CN106012741B - A kind of concrete road surface brick producing process with surface layer - Google Patents
A kind of concrete road surface brick producing process with surface layer Download PDFInfo
- Publication number
- CN106012741B CN106012741B CN201610302339.6A CN201610302339A CN106012741B CN 106012741 B CN106012741 B CN 106012741B CN 201610302339 A CN201610302339 A CN 201610302339A CN 106012741 B CN106012741 B CN 106012741B
- Authority
- CN
- China
- Prior art keywords
- surface layer
- brick body
- brick
- concrete
- sandstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of concrete road surface brick producing process with surface layer, including surface layer brick body and bottom brick body, specifically includes the following steps: the first step, bottom brick body is made of concrete and sandstone, component ratio between concrete and sandstone is 1-1.5:1, and concrete is made with sandstone of vibration pressurization;Second step carries out heating preheating to bottom brick body, is kept for 2-5 minutes;Third step, to bottom brick body uniformly spray-applied primer;4th step, manufactures surface layer brick body above priming paint, and surface layer brick body is made of cement, coarse sand, silicon ash, lotion;Meanwhile in surface layer brick body manufacturing process, curing agent is mixed;5th step heats surface layer brick body, is kept for 3-5 minutes.The present invention improves the color of pavement brick, allow pavement brick that there is permanent service life in complicated external environment, the corruption of water resistant and wind increases high temperature resistant, the antifriction characteristic of pavement brick, pavement brick can be made to keep original color for a long time, prevent the anti-alkali of pavement brick.
Description
Technical field
The present invention relates to concrete road pavement brick technical field more particularly to a kind of concrete road pavement brick manufacturers with surface layer
Method.
Background technique
Concrete road pavement brick in the prior art be using cement and stone as main raw material(s), it is processed, pressurization or other
Concrete road pavement brick of various shapes is made in moulding process, and concrete road pavement brick is mainly used for being laid with urban road, pavement, city
The block of the concrete road surfaces such as city square and ground surface works, plate etc..Pavement brick due to being exposed in complicated external environment for a long time,
The problems such as water erosion, wind corruption, temperature change, the reasons such as friction are easy the color for making it lose script, and aesthetic degree declines, nothing
The service life of method guarantee construction quality and pavement brick.
Summary of the invention
It is an object of the present invention to overcome above-mentioned the deficiencies in the prior art, and then provide a kind of coagulation with surface layer
Soil surface brick producing process improves the color of pavement brick, has pavement brick for a long time in complicated external environment
Service life, water resistant and wind corruption, increases high temperature resistant, the antifriction characteristic of pavement brick, pavement brick can be made to protect for a long time
Original color is held, anti-alkali of pavement brick etc. is prevented.
Technical solution of the present invention:
A kind of concrete road surface brick producing process with surface layer, including surface layer brick body and bottom brick body, specifically include following
Step:
The first step bottom brick body is made of concrete and sandstone, the group between the concrete and the sandstone
Dividing ratio is 1-1.5:1, and the concrete is made with the sandstone of vibration pressurization;
Second step carries out heating preheating to the bottom brick body, is kept for 2-5 minutes;
Third step, Xiang Suoshu bottom brick body uniformly spray-applied primer;
4th step manufactures the surface layer brick body above the priming paint, and the surface layer brick body is by cement, coarse sand, silicon ash, cream
Liquid is made;Meanwhile in the surface layer brick body manufacturing process, curing agent is mixed;
5th step heats the surface layer brick body, is kept for 3-5 minutes.
Further, the cement, coarse sand, silicon ash, the ratio of lotion are 4:2:2:2.
Further, the heating preheating temperature range in the second step is 60-80 DEG C.
Further, the bottom brick body heat using infrared heating preheating method in institute's second step pre-
Heat.
Further, the priming paint is underwater paint, and the coating thickness of the priming paint is 0.5-1mm.
Further, the heating preheating temperature range in the 5th step is 50-70 DEG C.
Further, heating preheating is carried out to the surface layer brick body using infrared heating preheating method in the 5th step.
The present invention has the advantages that the concrete road pavement brick disclosed by the invention with surface layer compared with the existing technology
Manufacturing method can not only prevent the anti-alkali of pavement brick from appearing in surface, completely cut off the moisture of pavement brick lower layer, can more accelerate paint
Rate of drying, while paint being made to become firmer.The color for improving pavement brick allows pavement brick in complicated external environment
In there is permanent service life, the corruption of water resistant and wind increases high temperature resistant, the antifriction characteristic of pavement brick, when can be long
Between so that pavement brick is kept original color.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
It obtains obviously, or recognized by the practice of invention.
