CN109627750A - 耐高温无卤阻燃尼龙材料制作工艺 - Google Patents

耐高温无卤阻燃尼龙材料制作工艺 Download PDF

Info

Publication number
CN109627750A
CN109627750A CN201811517016.4A CN201811517016A CN109627750A CN 109627750 A CN109627750 A CN 109627750A CN 201811517016 A CN201811517016 A CN 201811517016A CN 109627750 A CN109627750 A CN 109627750A
Authority
CN
China
Prior art keywords
high temperature
retardant
temperature resistant
halogen
free flame
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811517016.4A
Other languages
English (en)
Inventor
孙平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Industrial Park Kechuang Rubber & Plastic Co Ltd
Original Assignee
Suzhou Industrial Park Kechuang Rubber & Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Industrial Park Kechuang Rubber & Plastic Co Ltd filed Critical Suzhou Industrial Park Kechuang Rubber & Plastic Co Ltd
Priority to CN201811517016.4A priority Critical patent/CN109627750A/zh
Publication of CN109627750A publication Critical patent/CN109627750A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种有机高分子复合材料，更具体地说，是涉及一种耐高温无卤阻燃尼龙材料制作工艺，是由以下成分按重量比组成，高温尼龙：60‑80％，溴系阻燃剂：5‑15％，无卤无碱玻纤：10‑20％；热稳定剂：0.1‑2.0％；抗氧化剂0.1‑2.0％；润滑剂：0.3‑1.0％,其他助剂：0.3‑5.5％。本发明的一种耐高温无卤阻燃尼龙材料制作工艺，将高阻燃性，高强度和高熔点能集于一身，这种材料可以耐200OC的持续高温，并且还能保持良好的尺寸稳定性，并具有良好的延展性与低翘曲，几乎所有尺寸不同、要求严格的应用领域都能使用。

Description

耐高温无卤阻燃尼龙材料制作工艺
技术领域
本发明涉及一种有机高分子复合材料，更具体地说，是涉及一种耐高温无卤阻燃尼龙材料制作工艺。本发明还涉及制作这种尼龙原料的方法。
背景技术
目前，RoHS法规促使业界在印刷电路板上进行连接器表面安装时，采用符合无铅规定的焊接工艺，由此对材料提出更高的耐温与环保要求，同时各种工业与民用的产品的差异化设计也对材料提出了能够耐受更加严酷环境仍然高度安全的要求，并且还要同时符合各种环保指令规定。同时产品的薄壁化和复杂结构又对材料的流动性提出极高要求。
本特种复合材料发明正是在这种背景下应运而生，将高阻燃性，高强度和高熔点能集于一身，这种材料可以耐200℃的持续高温，并且还能保持良好的尺寸稳定性，并具有良好的延展性与低翘曲，几乎所有尺寸不同、要求严格的应用领域都能使用。该产品充分符合欧盟“废旧电子电气设备”(WEEE)和“有害物质限用指令”(RoHS)法规以及PAHS等等环保要求。相比使用传统材料，该产品更加具有高端机械和电气性能，同时还有易加工、外形美观及激光打标等特点，并在潮湿环境下提供相同的强度和韧性卓越的耐化学性尺寸稳定性优异的电特性。与传统的尼龙6,66相比，其吸水量少70％，内膨胀系数低，与金属类似。
发明内容
本发明的目的在于有效的克服了现有尼龙的缺陷，提供一种具有高阻燃性、高强度和高熔点的耐高温无卤阻燃尼龙原料。
本发明提供的技术方案如下：一种耐高温无卤阻燃尼龙原料，是由以下成分按重量比组成：高温尼龙：60-80％，溴系阻燃剂：5-15％，；无卤无碱玻纤：10-20％；热稳定剂：0.1-2.0％；抗氧化剂0.1-2.0％；润滑剂：0.3-1.0％,其他助剂：0.3-5.5％。
本发明所述的耐高温无卤阻燃尼龙的制备方法，包括如下步骤：先将高温尼龙粒子用100度的温度烘烤4-5小时，然后与溴系阻燃剂按比例混合后在50度恒温条件下放置12小时，再及时与热稳定剂、抗氧化剂、润滑剂、其他助剂按照比例称量后在混料机中低速混合10分钟，再及时经双螺杆挤出机在中等强度剪切的螺杆组合情况下由侧面加入无卤无碱玻纤进行混炼挤出，水冷拉条切粒再经过筛分脱水制得一种耐高温无卤阻燃尼龙材料。
本发明有效的克服了现有尼龙的缺陷，具有以下优点：
本发明一种耐高温无卤阻燃尼龙将高阻燃性、高强度和高熔点能集于一身，这种材料可以耐200℃的持续高温，并且还能保持良好的尺寸稳定性，并具有良好的延展性与低翘曲，几乎所有尺寸不同、要求严格的应用领域都能使用，并且具有高端机械和电气性能，同时还有易加工、外形美观及激光打标等特点，并在潮湿环境下提供相同的强度和軔性卓越的耐化学性尺寸稳定性优异的电特性。与传统的尼龙6,66相比，其吸水量少70％，内膨胀系数低，与金属类似。
具体实施方式
以下是本发明所述的耐高温无卤阻燃尼龙的实施例，并不因此限定本发明的保护范围。
实施例一，提供一种耐高温无卤阻燃尼龙，是由以下成分按重量比组成：高温尼龙：60％，主阻燃剂：10％,辅助阻燃剂：5％；无卤无碱玻纤：15％；高流动助剂：4％；热稳定剂：2％，润滑剂：2％,其他助剂：2％。
本发明所述的耐高温无卤阻燃尼龙的制备方法，包括如下步骤：先将高温尼龙粒子用100度的温度烘烤4-5小时，然后与溴系阻燃剂按比例混合后在50度恒温条件下放置12小时，再及时与热稳定剂、抗氧化剂、润滑剂、其他助剂按照比例称量后在混料机中低速混合10分钟，再及时经双螺杆挤出机在中等强度剪切的螺杆组合情况下由侧面加入无卤无碱玻纤进行混炼挤出，水冷拉条切粒再经过筛分脱水制得一种耐高温无卤阻燃尼龙材料。

Claims (2)

1.一种耐高温无卤阻燃尼龙材料制作工艺，其特征在于：是由以下成分按重量比组成，高温尼龙：60-80％，溴系阻燃剂：5-15％，；无卤无碱玻纤：10-20％；热稳定剂：0.1-2.0％；抗氧化剂0.1-2.0％；润滑剂：0.3-1.0％,其他助剂：0.3-5.5％。
2.—种耐高温无卤阻燃尼龙材料制作工艺，其特征在于包括如下步骤：先将高温尼龙粒子用100度的温度烘烤4-5小时，然后与溴系阻燃剂按比例混合后在50度恒温条件下放置12小时，再及时与热稳定剂、抗氧化剂、润滑剂、其他助剂按照比例称量后在混料机中低速混合10分钟，再及时经双螺杆挤出机在中等强度剪切的螺杆组合情况下由侧面加入无卤无碱玻纤进行混炼挤出，水冷拉条切粒再经过筛分脱水制得一种耐高温无卤阻燃尼龙材料。
CN201811517016.4A 2018-12-12 2018-12-12 耐高温无卤阻燃尼龙材料制作工艺 Pending CN109627750A (zh)