CN109517510A - A kind of Environmental Protective Water-paint and preparation method for wood furniture - Google Patents
A kind of Environmental Protective Water-paint and preparation method for wood furniture Download PDFInfo
- Publication number
- CN109517510A CN109517510A CN201811357168.2A CN201811357168A CN109517510A CN 109517510 A CN109517510 A CN 109517510A CN 201811357168 A CN201811357168 A CN 201811357168A CN 109517510 A CN109517510 A CN 109517510A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- paint
- environmental protective
- wood furniture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to water paint fields, disclose a kind of Environmental Protective Water-paint and preparation method for wood furniture.Including following preparation process: (1) by velveteen, gypsum powder co-grinding, then with dilute sulfuric acid, dispersant and high speed homogenization, dispersion pulp is made;(2) sodium citrate is added after heating dispersion pulp, composite crystal palpus is made;(3) composite crystal palpus, acrylate copolymer emulsion, polyaminoester emulsion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water are uniformly dispersed, the Environmental Protective Water-paint for wood furniture is made.In coating produced by the present invention, composite crystal must have good flexible toughness, good with coating matrix dispersion compatibility, thus dispersibility and suspension stability are good, and obtained Environmental Protective Water-paint has good crack resistance, strong to wood furniture adhesive force, coating is wear-resisting, and water repelling property is excellent.
Description
Technical field
The present invention relates to water paint fields, disclose a kind of for the Environmental Protective Water-paint of wood furniture and preparation side
Method.
Background technique
In the source of atmospheric pollution of people's common concern, volatile organic matter (VOC) is one of significant contributor.It is existing
Oil paint makes one of VOC primary discharge source.The volatilization of the high VOC of organic solvent content therein is big.Especially as indoor dress
Wooden furniture is adornd, carries out coating using a large amount of coating.Therefore the aqueous wooden ware coatings for furniture for developing environmental protection is that VOC is avoided to generate
Most effective approach.
Water paint is either produced, is stored, construction compared to oil paint, or is applied to indoor furniture, is all reduced
Pollution of the VOC to environment.Water paint includes water soluble paint, water-reducible coating, water-dispersible paint (latex paint) 3
Kind.Using water-soluble resin as film forming matter, using polyvinyl alcohol and its various modifiers as representative, in addition to this also water soluble paint is
There are water-soluble alkyd resin, water-soluble epoxy resin and inorganic polymer water-base resin etc..
Water-borne wood coating mainly has acrylic acid and polyurethane system at present.Acrylic acid aqueous wooden ware as main component
Paint, is mainly characterized by that adhesive force is good, will not deepen the color of woodenware;Polyurethane aqueous paint, comprehensive performance is superior, richness
Height, hardness of paint film is high, and wear-resisting property is even more than oil paint, all has a clear superiority in terms of service life, color conditioning;Acrylic acid
With the synthetic aqueous woodware paint as main component of polyurethane, feature increases other than the characteristics of adhering to acrylic paint
Wear-resisting and strong chemical resistance feature.The research and application of novel aqueous woodwork coating are still current hot subject.
Chinese invention patent application number 201410406711.9 discloses a kind of water paint that indoor woodenware uses, according to
Parts by weight, ingredient include 20 ~ 30 parts of silicone acrylic emulsion, 5 ~ 20 parts of color filters, 5 ~ 10 parts of modifying agent, 10 ~ 30 parts of compounded mix,
40 ~ 50 parts of water, wherein color filters include 2 ~ 8 parts of low arsenic iron oxide, 5 ~ 11 parts of iron oxide red, 1 ~ 2 part of toluene, compounded mix packet
Include 1 ~ 5 part of silica solution, 5 ~ 15 parts of calcium carbonate, 1 ~ 5 part of scratch resistance wax assistant.The advantages of invention, is low arsenic iron oxide, oxidation
Iron oxide red, toluene are color forming property as paratonere, the even property of color is preferable, and silicone acrylic emulsion can effectively solve water paint to a certain extent
Anticorrosion;Modifying agent makes curing rate also be improved;The effect of indoor woodenware painting is preferable, extends using the longevity
Life is suitable for promoting.
