CN109549410A - A kind of fiber promoting sleep - Google Patents
A kind of fiber promoting sleep Download PDFInfo
- Publication number
- CN109549410A CN109549410A CN201811476015.XA CN201811476015A CN109549410A CN 109549410 A CN109549410 A CN 109549410A CN 201811476015 A CN201811476015 A CN 201811476015A CN 109549410 A CN109549410 A CN 109549410A
- Authority
- CN
- China
- Prior art keywords
- fiber
- pomegranate leaf
- essential oil
- flask
- leaf essential
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of fiber promoting sleep, it is characterised in that by 80~40% polyester fiber, 20~60% functional fiber composition.
Description
The application is a kind of entitled functional core and its processing technology application No. is 201610660417X, Shen
It please be the divisional application of the application for a patent for invention of 2016.06.02 day.
Technical field
The present invention relates to a kind of fiber for promoting sleep and its processing technologys.
Background technique
There are mainly four types of cores currently on the market: one: by all quilts, fiber should be calculated porous fibre
It is that price is most moderate, price is generally at 300 yuan or so.Fiber can be divided four holes, seven apertures in the human head, nine hole quilts etc., and holes on synthetic fibres is got over
Its more warmth retention property, elasticity, gas permeability are also better.Now, the quantity of such core " hole " is more and more, and technology is also more and more first
Into.As the design of seven-hole hollow structure, not only possess good screen resilience, bulkiness, also enhance the cohesive force of fiber and keeps warm
Sexual function.It can exactly machine-wash there are also a big advantage, will not deform.Two: silk quilt.Best silk quilt should be used
100% mulberry silk makees filler.Because silkworm cannot touch the chemical substances such as pesticide during the growth process, therefore silk quilt should be
The quilt of " green " environmental protection.The main component of silk is animal protein fibre, contains ten several amino acid, beneficial to human body.Silk flosssilk wadding
By material be natural silk, ventilative, light and soft, sense of touch is comfortably its maximum feature, and someone even describes it such as the of people
Two layers of skin, it is seen that " personal " degree of silk flosssilk wadding.Silk is pure natural animal protein fibre, has very high moisture absorption, breathes freely
Property, it is known as " fiber queen ".With the silk quilt that silk fills, skin can be allowed freely to perspire, secrete, keep skin
Cleaning is made us fully feeling comfortable.Three: wool comforter.Cashmere is the last word released this year.Wool fiber has good curling
Feature, therefore the heat insulating ability of wool is indubitable.Wool (cashmere) can be described as most personal quilt, this is taken from sheep
The born drapability of hair, its snug fit is good selecting object;In general, average family can choose such quilt
Son, wool quilt is warmer, and gas permeability is more slightly lower than natural feather and silk, but wool comforter cost is not high, and suitable family makes
With.Wool comforter is more natural, will not worry to jump suede as eiderdown quilt, be strayed into respiratory tract, discomfort is caused, also than silk quilt
Wind is more pressed, therefore is very suitable to children's use.Four: eiderdown quilt.The object that is filled primarily with of eiderdown quilt is goose down and two kinds of duck's down.It protects
Warm property is good, and has good hygroscopicity, having a good sweat property, dryer and comfortableer.If you are a kind of people exigent to quality of the life,
A good eiderdown quilt might as well be selected, it not only has good warmth retention property and softness, and does not have constriction and feeling of oppression and heat,
Also there are moisture absorption sweat discharging functions.Compared with the quilt of same volume, the weight of eiderdown quilt is most light, and only 1 to 1.5 kilograms, about
Cotton-wadded quilt 1/3, wool comforter and cocoon-fibre quilt 1/2.Therefore, high mountain uses mountain-climbing sleeping bag all using high-quality natural feather as packing material.Separately
Outside, eiderdown quilt is extremely durable, not hardened, indeformable, and the usual service life is up to twenty or thirty year.But with people's lives water in recent years
Flat raising, people are higher and higher to the comfort and Functional Requirement of household textiles, and the final finishing of textile has become
Improve its function and improves one of the important channel of added value of product.The core of existing market is difficult reaching light comfortable same
When, also there is antibacterial, fragrance and there can be certain vermins-proof effect.
