CN109594196A - The preparation method of antimicrobial form wall paper non-woven fabrics - Google Patents
The preparation method of antimicrobial form wall paper non-woven fabrics Download PDFInfo
- Publication number
- CN109594196A CN109594196A CN201811320502.7A CN201811320502A CN109594196A CN 109594196 A CN109594196 A CN 109594196A CN 201811320502 A CN201811320502 A CN 201811320502A CN 109594196 A CN109594196 A CN 109594196A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- polymer
- preparation
- wall paper
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of antimicrobial form wall paper non-woven fabrics, comprising the following steps: S1: by the mixture of fine fibre polymer and binder fibre by big screw at high temp melting extrusion, heating temperature is 260~280 DEG C, obtains the polymer A of molten condition;S2: the stretched device of spinneret is stretched through extruder with 4.8~5.3MPa pressurization spinneret by polymer A, fiber draw object B is formed, and guide and carry out 4~8h of immersion into soak, is then directed on lapper;S3: when three layers or four layers of fiber draw object B is laminated on lapper, guiding sandwich hot rolling into hot-rolling mill, and resin-oatmeal is uniformly sprayed on fiber draw object surface when hot rolling, and hot-rolled condition is 160~180 DEG C, 4MPa, obtains non-woven fabrics, coiling and molding.On the basis of guaranteeing tough, have antibacterial ability, is particularly suitable for family that is moist or having infant and uses.
Description
Technical field
The present invention relates to non-woven fabrics preparation fields, and in particular to a kind of preparation method of antimicrobial form wall paper non-woven fabrics.
Background technique
Non-woven fabrics is a kind of non-woven cloth, it is that fiber is directly passed through gas using high polymer slice, staple fiber or long filament
Then spun lacing is passed through in stream or mechanical networking, needle thorn or hot rolling are reinforced, the non-woven cloth finally formed by final finishing.Tool
There is soft, ventilative and planar structure tencel product, advantage is not generate Soft flocks, it is tough, durable, silky soft,
It is one kind of reinforcing material, and there are also the feelings of cotton to compare with cotton goods, the sack of non-woven fabrics is easily formed, Er Qiezao
Valence is cheap.
The extension of the application field of non-woven fabrics, non-woven fabrics is gradually applied in the wall paper field of house ornamentation, but current nonwoven
Although cloth wall paper, than high-tenacity, generally without antibacterial ability, family and not all resident can possess abundance at present
Sunlight, and bacterium easy to breed, especially family have the family of infant on moist wall paper, infant does not have health perception,
It can grab, touch or even metope can be gnawed, cause certain healthy hidden danger.
Summary of the invention
To solve the above-mentioned problems, the present invention provides a kind of preparation method of antimicrobial form wall paper non-woven fabrics, is guaranteeing by force
On the basis of tough, have antibacterial ability, is particularly suitable for family that is moist or having infant and uses.
To achieve the goals above, the invention adopts the following technical scheme: a kind of preparation of antimicrobial form wall paper non-woven fabrics
Method, comprising the following steps:
S1: by the mixture of fine fibre polymer and binder fibre by big screw at high temp melting extrusion, heating temperature 260
~280 DEG C, obtain the polymer A of molten condition;
S2: the stretched device of spinneret is stretched, is formed with 4.8~5.3MPa pressurization spinneret through extruder by polymer A
Fiber draw object B, and guide and carry out 4~8h of immersion into soak, it is then directed on lapper;
S3: when three layers or four layers of fiber draw object B is laminated on lapper, guiding sandwich hot rolling into hot-rolling mill,
Resin-oatmeal is uniformly sprayed on fiber draw object surface when hot rolling, and hot-rolled condition is 160~180 DEG C, 4MPa, obtains non-woven fabrics, winds
Molding.By the way that fiber high temperature melt-out spinning is formed wire drawing object, first one-step forming simultaneously sterilized, subsequently into being impregnated in soak, into
One step improves antibacterial ability, while by addition resin-oatmeal, further enhancing the toughness and intensity of non-woven fabrics, keeping it not easily broken
It splits, the resin-oatmeal can be one kind of thermosetting resin.
Further, enter hot rolling by infrared radiation 2~3 times after sprinkling resin-oatmeal in the step S3.By
After ultraviolet radiation, preferably sterilization and fusion are played, the antibacterial effect of non-woven fabrics is improved.
Further, the soak component is as follows: 30~40 parts of biennial wormwood extract, 20~40 parts of acrylate, three
Chlorine is 0.01~0.02 part, 30~40 parts of ethylene glycol raw.By the action of soaking of soak, so that non-woven fabrics has while sterile
There is bacteriostasis efficacy, and the duration is long, to no damage to human body, meets the requirement of environment protection health.
