CN109694533A - A kind of environmental protection flame retardant wall paper and its production technology - Google Patents
A kind of environmental protection flame retardant wall paper and its production technology Download PDFInfo
- Publication number
- CN109694533A CN109694533A CN201811609536.8A CN201811609536A CN109694533A CN 109694533 A CN109694533 A CN 109694533A CN 201811609536 A CN201811609536 A CN 201811609536A CN 109694533 A CN109694533 A CN 109694533A
- Authority
- CN
- China
- Prior art keywords
- cooling
- parts
- environmental protection
- wall paper
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection flame retardant wall paper and its production technology, the environmental protection flame retardant wall paper by following component by weight: 100 parts of PVC powder；30-56 parts of plasticizer；2 parts of epoxidized soybean oil；2.5-3.5 parts of stabilizer；30-50 parts of calcium carbonate；0.3-0.8 parts of processing aid；6.0-12.0 parts of titanium dioxide；0.1-2.0 parts of pigment；2.0-5.0 parts of fire retardant.The present invention can fire safety, energy loss can be greatlyd save, it is not mouldy, do not have peculiar smell, secondary pollution will not be generated.The decorative pattern that various color can be printed on outer layer forms decorative layer, and interior decoration aesthetic feeling is improved while reaching fire safety.
Description
Technical field
The invention belongs to wall paper fields, and in particular to a kind of environmental protection flame retardant wall paper and its production technology.
Background technique
Currently, people's lives level is greatly improved, beautiful to the interior decoration of study, work, amusement, inhabitation
It is required that also higher and higher；Previous people's paintbrush metope so that metope is completely beautiful, but is painted to contain and is largely harmful to the human body
Substance, in addition, the engineering of painting metope is complicated, and do not bear dirty, be also not easy to repair after dirty.To solve these problems, wallpaper
It is more and more common, liked by the numerous people masses, however a large amount of pollution can be generated in wallpaper manufacturing process, and viscous
A large amount of glue is needed when wallpaper, while indoor environment is polluted, and easily de- after wet weather, wallpaper moisture absorption
It falls, mildew, deforms, destroy the aesthetics of metope.Then, people begin to use fabric trim metope, and wall paper is often used in conduct
The material for decorating indoor wall, due to the strong absorptive of wall paper, airtight, the easy delamination on plastic-coated surface layer is mouldy to have peculiar smell, mutability
Color, decorative pattern alter color and dullness；Therefore, indoor decorative effect is significantly affected；Especially wall paper does not have anti-flammability, Yi Fa
It lights a fire calamity, has very big trouble and worry when in use to existing wall paper to people.
Summary of the invention
Goal of the invention: in order to solve the deficiencies in the prior art, the present invention provides a kind of environmental protection flame retardant wall paper and its productions
Technique.
Technical solution: a kind of environmental protection flame retardant wall paper, the environmental protection flame retardant wall paper is by following component group according to parts by weight
At:
As optimization: the fire retardant is antimony oxide or zinc borate system.
A kind of production technology of the environmental protection flame retardant wall paper according to, includes the following steps:
(1) it measures: by automatic metering system, required component accurate measurement in formula；
(2) it mixes: each component blanking to the high-speed mixer that metering is completed is mixed, in high-speed starting,
Fire retardant is put into and is mixed, time 260-320 second, 85 ± 5 DEG C of maximum temperature；
(3) cold mixing: the component for mixing completion is transported in low speed cold mixing machine, is stirred cooling, and Wen Du control makes≤55 DEG C；
(4) squeeze out: the component that cold mixing is completed is input to planetary extruder, and temperature is controlled at 140 DEG C -165 DEG C, and discharging is bright
At twisted shape clinker；
(5) filter: after connecing the sizing material that extruder comes, after 80 mesh, 80 mesh, two layers of filter screen at cylindric clinker
It conveys to pricking turbine, within the scope of 140 DEG C -165 DEG C of temperature；
(6) prick turbine: after the sizing material after filter is further plasticized, the sheet that is in line material directly transports host, temperature
Control is at 160 DEG C -165 DEG C；
(7) form: five-roller temperature from high to low, is followed successively by 186 DEG C -192 DEG C, 186 DEG C -192 from 1-5 roll temperature
DEG C, 185 DEG C -190 DEG C, 185 DEG C -188 DEG C, 130 DEG C -140 DEG C, speed ratio is adjusted at 1.1-1.3 times, is involved after molding by traction wheel
To cooling wheel；
(8) cooling and shaping: lead to cooling water or chilled water in cooling wheel, make shaped article cooling and shaping；
(9) batch packaging: for the product after cooling and shaping after coiling machine rolling into barrel-shape, it is qualified to examine through quality inspection personnel,
Metering packing waits delivering.
