CN109570162A - The cleaning method of vacuum formed box - Google Patents
The cleaning method of vacuum formed box Download PDFInfo
- Publication number
- CN109570162A CN109570162A CN201811420714.2A CN201811420714A CN109570162A CN 109570162 A CN109570162 A CN 109570162A CN 201811420714 A CN201811420714 A CN 201811420714A CN 109570162 A CN109570162 A CN 109570162A
- Authority
- CN
- China
- Prior art keywords
- vacuum formed
- formed box
- cleaning
- cleaning method
- box according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of cleaning methods of vacuum formed box, it is related to glass panel recruitment harness field, a kind of vacuum formed box cleaning method, comprising the following steps: the vacuum formed box after being used in turn is soaked in containing 3-10min in cleaning solution, the cleaning of vacuum formed box is completed after then washing with water again;Cleaning solution includes the raw material of following weight percent: AE activating agent 5-8%, sodium citrate 10-15%, citric acid 5-10%, anti-corrosion potassium sorbate 5-10% and buffer 3-5%, surplus are water.Existing cleaning method can be alleviated using the vacuum formed box cleaning method and scrub the technical issues of being not thorough, scrubbing low efficiency, achieve the purpose that improve production efficiency.
Description
Technical field
The present invention relates to glass panel recruitment harness fields, more particularly, to a kind of cleaning method of vacuum formed box.
Background technique
In the production process of mobile phone glass panel, it usually needs be used as all rotating toolings of glass panel using vacuum formed box
Tool.Its circular flow after the completion of chemical tempering, need to carry out size full inspection approximately as: mobile phone glass panel, and employee is from pressurization
Vertical feeding in frame lies in vacuum formed box (vacuum formed box has 10 or 8 on chip specifications on chip) after the completion of test again, without in addition
Insert rack scratches risk to avoid increase.When glass panel be circulated to it is next return grinder sequence after, employee from vacuum formed box feeding place
It is ground in grinding machine to remove glass panel potassium nitrate remained on surface.In reclaiming process, employee's remaining milling on hand
Water slurry can drip contamination on vacuum formed box, and the water slurry that is milled after multiple turnaround cycle use is being inhaled with dirt pits, the dry grumeleuse of impurity
It moulds in box, such as in right-angle position and plate contact position and an actor's rendering of an operatic tune, formation intractable is dirty, hereafter will increase in use
The risk that mobile phone glass panel scratches.
Existing cleaning process is pure artificial scrub, and employee is scrubbed using hairbrush.Because of vacuum formed box an actor's rendering of an operatic tune right-angle position and reinforcing
Hole location is more and artificial scrub is forbidden to use soda acid liquid medicine, thus on vacuum formed box the intractables such as milling it is dirty be not thorough in the presence of scrub and
The problems such as scrubbing low efficiency.
In view of this, the present invention is specifically proposed.
Summary of the invention
The purpose of the present invention is to provide a kind of vacuum formed box cleaning method, with alleviate existing cleaning method do the wash it is not thorough
Bottom, the technical issues of scrubbing low efficiency.
In order to realize above-mentioned purpose of the invention, the following technical scheme is adopted:
A kind of vacuum formed box cleaning method, comprising the following steps:
Vacuum formed box after being used in turn is soaked in 3-10min in cleaning solution, completes vacuum formed box after then washing with water again
Cleaning;
The cleaning solution includes the raw material of following weight percent:
AE activating agent 5-8%, sodium citrate 10-15%, citric acid 5-10%, anti-corrosion potassium sorbate 5-10% and buffer
3-5%, surplus are water.
Further, the cleaning solution includes the raw material of following weight percent:
AE activating agent 6-8%, sodium citrate 12-14%, citric acid 6-9%, anti-corrosion potassium sorbate 6-9% and buffer 4-
5%, surplus is water.
Further, the temperature of cleaning solution is 50-70 DEG C.
Further, the vacuum formed box is cleaned with water by the way of the flushing of two steps.
Further, cleaning is first sprayed in spray groove, then sprays cleaning in cleaning machine again.
Further, in spray groove, the time of each vacuum formed box spray cleaning is 20-30s.
Further, the water temperature in the cleaning machine is 40-60 DEG C, up and down to spraying power 1.3-1.7Kg/cm2, transmission speed
Rate 2m/min sprays scavenging period 2-7min.
Further, the material of the vacuum formed box is polyolefin or poly(aryl ether ketone).
Further, the polyolefin is PP or PE.
Further, the poly(aryl ether ketone) is PEEK, PEK, PEKK or PEKEKK.
