CN109577497A - A kind of construction technology of resinousness water-repellent paint - Google Patents
A kind of construction technology of resinousness water-repellent paint Download PDFInfo
- Publication number
- CN109577497A CN109577497A CN201811589828.XA CN201811589828A CN109577497A CN 109577497 A CN109577497 A CN 109577497A CN 201811589828 A CN201811589828 A CN 201811589828A CN 109577497 A CN109577497 A CN 109577497A
- Authority
- CN
- China
- Prior art keywords
- aggregate
- fabric
- resinousness
- water
- repellent paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of construction technologies of resinousness water-repellent paint, include the following steps;S1, after the watertight area constructed being needed to clean up, the watertight area constructed will be needed to clean again using dust catcher;S2, one layer of solvent naphtha is smeared on the anti-pool surface for needing to construct;S3, bottom material is applied on the anti-pool for needing to construct;S4, after bottom material is cooling, bottom material is polished using angle grinder;S5, one layer of solvent naphtha is smeared in bottom material upper surface;S6, one layer of aggregate is smeared in the upper surface of bottom material;S7, aggregate is flattened using roller machine;S8, fabric is poured into leaching along the edge of aggregate, after fabric interior on aggregate edge is dry, then remaining fabric is poured to the upper surface for pouring aggregate.The present invention can to keep preferable waterproof performance, weather resistance and preferable intensity by resinousness water-repellent paint treated roofing.
Description
Technical field
The present invention relates to the field of building materials, and in particular to a kind of construction technology of resinousness water-repellent paint.
Background technique
In present engineering, most of engineering structure surface needs to coat waterproof coating, to prevent water vapour from entering engineering knot
Structure is damaged in structure.The considerations of present plant area's structure is in order to build cost, generallys use steel construction, and steel construction is in order to protect
The requirement such as waterproof of its roofing is demonstrate,proved, needs to smear waterproof coating on its surface.
The construction technology of present water-repellent paint has preferable effect only for existing conventional water-repellent paint, but right
It is anti-after construction when present conventional water-repellent paint especially being applied to resinousness water-repellent paint in special water-repellent paint
The weather-proof poor effect of water, cannot reach resinousness water-repellent paint should have to water-proof climate resisting effect, while water-repellent paint is being applied now
Need to guarantee the Land leveling of construction when work, which increase the process flow of construction and difficulty, while improving cost.
Summary of the invention
In view of the above drawbacks of the prior art, it is an object of the invention to provide a kind of constructions of resinousness water-repellent paint
Technique can to keep preferable waterproof performance, weather resistance and preferably by resinousness water-repellent paint treated roofing
Intensity.
It is realized the purpose of the present invention is technical solution in this way:
A kind of construction technology of resinousness water-repellent paint, includes the following steps;
S1, after the watertight area constructed being needed to clean up, using dust catcher by the watertight area for needing to construct again
Cleaning;
S2, one layer of solvent naphtha is smeared on the anti-pool surface for needing to construct;
S3, bottom material is applied on the anti-pool for needing to construct;
S4, after bottom material is cooling, bottom material is polished using angle grinder;
S5, one layer of solvent naphtha is smeared in bottom material upper surface;
S6, one layer of aggregate is smeared in the upper surface of bottom material;
S7, aggregate is flattened using roller machine;
S8, fabric is poured into leaching along the edge of aggregate, is poured after fabric interior on aggregate edge is dry, then by remaining fabric
Pour the upper surface of aggregate.
Further, in the step S2, the thickness of solvent naphtha is no more than 0.2 millimeter;In step s3, the smearing of bottom
Thickness is not less than 2 millimeters.
Further, in the step S5, it is Celsius before smearing solvent naphtha the upper surface of bottom to be heated to 50-60
Degree.
Further, in the step S6, when smearing aggregate, the temperature of aggregate is not less than 100 degrees Celsius.
Further, in the step S1, in the enclosing circle for needing certain altitude on brick work outside the watertight area constructed;Institute
It states in step S6, aggregate edge is 0.5-1 centimetres far from the distance on the inside of enclosing circle;In step S8, by fabric along the edge of aggregate
It pours leaching and refers to pour fabric and pour aggregate edge far from the gap between on the inside of enclosing circle.
Further, in the step S8, fabric is poured into leaching along the edge of aggregate and is included the following steps;
SJ1, fabric is poured into leaching along the inner wall of enclosing circle;
SJ2, after aggregate layer is fully cooled to room temperature, the intersection along aggregate and fabric pours fabric, until fabric
Surface is flushed with aggregate upper surface.
Further, in the step S7, the temperature to aggregate upper surface uses roller machine pair 60 degrees Celsius when
Aggregate upper surface is flattened.
Further, temperature is higher than 60 degrees Celsius when the bottom material is smeared.
Further, the interval time that bottom material and aggregate are smeared is no less than 20 hours.
Further, in the step S1, one is smeared in the watertight area for needing to construct after cleaning again using dust catcher
Thickness degree is no more than 0.1 millimeter of fabric, carries out the operation of step S2 again after fabric is smeared 24 hours.
