CN109623095B - 一种用于高硬材料焊补的等温焊道方法 - Google Patents
一种用于高硬材料焊补的等温焊道方法 Download PDFInfo
- Publication number
- CN109623095B CN109623095B CN201910091469.3A CN201910091469A CN109623095B CN 109623095 B CN109623095 B CN 109623095B CN 201910091469 A CN201910091469 A CN 201910091469A CN 109623095 B CN109623095 B CN 109623095B
- Authority
- CN
- China
- Prior art keywords
- welding
- bead
- isothermal
- repair
- hardness material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种用于高硬材料焊补的等温焊道设计,具体的焊接步骤如下:用于高硬材料焊补的等温焊道设计,焊道基本形状为由内向外螺旋展开,相邻焊道搭接1/3至1/2;每个焊道在焊接过程中,头尾及中间部分温度基本一致;每个焊道停焊后,有1‑5秒的时间窗口用于热态锤击形变,获得细致的合金锻造组织并消除焊接拉应力。每个焊道区域为直径不超过50mm的圆形区域。本发明的有益效果是能够使裂纹敏感的高硬度母材(HRC55以上),在焊接过程不出现焊接引起的热裂纹,并提高焊补效率。特别适合上述特殊材质的磨损、掉肉、裂纹、断裂部位的焊补和修复。
Description
技术领域
本发明涉及一种用于高硬材料焊补的等温焊道方法,属于高硬材料焊补技术领域。
背景技术
冶金、电力、矿山、煤炭等大型设备的动力传输,大量采用各类减速机。大部分属于重载齿轮,基本上是齿轮合金钢锻压、热处理后加工而成,重量从几吨到几十吨不等,许多零件表面还经过渗碳、渗氮或碳氮共渗处理,硬度均在HRC55以上,具有极高的耐磨性,但是可焊性极差。由于承担巨大载荷,使用中除了磨损外,腐蚀、疲劳掉肉、异物咬入等时有发生,甚至出现裂纹、断裂,导致设备故障和恶性事故。由于部件精度高、价值昂贵、采购周期长,修复意义重大。但由于表面硬度极高(HRC55-65),材料几乎没有任何塑性变形能力,对焊接热输入、变形十分敏感,哪怕是一点点焊接,焊道收缩应力就会把母材拉裂,出现越焊越坏的结果。
众所周知,电弧焊接过程中,不论是焊条还是焊丝焊接操作,大都必须经过起弧、运条焊接、收弧停焊三个阶段,运条方式有直线运动、折线摆动、画圈摆动等手法,但是焊道基本都是一条直线或曲线。这在常规焊接中,有利于提高速度、排出焊渣和熔池杂质而被广泛应用。但是,这种焊道的温度场是一个不均匀的温度场,焊道头部和尾部的温差很大。尤其是焊道头部由于凝固收缩和焊道降温收缩,在焊道和相邻母材均产生较大的拉应力。当遇到母材或焊材塑性较差时,焊道还没停止,就会在母材和焊缝出现裂纹。常规处置经验就是缩短焊道长度,然后锤击。这种方法,对于表面经过渗碳、渗氮或碳氮共渗处理,硬度均在HRC55以上的母材,再短的焊道也不能保证不出现裂纹。
发明内容
本发明针对常规的焊接方法因为焊道收缩应力就会把母材拉裂,出现越焊越坏的结果,提供一种用于高硬材料焊补的等温焊道方法。
本发明解决上述技术问题的技术方案如下:
本发明涉及一种用于高硬材料焊补的等温焊道设计,其特殊之处在于,焊道基本形状为由内向外螺旋展开,相邻焊道搭接1/3至1/2。
在补焊的过程中,根据情况的不同,补焊操作的过程,进行如下相应的修改:
每个焊道在焊接过程中,头尾及中间部分温度基本一致。
