through the irradiation and curve temperature of equipment The reticular structure and the most suitable range hole of tension of degree, investigation molecule, can reach the best gas permeability of finished product, watertightness is being passed through After high/low temperature heating, product can generate the characteristic of self-crosslinking, and molecular chain structure will form netted, and make this product with more spy Fixed flexibility is best, adjusts using low temperature, cooling finished product out.
2. a kind of method for producing porcelain tendre according to claim 1, it is characterised in that: the laterite generally in maroon, With high-moisture percentage, low-density and intensity is higher, soil of the lower characteristic of compressibility, the carclazyte is canescence particle powder, tool There are biggish specific surface area and Kong Rong, there is special adsorption capacity and ion-exchange performance, there is stronger decoloring ability and work Property, and the rear stability that decolourizes can be good, the black earth is the clayey soil for having strong breathing and disturbing characteristic.
3. a kind of method for producing porcelain tendre according to claim 1, it is characterised in that: the natural stone-powder is natural magnesium Salt monoclinic system mineral admant by it is selected, by modern production process processing grinding after the powder that is formed, main component be containing Aqueous carbonate calcium, the miberal powder refer to obtained feed powder after mined ore progress crushing and processing.
4. a kind of method for producing porcelain tendre according to claim 1, it is characterised in that: the wood fibre is naturally can be again Organic wadding fibrous substance that green wood is processed by chemical treatment, Mechanical Method.
5. a kind of method for producing porcelain tendre according to claim 1, it is characterised in that: the multifunctional assistant is AMP-95 Type auxiliary agent.
CN201811617372.3A 2018-12-28 2018-12-28 A method of producing porcelain tendre Pending CN109704633A (en)