CN105350327A - Flax bright canvas - Google Patents
Flax bright canvas Download PDFInfo
- Publication number
- CN105350327A CN105350327A CN201510790351.1A CN201510790351A CN105350327A CN 105350327 A CN105350327 A CN 105350327A CN 201510790351 A CN201510790351 A CN 201510790351A CN 105350327 A CN105350327 A CN 105350327A
- Authority
- CN
- China
- Prior art keywords
- parts
- flax
- emulsion
- canvas
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A flax bright canvas is disclosed. A preparation method for the flax bright canvas comprises (1) preparing a bottom glue, concretely uniformly dispersing 20-25 parts of pure acrylic emulsion, 10-15 parts of deionized water, and 20-25 parts of a clear slurry; (2) preparing a surface glue, concretely, uniformly dispersing 30-33 parts of deionized water, 25-30 parts of pure acrylic high-glossiness emulsion, 12-15 parts of titanium dioxide, 10-12 parts of talcum powder, 8-13 parts of lithopone, 8-13 parts of heavy calcium carbonate, 0.3-0.4 part of a dispersant, 0.2-0.3 part of an antifoaming agent, 1-2 parts of a multifunctional auxiliary agent, and 1-2 parts of a brightener; (3) uniformly coating flax basal cloth with the bottom glue in a shower way, and putting in a baking oven with the temperature of 100-120 DEG C for drying; and (4) coating the base material obtained in the step (3) with the surface glue in a shower way, and putting in a baking oven with the temperature of 70-80 DEG C for drying. The canvas possesses brightness, is strong in painting stereo perception, good in handfeel and soft in cloth surface, possesses relatively good affinity with pigments, is relatively high in pattern sharpness, and can be stored for a long time.
Description
Technical field
The present invention relates to canvas technical field, especially relate to one and to grow flax polish oil painting canvas and preparation method thereof.
Background technology
Tradition painting canvas is main mainly with cotton and polyester-mixed cotton cloth greatly, and the white end, without light, is difficult to present special visual effect.Cloth cover has had brightness, and during drawing, third dimension strengthens, and presents color full, makes different visual effect.Adopt flax material base cloth, painting canvas texture is good, and cloth cover softness makes painting canvas and pigment have more affinity, can preserve for a long time.
Summary of the invention
For the problems referred to above that prior art exists, the applicant provides one and to grow flax polish oil painting canvas.This painting canvas has brightness, and drawing third dimension is strong; Painting canvas good hand touch, cloth cover is soft; Painting canvas and pigment have more affinity, and pattern definition is higher, can preserve for a long time.
Technical scheme of the present invention is as follows:
One grows flax polish oil painting canvas, and its preparation method is as follows:
(1) make primer: pure-acrylic emulsion 20-25 part, deionized water 10-15 part, clean plasm 20-25 part, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) make face glue: deionized water 30-33 part, pure third high light emulsion 25-30 part, titanium dioxide 12-15 part, talcum powder 10-12 part, lithopone 8-13 part, carbonic acid coarse whiting 8-13 part, dispersant 0.3-0.4 part, defoamer 0.2-0.3 part, multifunctional assistant 1-2 part, brightener 1 ~ 2 part, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(3) primer is starched even showering on the base cloth of flax material, enter 100-120 DEG C of oven for drying;
(4) by face glue showering on step (3) gained base material, enter the oven for drying of 70-80 DEG C;
The number of the above raw material is parts by weight.
Described pure third high light emulsion is dimethyl formamide 20-30 part, styrene 40-50 part, methyl chloroacetate 30-40 part, and heating water bath is warming up to 75 DEG C, stirs the emulsion of synthesis after 3 hours.
Described brightener is organosilicon polysiloxane; Described dispersant many joins polyalcohol and many aziridines block copolymer in oneself, and described defoamer is polyvinyl isobutyl ether; Described multifunctional assistant is 2-amino-2-methyl-1-propanol.Described multifunctional assistant can regulate pH value, and has the effect of dispersion.
The technique effect that the present invention is useful is:
The present invention uses the high light emulsion of independent research, is styrene, dimethyl formamide, and the emulsion of methyl chloroacetate synthesis, makes painting canvas have brightness, and drawing third dimension is strong; Use multifunctional assistant, make the fine and smooth good leveling property of slurry, painting canvas uniform absorption, makes painting canvas good hand touch, and cloth cover is soft; Use linen as base material, adopt spraying technique, woven design sense is strong, and make painting canvas and pigment have more affinity, pattern definition is higher, can preserve for a long time.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is specifically described.
Embodiment 1:
1, primer is made: pure-acrylic emulsion 25 parts, deionized water 15 parts, clean plasm 25 parts are be uniformly dispersed in the dispersion machine of 3000 turns/min at rotating speed.