The utility model has the advantages that the present invention can fire safety, energy loss can be greatlyd save, it is not mouldy, do not have peculiar smell, will not
Generate secondary pollution.The decorative pattern that various color can be printed on outer layer forms decorative layer, is reaching fire safety
While improve interior decoration aesthetic feeling.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field
Personnel can better understand advantages and features of the invention, to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, those of ordinary skill in the art's every other implementation obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of environmental protection flame retardant wall paper, the environmental protection flame retardant wall paper by following component by weight:
The fire retardant is antimony oxide or zinc borate system.
A kind of production technology of the environmental protection flame retardant wall paper according to, includes the following steps:
(1) it measures: by automatic metering system, required component accurate measurement in formula；
(2) it mixes: each component blanking to the high-speed mixer that metering is completed is mixed, in high-speed starting,
Fire retardant is put into and is mixed, the time 260 seconds, 80 DEG C of maximum temperature；
(3) cold mixing: the component for mixing completion is transported in low speed cold mixing machine, is stirred cooling, and Wen Du control makes≤55 DEG C；
(4) squeeze out: the component that cold mixing is completed is input to planetary extruder, and temperature is controlled at 140 DEG C, and discharging light is at fried dough twist
Shape clinker；
(5) filter: after connecing the sizing material that extruder comes, after 80 mesh, 80 mesh, two layers of filter screen at cylindric clinker
Convey to prick turbine, 140 DEG C of temperature；
(6) prick turbine: after the sizing material after filter is further plasticized, the sheet that is in line material directly transports host, temperature
Control is at 160 DEG C；
(7) form: five-roller temperature from high to low, is followed successively by 186 DEG C, 186 DEG C, 185 DEG C, 185 from 1-5 roll temperature
DEG C, 130 DEG C, speed ratio 1.1 times adjust, involved by traction wheel to cooling wheel after molding；
(8) cooling and shaping: lead to cooling water or chilled water in cooling wheel, make shaped article cooling and shaping；
(9) batch packaging: for the product after cooling and shaping after coiling machine rolling into barrel-shape, it is qualified to examine through quality inspection personnel,
Metering packing waits delivering.
Embodiment 2
A kind of environmental protection flame retardant wall paper, the environmental protection flame retardant wall paper by following component by weight:
The fire retardant is antimony oxide or zinc borate system.
A kind of production technology of the environmental protection flame retardant wall paper according to, includes the following steps:
(1) it measures: by automatic metering system, required component accurate measurement in formula；
(2) it mixes: each component blanking to the high-speed mixer that metering is completed is mixed, in high-speed starting,
Fire retardant is put into and is mixed, the time 320 seconds, 90 DEG C of maximum temperature；
(3) cold mixing: the component for mixing completion is transported in low speed cold mixing machine, is stirred cooling, and Wen Du control makes≤55 DEG C；
(4) squeeze out: the component that cold mixing is completed is input to planetary extruder, and temperature is controlled at 165 DEG C, and discharging light is at fried dough twist
Shape clinker；
(5) filter: after connecing the sizing material that extruder comes, after 80 mesh, 80 mesh, two layers of filter screen at cylindric clinker
Convey to prick turbine, 165 DEG C of temperature；
(6) prick turbine: after the sizing material after filter is further plasticized, the sheet that is in line material directly transports host, temperature
Control is at 165 DEG C；
(7) form: five-roller temperature from high to low, is followed successively by 192 DEG C, 192 DEG C, 190 DEG C, 188 from 1-5 roll temperature
DEG C, 140 DEG C, speed ratio 1.3 times adjust, involved by traction wheel to cooling wheel after molding；
(8) cooling and shaping: lead to cooling water or chilled water in cooling wheel, make shaped article cooling and shaping；
(9) batch packaging: for the product after cooling and shaping after coiling machine rolling into barrel-shape, it is qualified to examine through quality inspection personnel,
Metering packing waits delivering.
