CN109628016A - 一种方便快速型补胎胶浆 - Google Patents
一种方便快速型补胎胶浆 Download PDFInfo
- Publication number
- CN109628016A CN109628016A CN201811497364.XA CN201811497364A CN109628016A CN 109628016 A CN109628016 A CN 109628016A CN 201811497364 A CN201811497364 A CN 201811497364A CN 109628016 A CN109628016 A CN 109628016A
- Authority
- CN
- China
- Prior art keywords
- rubber
- tire patching
- fast
- rubber cement
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及补胎胶浆技术领域,具体涉及一种方便快速型补胎胶浆,包括以下重量份的原料:橡胶30%‑55%、橡胶硫化剂5%‑10%、溶剂15%‑25%、防老剂0.2%‑0.45%、微晶蜡0.1%‑0.3%、玄武岩纤维4.5%‑5.5%。与现有技术相比,本发明具有如下的有益效果:本发明的补胎胶浆是一种应急使用的补胎产品,在轮胎被扎造成亏气,并且暂时没有维修条件时使用;优势在于简单快捷,不用更换备胎,也不用使用千斤顶,之后可以正常行驶至维修店;其操作简便,修补效果好,没有碎屑粘附,不会持久影响车辆动平衡。
Description
技术领域
本发明涉及补胎胶浆技术领域,具体涉及一种方便快速型补胎胶浆。
背景技术
随着社会高速发展,自行车已经逐渐远离人们的视野,摩托车因为其不安全性,也渐渐被人们抛弃,汽车安全舒适,移动速度快,已经成为当今社会的主流交通工具,但是人们对于轮胎补胎胶浆的认知,还停留在自行车轮胎胶水的层面上,认知较少,但是其快速补胎的实用性给补胎带来了很多的便利性。
目前的补胎胶浆全部通过气嘴灌入,且为流动液体长时间在轮胎内部会对轮毂造成腐蚀,同时影响车辆的动平衡,还会有一部分固化粘在轮胎和轮毂内壁上很难清理。
发明内容
本发明的目的在于提供一种方便快速型补胎胶浆,以解决上述背景技术中提出的问题。
为实现上述目的,本发明提供如下技术方案:
一种方便快速型补胎胶浆,包括以下重量份的原料:
橡胶30%-55%、橡胶硫化剂5%-10%、溶剂15%-25%、防老剂0.2%-0.45%、微晶蜡0.2%、玄武岩纤维4.5%-5.5%。
作为本发明的进一步技术方案是:包括以下重量份的原料:
橡胶40%、橡胶硫化剂7%、溶剂15%-25%、防老剂0.3%、微晶蜡0.2%、玄武岩纤维5.0%。
作为本发明的再进一步技术方案是:所述橡胶硫化剂为DTDM二硫代二吗啉。
作为本发明的再进一步技术方案是:所述防老剂为二苯胺的低级烷氧基化。
作为本发明的再进一步技术方案是:当橡胶为生胶时,其溶剂为烷烃溶剂,且重量份为20%-25%。
作为本发明的再进一步技术方案是:当橡胶为丁基橡胶时,其溶剂为四氯化碳,且重量份为15%-20%。
与现有技术相比,本发明具有如下的有益效果:本发明的补胎胶浆是一种应急使用的补胎产品,在轮胎被扎造成亏气,并且暂时没有维修条件时使用;优势在于简单快捷,不用更换备胎,也不用使用千斤顶,之后可以正常行驶至维修店;其操作简便,修补效果好,没有碎屑粘附,不会持久影响车辆动平衡。
具体实施方式
下面结合具体实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1:
本实施例的一种方便快速型补胎胶浆,包括以下重量份的原料:
橡胶30%、橡胶硫化剂5%、溶剂15%-25%、防老剂0.2%、微晶蜡0.2%、玄武岩纤维4.5%。