Chinese invention patent application number 201710022007.7 discloses a kind of woodenware renovation water paint and its preparation
Method, wherein each component raw material of the woodenware renovation with water paint comprising following parts by weight: self-crosslinking aqueous resin 70 ~ 90
Part;3 ~ 5 parts of coalescing agent;0.1 ~ 0.3 part of wetting agent;0.1 ~ 0.5 part of defoaming agent;0.2 ~ 0.6 part of thickener;Grinding auxiliary agent 1 ~ 3
Part;0.1 ~ 2.0 part of adhesion promoter;0.1 ~ 0.3 part of fungicide;1.2 ~ 12.4 parts of deionized water.It is aqueous described in the invention
Coating has well solved current aqueous woodware paint coating and the bad problem of oil paint adhesive force, while woodenware renovation is used
Water paint has very high dry and wet film transparency, good grinability and faster rate of drying.
According to above-mentioned, in the water paint of woodenware in existing scheme, since acrylic acid and aqueous polyurethane itself lack
It falls into, the coating hardness that is formed for wood furniture and wears no resistance, and is poor water resistance, easy to crack, it usually needs inorganic fills out is added
Expect to improve the hardness and water resistance of coating, and in practice, since inorganic filler and coating matrix dispersion compatibility are poor, shadow
The film-formation result for having rung coating causes coating easy to crack.
Summary of the invention
The wider water paint for wood furniture is applied at present, there are coating hardness and is worn no resistance, poor water resistance,
Defect easy to crack, and usually by be added inorganic filler method, due to inorganic filler and coating matrix dispersion compatibility compared with
Difference affects the film-formation result of coating, causes coating to have the defects that wear no resistance, is easy to crack.
To solve the above problems, the invention adopts the following technical scheme:
A kind of preparation method of the Environmental Protective Water-paint for wood furniture, the detailed process of preparation are as follows:
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 10-15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be divided
It is dispersed in gypsum, dispersion pulp is made;
(2) dispersion pulp that step (1) obtains is heated to 90 ~ 100 DEG C, and in the state of being stirred continuously, sodium citrate is added,
Under sodium citrate effect, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound,
Then it is aged 24 ~ 25h, it is dry, the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound is made;
(3) by composite crystal that step (2) obtains must, solid content be 20 ~ 40% acrylate copolymer emulsions, solid content be 30 ~
50% polyaminoester emulsion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made
Environmental Protective Water-paint for wood furniture.
Preferably, step (1) velveteen is by least one in sea island cotton, Egyptian cotton, dry goods cotton, upland cotton, Asiatic cotton
Kind is extracted and is obtained.
Preferably, step (1) dispersing agent be polyethylene glycol, oxidized polyethylene wax, in stearic acid monoglyceride at least
It is a kind of.
Preferably, in step (1): 30 ~ 35 parts by weight of velveteen, 10 ~ 15 parts by weight of gypsum powder, 47 ~ 59 weight of dilute sulfuric acid
Part, 1 ~ 3 parts by weight of dispersing agent.
Preferably, in step (2): 94 ~ 97 parts by weight of dispersion pulp, 3 ~ 6 parts by weight of sodium citrate.
Preferably, step (3) levelling agent is isophorone, diacetone alcohol, dimethyl silicone polymer, polymethyl-benzene base
At least one of siloxanes.
Preferably, step (3) coalescing agent is decylene glycol ester.
Preferably, step (3) thickener is aerosil powder.