Compared with the prior art, the invention has the following beneficial effects:
The cleaning method of vacuum formed box provided by the invention impregnates vacuum formed box using the cleaning solution of specific composition ingredient
Processing, after soaking, cleaning solution can make milling for being bonded in vacuum formed box surface etc. completely disengage vacuum formed box, to reach cleaning
The purpose of vacuum formed box.Compared with the method for traditional artificial scrub, the cleaning method of vacuum formed box provided by the invention can be mentioned effectively
Vacuum formed box cleanliness is risen, turnover jig cyclic utilization rate is improved, the dirty residuals such as vacuum formed box milling is reduced and scratches mobile phone glass face
The risk of plate, while the working strength of vacuum formed box cleaning personnel is reduced, reach labor-saving purpose.
Cleaning method provided by the invention does not use the cleaning agents such as strong acid or highly basic, but the weakly acidic cleaning used
Agent, which has no corrosion impact to vacuum formed box itself, and has to the milling being adhered on vacuum formed box stronger clear
Clean ability is detached from it with vacuum formed box.
Through testing, cleaning method provided by the invention, compared with traditional artificial scrub methods, the production efficiency of per person
2 times or more can be improved, so that effectively save human cost, improves production efficiency.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the invention.It is not specified in embodiment specific
Condition person carries out according to conventional conditions or manufacturer's recommended conditions.Reagents or instruments used without specified manufacturer is
The conventional products that can be obtained by commercially available purchase.
On the one hand, the present invention provides a kind of vacuum formed box cleaning methods, comprising the following steps:
Vacuum formed box after being used in turn is soaked in 3-10min in cleaning solution, completes vacuum formed box after then washing with water again
Cleaning;
The cleaning solution includes the raw material of following weight percent:
AE activating agent 5-8%, sodium citrate 10-15%, citric acid 5-10%, anti-corrosion potassium sorbate 5-10% and buffer
3-5%, surplus are water.
AE activating agent also known as the thio benzothiazole ester of 2- (2- amino -4- thiazolyl) -2- (methoxyimino) acetic acid are changed
Digest society (Chemical Abstracts Service, abbreviation CAS) registration number is 80756-85-0.
The cleaning method of vacuum formed box provided by the invention impregnates vacuum formed box using the cleaning solution of specific composition ingredient
Processing, after soaking, cleaning solution can make milling for being bonded in vacuum formed box surface etc. completely disengage vacuum formed box, to reach cleaning
The purpose of vacuum formed box.Compared with the method for traditional artificial scrub, the cleaning method of vacuum formed box provided by the invention can be mentioned effectively
Vacuum formed box cleanliness is risen, turnover jig cyclic utilization rate is improved, the dirty residuals such as vacuum formed box milling is reduced and scratches mobile phone glass face
The risk of plate, while the working strength of vacuum formed box cleaning personnel is reduced, reach labor-saving purpose.
Cleaning method provided by the invention does not use the cleaning agents such as strong acid or highly basic, but the weakly acidic cleaning used
Agent, which has no corrosion impact to vacuum formed box itself, and has to the milling being adhered on vacuum formed box stronger clear
Clean ability is detached from it with vacuum formed box.
Through testing, cleaning method provided by the invention, compared with traditional artificial scrub methods, the production efficiency of per person
2 times or more can be improved, so that effectively save human cost, improves production efficiency.
It by taking the process of mobile phone glass panel as an example, is used in turn, refers to that vacuum formed box is processed in mobile phone glass panel
For carrying mobile phone glass panel in each processing step of journey, in order to the processing and turnover of mobile phone glass panel.
In certain embodiments of the present invention, the material of the vacuum formed box is polyolefin or poly(aryl ether ketone).Wherein, polyene
Hydrocarbon for example can be polypropylene (being abbreviated as PP) or polyethylene (being abbreviated as PE), preferably PP.Poly(aryl ether ketone) for example can be poly-
Ether ether ketone (being abbreviated as PEEK), polyether-ketone (being abbreviated as PEK), polyether ketone ketone (being abbreviated as PEKK) or polyetherketoneetherketoneketone (abbreviation
For PEKEKK), preferably PEEK.Cleaning method provided by the invention has very well the vacuum formed box of polyolefin or poly(aryl ether ketone) material
Cleaning effect.For the vacuum formed box of PP material or PEEK material, cleaning method provided by the invention can achieve preferably clear
Wash effect.
In certain embodiments of the present invention, the cleaning solution includes the raw material of following weight percent:
AE activating agent 6-8%, sodium citrate 12-14%, citric acid 6-9%, anti-corrosion potassium sorbate 6-9% and buffer 4-
5%, surplus is water.
By advanced optimizing the composition of cleaning solution, the cleaning effect of vacuum formed box can be further improved, when shortening cleaning
Between.
