CN109535884A - Inorganic nano self-cleaning coating - Google Patents
Inorganic nano self-cleaning coating Download PDFInfo
- Publication number
- CN109535884A CN109535884A CN201710690567.XA CN201710690567A CN109535884A CN 109535884 A CN109535884 A CN 109535884A CN 201710690567 A CN201710690567 A CN 201710690567A CN 109535884 A CN109535884 A CN 109535884A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic nano
- cleaning coating
- nano self
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inorganic nano self-cleaning coating, which weighs following components by weight: 60-100 parts of photocatalyst mixed liquor, 30-45 parts of silicone acrylic emulsion, 15-20 parts of fluorine carbon emulsion, auxiliary agent 4-8 parts hydrophobic, 3-13 parts of nano silica, 5-10 parts of polysiloxanes, 5-15 parts of nanometer anatase titania, konilite 1-5 parts porous, 10-15 parts of titanium tetrachloride, 5-10 parts of Titanium Nitrate, 2-5 parts of calcite, 1-2 parts of ethylene glycol, 0.5-1 parts of thickener, 1-3 parts of coalescing agent, 1-2 parts of dispersing agent and 30-40 parts of water.The present invention uses inorganic nano self-cleaning coating, can reach self-cleaning effect well, not vulnerable to rainwater pollution, contamination spot, avoids cleaning repeatedly expending a large amount of human and material resources and financial resources, also avoids field high altitude operation, social benefit is obvious.
Description
Technical field
The present invention relates to inorganic nano self-cleaning coating technical fields, and in particular to a kind of inorganic nano self-cleaning coating.
Background technique
Currently, building materials, the vehicles, traditional coating used in pipe network bridge are vulnerable to rainwater pollution, contamination spot, repeatedly
Cleaning, which expends a large amount of human and material resources and financial resources, field high altitude operation, can also jeopardize personal safety, therefore, need art technology
Personnel develop a kind of inorganic nano self-cleaning coating.
Summary of the invention
The problem to be solved in the present invention is to have overcome the deficiencies of the prior art and provide a kind of inorganic nano self-cleaning coating.
Its technical scheme applied to solve the technical problem is: a kind of inorganic nano self-cleaning coating, and the inorganic nano is certainly
Cleaning coating weighs following components by weight: 60-100 parts of photocatalyst mixed liquor, 30-45 parts of silicone acrylic emulsion, fluorine carbon emulsion 15-
20 parts, auxiliary agent 4-8 parts hydrophobic, 3-13 parts of nano silica, 5-10 parts of polysiloxanes, nanometer anatase titania 5-15
Part, konilite 1-5 parts porous, 10-15 parts of titanium tetrachloride, 5-10 parts of Titanium Nitrate, 2-5 parts of calcite, 1-2 parts of ethylene glycol, thickening
0.5-1 parts of agent, 1-3 parts of coalescing agent, 1-2 parts of dispersing agent and 30-40 parts of water, preparation method are as follows: in photocatalyst mixed liquor
Silicone acrylic emulsion, fluorine carbon emulsion, nano silica, polysiloxanes, nanometer anatase titania, porous konilite, four is added
Titanium chloride, Titanium Nitrate, calcite, ethylene glycol, thickener, coalescing agent, dispersing agent and water, with high speed mixer with 100000r/
The speed of min is sufficiently mixed to get inorganic nano self-cleaning coating.
Preferably, the hydrophobic auxiliary agent is modified natural nanoclay.
Preferably, the thickener is methylcellulose thickener.
Preferably, the inorganic nano self-cleaning coating further includes following parts by weight of component: 1-2 parts of mould inhibitor and being disappeared
1-3 parts of infusion.
Preferably, the inorganic nano self-cleaning coating weighs following components by weight: photocatalyst mixed liquor 60
Part, 30 parts of silicone acrylic emulsion, 15 parts of fluorine carbon emulsion, 4 parts of hydrophobic auxiliary agent, 3 parts of nano silica, 5 parts of polysiloxanes, anatase titanium dioxide are received
Rice 5 parts of titanium dioxide, 1 part of porous konilite, 10 parts of titanium tetrachloride, 5 parts of Titanium Nitrate, 2 parts of calcite, 1 part of ethylene glycol, thickener
0.5 part, 1 part of coalescing agent, 1 part of dispersing agent and 30 parts of water.
Preferably, the inorganic nano self-cleaning coating further includes following parts by weight of component: 1 part of mould inhibitor and defoaming
1 part of agent.
The invention has the benefit that using inorganic nano self-cleaning coating self-cleaning effect well can be reached, no
Vulnerable to rainwater pollution, contamination spot, avoids cleaning repeatedly expending a large amount of human and material resources and financial resources, also avoid field height
Idle job, social benefit are obvious.
Specific embodiment
Below with reference to embodiment the present invention will be further explained explanation.