Preferably, in step (3): 11 ~ 14 parts by weight of composite crystal palpus, are gathered at 22 ~ 26 parts by weight of acrylate copolymer emulsion
20 ~ 23 parts by weight of urethane lotion, 1 ~ 3 parts by weight of levelling agent, 1 ~ 3 parts by weight of coalescing agent, increase 7 ~ 12 parts by weight of nano mica powder
Thick dose of 1 ~ 3 parts by weight, 16 ~ 37 parts by weight of deionized water.
A kind of Environmental Protective Water-paint for wood furniture prepared by the above method, velveteen and gypsum powder are mixed
Conjunction is uniformly crushed through airslide disintegrating mill;Then with dilute sulfuric acid, dispersing agent through homogenizer high speed homogenization, velveteen is cracked into cellulose and receives
Meter Jing Xu, which is dispersed in gypsum, obtains dispersion pulp;Dispersion pulp is heated, and is stirred continuously, sodium citrate is added, in citric acid
Under sodium effect, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound, after ageing
It is dry, obtain the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound;By composite crystal palpus and acrylate copolymer
Lotion, polyaminoester emulsion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water are uniformly dispersed.
The present invention provides a kind of Environmental Protective Water-paints and preparation method for wood furniture, compared with prior art,
Its feature protruded and excellent effect are:
1, wood furniture must be used at composite crystal by calcium sulfate crystal whiskers and Cellulose nanocrystal palpiform for raw material preparation by proposing
The method of Environmental Protective Water-paint.
2, the present invention is converted into calcium sulfate crystalline substance by gypsum by the way that Cellulose nanocrystal must be dispersed in gypsum water
Calcium sulfate crystal whiskers and Cellulose nanocrystal must must be wound in situ to obtain composite crystal palpus, gained composite crystal there must be good flexibility
Toughness, it is good with coating matrix dispersion compatibility;After especially Cellulose nanocrystal must be wound with calcium sulfate crystal whiskers, sulphur can be assigned
The good dispersed, suspension stability of sour calcium pyroborate, can effectively add modification and prepare high-performance aqueous coating.
3, Environmental Protective Water-paint produced by the present invention has good crack resistance, and strong to wood furniture adhesive force, coating is resistance to
Mill, water repelling property are excellent.
Specific embodiment
In the following, the present invention will be further described in detail by way of specific embodiments, but this should not be interpreted as to the present invention
Range be only limitted to example below.Without departing from the idea of the above method of the present invention, according to ordinary skill
The various replacements or change that knowledge and customary means are made, should be included in the scope of the present invention.
Embodiment 1
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be dispersed
In gypsum, dispersion pulp is made;Velveteen is extracted to obtain by sea island cotton;Dispersing agent is polyethylene glycol;Wherein: 33 weight of velveteen
Part, 13 parts by weight of gypsum powder, 52 parts by weight of dilute sulfuric acid, 2 parts by weight of dispersing agent;
(2) dispersion pulp that step (1) obtains is heated to 94 DEG C, and in the state of being stirred continuously, sodium citrate is added, in lemon
Under the effect of sour sodium, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound, then
It is aged 24.5h, it is dry, the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound is made;Wherein: 95 weight of dispersion pulp
Part, 5 parts by weight of sodium citrate;
(3) by composite crystal that step (2) obtains must, solid content be 28% acrylate copolymer emulsion, solid content be 38% it is poly-
Urethane lotion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made for woodenware
The Environmental Protective Water-paint of furniture;Levelling agent is isophorone;Coalescing agent is decylene glycol ester;Thickener is aerosil
Powder;Wherein: composite crystal must 13 parts by weight, 23 parts by weight of acrylate copolymer emulsion, 21 parts by weight of polyaminoester emulsion, nanometer cloud
9 parts by weight of female powder, 2 parts by weight of levelling agent, 2 parts by weight of coalescing agent, 2 parts by weight of thickener, 28 parts by weight of deionized water.
Environmental Protective Water-paint made from embodiment 1, abrasion test mass loss rate, coating cracking situation are as shown in table 1.
