CN109568800A - 一种用于改善血液循环缓解风湿的可重复利用的理疗贴片 - Google Patents
一种用于改善血液循环缓解风湿的可重复利用的理疗贴片 Download PDFInfo
- Publication number
- CN109568800A CN109568800A CN201811303128.XA CN201811303128A CN109568800A CN 109568800 A CN109568800 A CN 109568800A CN 201811303128 A CN201811303128 A CN 201811303128A CN 109568800 A CN109568800 A CN 109568800A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- thin film
- nano crystal
- lanthanum boride
- gel thin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及理疗器材，旨在提供一种用于改善血液循环缓解风湿的可重复利用的理疗贴片。该理疗贴片具有相互贴合的层叠结构，其中位于两侧的是硅胶薄膜，在其中一侧硅胶薄膜的外表面均布有微凹坑；在两层硅胶薄膜之间是纳米单晶硼化镧层，单位面积中纳米单晶硼化镧的含量为1～100mg/cm2。本发明能够利用自然太阳光作为红外辐射源，将近红外光转换成热量，达到治疗效果。无需专用医疗场所和专用设备，治疗便利。贴片的一侧分布众多微吸盘，可贴于患处，也可从患处撕下，对皮肤不会构成任何损伤。贴片可以重复利用而不会失效。对于血液循环和微循环障碍引起的多种疾病均具有改善和防治作用，具有极好的市场前景。
Description
技术领域
本发明涉及理疗器材，特别涉及一种用于改善血液循环缓解风湿的可重复利用的理疗贴片。通过光线照射贴于患处的光制热贴片产生热效应改善血液循环，缓解风湿等病痛，能用水洗清除、可重复使用。
背景技术
广义上认为凡是引起骨关节，肌肉疼痛的疾病皆可归属为风湿病。延续下来，至今在风湿病分类上，广义的已有100多种疾病，包括了感染性、免疫性、代谢性、内分泌性、遗传性、退行性、肿瘤性、地方性、中毒性等多种原因引起的疾病。狭义上应该仅限于内科与免疫相关范畴的几十种疾病。风湿病通常是一组侵犯关节、骨骼、肌肉、血管及有关软组织或结缔组织为主的疾病，累及骨、关节及其周围组织如肌肉、肌腱、滑囊、筋膜、韧带、神经等部位，以疼痛为主要临床表现的一大类疾病的总称。因其与自身免疫有关，多数疾病缠绵难愈，隐蔽而缓慢，病程较长，且大多具有遗传倾向。程度不同的免疫性炎症反应，可致成各种组织和器官损伤，严重影响其正常功能，甚至造成致命性损害，有的患者需终身服药治疗。
目前尚无根治此类疾病的药物，西医治疗主要为非甾抗炎药、免疫抑制剂及激素，其长期用药的副作用与其治疗作用一样不应被忽视。这些药物对人体重要的脏器(肝，肾，膀胱，肺，胃肠，生殖腺)和组织(骨髓)各有不同的毒性作用，副作用较大。中医采用针灸、膏药外敷等手段进行治疗。膏药外敷容易引起皮肤过敏，不宜长贴。理疗可以可促进气血运行，舒筋通络，减轻疼痛，提高药效，是风湿病的辅助治疗手段。常用的理疗手段有红外线照射、蜡(热)疗、刮痧疗法、按摩疗法等等。
发明内容