In certain embodiments of the present invention, the temperature of cleaning solution is 50-70 DEG C.The work of cleaning solution is improved by heating
Property, and then further increase its cleaning capacity.
In certain embodiments of the present invention, the vacuum formed box is cleaned with water by the way of the flushing of two steps.
For example, first spraying cleaning in spray groove, cleaning is then sprayed in cleaning machine again.By spraying cleaning in spray groove, with
The milling and remaining cleaning agent on vacuum formed box are removed, then cleans the thorough cleaning for carrying out vacuum formed box with cleaning machine again.
Wherein, in spray groove, the time of each vacuum formed box spray cleaning preferably can be 20-30s.
In certain embodiments of the present invention, the water temperature in the cleaning machine is 40-60 DEG C, up and down to spraying power 1.3-
1.7Kg/cm2, transfer rate 2m/min, spray scavenging period 2-7min.Using cleaning machine can simultaneously to multiple vacuum formed boxes into
Row cleaning, improves cleaning efficiency.
Below in conjunction with embodiment and comparative example, the present invention will be further described in detail.
Embodiment 1
The present embodiment is a kind of cleaning method of the vacuum formed box of PP material, comprising the following steps:
A) soaked slot configures 1 people, and by vacuum formed box to be cleaned, successively dislocation is disposed vertically in stainless steel basketry: 20/
Basket, then (5 baskets/slot) are placed in the soaked slot equipped with cleaning solution, 60 DEG C of soaking temperature, soaking time 7min;
Wherein, the cleaning solution in soaked slot includes the raw material of following weight percent: AE activating agent 6%, sodium citrate
10%, citric acid 8%, anti-corrosion potassium sorbate 6% and buffer 4%, surplus are water;
B the whole basket of the vacuum formed box impregnated) will be completed to take out, be placed in spray groove, spray groove configures 2 people and is responsible for dirt removal, often
A vacuum formed box dirt removal time average out to 25s;
C) vacuum formed box for completing dirt removal is sequentially placed into hoop board cleaning machine, is automatically performed cleaning, drying, cleaning machine is matched
It sets 2 people and is responsible for feeding, rewinding;50 DEG C of water temperature of cleaning, up and down to spraying power 1.5Kg/cm2, complete machine transfer rate 2m/min, effectively
Scavenging period 4min is sprayed, vacuum formed box cleaning rate 15.6s/ is a, 230/hour of highest production capacity.
Embodiment 2
The present embodiment is a kind of cleaning method of the vacuum formed box of PP material, comprising the following steps:
A) soaked slot configures 1 people, and by vacuum formed box to be cleaned, successively dislocation is disposed vertically in stainless steel basketry: 20/
Basket, then (5 baskets/slot) are placed in the soaked slot equipped with cleaning solution, 55 DEG C of soaking temperature, soaking time 7min;
Wherein, the cleaning solution in soaked slot includes the raw material of following weight percent: AE activating agent 6%, sodium citrate
12%, citric acid 7%, anti-corrosion potassium sorbate 5% and buffer 5%, surplus are water;
B the whole basket of the vacuum formed box impregnated) will be completed to take out, be placed in spray groove, spray groove configures 2 people and is responsible for dirt removal, often
A vacuum formed box dirt removal time average out to 25s;
C) vacuum formed box for completing dirt removal is sequentially placed into hoop board cleaning machine, is automatically performed cleaning, drying, cleaning machine is matched
It sets 2 people and is responsible for feeding, rewinding;58 DEG C of water temperature of cleaning, up and down to spraying power 1.3Kg/cm2, complete machine transfer rate 2m/min, effectively
Scavenging period 4min is sprayed, vacuum formed box cleaning rate 15.6s/ is a, 230/hour of highest production capacity.
Embodiment 3
The present embodiment is a kind of cleaning method of the vacuum formed box of PP material, comprising the following steps:
A) soaked slot configures 1 people, and by vacuum formed box to be cleaned, successively dislocation is disposed vertically in stainless steel basketry: 20/
Basket, then (5 baskets/slot) are placed in the soaked slot equipped with cleaning solution, 60 DEG C of soaking temperature, soaking time 5min;
Wherein, the cleaning solution in soaked slot includes the raw material of following weight percent: AE activating agent 5%, sodium citrate
10%, citric acid 6%, anti-corrosion potassium sorbate 6% and buffer 5%, surplus are water;
B the whole basket of the vacuum formed box impregnated) will be completed to take out, be placed in spray groove, spray groove configures 2 people and is responsible for dirt removal, often
A vacuum formed box dirt removal time average out to 25s;
C) vacuum formed box for completing dirt removal is sequentially placed into hoop board cleaning machine, is automatically performed cleaning, drying, cleaning machine is matched
It sets 2 people and is responsible for feeding, rewinding;50 DEG C of water temperature of cleaning, up and down to spraying power 1.5Kg/cm2, complete machine transfer rate 2m/min, effectively
Scavenging period 4min is sprayed, vacuum formed box cleaning rate 15.6s/ is a, 230/hour of highest production capacity.