Embodiment 2
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be dispersed
In gypsum, dispersion pulp is made;Velveteen is extracted to obtain by Egyptian cotton;Dispersing agent is oxidized polyethylene wax;Wherein: 31 weight of velveteen
Measure part, 12 parts by weight of gypsum powder, 56 parts by weight of dilute sulfuric acid, 1 parts by weight of dispersing agent;
(2) dispersion pulp that step (1) obtains is heated to 92 DEG C, and in the state of being stirred continuously, sodium citrate is added, in lemon
Under the effect of sour sodium, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound, then
Ageing is for 24 hours, dry, and the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound is made;Wherein: 95 weight of dispersion pulp
Part, 5 parts by weight of sodium citrate;
(3) by composite crystal that step (2) obtains must, solid content be 25% acrylate copolymer emulsion, solid content be 35% it is poly-
Urethane lotion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made for woodenware
The Environmental Protective Water-paint of furniture;Levelling agent is diacetone alcohol;Coalescing agent is decylene glycol ester;Thickener is aerosil
Powder;Wherein: composite crystal must 12 parts by weight, 23 parts by weight of acrylate copolymer emulsion, 21 parts by weight of polyaminoester emulsion, nanometer cloud
8 parts by weight of female powder, 2 parts by weight of levelling agent, 1 parts by weight of coalescing agent, 1 parts by weight of thickener, 32 parts by weight of deionized water.
Environmental Protective Water-paint made from embodiment 2, abrasion test mass loss rate, coating cracking situation are as shown in table 1.
Embodiment 3
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be dispersed
In gypsum, dispersion pulp is made;Velveteen is extracted to obtain by dry goods cotton;Dispersing agent is stearic acid monoglyceride;Wherein: 34 weight of velveteen
Measure part, 14 parts by weight of gypsum powder, 50 parts by weight of dilute sulfuric acid, 2 parts by weight of dispersing agent;
(2) dispersion pulp that step (1) obtains is heated to 98 DEG C, and in the state of being stirred continuously, sodium citrate is added, in lemon
Under the effect of sour sodium, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound, then
It is aged 25h, it is dry, the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound is made;Wherein: 96 weight of dispersion pulp
Part, 4 parts by weight of sodium citrate;
(3) by composite crystal that step (2) obtains must, solid content be 35% acrylate copolymer emulsion, solid content be 45% it is poly-
Urethane lotion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made for woodenware
The Environmental Protective Water-paint of furniture;Levelling agent is dimethyl silicone polymer;Coalescing agent is decylene glycol ester;Thickener is silica
Airsetting rubber powder;Wherein: composite crystal must 13 parts by weight, 25 parts by weight of acrylate copolymer emulsion, 22 parts by weight of polyaminoester emulsion,
10 parts by weight of nano mica powder, 3 parts by weight of levelling agent, 3 parts by weight of coalescing agent, 2 parts by weight of thickener, 22 weight of deionized water
Part.
Environmental Protective Water-paint made from embodiment 3, abrasion test mass loss rate, coating cracking situation are as shown in table 1.
Embodiment 4
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be dispersed
In gypsum, dispersion pulp is made;Velveteen is extracted to obtain by upland cotton;Dispersing agent is polyethylene glycol;Wherein: 30 weight of velveteen
Part, 10 parts by weight of gypsum powder, 59 parts by weight of dilute sulfuric acid, 1 parts by weight of dispersing agent;
(2) dispersion pulp that step (1) obtains is heated to 90 DEG C, and in the state of being stirred continuously, sodium citrate is added, in lemon
Under the effect of sour sodium, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound, then
Ageing is for 24 hours, dry, and the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound is made;Wherein: 94 weight of dispersion pulp
Part, 6 parts by weight of sodium citrate;
(3) by composite crystal that step (2) obtains must, solid content be 20% acrylate copolymer emulsion, solid content be 30% it is poly-
Urethane lotion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made for woodenware
The Environmental Protective Water-paint of furniture;Levelling agent is polymethylphenylsiloxane;Coalescing agent is decylene glycol ester;Thickener is titanium dioxide
Silica aerogel powder;Wherein: composite crystal must 11 parts by weight, 22 parts by weight of acrylate copolymer emulsion, 20 weight of polyaminoester emulsion
Part, 7 parts by weight of nano mica powder, 1 parts by weight of levelling agent, 1 parts by weight of coalescing agent, 1 parts by weight of thickener, 37 weight of deionized water
Measure part.