本发明要解决的技术问题是，克服现有技术中的不足，提供一种用于改善血液循环缓解风湿的可重复利用的理疗贴片一种用于改善血液循环缓解风湿的可重复利用的理疗贴片。
为解决上述技术问题，本发明的解决方案是：
提供一种用于改善血液循环缓解风湿的可重复利用的理疗贴片，该理疗贴片具有相互贴合的层叠结构，其中位于两侧的是厚度0.1～0.3mm的硅胶薄膜，在其中一侧硅胶薄膜的外表面均布有直径为2～5mm的微凹坑；在两层硅胶薄膜之间是纳米单晶硼化镧层，单位面积中纳米单晶硼化镧的含量为1～100mg/cm2；该纳米单晶硼化镧的理化性能测试数据：纯度为99.99％，平均粒径200nm、比表面积75m2/g、体积密度0.4g/cm3、密度4.7g/cm3。
本发明中，所述硅胶薄膜是由硅树脂制成；硅树脂是甲基苯基硅树脂、甲基硅树脂、苯基硅树脂中的任意一种。
本发明中，所述硅胶薄膜外表面在单位面积内的微凹坑数量为1～4个/cm2。
本发明中，所述纳米单晶硼化镧是通过下述方式制备获得的：
(1)按镧和硼的摩尔比为1∶6称取氢氧化镧和硼氢化锂粉末的粉末，一并加入球磨罐中；球磨2小时后得到机械混合物；
(2)将机械混合物转移至反应器中，从室温加热至600℃，继续保温2小时；释放反应生成的氢气；
(3)固体产物冷却至室温后，经水洗、离心分离和真空干燥，得到纳米单晶硼化镧。
本发明中，所述步骤(1)中，球磨时控制转速为400rpm。
本发明中，所述步骤(2)中，控制反应器中的升温速率为2℃/min。
本发明中，所述步骤(3)中，控制真空干燥时的温度为80℃。
本发明进一步提供了前述理疗贴片的制备方法，包括以下步骤：
(1)按质量比1∶1∶98称取纳米单晶硼化镧、非离子表面活性剂和去离子水；
(2)将非离子表面活性剂溶于去离子水中，再加入纳米单晶硼化镧，经超声处理15分钟后，得到分散液；
(3)以静电喷涂的方式将分散液喷涂在硅胶薄膜的表面，干燥后在该表面形成纳米单晶硼化镧层；然后在纳米单晶硼化镧层上再覆盖一层硅胶薄膜，形成层叠结构的中间产品；
(4)将层叠结构的中间产品通过轧辊，在150～300℃条件下进行轧制，得到理疗贴片贴片产品；轧辊的表面均布直径为2～5mm的微球凸起，使层叠结构经轧制后内部紧密贴合，同时还在其中一侧硅胶薄膜的外表面形成均布的微凹坑。
本发明中，所述非离子表面活性剂的亲水亲油平衡值为4.7～15.3，是下述的任意一种：山梨糖醇酐单硬脂酸酯、聚氧乙烯二油酸酯、聚氧乙烯十六烷基醚、聚氧乙烯油基醚。
本发明所述理疗贴片的使用方法：
将理疗贴片覆盖于风湿病痛处的皮肤表面，稍用力按压平伏，通过挤出微坑中的空气而形成负压，从而实现在皮肤上的紧密附着。
发明原理描述：
红外线是在所有太阳光中最能够深入皮肤和皮下组织的一种射线。常见的红外理疗是利用具有较强的渗透力和辐射力的远红外线，具有显著的温控效应和共振效应，它易被物体吸收并转化为物体的内能。远红外线被人体吸收后，可使体内水分子产生共振，使水分子活化，增强其分子间的结合力，从而活化蛋白质等生物大分子，使生物体细胞处于最高振动能级。由于生物细胞产生共振效应，可将远红外热能传递到人体皮下较深的部分，以下深层温度上升，产生的温热由内向外散发。这种作用强度，使毛细血管扩张，促进血液循环，有利于清除血管囤积物及体内有害物质，将妨害新陈代谢的障碍清除，重新使组织复活，促进酵素生成，达到活化组织细胞、防止老化、强化免疫系统和各组织之间的新陈代谢，增加组织的再生能力，调节精神的异常兴奋状态，从而产生医疗保健的作用。所以远红外线对于血液循环和微循环障碍引起的多种疾病均具有改善和防治作用，如缓解风湿筋骨、肌肉酸痛、肌腱炎、褥疮、烫伤及伤口不易愈合等疾病，都可以利用远红外线促进血液循环的特性，而达到辅助治疗的目的。