Bombax cotton is due to its unique performance, such as most thin, most light, degree of hollowness highest, most warming Fiber Materials.Have
It is mould proof, soft, waterproof, not thermally conductive, it keeps warm, the features such as hygroscopicity is strong.It is also widely used in various home textile class products at present.
Pomegranate leaf is the leaf of pomegranate, is Punicaceae Punica species.Pomegranate is machaka or arbor, and Gao Tongchang 3-5m is dilute to reach
10m.Branch top is often at sharp sharp lunge, and sprout has corner angle, and hairless, old branch are closely cylindrical.Pomegranate leaf have antibacterial, astringing to arrest diarrhea,
Kill worm, main diarrhea, variolar carbuncle, impetigo, traumatic injury and other effects in angle.The present invention utilizes improved extraction of essential oil technology, micro- glue
Capsule technology and the hollow characteristic of bombax cotton, are used for fiber finishing after microcapsules are made in finishing agent, can be in kapok fibre
Dimension is internal to obtain good finishing agent keeping quality, and useful life longevity is good.
Summary of the invention
Hollow performance and improved extraction of essential oil of the present invention by the experimental selection to multiple fiber, using bombax cotton
Technology, microcapsules technology enable the fiber and core long-time, slow release pomegranate leaf essential oil of manufacture, and play anti-
Bacterium, insect prevention, the effect for helping sleep.
In order to achieve the above objectives, the present invention provides a kind of functional fiber for promoting sleep, it is characterised in that by 80~4
0% polyester fiber, 20~60% functional fiber composition.
The functional fiber is the functional fiber containing pomegranate leaf essential oil.
The pomegranate leaf essential oil is that under type such as extracts: pomegranate leaf crushed 40 meshes, weigh 5g, in 250ml triangle
In bottle, normal hexane 150mL is added by solid-liquid ratio 1:15, sufficiently infiltration is placed in micro-wave oven, microwave treatment conditions: microwave power
For middle-grade (484W), radiated time 5min, fixed frequency 2450MHz.After a certain period of time, taking-up is cooled to room temperature, and is filtered, is filtered out
Extracting solution is placed in 500mL round-bottomed flask, and weigh up in advance weight be W1, under the conditions of -0.80Mpa and 40 DEG C~45 DEG C into
Row rotary evaporation is concentrated to small size, and recycling design waves most solvent, and weigh W2.
The round-bottomed flask is the flask used on Rotary Evaporators.
For pomegranate leaf essential oil, treated that bombax cotton is mixed with polyester fiber for it.
It is a kind of functionality core, it is characterised in that filler by 80 ~ 40% polyester fiber, 20 ~ 60% functional fiber
Composition, preferably 78% polyester fiber and 22% functional fiber, more preferable 60% polyester fiber and 40% functionality it is fine
Dimension, the functional fiber are the functional fiber containing pomegranate leaf essential oil.Percentage is weight percentage.
The preparation method of core, it is characterised in that be prepared including following methods:
Step 1: extracting pomegranate leaf essential oil.Pomegranate leaf be crushed into 40-50 mesh, weigh 10-20g, in 250mL boiling flask
In, n-hexane or normal butane 150-200mL is added by solid-liquid ratio 1:15-1:20, is placed in shaking table in 50-60 DEG C, 100-150
Secondary/min oscillation extraction 3-5h, then carries out heating and refluxing extraction in water-bath, and Extracting temperature is 30-50 DEG C, extraction time
For 25min.Taking-up is cooled to room temperature, filter, filter out extracting solution and be placed in 500mL round-bottomed flask, -0.80Mpa and 40 DEG C~
Rotary evaporation is carried out under the conditions of 45 DEG C and is concentrated to small size, and recycling design waves most solvent, obtains pomegranate leaf essential oil;
Step 2: under conditions of water bath with thermostatic control, by pomegranate leaf essential oil, 1-10g pyrethrins, 1-8g zinc acetate, 2-5g diformazan
Benzene sulfonic acid potassium, 2-10g polyurethanes, are put into microcapsule solution, are heated to stirring evenly, and sequentially add 2.5-5g and smoke clothing
Careless extracting solution, dispersing agent and adhesive, stirring, are made microcapsule dressing agent;Wherein dispersing agent is glyceryl tristearate, paraffin
Equal conventional dispersants, adhesive are starch, dextrin, polyvinyl alcohol, carboxymethyl cellulose, vinyl acetate resin, acrylic resin
Or chlorinated rubber etc.;Microcapsule solution is gelatin or instant Arabic gum.