Embodiment
A kind of inorganic nano self-cleaning coating, the inorganic nano self-cleaning coating weigh following components by weight: photocatalyst is mixed
Close liquid 60-100 parts, 30-45 parts of silicone acrylic emulsion, 15-20 parts of fluorine carbon emulsion, auxiliary agent 4-8 parts hydrophobic, nano silica 3-13
Part, 5-10 parts of polysiloxanes, 5-15 parts of nanometer anatase titania, konilite 1-5 parts porous, 10-15 parts of titanium tetrachloride, nitre
Sour titanium 5-10 parts, 2-5 parts of calcite, 1-2 parts of ethylene glycol, 0.5-1 parts of thickener, 1-3 parts of coalescing agent, 1-2 parts of dispersing agent and
30-40 parts of water, preparation method are as follows: silicone acrylic emulsion is added in photocatalyst mixed liquor, fluorine carbon emulsion, nano silica, gathers
Siloxanes, nanometer anatase titania, porous konilite, titanium tetrachloride, Titanium Nitrate, calcite, ethylene glycol, thickener, at
Film auxiliary agent, dispersing agent and water are sufficiently mixed with high speed mixer with the speed of 100000r/min to get inorganic nano automatically cleaning
Coating.
The hydrophobic auxiliary agent is modified natural nanoclay.The thickener is methylcellulose thickener.It is described inorganic
Nano self-cleaning paint weighs following components by weight: 60 parts of photocatalyst mixed liquor, 30 parts of silicone acrylic emulsion, fluorine carbon emulsion 15
Part, 4 parts of hydrophobic auxiliary agent, 3 parts of nano silica, 5 parts of polysiloxanes, 5 parts of nanometer anatase titania, porous konilite 1
Part, 10 parts of titanium tetrachloride, 5 parts of Titanium Nitrate, 2 parts of calcite, 1 part of ethylene glycol, 0.5 part of thickener, 1 part of coalescing agent, dispersing agent 1
Part and 30 parts of water.The inorganic nano self-cleaning coating further includes following parts by weight of component: 1 part and 1 part of defoaming agent of mould inhibitor.
Above content is example and explanation of the invention, but does not mean that the obtainable advantage of the present invention is so limited, all
It is wherein one the advantages of may being realized in simple transformation, and/or some embodiments to structure in practice process of the present invention
It is a or it is multiple within the scope of protection of this application.
Claims (6)
1. a kind of inorganic nano self-cleaning coating, it is characterised in that: the inorganic nano self-cleaning coating weighs following by weight
Component: 60-100 parts of photocatalyst mixed liquor, 30-45 parts of silicone acrylic emulsion, 15-20 parts of fluorine carbon emulsion, auxiliary agent 4-8 parts hydrophobic, nanometer
3-13 parts of silica, 5-10 parts of polysiloxanes, 5-15 parts of nanometer anatase titania, konilite 1-5 parts porous, four chlorinations
10-15 parts of titanium, 2-5 parts of calcite, 1-2 parts of ethylene glycol, 0.5-1 parts of thickener, 1-3 parts of coalescing agent, divides 5-10 parts of Titanium Nitrate
1-2 parts and water 30-40 parts of powder, preparation method are as follows: silicone acrylic emulsion, fluorine carbon emulsion, nanometer are added in photocatalyst mixed liquor
Silica, polysiloxanes, nanometer anatase titania, porous konilite, titanium tetrachloride, Titanium Nitrate, calcite, second two
Alcohol, thickener, coalescing agent, dispersing agent and water are sufficiently mixed with high speed mixer with the speed of 100000r/min to get nothing
Machine nano self-cleaning paint.
2. inorganic nano self-cleaning coating according to claim 1, it is characterised in that: the hydrophobic auxiliary agent is modified natural
Nanoclay.
3. inorganic nano self-cleaning coating according to claim 1, it is characterised in that: the thickener is methylcellulose
Thickener.
4. inorganic nano self-cleaning coating according to claim 1, it is characterised in that: the inorganic nano self-cleaning coating
It further include following parts by weight of component: 1-2 parts and defoaming agent 1-3 parts of mould inhibitor.
5. inorganic nano self-cleaning coating according to claim 1, it is characterised in that: the inorganic nano self-cleaning coating
Weigh following components by weight: 60 parts of photocatalyst mixed liquor, 30 parts of silicone acrylic emulsion, 15 parts of fluorine carbon emulsion, 4 parts of hydrophobic auxiliary agent,
3 parts of nano silica, 5 parts of polysiloxanes, 5 parts of nanometer anatase titania, 1 part of porous konilite, 10 parts of titanium tetrachloride,
5 parts of Titanium Nitrate, 2 parts of calcite, 1 part of ethylene glycol, 0.5 part of thickener, 1 part of coalescing agent, 1 part of dispersing agent and 30 parts of water.
6. inorganic nano self-cleaning coating according to claim 4, it is characterised in that: the inorganic nano self-cleaning coating
It further include following parts by weight of component: 1 part and 1 part of defoaming agent of mould inhibitor.