此外，对人体内的一些有害物质，例如食品中的重金属和其它有毒物质、乳酸、游离脂肪酸、脂肪和皮下脂肪、钠离子、尿酸、积存在毛细孔中化妆品残余物等，就能够借助代谢的方式，不必透过肾脏，直接从皮肤和汗水一起排出，可避免增加肾脏的负担。
近红外线或称短波红外线，波长0.76～1.5微米，穿透人体组织较深,约5～10毫米；远红外线或称长波红外线，波长1.5～400微米，多被表层皮肤吸收，穿透组织深度小于2毫米。然而远红外线照射面积大，导致针对性不够。对于患处的局部处理能力弱，如褥疮、烫伤及伤口久治不愈等不需要大面积照射。因此，本发明利用局部光制热贴片可以解决局部患处的治疗矛盾。
硼化镧是一种红紫色晶体，常温下不溶于水和酸，具有很高的化学稳定性。硼化镧的用途十分广泛，利用其低的功函数，低的挥发性，低电阻，高机械强度，高化学稳定性的优点，主要应用于雷达航空航天、电子工业、仪表仪器、医疗器械、家电冶金、环保等二十余个军事和高科技领域。六硼化镧产品主要包括无定形、多晶体、单晶体六硼化镧。特别是六硼化镧单晶，具有良好的近红外辐射吸收转变成热的特性，可作为一种化学稳定性高的光制热材料。
金属硼化物的制备有热压烧结、机械合金化、自蔓延高温合成、电解熔盐、溶剂热法、放电等离子烧结等合成方法。这些方法生产品的硼化镧质量控制困难，无法大批量工业化生产。而利用镧化合物和碱金属硼氢化合物反应可批量生产纳米单晶硼化镧。
硅树脂一般以有机氯硅烷混合物或有机乙氧基硅烷为原料，在混合溶剂中经过水解、缩聚反应制得。硅树脂的固化是在加热或催化剂作用下，转变成具有三维网状结构、不溶不熔的热固性树脂的过程。硅树脂是具有高度交联结构的热固性聚有机硅氧烷，因其特殊的结构，以硅树脂制备的薄膜具有优异的耐热性、耐寒性、耐候性、电绝缘性、疏水性及防粘脱模性等，即使在紫外线强烈照射下，硅树脂也耐泛黄。因此，被广泛用作耐高低温绝缘漆、耐热涂料、耐候涂料、耐烧蚀涂料及耐高低温、电绝缘的模塑料等。因此，以硅树脂为基材的光制热贴片具有美观，耐候，结实耐用，具有良好的生物相容性，对人体组织无刺激性、无毒性、无过敏反应、机体排异反应极少；具有良好的理化特性，与皮肤组织接触过程中能保持其原有的弹性和柔软度，不被降解，是一种相当稳定的惰性物质。能耐高温，可消毒。加工成型方便，易高温固化成型，使用方便，是贴片的理想基材。
吸盘是一种利用内外大气压力的差，吸附在物体上的一种挂件，或者是抓取物体的一种工具。如动物的吸附器官，一般呈圆形、中间凹陷的盘状。吸盘有吸附、摄食和运动等功能，例如，蚂蝗前端的口部周围和后端各长有一个吸盘。因此，贴片上构建众多微吸盘，就可以轻松将贴片贴于患处，也可以轻松撕下。不同于膏药以及创可贴的胶带部分，本发明利用了微吸盘的附着力，不需要粘结剂，因此不会产生贴敷膏药所产生的副作用，如皮肤过敏，拔汗毛等现象。
与现有技术相比，本发明的有益效果是：
1、能够利用自然太阳光作为红外辐射源，通过贴于患处的微吸盘光制热贴片将近红外光转换成热量，达到治疗效果。
2、无需专用医疗场所和专用设备，治疗便利。不限于场所，只要在阳光下晒太阳就能有治疗效果。
3、贴片的一侧分布众多微吸盘，可贴于患处，也可从患处撕下，对皮肤不会构成任何损伤。贴片可以重复利用而不会失效。