Third step, after microcapsule dressing agent is applied to fiber surface by the means being atomized by ultrasonic atomization equipment,
One microcapsule finishing agent film of its Surface mulch completes pretreatment;
Then pretreated bombax cotton is put into microcapsule dressing agent again and impregnates by the 4th step, liquid carrying rate 90-100%;
Then it is dehydrated 2 minutes at 30-45 DEG C again, subsequent 60-70 DEG C of low temperature preliminary drying, last naturally dry, functional fiber is made;
Treated bombax cotton and polyester fiber are mixed and made into core by the 5th step.
The preparation method of the core, it is characterised in that: the frequency of oscillation of ultrasonic atomization processing is 1.7MHz-
2.4MHz。
In addition, pomegranate leaf extraction of essential oil can be carried out by following two mode:
One, the organic solvent way of distillation:
Pomegranate leaf crushed 40 meshes, weigh 10g, and in 250mL boiling flask, normal hexane 150mL is added by solid-liquid ratio 1:15,
It is placed in shaking table in 50 DEG C, 100 times/min oscillation extraction 4h.Then heating and refluxing extraction is carried out in water-bath.Extracting temperature
It is 55 DEG C, extraction time 30min.Taking-up is cooled to room temperature, and is filtered, and is filtered out extracting solution and is placed in (the rotation steaming of 500mL round-bottomed flask
The flask used on hair instrument, and weighing up weight in advance is W1) in, it is rotated under the conditions of -0.80Mpa and 40 DEG C~45 DEG C
It is concentrated by evaporation small size, recycling design waves most solvent, and weigh W2.It is calculated as follows and smokes clothing oil extract rate:
Pomegranate leaf extraction of essential oil rate=(weight g) × 100% of (W2-W1) g/ dried flower
Two, microwave―assisted extraction
Pomegranate leaf crushed 40 meshes, weigh 5g, in 250ml triangular flask, normal hexane 150mL is added by solid-liquid ratio 1:15, fills
Sub-dip profit is placed in micro-wave oven, microwave treatment conditions: microwave power is middle-grade (484W), radiated time 5min, fixed frequency
2450MHz.After a certain period of time, taking-up is cooled to room temperature, and is filtered, is filtered out extracting solution and be placed in 500mL round-bottomed flask (Rotary Evaporators
On the flask that uses, and weighing up weight in advance is W1) in, carry out rotary evaporation under the conditions of -0.80Mpa and 40 DEG C~45 DEG C
It is concentrated to small size, recycling design waves most solvent, and weigh W2.Clothing oil extract rate is smoked by above formula calculating.
Compared with prior art, the application has the advantages that
(1) microcapsules technology of the invention forms partial size in the microcapsules of 0.1-0.9 micron range, and mode of appearance is good, point
It is good to dissipate property, and bombax cotton degree of hollowness is high, therefore under the two cooperation, microcapsules can be efficiently entering and be adsorbed on fiber
On;
(2) present invention before impregnation, first pre-processes bombax cotton, is arranged microcapsules with ultrasonic atomization equipment
After agent is applied to fiber surface by the means being atomized, in one microcapsule finishing agent film of its Surface mulch, this means
Using enabling in addition to fibrous inside coats functional material, additionally it is possible to be adhered in outside, effectively increase function
The adhesive rate and releasing effect of property finishing agent;
(3) test is repeated in the various process parameters of pomegranate leaf extraction of essential oil of the present invention, the essential oil purity is high finally obtained,
Had good sustained release effect.And pyrethrins, three kinds of zinc acetate, xylene monosulfonic acid potassium substances are added when manufacturing microcapsule solution, it
Act synergistically with pomegranate leaf essential oil, have the effects that antibacterial, enhance human immunity and anti-relieving itching, in addition, smoking
The addition of clothing grass extracting solution is but also the smell that manufactured core has fragrance pleasant, is urged into sleep, antidepression.