2, face glue is made: deionized water 33 parts, pure third high light emulsion 30 parts, titanium dioxide 15 parts, talcum powder 12 parts, 13 parts, lithopone, carbonic acid coarse whiting 13 parts, dispersant 0.4 part, defoamer 0.3 part, multifunctional assistant 2 parts, brightener 2 parts are be uniformly dispersed in the dispersion machine of 3000 turns/min at rotating speed.Wherein pure third high light emulsion is dimethyl formamide 30 parts, styrene 50 parts, methyl chloroacetate 40 parts, and heating water bath is warming up to 80 DEG C, stirs the emulsion of synthesis after 3 hours.
3, primer is starched even showering on the base cloth of flax material, enter 120 DEG C of oven for drying.
4, by face glue showering on above-mentioned base material, enter the oven for drying of 80 DEG C.
Embodiment 2:
1, primer is made: pure-acrylic emulsion 20 parts, deionized water 10 parts, clean plasm 20 parts are be uniformly dispersed in the dispersion machine of 2000 turns/min at rotating speed.
2, face glue is made: deionized water 30 parts, pure third high light emulsion 25 parts, titanium dioxide 12 parts, talcum powder 10 parts, 8 parts, lithopone, carbonic acid coarse whiting 8 parts, dispersant 0.3 part, defoamer 0.2 part, multifunctional assistant 1 part, brightener 1 part are be uniformly dispersed in the dispersion machine of 2000 turns/min at rotating speed.Wherein pure third high light emulsion is dimethyl formamide 20 parts, styrene 40 parts, methyl chloroacetate 30 parts, and heating water bath is warming up to 70 DEG C, stirs the emulsion of synthesis after 2 hours.
3, primer is starched even showering on the base cloth of flax material, enter 100 DEG C of oven for drying.
4, by face glue showering on above-mentioned base material, enter the oven for drying of 70 DEG C.
Embodiment 3:
1, primer is made: pure-acrylic emulsion 23 parts, deionized water 12 parts, clean plasm 23 parts are be uniformly dispersed in the dispersion machine of 2500 turns/min at rotating speed.
2, face glue is made: deionized water 32 parts, pure third high light emulsion 28 parts, titanium dioxide 13 parts, talcum powder 11 parts, 10 parts, lithopone, carbonic acid coarse whiting 10 parts, dispersant 0.35 part, defoamer 0.25 part, multifunctional assistant 1.5 parts, brightener 1.5 parts are be uniformly dispersed in the dispersion machine of 2500 turns/min at rotating speed.Wherein pure third high light emulsion is dimethyl formamide 25 parts, styrene 45 parts, methyl chloroacetate 35 parts, and heating water bath is warming up to 75 DEG C, stirs the emulsion of synthesis after 3 hours.
3, primer is starched even showering on the base cloth of flax material, enter 110 DEG C of oven for drying.
4, by face glue showering on above-mentioned base material, enter the oven for drying of 75 DEG C.
Described in embodiment 1 ~ 3, brightener is organosilicon polysiloxane; Described dispersant many joins polyalcohol and many aziridines block copolymer in oneself, and described defoamer is polyvinyl isobutyl ether; Described multifunctional assistant is 2-amino-2-methyl-1-propanol.
Test example:
1, the painting canvas that obtains of embodiment 1 ~ 3, brightness effect has been seen on surface.
2, linseed oil is dropped in painting canvas surface, within 24 hours, oil droplet diffusion absorbs 2 times that are no more than oil droplet.
3, be coated on painting canvas by oil colour, after 24 hours, the back side is non-leakage without oil drop.
Claims (3)
1. one to grow flax polish oil painting canvas, it is characterized in that its preparation method is as follows:
(1) make primer: pure-acrylic emulsion 20-25 part, deionized water 10-15 part, clean plasm 20-25 part, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) make face glue: deionized water 30-33 part, pure third high light emulsion 25-30 part, titanium dioxide 12-15 part, talcum powder 10-12 part, lithopone 8-13 part, carbonic acid coarse whiting 8-13 part, dispersant 0.3-0.4 part, defoamer 0.2-0.3 part, multifunctional assistant 1-2 part, brightener 1 ~ 2 part, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(3) primer is starched even showering on the base cloth of flax material, enter 100-120 DEG C of oven for drying;
(4) by face glue showering on step (3) gained base material, enter the oven for drying of 70-80 DEG C;
The number of the above raw material is parts by weight.
2. flax polish oil painting canvas according to claim 1, is characterized in that described brightener is organosilicon polysiloxane; Described dispersant many joins polyalcohol and many aziridines block copolymer in oneself, and described defoamer is polyvinyl isobutyl ether; Described multifunctional assistant is 2-amino-2-methyl-1-propanol.
3. flax polish oil painting canvas according to claim 1, it is characterized in that described pure third high light emulsion is dimethyl formamide 20-30 part, styrene 40-50 part, methyl chloroacetate 30-40 part, heating water bath is warming up to 70 ~ 80 DEG C, stirs the emulsion of synthesis after 2 ~ 3 hours.