Embodiment 4
The present embodiment is a kind of cleaning method of the vacuum formed box of PEEK material, and specific cleaning step is same as Example 1.
Comparative example 1
This comparative example is a kind of cleaning method of the vacuum formed box of PP material, the cleaning method be using manually to vacuum formed box into
Row scrub.Everyone 1 hourly average scrubs 20.
Each vacuum formed box to 100 groups of PP materials of cleaning method for being utilized respectively embodiment 1-3 and the offer of comparative example 1 carries out clearly
It washes, then checks whether the appearance cleanliness of the vacuum formed box after cleaning is up to standard, and inspection result is listed in table 1.
Each vacuum formed box to 100 groups of PEEK materials of cleaning method that embodiment 4 and comparative example 1 provide is utilized respectively to carry out clearly
It washes, then checks whether the appearance cleanliness of the vacuum formed box after cleaning is up to standard, and inspection result is listed in table 2.
Wherein, test condition: white lamp box, illumination 1000-1200Lux, vacuum formed box are laid flat to lamp box.
Test stone: it examines grind quantity and whether there is or not dirty, vacuum formed box an actor's rendering of an operatic tune and panels after this process flow cleaning
Contact position is dirty whether there is or not intractable and grind is bad, remaining position is visually dirty without bulk, and the intracavitary area of single row is big
In 0.25mm2The bad number of grind is qualified product less than 5.
1 appearance test result of table
Inspection project | Accepted product percentage |
Embodiment 1 | 96% |
Embodiment 2 | 92% |
Embodiment 3 | 90% |
Comparative example 1 | 50% |
2 appearance test result of table
Inspection project | Accepted product percentage |
Embodiment 4 | 91% |
Comparative example 1 | 47% |
It is simple to can be seen that cleaning method technological operation provided by the invention by the data in table 1 and table 1, can save
Manpower reduces vacuum formed box and cleans person works' intensity, realizes the circulation turnover of PP material vacuum formed box and PEEK material vacuum formed box
The raising of utilization rate.
Although illustrate and describing the present invention with specific embodiment, it will be appreciated that without departing substantially from of the invention
Many other change and modification can be made in the case where spirit and scope.It is, therefore, intended that in the following claims
Including belonging to all such changes and modifications in the scope of the invention.
Claims (10)
1. a kind of cleaning method of vacuum formed box, which comprises the following steps:
Vacuum formed box after being used in turn is soaked in 3-10min in cleaning solution, is then washed with water again, the clear of vacuum formed box is completed
It washes;
The cleaning solution includes the raw material of following weight percent:
AE activating agent 5-8%, sodium citrate 10-15%, citric acid 5-10%, anti-corrosion potassium sorbate 5-10% and buffer 3-
5%, surplus is water.
2. the cleaning method of vacuum formed box according to claim 1, which is characterized in that the cleaning solution includes following weight hundred
Divide the raw material of ratio:
AE activating agent 6-8%, sodium citrate 12-14%, citric acid 6-9%, anti-corrosion potassium sorbate 6-9% and buffer 4-5%,
Surplus is water.
3. the cleaning method of vacuum formed box according to claim 1, which is characterized in that the temperature of cleaning solution is 50-70 DEG C.
4. the cleaning method of vacuum formed box according to claim 1-3, which is characterized in that the side rinsed using two steps
Formula cleans the vacuum formed box with water.
5. the cleaning method of vacuum formed box according to claim 4, which is characterized in that first spray cleaning in spray groove, so
Spray cleaning in cleaning machine again afterwards.
6. the cleaning method of vacuum formed box according to claim 5, which is characterized in that in spray groove, each vacuum formed box spray
The time of cleaning is 20-30s.
7. the cleaning method of vacuum formed box according to claim 5, which is characterized in that the water temperature in the cleaning machine is 40-
60 DEG C, up and down to spraying power: 1.3-1.7Kg/cm2, transfer rate 2m/min, spray scavenging period 2-7min.
8. the cleaning method of vacuum formed box according to claim 1-3, which is characterized in that the material of the vacuum formed box
For polyolefin or poly(aryl ether ketone).
9. the cleaning method of vacuum formed box according to claim 8, which is characterized in that the polyolefin is PP or PE.
10. the cleaning method of vacuum formed box according to claim 8, which is characterized in that the poly(aryl ether ketone) be PEEK, PEK,
PEKK or PEKEKK.