4、对于血液循环和微循环障碍引起的多种疾病均具有改善和防治作用，特别是对于风湿筋骨、肌肉酸痛、肌腱炎的辅助治疗，既安全便利，又省事省钱，具有极好的市场前景。
附图说明
图1为本发明贴片的叠层结构。
图中附图标记：1-1硅胶薄膜，1-2纳米单晶硼化镧层，1-3硅胶薄膜，1-4微凹坑。
具体实施方式
下面结合具体实施方式对本发明作进一步详细描述：
实施例一：纳米单晶硼化镧合成
按镧和硼的摩尔比为1∶6(La：B＝1∶6)称取氢氧化镧(0.19g)和硼氢化锂(0.26g)粉末加入球磨罐，在400rpm转速下球磨2小时后得到混合物置于反应器中，升温速率2℃/min从室温加热至600℃后保温2小时，释放掉氢气。冷却至室温后水洗，离心分离，80℃下真空干燥所制得纳米单晶硼化镧。
该纳米单晶硼化镧的理化性能测试数据：平均粒径200nm、纯度99.99(％)、比表面积75(m2/g)、体积密度0.4(g/cm3)、密度4.7(g/cm3)。
实施例二：纳米单晶硼化镧的分散液调制
取HLB值为4.7的山梨糖醇酐单硬脂酸酯1g，与98mL去离子水充分溶解，加入实施例一中制得的纳米单晶硼化镧1g，超声处理15分钟，得到纳米单晶硼化镧的分散液。
实施例三：甲基硅树脂为基材的光制热贴片制备
取HLB值为7.5的聚氧乙烯二油酸酯1g，与98mL去离子水充分溶解，加入实施例一中制得的纳米单晶硼化镧1g，超声处理15分钟，得到纳米单晶硼化镧的分散液。
通过静电喷涂，将上述纳米单晶硼化镧均匀喷涂到厚度为0.1mm的甲基硅树脂薄膜上，纳米单晶硼化镧的喷涂量为1mg/cm2，干燥后再覆盖一层厚度为0.1mm的甲基硅树脂薄膜，然后通过带直径为2mm微球凸起的轧辊，在150℃轧制，获得带有直径为2mm微坑的光制热贴片。硅胶薄膜外表面在单位面积内的微凹坑数量为4个/cm2。
若通过带直径为3mm微球凸起的轧辊，在150℃轧制，获得带有直径为3mm微坑的光制热贴片。硅胶薄膜外表面在单位面积内的微凹坑数量为2个/cm2。
若通过带直径为5mm微球凸起的轧辊，在150℃轧制，获得带有直径为5mm微坑的光制热贴片。硅胶薄膜外表面在单位面积内的微凹坑数量为1个/cm2。
实施例四：甲基苯基硅树脂为基材的光制热贴片制备
取HLB值为10.3的聚氧乙烯十六烷基醚1g，与98mL去离子水充分溶解，加入实施例一中制得的纳米单晶硼化镧1g，超声处理15分钟，得到纳米单晶硼化镧的分散液。
通过静电喷涂，将上述纳米单晶硼化镧均匀喷涂到厚度为0.2mm的甲基苯基硅树脂薄膜上，纳米单晶硼化镧的喷涂量为50mg/cm2，干燥后再覆盖一层厚度为0.2mm的甲基苯基硅树脂薄膜，然后通过带直径为3mm微球凸起的轧辊，在200℃轧制，获得带有直径为3mm微坑的光制热贴片。硅胶薄膜外表面在单位面积内的微凹坑数量为2个/cm2。
实施例五：苯基硅树脂为基材的光制热贴片制备
取HLB值为15.3的聚氧乙烯油基醚1g，与98mL去离子水充分溶解，加入实施例一中制得的纳米单晶硼化镧1g，超声处理15分钟，得到纳米单晶硼化镧的分散液。
通过静电喷涂，将上述纳米单晶硼化镧均匀喷涂到厚度为0.3mm的苯基硅树脂薄膜上，纳米单晶硼化镧的喷涂量为100mg/cm2，干燥后再覆盖一层厚度为0.3mm的苯基硅树脂薄膜，然后通过带直径为5mm微球凸起的轧辊，在300℃轧制，获得带有直径为5mm微坑的光制热贴片。硅胶薄膜外表面在单位面积内的微凹坑数量为1个/cm2。