每个焊道停焊后,有1-5秒的时间窗口用于热态锤击形变,获得细致的合金锻造组织并消除焊接拉应力。即,在一次焊接结束后,第二次焊接开始前,有1-5秒的间隔,这期间采用热态锤击形。
每个焊道区域为直径不超过50mm的圆形区域。
大面积补焊时,多个焊道区域先互相孤立,间隔约30mm,最后再逐次填补形成整个堆焊面。
等温焊道的焊接方法可以是手工电弧焊、二保焊、氩弧焊中任意一种电弧焊接。
本发明的有益效果是能够使裂纹敏感的高硬度母材(HRC55以上),特别是表面渗碳、渗氮、碳氮共渗的淬火面,在焊接过程不出现焊接引起的热裂纹,并提高焊补效率。特别适合上述特殊材质的磨损、掉肉、裂纹、断裂部位的焊补和修复。由于螺旋焊道的布置方式,焊道头部位于焊道区域中央,所有先焊部分均持续被后焊部分加热保温,形成整个焊道区域温度一致,维持在一个比母材高约500℃的状态,热膨胀差异足够抵消凝固收缩量,整个焊道和母材区域均呈现一个适度压应力的稳定状态,此时有足够的时间窗口,供采取焊道锤击变形锻造操作,直至焊道温度降至临近母材温度。整个操作过程焊缝及母材区域均是在适度压应力状态下进行,所以根本不会出现任何裂纹。而且,适度的压应力有利于提高零件修复表面的疲劳寿命。
附图说明
图1为单个等温焊道示意图;
图2为多个等温焊道相对位置示意图
图3为整个堆焊面示意图。
具体实施方式
以下结合附图对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
一种用于高硬材料焊补的等温焊道设计,具体的焊接步骤如下:用于高硬材料焊补的等温焊道设计,焊道基本形状为由内向外螺旋展开,相邻焊道搭接1/3至1/2;每个焊道在焊接过程中,头尾及中间部分温度基本一致;每个焊道停焊后,有1-5秒的时间窗口用于热态锤击形变,获得细致的合金锻造组织并消除焊接拉应力。每个焊道区域为直径不超过50mm的圆形区域。
大面积补焊时,多个焊道区域先互相孤立,间隔约30mm,最后再逐次填补形成整个堆焊面
所述的焊接方法为手工电弧焊、二保焊、氩弧焊中任意一种。
以下,以具体焊接过程为例,解释本申请的焊接方法,具体过程如下(如图1-3):
1)准备好待焊接表面,打磨清理干净。
2)采用与母材硬度相当的焊条,采用TIG焊,电流电压按焊材正常要求设置,起弧后按照顺时针或逆时针方向,由内向外螺旋围绕展开,焊道搭接1/3至1/2;过程观察整个焊接区域颜色均匀一致,不得出现中心发暗。红外测温仪测试焊道温度,不低于500℃。
3)当焊道区域直径达到30mm左右时停止焊接,立即用提前准备好的手锤或气锤,对焊缝强力锻打,充分变形,直至焊道温度与周边母材基本一致。
4)在距离上次焊道一定距离(至少50mm),开始第二个螺旋等温焊道焊接,重复步骤2)、3)。直至所有区域布满焊道,形成整个堆焊面。
5)正常遮盖缓冷。
6)打磨后进行探伤和硬度检测。
7)如有必要,在第一层上,按照1)-6)步骤,实施第二层焊接,直至需要厚度。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种用于高硬材料焊补的等温焊道方法,其特征在于,焊道基本形状为由内向外螺旋展开,相邻焊道搭接1/3至1/2;每个焊道在焊接过程中,头尾及中间部分温度基本一致;每个焊道停焊后,有1-5秒的时间窗口用于热态锤击形变,获得细致的合金锻造组织并消除焊接拉应力;每个焊道区域为直径不超过50mm的圆形区域。
2.根据权利要求1所述的用于高硬材料焊补的等温焊道方法,其特征在于,大面积补焊时,多个焊道区域先互相孤立,间隔约30mm,最后再逐次填补形成整个堆焊面。
3.根据权利要求1所述的用于高硬材料焊补的等温焊道方法,其特征在于,等温焊道的焊接方法可以是手工电弧焊、二保焊、氩弧焊中任意一种电弧焊接。