Further, the fine fibre polymer includes low melting point chemical fibre, carpenter's fiber and wood pulp, low melting point
Chemical fibre: wood pulp cellulose: carpenter=5:3:1.The good toughness for the non-woven fabrics prepared under this ratio, intensity is high, is not easy out
It splits, and easily colouring.
Further, the lapper is random web-laying equipment, the quantification of 100g/m of the networking of random web-laying equipment2~
120g/m2.This while guaranteeing using function, is conducive to the printing of pattern at reticular density, too thin or too close will affect print
Effect processed.
Bring of the present invention has the beneficial effect that 1) present invention is by forming wire drawing object for fiber high temperature melt-out spinning, tentatively
It forms and sterilizes, subsequently into impregnating in soak, further increase antibacterial ability, while by addition resin-oatmeal, further
The toughness and intensity for enhancing non-woven fabrics, keep its not easy to break;
2) herbal medicine immersion liquid is added, certain bacteriostasis is made it have while improving bacteriostasis, and meet
The requirement of environment protection health is particularly suitable for room humidity or has the family of infant to use to no damage to human body.
Specific embodiment
The present invention is described in detail combined with specific embodiments below.
Embodiment 1
S1: institute's fine fibre polymer includes low melting point chemical fibre, carpenter's fiber and wood pulp, low melting point chemical fibre: wood
Pulp fibres: carpenter=5:3:1, by the mixture of fine fibre polymer and binder fibre by big screw at high temp melting extrusion, heating
Temperature is 260 DEG C, obtains the polymer A of molten condition;
S2: the stretched device of spinneret is stretched with 4.8MPa pressurization spinneret by extruder, is formed fiber by polymer A
Wire drawing object B, and guide and carry out immersion 4h into soak, it is then directed on random web-laying equipment, the soak component is such as
Under: 30 parts of biennial wormwood extract, 20 parts of acrylate, 0.01 part of triclosan, 30 parts of ethylene glycol;
S3: when three layers of fiber draw object B is laminated on lapper, guiding sandwich hot rolling into hot-rolling mill, when hot rolling
Resin-oatmeal is uniformly sprayed on fiber draw object surface, by infrared radiation 2 times enter hot rolling, hot-rolled condition be 160 DEG C, 4MPa,
Obtain non-woven fabrics, coiling and molding.
Detailed data the results are shown in Table 1.
Embodiment 2
S1: institute's fine fibre polymer includes low melting point chemical fibre, carpenter's fiber and wood pulp, low melting point chemical fibre: wood
Pulp fibres: carpenter=5:3:1, by the mixture of fine fibre polymer and binder fibre by big screw at high temp melting extrusion, heating
Temperature is 280 DEG C, obtains the polymer A of molten condition;
S2: the stretched device of spinneret is stretched with 5.3MPa pressurization spinneret by extruder, is formed fiber by polymer A
Wire drawing object B, and guide and carry out immersion 8h into soak, it is then directed on random web-laying equipment, the soak component is such as
Under: 40 parts of biennial wormwood extract, 40 parts of acrylate, 0.02 part of triclosan, 40 parts of ethylene glycol;
S3: when four layers of fiber draw object B is laminated on lapper, guiding sandwich hot rolling into hot-rolling mill, when hot rolling
Resin-oatmeal is uniformly sprayed on fiber draw object surface, by infrared radiation 3 times enter hot rolling, hot-rolled condition be 180 DEG C, 4MPa,
Obtain non-woven fabrics, coiling and molding.
Detailed data the results are shown in Table 1.
Reference examples 1
S1: for the mixture of institute's fine fibre and binder fibre by big screw at high temp melting extrusion, heating temperature is 260 DEG C, is obtained
To the polymer A of molten condition;
S2: the stretched device of spinneret is stretched with 4.8MPa pressurization spinneret by extruder, is formed fiber by polymer A
Wire drawing object B, and guide and carry out immersion 4h into soak, it is then directed on random web-laying equipment, the soak component is such as
Under: 30 parts of biennial wormwood extract, 20 parts of acrylate, 0.01 part of triclosan, 30 parts of ethylene glycol;
S3: when three layers of fiber draw object B is laminated on lapper, guiding sandwich hot rolling into hot-rolling mill, when hot rolling
Resin-oatmeal is uniformly sprayed on fiber draw object surface, by infrared radiation 2 times enter hot rolling, hot-rolled condition be 160 DEG C, 4MPa,
Obtain non-woven fabrics, coiling and molding.