所述橡胶硫化剂为DTDM二硫代二吗啉。
所述防老剂为二苯胺的低级烷氧基化。
当橡胶为生胶时,其溶剂为烷烃溶剂,且重量份为20%-25%。
当橡胶为丁基橡胶时,其溶剂为四氯化碳,且重量份为15%-20%。
实施例2:
本实施例的一种方便快速型补胎胶浆,包括以下重量份的原料:
橡胶55%、橡胶硫化剂10%、溶剂15%-25%、防老剂0.45%、微晶蜡0.2%、玄武岩纤维5.5%。
所述橡胶硫化剂为DTDM二硫代二吗啉。
所述防老剂为二苯胺的低级烷氧基化。
当橡胶为生胶时,其溶剂为烷烃溶剂,且重量份为20%-25%。
当橡胶为丁基橡胶时,其溶剂为四氯化碳,且重量份为15%-20%。
实施例3:
本实施例的一种方便快速型补胎胶浆,包括以下重量份的原料:
橡胶40%、橡胶硫化剂7%、溶剂15%-25%、防老剂0.3%、微晶蜡0.2%、玄武岩纤维5.0%。
所述橡胶硫化剂为DTDM二硫代二吗啉。
所述防老剂为二苯胺的低级烷氧基化。
当橡胶为生胶时,其溶剂为烷烃溶剂,且重量份为20%-25%。
当橡胶为丁基橡胶时,其溶剂为四氯化碳,且重量份为15%-20%。
当橡胶制品因外伤产生新的胶面时,补胎胶浆中的微晶蜡可继续移到新的表面,形成新的保护薄膜,该微晶蜡与化学防老剂结合使用将产生良好的加乘作用,主要用于半钢、全钢子午线轮胎及各种橡胶制品;根据地区气候选择微晶蜡组分:气候比较寒冷地区使用要选用分子量大的微晶蜡;载重轮胎和气候较热地区使用要选用分子量大的微晶蜡。
通过向其中添加增强短切纤维可以强化其抗拉伸能力,添加量:以玄武岩纤维为例每公斤胶浆添加50g±5g为佳。
由于本品挥发性组分含量较高,应密封,阴凉保存。
本发明的补胎胶浆是一种应急使用的补胎产品,在轮胎被扎造成亏气,并且暂时没有维修条件时使用;优势在于简单快捷,不用更换备胎,也不用使用千斤顶,之后可以正常行驶至维修店;其操作简便,修补效果好,没有碎屑粘附,不会持久影响车辆动平衡。
补胎胶浆的质量要求:
补胎胶浆的好坏不但影响工艺操作,而且对轮胎修补质量起关键作用,特别是自然硫化的胶料,既要有良好的粘合性能,又要求能在低温下快速硫化,同时要求很高物性。补胎胶浆配方设计要点:胶料半成品流动性能要好,便于修补时滚压结实、光滑,所以生胶塑炼时控制在2~3段,同样成品、半成品的硬度要低些,有利于粘合,则硬炭黑等填料要少些,油量可多些,同时可增加一部分粘合剂,此外还要求耐曲挠、耐老化和抗撕裂。
本发明的使用范围是:
可修补轮胎:轮胎胎体骨架(帘布+钢丝圈),本要求允许可修补的轮胎指:位于轮胎骨架(帘布+钢丝圈)内外表面的胶层出现局部外观缺陷的轮胎。
禁止修补的缺陷有:
帘线、帘布层、钢丝圈不得断裂、走位、脱层、稀开和松散。
冠部中心花纹接地部位禁止进行需要补胶类修补(夹补、套模)。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (6)
1.一种方便快速型补胎胶浆,其特征在于,包括以下重量份的原料:
橡胶30%-55%、橡胶硫化剂5%-10%、溶剂溶剂15%-25%、防老剂0.2%-0.45%、微晶蜡0.2%、玄武岩纤维4.5%-5.5%。
2.根据权利要求1所述的方便快速型补胎胶浆,其特征在于,包括以下重量份的原料:
橡胶40%、橡胶硫化剂7%、溶剂15%-25%、防老剂0.3%、微晶蜡0.2%、玄武岩纤维5.0%。
3.根据权利要求2所述的方便快速型补胎胶浆,其特征在于,所述橡胶硫化剂为DTDM二硫代二吗啉。
4.根据权利要求2或3所述的方便快速型补胎胶浆,其特征在于,所述防老剂为二苯胺的低级烷氧基化。
5.根据权利要求1所述的方便快速型补胎胶浆,其特征在于,当橡胶为生胶时,其溶剂为烷烃溶剂,且重量份为20%-25%。
6.根据权利要求1所述的方便快速型补胎胶浆,其特征在于,当橡胶为丁基橡胶时,其溶剂为四氯化碳,且重量份为15%-20%。