By adopting the above-described technical solution, the present invention has the advantage that:
This construction technology, by smearing solvent oil reservoir on the ground before smearing bottom material, so that the lower surface of bottom material can be
Under the action of solvent naphtha, so that the lower surface of bottom material can carry out good contact and suction with the construction surface of out-of-flatness
It is attached;By bottom material upper surface by angle grinder it is smooth after so that the aggregate being applied on bottom material upper surface is in the variation by the temperature difference
When, deformation expansion will not be corrupted to bottom, so as to reinforce waterproof performance and extend the service life of bottom.
Make aggregate in deformation by smearing fabric at the edge of aggregate, still keeps the waterproofness of aggregate fringe region
Energy.
Other advantages, target and feature of the invention will be illustrated in the following description to a certain extent, and
And to a certain extent, based on will be apparent to those skilled in the art to investigating hereafter, Huo Zheke
To be instructed from the practice of the present invention.Target and other advantages of the invention can be wanted by following specification and right
Book is sought to be achieved and obtained.
Specific embodiment
Below with reference to embodiment, the invention will be further described.
Embodiment 1:
The production method of resinousness water-repellent paint, including bottom material production, aggregate production and fabric production;
Take weight ratio 20 parts of 250 parts of 100 parts of 150 parts of raw material thermoplastic resin, thermosetting resin, water emulsion, dispersing agent,
10 parts of defoaming agent, 30 parts of mineral oil, 20 parts of acetone extract, 10 parts of mould inhibitor, 60 parts of pitch.
The bottom material production includes the following steps;
SD1,25% mineral oil of the pitch of weight ratio 40% and weight ratio is subjected to heating mixing;Heating temperature is
120 degrees Celsius, mixing speed 10r/min, mixing time is 25 minutes;
SD2,45% acetone extract that weight ratio is added, are further continued for heating stirring;
SD3, stop stirring continuous heating;
During bottom material production, the pressure inside container is kept to be no more than 0.05 standard atmospheric pressure.
The aggregate production includes the following steps;
SG1,50% dispersant of thermosetting resin and weight ratio is heated;The temperature of heating is 160 degrees Celsius;
SG2, the pitch addition of weight ratio 60% is persistently stirred again;The temperature of mixing is 150 degrees Celsius, blender
Top opening is communicated with the atmosphere;
SG3, be added weight ratio 25% defoaming agent after, agitating and heating keep temperature;
In aggregate production, the temperature of mixture is not less than 110 degrees Celsius, and aggregate storage temperature after processing is completed is not low
In 100 degrees Celsius;
The fabric production includes the following steps;
SM1, it will be stirred in thermoplasticity resin and water emulsion heating reaction kettle, carry out vacuum dehydration reaction;
SM2,50% dispersing agent of weight ratio is added in reaction kettle, keeping temperature is 65 degrees Celsius;
SM3, reaction kettle is added in 75% mineral oil of weight ratio, 55% acetone extract of weight ratio and mould inhibitor
In, keeping temperature is 82 degrees Celsius;
SM3,75% defoaming agent that weight ratio is added continue to be stirred;The speed of stirring is 120r/min, when stirring
Between 40 minutes.
A kind of construction technology of resinousness water-repellent paint, includes the following steps;
S1, in the enclosing circle for needing certain altitude on brick work outside the watertight area constructed, the watertight area that will need to construct
After cleaning up, the watertight area constructed will be needed to clean again using dust catcher;
It is needing the watertight area constructed to smear the fabric that a layer thickness is no more than 0.1 millimeter, is being smeared 24 hours to fabric
Carry out the operation of step S2 again afterwards,
It needs the impurity for the anti-pool upper surface constructed that can make bottom material after smearing by cleaning, constructs with needs
There are enough adsorption strengths in anti-pool upper surface;The purpose for smearing fabric again is in order to thin on the anti-pool that will need to construct
Small bumps and gap etc. are irrigated sealing, while fabric has the function of that high ductibility can play first layer waterproof;
S2, the anti-pool surface constructed is being needed to smear the solvent naphtha that a layer thickness is no more than 2 millimeters;
The purpose for smearing solvent naphtha is that the pitch in bottom material is allowed to be dissolved in solvent naphtha, and such bottom material remains unchanged after the cooling period
There is good surface to contact with the anti-pool that needs are constructed.
S3, bottom material is applied on the anti-pool for needing to construct, the smearing thickness of bottom is not less than 2 millimeters, and bottom material is smeared
Shi Wendu is higher than 60 degrees Celsius.
It is to facilitate construction simultaneously in order to which the pitch in bottom material is in a molten state that temperature, which is higher than 60 degrees Celsius, when bottom material is smeared
Pitch is facilitated to be paved with all surface.
S4, after bottom material is cooling, bottom material is polished using angle grinder;
By bottom material upper surface by angle grinder it is smooth after so that the aggregate being applied on bottom material upper surface is by the temperature difference
When variation, deformation expansion will not be corrupted to bottom, so as to reinforce waterproof performance and extend the service life of bottom.