Environmental Protective Water-paint made from embodiment 4, abrasion test mass loss rate, coating cracking situation are as shown in table 1.
Embodiment 5
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be dispersed
In gypsum, dispersion pulp is made;Velveteen is extracted to obtain by Asiatic cotton;Dispersing agent is oxidized polyethylene wax;Wherein: 35 weight of velveteen
Measure part, 15 parts by weight of gypsum powder, 47 parts by weight of dilute sulfuric acid, 3 parts by weight of dispersing agent;
(2) dispersion pulp that step (1) obtains is heated to 100 DEG C, and in the state of being stirred continuously, sodium citrate is added, in lemon
Under the effect of lemon acid sodium, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal compound, connects
Ageing 25h, it is dry, calcium sulfate crystal whiskers are made and composite crystal palpus that Cellulose nanocrystal must be wound;Wherein: 97 weight of dispersion pulp
Part, 3 parts by weight of sodium citrate;
(3) by composite crystal that step (2) obtains must, solid content be 40% acrylate copolymer emulsion, solid content be 50% it is poly-
Urethane lotion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made for woodenware
The Environmental Protective Water-paint of furniture;Levelling agent is isophorone;Coalescing agent is decylene glycol ester;Thickener is aerosil
Powder;Wherein: composite crystal must 14 parts by weight, 26 parts by weight of acrylate copolymer emulsion, 23 parts by weight of polyaminoester emulsion, nanometer cloud
12 parts by weight of female powder, 3 parts by weight of levelling agent, 3 parts by weight of coalescing agent, 3 parts by weight of thickener, 16 parts by weight of deionized water.
Environmental Protective Water-paint made from embodiment 5, abrasion test mass loss rate, coating cracking situation are as shown in table 1.
Embodiment 6
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be dispersed
In gypsum, dispersion pulp is made;Velveteen is extracted to obtain by Asiatic cotton;Dispersing agent is stearic acid monoglyceride;Wherein: 32 weight of velveteen
Measure part, 13 parts by weight of gypsum powder, 53 parts by weight of dilute sulfuric acid, 2 parts by weight of dispersing agent;
(2) dispersion pulp that step (1) obtains is heated to 95 DEG C, and in the state of being stirred continuously, sodium citrate is added, in lemon
Under the effect of sour sodium, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound, then
It is aged 24.5h, it is dry, the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound is made;Wherein: 96 weight of dispersion pulp
Part, 4 parts by weight of sodium citrate;
(3) by composite crystal that step (2) obtains must, solid content be 30% acrylate copolymer emulsion, solid content be 40% it is poly-
Urethane lotion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made for woodenware
The Environmental Protective Water-paint of furniture;Levelling agent is polymethylphenylsiloxane;Coalescing agent is decylene glycol ester;Thickener is titanium dioxide
Silica aerogel powder;Wherein: composite crystal must 12 parts by weight, 24 parts by weight of acrylate copolymer emulsion, 22 weight of polyaminoester emulsion
Part, 10 parts by weight of nano mica powder, 2 parts by weight of levelling agent, 2 parts by weight of coalescing agent, 2 parts by weight of thickener, deionized water 26
Parts by weight.
Environmental Protective Water-paint made from embodiment 6, abrasion test mass loss rate, coating cracking situation are as shown in table 1.
