CN109590188A - A kind of artificial stone bath tub surface elastic process technique - Google Patents
A kind of artificial stone bath tub surface elastic process technique Download PDFInfo
- Publication number
- CN109590188A CN109590188A CN201811472531.5A CN201811472531A CN109590188A CN 109590188 A CN109590188 A CN 109590188A CN 201811472531 A CN201811472531 A CN 201811472531A CN 109590188 A CN109590188 A CN 109590188A
- Authority
- CN
- China
- Prior art keywords
- bath tub
- artificial stone
- process technique
- bathtub
- surface elastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of artificial stone bath tub surface elastic process techniques, belong to field of stone processing.It solves the problems, such as that the surface feel after processing in existing artificial stone bath tub surface elastic process technique is uncomfortable.This artificial stone bath tub surface elastic process technique, the following steps are included: bathtub mold is made according to setting bathtub shape, to one layer of priming paint of bathtub mold even application, then a level paint is uniformly sprayed to the bathtub mold outer surface after spray-applied primer, then the raw material for being used for surface elasticity is uniformly deployed in proportion, and the raw material is by the mute oil of PU-8501Y, GH-01 curing agent and XT-01 solvent or diluent form, then it carries out out oil and above-mentioned raw materials is subjected to uniform stirring, again by the raw material even application after uniform stirring in bathtub mold, finally the bathtub grinding tool uniformly smeared is dried.The present invention makes surface high resilience after having the advantages that processing.
Description
Technical field
The invention belongs to field of stone processing, in particular to a kind of artificial stone bath tub surface elastic process technique.
Background technique
Bathtub is a kind of pipe device, is used for taking a shower or taking a shower, and usual device is in household bathroom.The bath in old-fashioned west
The steel or iron that cylinder is usually crossed by antirust treatment, all the time, most bathtub all belongs to rectangle, in recent years since polymethyl methacrylate adds
Heat bathtub is gradually popularized, and starts various bathtubs of different shapes occur.The most common color of bathtub is white, also there is other examples
Such as pink colour tone, most bath bases all have water level, and the water level that goes for preventing completely rushing down also is equipped on top, some, and hose is pacified
Mounted in bathtub marginal position.
Existing bathtub is broadly divided into ceramic bathtub and two kinds of natural stone bathtub.Ceramic bathtub is in manufacture view preparation method letter
It is single, but ceramic bathtub exists and is easy to skid, furthermore the bathtub of ceramic is easy damaged and breaks, thus now gradually by
Eliminate, and natural stone bathtub although have it is firm in structure, durable, using comfortable advantage, but since natural stone is prohibitively expensive, nothing
Method is promoted in people's lives；In addition, existing bath tub surface is excessively tight and hale and hearty, feel is although smooth comfortable, but by
In hale and hearty material, consumer feels shortcoming comfort.
Summary of the invention
The purpose of the present invention is being directed to the above-mentioned problems in the prior art, a kind of flexible people in surface is provided
Make stone bath tub surface elastic process technique.
Object of the invention can be realized by the following technical scheme: a kind of artificial stone bath tub surface elastic process technique,
Characterized by comprising the following steps:
A, bathtub mold is made according to setting bathtub shape；
B, the bathtub mold of Xiang Suoshu uniformly spray one layer by PU10 base paint special, PG849 color inhibition bottom curing agent with
The priming paint that the bottom PU205A is formulated in proportion with diluent；
C, after completing above-mentioned steps, one layer is uniformly sprayed by PU sub- fine flour entirely to the bathtub mold outer surface after spray-applied primer
Paint, the PU finishing coat that sub- black finish, PU217 stone material surface diluent and PG881 matt curing agent are formulated in proportion entirely；
D, complete above-mentioned steps after, in proportion uniformly allotment be used for surface elasticity raw material, and the raw material by PU-8501Y it is mute oil,
GH-01 curing agent and XT-01 solvent or diluent form；
E, it after completing above-mentioned steps, carries out out oil and above-mentioned raw materials is subjected to uniform stirring；
F, after completing above-mentioned steps, by the raw material even application after uniform stirring in bathtub mold；
G, after completing above-mentioned steps, the bathtub grinding tool uniformly smeared is dried.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the PU10 base paint special, the resistance to Huang of PG849
Become the configuration proportion of bottom curing agent and the bottom PU205A diluent as 1:0.3:0.4.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, sub- white finish paint and PU are complete sub- black entirely by the PU
The spraying model of finishing coat is 7702 colors.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, sub- white finish paint and PU are complete sub- black entirely by the PU
Finishing coat configuration proportion is 0.88:0.12.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the PU217 stone material surface diluent
Proportion is 60% to 80%.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the PG881 matt curing agent institute accounting
Example is 50%.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the mute oil of the PU-8501Y, GH-01 solidification
Configuration proportion between agent and XT-01 solvent or diluent is 10:2:4.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the mute oil of the PU-8501Y, GH-01 solidification
The spraying number of agent and XT-01 solvent or diluent is 3 to 4 rifles.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, temperature when the described drying is controlled 70
DEG C, the time controlled at 30 minutes.