Detailed data the results are shown in Table 1.
Reference examples 2
S1: institute's fine fibre polymer includes low melting point chemical fibre, carpenter's fiber and wood pulp, low melting point chemical fibre: wood
Pulp fibres: carpenter=5:3:1, by the mixture of fine fibre polymer and binder fibre by big screw at high temp melting extrusion, heating
Temperature is 260 DEG C, obtains the polymer A of molten condition;
S2: the stretched device of spinneret is stretched with 4.8MPa pressurization spinneret by extruder, is formed fiber by polymer A
Wire drawing object B, and guide to random web-laying equipment;
S3: when three layers of fiber draw object B is laminated on lapper, guiding sandwich hot rolling into hot-rolling mill, when hot rolling
Resin-oatmeal is uniformly sprayed on fiber draw object surface, by infrared radiation 2 times enter hot rolling, hot-rolled condition be 160 DEG C, 4MPa,
Obtain non-woven fabrics, coiling and molding.
Detailed data the results are shown in Table 1.
Reference examples 3
S1: institute's fine fibre polymer includes low melting point chemical fibre, carpenter's fiber and wood pulp, low melting point chemical fibre: wood
Pulp fibres: carpenter=5:3:1, by the mixture of fine fibre polymer and binder fibre by big screw at high temp melting extrusion, heating
Temperature is 260 DEG C, obtains the polymer A of molten condition;
S2: the stretched device of spinneret is stretched with 4.8MPa pressurization spinneret by extruder, is formed fiber by polymer A
Wire drawing object B, and guide and carry out immersion 4h into soak, it is then directed on random web-laying equipment, the soak component is such as
Under: 30 parts of biennial wormwood extract, 20 parts of acrylate, 0.01 part of triclosan, 30 parts of ethylene glycol;
S3: when three layers of fiber draw object B is laminated on lapper, sandwich hot rolling into hot-rolling mill, hot rolling item are guided
Part is 160 DEG C, 4MPa, obtains non-woven fabrics, coiling and molding.
Detailed data the results are shown in Table 1.
Table 1
As shown in Table 1, when replacing fiber or being not added with resin, tension failure strength, breaking strength are substantially reduced, this Shen
Soak please can reduce adhesive force while having fungistatic effect, make it be not easy to fall ash, the present invention is not by above-described embodiment
Limitation, the above embodiments and description only illustrate the principle of the present invention, is not departing from spirit and scope of the invention
Under the premise of, various changes and improvements may be made to the invention, these changes and improvements both fall within the model of claimed invention
In enclosing.The scope of protection of present invention is defined by the appending claims and its equivalent thereof.
Claims (5)
1. a kind of preparation method of antimicrobial form wall paper non-woven fabrics, which comprises the following steps:
S1: by the mixture of fine fibre polymer and binder fibre by big screw at high temp melting extrusion, heating temperature is 260~
280 DEG C, obtain the polymer A of molten condition;
S2: the stretched device of spinneret is stretched with 4.8~5.3MPa pressurization spinneret by extruder, is formed fiber by polymer A
Wire drawing object B, and guide and carry out 4~8h of immersion into soak, it is then directed on lapper;
S3: when three layers or four layers of fiber draw object B is laminated on lapper, sandwich hot rolling into hot-rolling mill, hot rolling are guided
When fiber draw object surface uniformly spray resin-oatmeal, hot-rolled condition is 160~180 DEG C, 4MPa, obtains non-woven fabrics, coiling and molding.
2. according to right want 1 described in antimicrobial form wall paper non-woven fabrics preparation method, it is characterised in that: in the step S3
Enter hot rolling by infrared radiation 2~3 times after sprinkling resin-oatmeal.
3. according to right want 2 described in antimicrobial form wall paper non-woven fabrics preparation method, it is characterised in that: the soak group
Part is as follows: 30~40 parts of biennial wormwood extract, 20~40 parts of acrylate, 0.01~0.02 part of triclosan, 30~40 parts of ethylene glycol.
4. the preparation method of antimicrobial form wall paper non-woven fabrics according to claim 3, it is characterised in that: the fine fibre is poly-
Closing object includes low melting point chemical fibre, carpenter's fiber and wood pulp, low melting point chemical fibre: wood pulp cellulose: carpenter=5:3:1.
5. wanting the preparation method of any antimicrobial form wall paper non-woven fabrics of 1-4 according to right, it is characterised in that: it is described at
Net machine is random web-laying equipment.