实施例六：光制热贴片使用方法
将患部用纯净水清洗后，取实施例四中得到的光制热贴片，其面积以覆盖患处为宜，纯净水清洗后贴于患部，阳光照射后贴片温度慢慢上升，当患处有灼热感则停止照射，取下贴片，清洗后干燥保存，可重复利用。
实施例七：治疗风湿关节炎的操作步骤
将患部关节用纯净水清洗后，取实施例五中得到的光制热贴片，其面积以覆盖患处为宜，纯净水清洗后贴于患部，在15W红外线灯照射下，贴片温度慢慢上升，当患处有灼热感则停止照射，取下贴片，清洗后置于清水中保存，一日三次治疗，可有效促进血液循环，缓解风湿关节炎的疼痛。
最后，需要注意的是，以上列举的仅是本发明的具体实施例。显然，本发明不限于以上实施例，还可以有很多变形。本领域的普通技术人员能从本发明公开的内容中直接导出或联想到的所有变形，均应认为是本发明的保护范围。
Claims (9)
1.一种用于改善血液循环缓解风湿的可重复利用的理疗贴片，其特征在于，该理疗贴片具有相互贴合的层叠结构，其中位于两侧的是厚度0.1～0.3mm的硅胶薄膜，在其中一侧硅胶薄膜的外表面均布有直径为2～5mm的微凹坑；在两层硅胶薄膜之间是纳米单晶硼化镧层，单位面积中纳米单晶硼化镧的含量为1～100mg/cm2；该纳米单晶硼化镧的纯度为99.99％，平均粒径200nm、比表面积75m2/g、体积密度0.4g/cm3、密度4.7g/cm3。
2.根据权利要求1所述的理疗贴片，其特征在于，所述硅胶薄膜是由硅树脂制成；硅树脂是甲基苯基硅树脂、甲基硅树脂、苯基硅树脂中的任意一种。
3.根据权利要求1所述的理疗贴片，其特征在于，所述硅胶薄膜外表面在单位面积内的微凹坑数量为1～4个/cm2。
4.根据权利要求1所述的理疗贴片，其特征在于，所述纳米单晶硼化镧是通过下述方式制备获得的：
(1)按镧和硼的摩尔比为1∶6称取氢氧化镧和硼氢化锂粉末的粉末，一并加入球磨罐中；球磨2小时后得到机械混合物；
(2)将机械混合物转移至反应器中，从室温加热至600℃，继续保温2小时；释放反应生成的氢气；
(3)固体产物冷却至室温后，经水洗、离心分离和真空干燥，得到纳米单晶硼化镧。
5.根据权利要求1所述的理疗贴片，其特征在于，所述步骤(1)中，球磨时控制转速为400rpm。
6.根据权利要求1所述的理疗贴片，其特征在于，所述步骤(2)中，控制反应器中的升温速率为2℃/min。
7.根据权利要求1所述的理疗贴片，其特征在于，所述步骤(3)中，控制真空干燥时的温度为80℃。
8.权利要求1所述理疗贴片的制备方法，其特征在于，包括以下步骤：
(1)按质量比1∶1∶98称取纳米单晶硼化镧、非离子表面活性剂和去离子水；
(2)将非离子表面活性剂溶于去离子水中，再加入纳米单晶硼化镧，经超声处理15分钟后，得到分散液；
(3)以静电喷涂的方式将分散液喷涂在硅胶薄膜的表面，干燥后在该表面形成纳米单晶硼化镧层；然后在纳米单晶硼化镧层上再覆盖一层硅胶薄膜，形成层叠结构的中间产品；
(4)将层叠结构的中间产品通过轧辊，在150～300℃条件下进行轧制，得到理疗贴片贴片产品；轧辊的表面均布直径为2～5mm的微球凸起，使层叠结构经轧制后内部紧密贴合，同时还在其中一侧硅胶薄膜的外表面形成均布的微凹坑。
9.根据权利要求8所述的方法，其特征在于，所述非离子表面活性剂的亲水亲油平衡值为4.7～15.3，是下述的任意一种：山梨糖醇酐单硬脂酸酯、聚氧乙烯二油酸酯、聚氧乙烯十六烷基醚、聚氧乙烯油基醚。