Specific embodiment
The present invention is further elaborated below with reference to embodiment.
Embodiment 1
Step 1: extracting pomegranate leaf essential oil.Pomegranate leaf be crushed into 48 meshes, weigh 15g, in 250mL boiling flask, by material
N-hexane 180mL is added in liquor ratio 1:16, is placed in shaking table in 55 DEG C, 130 times/min oscillation extraction 4h, then in water-bath into
Row heating and refluxing extraction, Extracting temperature are 35 DEG C, extraction time 25min.Taking-up is cooled to room temperature, and is filtered, is filtered out extracting solution
It is placed in 500mL round-bottomed flask, rotary evaporation is carried out under the conditions of -0.80Mpa and 44 DEG C and is concentrated to small size, recycling design,
Most solvent is waved, pomegranate leaf essential oil is obtained;
Step 2: under conditions of water bath with thermostatic control, by the pomegranate leaf essential oil of extraction, 2.5g pyrethrins, 2g zinc acetate, 3g diformazan
Benzene sulfonic acid potassium, 8g polyurethanes, are put into 0.5g/dl gelatin solution, are heated to stirring evenly, and sequentially add lavender and mention
Liquid, dispersing agent and adhesive are taken, stirs, microcapsule dressing agent is made;
Third step, after microcapsule dressing agent is applied to fiber surface by the means being atomized by ultrasonic atomization equipment, in its table
Layer covers a microcapsule finishing agent film, completes pretreatment;The frequency of oscillation of ultrasonic atomization processing is 2.2MHz
Pretreated bombax cotton is put into microcapsule dressing agent and impregnates by the 4th step, liquid carrying rate 90-100%;Then again
It is dehydrated 2 minutes at 34 DEG C, subsequent 67 DEG C of low temperature preliminary dryings, last naturally dry, functional fiber is made;
Treated bombax cotton and polyester fiber are mixed and made into core by the 5th step.
Embodiment 2
Step 1: taking pomegranate leaf essential oil.Pomegranate leaf be crushed into 49 meshes, weigh 18g, in 250mL boiling flask, by feed liquid
Normal butane 180mL is added than 1:19, is placed in shaking table in 45 DEG C, 130 times/min oscillation extraction 4h, is then carried out in water-bath
Heating and refluxing extraction, Extracting temperature are 35 DEG C, extraction time 25min.Taking-up is cooled to room temperature, and is filtered, is filtered out extracting solution and set
In 500mL round-bottomed flask, rotary evaporation is carried out under the conditions of -0.80Mpa and 44 DEG C and is concentrated to small size, recycling design is waved
Solvent to the greatest extent, obtains pomegranate leaf essential oil;
Step 2: under conditions of water bath with thermostatic control, by pomegranate leaf essential oil, 1.5g pyrethrins, 1.5g zinc acetate, 1.5g dimethylbenzene
Potassium sulfonate, 4g polyurethanes, are put into 15%(weight percent) gumwater in, be heated to stirring evenly, successively
Lavender extracting solution, dispersing agent and adhesive is added, microcapsule dressing agent is made in stirring;
Third step, after microcapsule dressing agent is applied to fiber surface by the means being atomized by ultrasonic atomization equipment, in its table
Layer covers a microcapsule finishing agent film, completes pretreatment;The frequency of oscillation of ultrasonic atomization processing is 2MHz
Then pretreated bombax cotton is put into microcapsule dressing agent again and impregnates by the 4th step, liquid carrying rate 100%;Then
It is dehydrated 2 minutes at 38 DEG C again, subsequent 69 DEG C of low temperature preliminary dryings, last naturally dry, functional fiber is made;
Treated bombax cotton and polyester fiber are mixed and made into core by the 5th step.