Specific embodiment
Concrete road surface brick producing process with surface layer disclosed in the present embodiment, including surface layer brick body and bottom brick body, tool
Body the following steps are included:
Bottom brick body is made the first step of concrete and sandstone, and the component ratio between concrete and sandstone is 1-
1.5:1, it is preferable that the component ratio between concrete and sandstone disclosed in the present embodiment is 1:1, concrete and sandstone using shake
Dynamic pressurization is made;Shaking force is 240KN, and vibration frequency is 8~55Hz, and time of vibration 10-30S passes through Proper Match coagulation
Component ratio between soil and sandstone, and enough intensity and resistance to compression energy can have using bottom brick body made of vibration pressurization
Power is particularly suited for being laid with block, the plate of the concrete road surfaces such as urban road, pavement, city square and ground surface works, Ke Yiyou
Effect ground extends the service life of pavement brick.
Second step carries out heating preheating to above-mentioned bottom brick body, it is preferable that above-mentioned by the way of infrared heating preheating
The bottom brick body made carries out heating preheating, and is kept for 2-5 minutes;More specifically, the disclosed heating of the present embodiment preheats
Temperature range is controlled at 60-80 DEG C, subsequently spray painting can be facilitated to handle, the bottom brick body after preheating is easier japanning, and japanning
Effect is more uniform.
Third step, to the uniformly spray-applied primer of the bottom brick body after above-mentioned heating, it is preferable that priming paint uses waterproof
Paint, the effect of priming paint is the surface for preventing anti-alkali from appearing in pavement brick, completely cuts off the moisture of pavement brick lower layer.
4th step, manufactures surface layer brick body above priming paint, and surface layer brick body is made of cement, coarse sand, silicon ash, lotion;Meanwhile
In surface layer brick body manufacturing process, curing agent is mixed;Preferably, cement, coarse sand, silicon ash, the ratio of lotion are in surface layer brick body
4:2:2:2, surface layer brick body made of such ratio have compressive resistance high, and flexural capacity is good, and has the characteristics that pervious function is strong;
In the manufacturing process of surface layer brick body, sprinkling curing agent can preferably protect the surface layer of pavement brick;Make surface layer brick body and solidification
Agent is rapidly merged.
5th step heats above-mentioned surface layer brick body, is kept for 3-5 minutes, passes through heat treatment again, on the one hand, can
To accelerate the rate of drying of paint, while paint being made to become firmer;On the other hand, it improves between surface layer brick body and curing agent
Degrees of fusion;Preferably, in this step, to the heating preheating temperature scope control of surface layer brick body at 50-70 DEG C, also using red
The mode of outer heating preheating carries out heating preheating to surface layer brick body.
The present invention can not only prevent the anti-alkali of pavement brick from appearing in surface, completely cut off the moisture of pavement brick lower layer, can more accelerate
The rate of drying of paint, while paint being made to become firmer.The color for improving pavement brick allows pavement brick in the outer of complexity
There is permanent service life, the corruption of water resistant and wind increases high temperature resistant, the antifriction characteristic of pavement brick, energy in boundary's environment
It is enough that pavement brick is made to keep original color for a long time.
Above embodiments are exemplary description of this patent, do not limit its protection scope, those skilled in the art
Member can also be changed its part, as long as it does not exceed the essence of this patent, within the protection scope of the present patent.
Claims (4)
1. a kind of concrete road surface brick producing process with surface layer, which is characterized in that including surface layer brick body and bottom brick body, specifically
The following steps are included:
The first step bottom brick body is made of concrete and sandstone, the component ratio between the concrete and the sandstone
Example is 1-1.5:1, and the concrete is made with the sandstone of vibration pressurization;
Second step carries out heating preheating to the bottom brick body, is kept for 2-5 minutes;
Third step, uniformly spray-applied primer, the priming paint are underwater paint to Xiang Suoshu bottom brick body, and the spraying of the priming paint is thick
Degree is 0.5-1mm;
4th step manufactures the surface layer brick body above the priming paint, and the surface layer brick body is by cement, coarse sand, silicon ash, lotion system
At;Meanwhile in the surface layer brick body manufacturing process, curing agent is mixed;
5th step heats the surface layer brick body, is kept for 3-5 minutes;
Heating preheating temperature range in the second step is 60-80 DEG C;
Heating preheating is carried out to the bottom brick body using infrared heating preheating method in the second step.
2. a kind of concrete road surface brick producing process with surface layer according to claim 1, which is characterized in that the water
Mud, coarse sand, silicon ash, the ratio of lotion are 4:2:2:2.
3. a kind of concrete road surface brick producing process with surface layer according to claim 2, which is characterized in that the described 5th
Heating preheating temperature range in step is 50-70 DEG C.
4. a kind of concrete road surface brick producing process with surface layer according to claim 3, which is characterized in that the described 5th
Heating preheating is carried out to the surface layer brick body using infrared heating preheating method in step.