Compared with prior art, the advantages of this artificial stone bath tub surface elastic process technique are as follows: the artificial stone manufactured
Bath tub surface has flexible texture abundant, is not easy to skid, cracky and not break, and the bathtub table matter be smooth to the touch it is comfortable,
Improve comfort.
Specific embodiment
The following is specific embodiments of the present invention, and technical scheme of the present invention will be further described, but the present invention is simultaneously
It is not limited to these embodiments.
This artificial stone bath tub surface elastic process technique, which comprises the following steps:
A, bathtub mold is made according to setting bathtub shape；
B, the bathtub mold of Xiang Suoshu uniformly spray one layer by PU10 base paint special, PG849 color inhibition bottom curing agent with
The priming paint that the bottom PU205A is formulated in proportion with diluent；
C, after completing above-mentioned steps, one layer is uniformly sprayed by PU sub- fine flour entirely to the bathtub mold outer surface after spray-applied primer
Paint, the PU finishing coat that sub- black finish, PU217 stone material surface diluent and PG881 matt curing agent are formulated in proportion entirely；
D, complete above-mentioned steps after, in proportion uniformly allotment be used for surface elasticity raw material, and the raw material by PU-8501Y it is mute oil,
GH-01 curing agent and XT-01 solvent or diluent form；
E, it after completing above-mentioned steps, carries out out oil and above-mentioned raw materials is subjected to uniform stirring；
F, after completing above-mentioned steps, by the raw material even application after uniform stirring in bathtub mold；
G, after completing above-mentioned steps, the bathtub grinding tool uniformly smeared is dried.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the PU10 base paint special, the resistance to Huang of PG849
Become the configuration proportion of bottom curing agent and the bottom PU205A diluent as 1:0.3:0.4.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, sub- white finish paint and PU are complete sub- black entirely by the PU
The spraying model of finishing coat is 7702 colors.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, sub- white finish paint and PU are complete sub- black entirely by the PU
Finishing coat configuration proportion is 0.88:0.12.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the PU217 stone material surface diluent
Proportion is 60% to 80%.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the PG881 matt curing agent institute accounting
Example is 50%.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the mute oil of the PU-8501Y, GH-01 solidification
Configuration proportion between agent and XT-01 solvent or diluent is 10:2:4.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, the mute oil of the PU-8501Y, GH-01 solidification
The spraying number of agent and XT-01 solvent or diluent is 3 to 4 rifles.
In a kind of above-mentioned artificial stone bath tub surface elastic process technique, temperature when the described drying is controlled 70
DEG C, the time controlled at 30 minutes.
Specific embodiment described herein is only an example for the spirit of the invention.The neck of technology belonging to the present invention
The technical staff in domain can make various modifications or additions to the described embodiments or replace by a similar method
In generation, however, it does not deviate from the spirit of the invention or beyond the scope of the appended claims.
Although equal terms are used more herein, it does not exclude the possibility of using other terms.Use these arts
Language is only for the convenience of describing and explaining the nature of the invention；Being construed as any additional limitation is all
It is disagreed with spirit of that invention.
Claims (9)
1. a kind of artificial stone bath tub surface elastic process technique, which comprises the following steps:
A, bathtub mold is made according to setting bathtub shape；
B, the bathtub mold of Xiang Suoshu uniformly spray one layer by PU10 base paint special, PG849 color inhibition bottom curing agent with
The priming paint that the bottom PU205A is formulated in proportion with diluent；
C, after completing above-mentioned steps, one layer is uniformly sprayed by PU sub- fine flour entirely to the bathtub mold outer surface after spray-applied primer
Paint, the PU finishing coat that sub- black finish, PU217 stone material surface diluent and PG881 matt curing agent are formulated in proportion entirely；
D, complete above-mentioned steps after, in proportion uniformly allotment be used for surface elasticity raw material, and the raw material by PU-8501Y it is mute oil,
GH-01 curing agent and XT-01 solvent or diluent form；
E, it after completing above-mentioned steps, carries out out oil and above-mentioned raw materials is subjected to uniform stirring；
F, after completing above-mentioned steps, by the raw material even application after uniform stirring in bathtub mold；
G, after completing above-mentioned steps, the bathtub grinding tool uniformly smeared is dried.
2. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that the PU10
The configuration proportion of base paint special, PG849 color inhibition bottom curing agent and the bottom PU205A diluent is 1:0.3:0.4.
3. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that the PU is complete
The spraying model of sub- white finish paint and PU sub- black finish entirely is 7702 colors.
4. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that the PU is complete
Sub- black finish configuration proportion is 0.88:0.12 entirely by sub- white finish paint and PU.
5. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that described
The proportion of PU217 stone material surface diluent is 60% to 80%.
6. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that described
PG881 matt curing agent proportion is 50%.
7. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that the PU-
Configuration proportion between the mute oil of 8501Y, GH-01 curing agent and XT-01 solvent or diluent is 10:2:4.
8. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that the PU-
The spraying number of the mute oil of 8501Y, GH-01 curing agent and XT-01 solvent or diluent is 3 to 4 rifles.
9. a kind of artificial stone bath tub surface elastic process technique according to claim 1, which is characterized in that the drying
When temperature control at 70 DEG C, the time controlled at 30 minutes.