CN1095452C - Composite concrete liquid - Google Patents
Composite concrete liquid Download PDFInfo
- Publication number
- CN1095452C CN1095452C CN00113322A CN00113322A CN1095452C CN 1095452 C CN1095452 C CN 1095452C CN 00113322 A CN00113322 A CN 00113322A CN 00113322 A CN00113322 A CN 00113322A CN 1095452 C CN1095452 C CN 1095452C
- Authority
- CN
- China
- Prior art keywords
- present
- concrete
- water
- citric acid
- composite concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a composite liquid for concrete, which is composed of a naphthalene water reducing agent, lignosulfonic acid, inorganic calcium salt, citric acid and water. The present invention has the various functions of retardation, waterproof performance, water reduction, etc.; furthermore, the present invention has the advantages of good performance, no corrosion to steel bars, obvious early strength and enhancement effects, simple technology and low cost, the mixed amount of the present invention is cement is 2%, and the present invention can be suitable for mass concrete pouring and waterproof concrete engineering and pumped concrete.
Description
The present invention relates to a kind of concrete admixture, is multi-functional composite concrete liquids such as a kind of collection slow setting, waterproof, diminishing.
CN1082008A discloses a kind of composite concrete liquid, is calcite is dropped into concentrated hydrochloric acid reaction 4~6 hours, adds electrolytic aluminum, iron trichloride etc. and makes, this complex liquid chlorinity height, steel bar corrosion is had promoter action, and wherein contained iron(ic) chloride can increase concrete shrinkage, causes the crack; Cost is higher; Volume big (3%) in cement, and early potent fruit relatively a little less than.
The object of the present invention is to provide does not a kind ofly have corrosion to reinforcing bar, and concrete shrinkage is not had influence, and cost is low, and volume is little, and early potent fruit is obvious, and collection slow setting, waterproof, diminishing, curing, expansion is multi-functional and the composite concrete liquid of more excellent performance.
Complex liquid of the present invention is made up of following component and weight part:
Naphthalene water reducer 15-22
Calcium lignin sulphonate 10-15
Citric acid 5-10
Inorganic calcium salt 0.008-0.03
Surplus is a water.
Its preparation method is that calcium lignin sulphonate, inorganic calcium salt, citric acid powder are broken to 200 sieve meshes, adds excess water, is heated to 45-50 ℃, stirs 30-40 minute to dissolving, and cooling adds naphthalene water reducer again, stirs, and is finished product, product P H=7~8.
Complex liquid of the present invention is not chloride, so reinforcing bar is not had corrosion, does not contain FeCl
3Concrete shrinkage is not had influence, tangible morning of strong and reinforced effects is arranged, increased by 60%, 28 day and improve more than 15% volume little (2%) in cement in 3 days.Multiple functions such as collection slow setting, waterproof, diminishing, curing, expansion; Technology is simple, and cost is low, excellent property, and its presetting period is 6-7h, and final set is 10-12h, and water-reducing rate reaches 18-25%, and ultimate compression strength is big, applicable to mass concrete cast and water-proof concrete engineering and pump concrete application.
Embodiment 1
Naphthalene water reducer 15kg
Calcium lignin sulphonate 15kg
CaCl
2 0.01kg
Citric acid 10kg
Water 60kg
With calcium lignin sulphonate, CaCl
2, citric acid powder is broken to 200 sieve meshes, adds excess water, is heated to 45-50 ℃, is stirred to dissolving, cooling adds naphthalene water reducer again, stirs, and is finished product.Product P H=8-9, volume 2% in cement, and slow setting 6-8 hour, water-reducing rate 18%.Ultimate compression strength: C40 (3 days) 18.8MPa; C40 (7 days) 33.5MPa; C40 (28 days) 46.5MPa.
Embodiment 2
Naphthalene water reducer 22kg
Calcium lignin sulphonate 10kg
CaSO
4 0.008kg
Citric acid 8kg
Water 60kg
Method by embodiment 1 is made finished product.Volume 2% in the cement, water-reducing rate 25%, ultimate compression strength: C40 (3 days) 18.8MPa; C40 (7 days) 33.5MPa; C40 (28 days) 46.5MPa.
Embodiment 3
Naphthalene water reducer 20kg
Calcium lignin sulphonate 12kg
CaCO
3 0.03kg
Citric acid 6kg
Water 62kg makes finished product by embodiment 1 method.Experimental data is similar to preceding two examples.
Claims (2)
1, a kind of composite concrete liquid is characterized in that being made up of following component and weight part:
Naphthalene water reducer 15-22
Calcium lignin sulphonate 10-15
Citric acid 5-10
Calcium chloride, calcium sulfate 0.008-0.03
Surplus is a water.
2, a kind of preparation method of composite concrete liquid is characterized in that, earlier following solid material is mixed by following weight part:
Calcium lignin sulphonate 10-15 citric acid 5-10
Calcium chloride, calcium sulfate 0.008-0.03
And be crushed to 200 sieve meshes, add excess water.Be heated to 45-50 ℃, and stir 30-40 minute, cool off, add the naphthalene water reducer of weight part 15-22 again, stir, be finished product to dissolving.