S5, the upper surface of bottom is heated, after the temperature of bottom upper surface reaches 50-60 degrees Celsius, on bottom material
Smear one layer of solvent naphtha in surface;
Heating to bottom be in order to after smearing aggregate lower surface contacted with bottom material after will not be quickly cooled down and be hardened, thus bone
Material release stress completely and smooth provide the time.
S6, one layer of aggregate is smeared in the upper surface of bottom material, aggregate edge is 0.5-1 centimetres far from the distance on the inside of enclosing circle,
Smearing is the temperature of aggregate not less than 100 degrees Celsius.
It is for the time to the smooth and cooling release stress of aggregate that temperature when aggregate is smeared, which is not less than 100 degrees Celsius,.
S7, to aggregate upper surface temperature 60 degrees Celsius when, aggregate upper surface is flattened using roller machine.
Using the purpose that roller machine flattens be fabric coating thickness it is uniform as far as possible, guarantee the consistency of integral waterproofing.
S8, fabric is poured into leaching along the edge of aggregate, fabric is poured into leaching along the edge of aggregate and is included the following steps;
SJ1, fabric is poured into leaching along the inner wall of enclosing circle;
SJ2, after aggregate layer is fully cooled to room temperature, the intersection along aggregate and fabric pours fabric, until fabric
Surface is flushed with aggregate upper surface;
Purpose is that aggregate, which can be shunk, to become smaller during aggregate hardening by cooling, so that aggregate and the full internal layer of enclosing
Between gap generate variation, this part can be filled up completely by fabric, while fabric can also be in aggregate expanded by heating
When work as a buffer.
After fabric interior on aggregate edge is dry, then remaining fabric is poured to the upper surface for pouring aggregate.
In the present embodiment, the interval time that bottom material and aggregate are smeared is no less than 20 hours.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to skill of the invention
Art scheme is modified or replaced equivalently, and without departing from the objective and range of the technical program, should all be covered in the present invention
Scope of the claims in.
Claims (10)
1. a kind of construction technology of resinousness water-repellent paint, which is characterized in that the construction technology packet of the resinousness water-repellent paint
Include following steps;
S1, after the watertight area constructed being needed to clean up, the watertight area constructed will be needed to clean again using dust catcher;
S2, one layer of solvent naphtha is smeared on the anti-pool surface for needing to construct;
S3, bottom material is applied on the anti-pool for needing to construct;
S4, after bottom material is cooling, bottom material is polished using angle grinder;
S5, one layer of solvent naphtha is smeared in bottom material upper surface;
S6, one layer of aggregate is smeared in the upper surface of bottom material;
S7, aggregate is flattened using roller machine;
S8, fabric is poured into leaching along the edge of aggregate, after fabric interior on aggregate edge is dry, then remaining fabric is poured and is poured
The upper surface of aggregate.
2. the construction technology of resinousness water-repellent paint according to claim 1, which is characterized in that molten in the step S2
The thickness of agent oil is no more than 0.2 millimeter;In step s3, the smearing thickness of bottom is not less than 2 millimeters.
3. the construction technology of resinousness water-repellent paint according to claim 1, which is characterized in that in the step S5,
The upper surface of bottom is heated to 50-60 degrees Celsius before smearing solvent naphtha.
4. the construction technology of resinousness water-repellent paint according to claim 1, which is characterized in that in the step S6, apply
When smearing aggregate, the temperature of aggregate is not less than 100 degrees Celsius.
5. the construction technology of resinousness water-repellent paint according to claim 1, which is characterized in that in the step S1,
Outside the watertight area for needing to construct on brick work certain altitude enclosing circle;In the step S6, aggregate edge is far from enclosing circle inside
Distance be 0.5-1 centimetres;In step S8, fabric along the edge of aggregate is poured into leaching refers to pour fabric and pour aggregate edge away from enclosing
Gap between on the inside of retaining ring.
6. the construction technology of resinousness water-repellent paint according to claim 5, which is characterized in that, will in the step S8
Fabric pours leaching along the edge of aggregate and includes the following steps;
SJ1, fabric is poured into leaching along the inner wall of enclosing circle;
SJ2, after aggregate layer is fully cooled to room temperature, the intersection along aggregate and fabric pours fabric, until the surface of fabric
It is flushed with aggregate upper surface.
7. the construction technology of resinousness water-repellent paint according to claim 1, which is characterized in that in the step S7, to
The temperature of aggregate upper surface flattens aggregate upper surface when 60 degrees Celsius, using roller machine.
8. the construction technology of resinousness water-repellent paint according to claim 1, which is characterized in that the temperature when bottom material is smeared
Degree is higher than 60 degrees Celsius.
9. according to claim 1 in -8 any resinousness water-repellent paint construction technology, which is characterized in that bottom material and bone
The interval time that material is smeared is no less than 20 hours.
10. according to claim 1 in -8 any resinousness water-repellent paint construction technology, which is characterized in that the step
In rapid S1, the watertight area constructed is being needed to smear the face that a layer thickness is no more than 0.1 millimeter after cleaning again using dust catcher
Material carries out the operation of step S2 again after fabric is smeared 24 hours.