Embodiment 3
Step 1: taking pomegranate leaf essential oil.Pomegranate leaf be crushed into 50 meshes, weigh 15g, in 250mL boiling flask, by feed liquid
N-hexane 180mL is added than 1:20, is placed in shaking table in 45 DEG C, 130 times/min oscillation extraction 4h, is then carried out in water-bath
Heating and refluxing extraction, Extracting temperature are 35 DEG C, extraction time 25min.Taking-up is cooled to room temperature, and is filtered, is filtered out extracting solution and set
In 500mL round-bottomed flask, rotary evaporation is carried out under the conditions of -0.80Mpa and 44 DEG C and is concentrated to small size, recycling design is waved
Solvent to the greatest extent, obtains pomegranate leaf essential oil;
Step 2: under conditions of water bath with thermostatic control, by pomegranate leaf essential oil, 3g pyrethrins, 1g zinc acetate, 2.4g xylene monosulfonic acid
Potassium, 4.5g polyurethanes, are put into 10% gumwater, are heated to stirring evenly, and sequentially add lavender extraction
Liquid, dispersing agent and adhesive, stirring, are made microcapsule dressing agent;
Third step, after microcapsule dressing agent is applied to fiber surface by the means being atomized by ultrasonic atomization equipment, in its table
Layer covers a microcapsule finishing agent film, completes pretreatment;The frequency of oscillation of ultrasonic atomization processing is 1.8MHz
Then pretreated bombax cotton is put into microcapsule dressing agent again and impregnates by the 4th step, liquid carrying rate 100%;Then
It is dehydrated 2 minutes at 38 DEG C again, subsequent 69 DEG C of low temperature preliminary dryings, last naturally dry, functional fiber is made;
Treated bombax cotton and polyester fiber are mixed and made into core by the 5th step.
Comparative example 1
Bombax cotton in embodiment 1 is substituted for PET Hollow fiber.
Comparative example 2
It is other same as Example 2, but it is not added with three kinds of pyrethrins, zinc acetate, xylene monosulfonic acid potassium substances.
Comparative example 3
Not using ultrasonic atomization pretreatment, it is not added with lavender extracting solution, it is other same as Example 3,.
Through detecting, the core functional outcome of embodiment preparation is as follows:
Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | Comparative example 3 | |
The deep sleep time (hour) | 5.1 | 5.3 | 5.5 | 3 | 2.5 | 2.1 |
Antibiotic property (%) | 99 | 98 | 99.99 | 96 | 87 | 89 |
100 days release rates (%) | 65 | 66 | 63 | 44 | 42 | 40 |
100 days antibiotic rates (%) | 98 | 97.98 | 99.8 | 84 | 83 | 87 |
After washing 10 times | 90 | 89 | 91 | 79 | 73 | 64 |
Note: sleep quality is the mean depth sleeping time that millet bracelet surveys 30 evening of 50 people.
Claims (6)
1. a kind of fiber for promoting sleep, it is characterised in that by 80~40% polyester fiber, 20~60% functional fiber
Composition.
2. fiber as described in claim 1, it is characterised in that the functional fiber is the functionality containing pomegranate leaf essential oil
Fiber.
3. fiber as claimed in claim 2, it is characterised in that the pomegranate leaf essential oil is that under type such as extracts: pomegranate leaf powder
Broken 40 mesh of mistake, weighs 5g, in 250ml triangular flask, normal hexane 150mL is added by solid-liquid ratio 1:15, sufficiently infiltration is placed on
In micro-wave oven, microwave treatment conditions: microwave power is middle-grade (484W), radiated time 5min, fixed frequency 2450MHz.
4. after a certain period of time, taking-up is cooled to room temperature, filters, filter out extracting solution and be placed in 500mL round-bottomed flask, and claim in advance
Good weight is W1, and rotary evaporation is carried out under the conditions of -0.80Mpa and 40 DEG C~45 DEG C and is concentrated to small size, recycling design is waved to the greatest extent
Solvent, weigh W2.
5. fiber as claimed in claim 2, it is characterised in that the round-bottomed flask is the flask used on Rotary Evaporators.
6. fiber as claimed in claim 2, it is characterised in that it is fine for pomegranate leaf essential oil treated bombax cotton and terylene
Dimension is mixed.