Comparative example 1
Comparative example 1 not by calcium sulfate crystal whiskers and Cellulose nanocrystal must wind to obtain composite crystal must, but by calcium sulfate crystal whiskers
Directly replacement composite crystal palpus, Environmental Protective Water-paint obtained, abrasion test mass loss rate, coating cracking situation such as 1 institute of table
Show.
The test method of above-mentioned performance indicator are as follows:
Abrasion test mass loss rate: water paint obtained is uniformly coated in plank plane, sufficiently after solidification, is utilized
Taibo abrasion machine is tested, and figure layer cotton is put in reinforcing revolving wheel friction surface, the quality of coating after test wear 1000r
Difference, according to the ratio calculation mass loss rate of mass change value and initial mass;
Coating cracking situation: water paint produced by the present invention is uniformly coated in plank plane, sufficiently after solidification, by sample
It is 50 DEG C, in the environment of relative humidity is 90% that product, which are placed in temperature, the cracking situation of coating after observation 7d, 15d and 30d.
Table 1:
Claims (10)
1. a kind of preparation method of the Environmental Protective Water-paint for wood furniture, which is characterized in that the detailed process of preparation are as follows:
(1) velveteen, gypsum powder are uniformly mixed, airslide disintegrating mill is added and is crushed, by obtained powder and mass concentration
Dilute sulfuric acid, dispersant for 10-15% carry out high speed homogenization using homogenizer, and velveteen, which is cracked into Cellulose nanocrystal, to be divided
It is dispersed in gypsum, dispersion pulp is made;
(2) dispersion pulp that step (1) obtains is heated to 90 ~ 100 DEG C, and in the state of being stirred continuously, sodium citrate is added,
Under sodium citrate effect, gypsum is gradually converted into hemihydrate calcium sulfate crystal whisker, and must wind in situ with Cellulose nanocrystal it is compound,
Then it is aged 24 ~ 25h, it is dry, the composite crystal palpus that calcium sulfate crystal whiskers and Cellulose nanocrystal must be wound is made;
(3) by composite crystal that step (2) obtains must, solid content be 20 ~ 40% acrylate copolymer emulsions, solid content be 30 ~
50% polyaminoester emulsion, nano mica powder, levelling agent, coalescing agent, thickener, deionized water mixing, are uniformly dispersed, are made
Environmental Protective Water-paint for wood furniture.
2. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly (1) described velveteen is extracted by least one of sea island cotton, Egyptian cotton, dry goods cotton, upland cotton, Asiatic cotton and is obtained.
3. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly (1) described dispersing agent is at least one of polyethylene glycol, oxidized polyethylene wax, stearic acid monoglyceride.
4. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly in (1): 30 ~ 35 parts by weight of velveteen, 10 ~ 15 parts by weight of gypsum powder, 47 ~ 59 parts by weight of dilute sulfuric acid, 1 ~ 3 weight of dispersing agent
Part.
5. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly in (2): 94 ~ 97 parts by weight of dispersion pulp, 3 ~ 6 parts by weight of sodium citrate.
6. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly (3) described levelling agent is isophorone, diacetone alcohol, dimethyl silicone polymer, at least one in polymethylphenylsiloxane
Kind.
7. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly (3) described coalescing agent is decylene glycol ester.
8. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly (3) described thickener is aerosil powder.
9. a kind of preparation method of the Environmental Protective Water-paint for wood furniture according to claim 1, it is characterised in that: step
Suddenly in (3): composite crystal must 11 ~ 14 parts by weight, 22 ~ 26 parts by weight of acrylate copolymer emulsion, 20 ~ 23 weight of polyaminoester emulsion
Part, 1 ~ 3 parts by weight of thickener, is gone at 7 ~ 12 parts by weight of nano mica powder, 1 ~ 3 parts by weight of levelling agent, 1 ~ 3 parts by weight of coalescing agent
16 ~ 37 parts by weight of ionized water.
10. a kind of Environmental Protective Water-paint for wood furniture that any one of claim 1 ~ 9 the method is prepared.