Embodiment 3
A kind of environmental protection flame retardant wall paper, the environmental protection flame retardant wall paper by following component by weight:
The fire retardant is antimony oxide or zinc borate system.
A kind of production technology of the environmental protection flame retardant wall paper according to, includes the following steps:
(1) it measures: by automatic metering system, required component accurate measurement in formula；
(2) it mixes: each component blanking to the high-speed mixer that metering is completed is mixed, in high-speed starting,
Fire retardant is put into and is mixed, the time 290 seconds, 85 DEG C of maximum temperature；
(3) cold mixing: the component for mixing completion is transported in low speed cold mixing machine, is stirred cooling, and Wen Du control makes≤55 DEG C；
(4) squeeze out: the component that cold mixing is completed is input to planetary extruder, and temperature is controlled at 159 DEG C, and discharging light is at fried dough twist
Shape clinker；
(5) filter: after connecing the sizing material that extruder comes, after 80 mesh, 80 mesh, two layers of filter screen at cylindric clinker
It conveys to pricking turbine, within the scope of 157 DEG C of temperature；
(6) prick turbine: after the sizing material after filter is further plasticized, the sheet that is in line material directly transports host, temperature
Control is at 162 DEG C；
(7) form: five-roller temperature from high to low, is followed successively by 189 DEG C, 190 DEG C, 187 DEG C, 186 from 1-5 roll temperature
DEG C, 136 DEG C, speed ratio 1.2 times adjust, involved by traction wheel to cooling wheel after molding；
(8) cooling and shaping: lead to cooling water or chilled water in cooling wheel, make shaped article cooling and shaping；
(9) batch packaging: for the product after cooling and shaping after coiling machine rolling into barrel-shape, it is qualified to examine through quality inspection personnel,
Metering packing waits delivering.
The present invention can fire safety, energy loss can be greatlyd save, it is not mouldy, do not have peculiar smell, will not generate secondary
Pollution.The decorative pattern that various color can be printed on outer layer forms decorative layer, mentions while reaching fire safety
High interior decoration aesthetic feeling.
Claims (3)
1. a kind of environmental protection flame retardant wall paper, it is characterised in that: the environmental protection flame retardant wall paper is by following component group according to parts by weight
At:
2. environmental protection flame retardant wall paper according to claim 1, it is characterised in that: the fire retardant is antimony oxide or boron
Sour zinc system.
3. a kind of production technology of environmental protection flame retardant wall paper according to claim 1, characterized by the following steps:
(1) it measures: by automatic metering system, required component accurate measurement in formula；
(2) it mixes: each component blanking to the high-speed mixer that metering is completed being mixed, in high-speed starting, will be hindered
It fires agent investment to mix, time 260-320 second, 85 ± 5 DEG C of maximum temperature；
(3) cold mixing: the component for mixing completion is transported in low speed cold mixing machine, is stirred cooling, and Wen Du control makes≤55 DEG C；
(4) squeeze out: the component that cold mixing is completed is input to planetary extruder, and temperature is controlled at 140 DEG C -165 DEG C, and discharging light is at fiber crops
Flower-shaped clinker；
(5) filter: after connecing the sizing material that extruder comes, after 80 mesh, 80 mesh, two layers of filter screen at cylindric clinker conveyor
To pricking turbine, within the scope of 140 DEG C -165 DEG C of temperature；
(6) prick turbine: after the sizing material after filter is further plasticized, the sheet that is in line material directly transports host, temperature control
At 160 DEG C -165 DEG C；
(7) form: five-roller temperature from high to low, is followed successively by 186 DEG C -192 DEG C, 186 DEG C -192 DEG C, 185 from 1-5 roll temperature
DEG C -190 DEG C, 185 DEG C -188 DEG C, 130 DEG C -140 DEG C, speed ratio is adjusted at 1.1-1.3 times, is involved by traction wheel to cooling after molding
Wheel；
(8) cooling and shaping: lead to cooling water or chilled water in cooling wheel, make shaped article cooling and shaping；
(9) batch packaging: the product after cooling and shaping is after coiling machine rolling into barrel-shape, and it is qualified to examine through quality inspection personnel, metering
It packs wait deliver.