CN109516748A - Environment-friendly type peppermint thermal insulation material and preparation method thereof - Google Patents
Environment-friendly type peppermint thermal insulation material and preparation method thereof Download PDFInfo
- Publication number
- CN109516748A CN109516748A CN201910069110.6A CN201910069110A CN109516748A CN 109516748 A CN109516748 A CN 109516748A CN 201910069110 A CN201910069110 A CN 201910069110A CN 109516748 A CN109516748 A CN 109516748A
- Authority
- CN
- China
- Prior art keywords
- parts
- peppermint
- thermal insulation
- environment
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type peppermint thermal insulation material and preparation method thereof, environment-friendly type peppermint thermal insulation material includes the raw material of following parts by weight meter: 40~80 parts of flyash, 140~180 parts of blast-furnace cinder, 30~40 parts of soybean epoxy resin, 10~20 parts of Corvic, 30~60 parts of sodium alginate, 1~10 part of talcum powder, 10~15 parts of peppermint, 20~30 parts of paraffin, 1~5 part of ammonium carbonate, 30~80 parts of water.Method includes the following steps: peppermint is dried, crushes, then mix all raw materials, it is hot-forming.The present invention reduces resource waste the destruction with environment using blast-furnace cinder as the raw material of thermal insulation material.Peppermint has a certain impact to heating conduction, can slightly improve thermal insulation property.The compression strength of thermal insulation material can be improved in sodium alginate.
Description
Technical field
The invention belongs to building fields more particularly to a kind of environment-friendly type peppermint thermal insulation material and preparation method thereof.
Background technique
Thermal insulation material generally refers to the material that thermal coefficient is less than or equal to 0.12.Thermal insulation material have developed rapidly, in industry
With in building use good heat preservation technology and material, can often play a multiplier effect.
Application No. is the Chinese patent applications of CN201711122886.7 to disclose a kind of building thermal insulation material comprising anti-
Fiery base, insulating layer, thermal insulation layer, enhancement layer and outer finishing coat, the thermal insulation layer, insulating layer, enhancement layer and outer finishing coat are set in sequence
In the two sides of fire prevention base, the thermal insulation layer includes first thermal insulation layer and second thermal insulation layer, is passed through in the two sides of fire prevention base viscous
It connects agent and is respectively fixed with first thermal insulation layer and second thermal insulation layer, the insulating layer and enhancement layer setting are in fire prevention base and outer finishing coat
Between, the enhancement layer is carbon fiber layer, is provided with metal mesh in carbon fiber layer.The invention passes through the gold that is arranged in enhancement layer
Belong to net, the whole intensity and anti-bending strength for effectively increasing thermal insulation material improves thermal insulation material by the way that insulating layer is arranged
Thermal insulation property;Decorative layer dip dyeing has fireproof coating, improves the fire protecting performance of thermal insulation material, while having good heat insulating ability
Can, the temperature being effectively guaranteed in building avoids the loss of heat in building.The invention is the change by structure
Realize heat insulation effect
Summary of the invention
The present invention provides a kind of environment-friendly type peppermint thermal insulation materials and preparation method thereof, are led by the selection and technique of material
Heat is low and environmentally friendly.
In order to solve the above-mentioned technical problem, the invention adopts the following technical scheme:
Environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 40~80 parts of flyash, blast-furnace cinder 140
~180 parts, 30~40 parts of soybean epoxy resin, 10~20 parts of Corvic, 30~60 parts of sodium alginate, talcum powder 1~
10 parts, 10~15 parts of peppermint, 20~30 parts of paraffin, 1~5 part of ammonium carbonate, 30~80 parts of water.
Preferably, environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 60 parts of flyash, Blast Furnace Ore
160 parts of slag, 35 parts of soybean epoxy resin, 15 parts of Corvic, 40 parts of sodium alginate, 5 parts of talcum powder, 12 parts of peppermint, stone
25 parts of wax, 3 parts of ammonium carbonate, 50 parts of water.
Preferably, environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 40 parts of flyash, Blast Furnace Ore
140 parts of slag, 30 parts of soybean epoxy resin, 10 parts of Corvic, 30 parts of sodium alginate, 1 part of talcum powder, 10 parts of peppermint, stone
20 parts of wax, 1 part of ammonium carbonate, 30 parts of water.
Preferably, environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 80 parts of flyash, Blast Furnace Ore
180 parts of slag, 40 parts of soybean epoxy resin, 20 parts of Corvic, 60 parts of sodium alginate, 10 parts of talcum powder, 15 parts of peppermint, stone
30 parts of wax, 5 parts of ammonium carbonate, 80 parts of water.
Preferably, environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 50 parts of flyash, Blast Furnace Ore
150 parts of slag, 33 parts of soybean epoxy resin, 18 parts of Corvic, 50 parts of sodium alginate, 7 parts of talcum powder, 13 parts of peppermint, stone
22 parts of wax, 4 parts of ammonium carbonate, 40 parts of water.
Preferably, the degree of polymerization of the Corvic is 700~1200.
The preparation method of environment-friendly type peppermint thermal insulation material, comprising the following steps: peppermint is dried, crushes, then will own
Raw material mixing, it is hot-forming.
Preferably, the hot pressing pressure is 15~17Mpa, hot pressing temperature is 400~4200 DEG C.
The present invention reduces resource waste the destruction with environment using blast-furnace cinder as the raw material of thermal insulation material.Peppermint pair
Heating conduction has a certain impact, and can slightly improve thermal insulation property.The compression strength of thermal insulation material can be improved in sodium alginate.
Specific embodiment
The present invention is further described in detail combined with specific embodiments below.
Embodiment 1
Environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 60 parts of flyash, 160 parts of blast-furnace cinder, big
35 parts of beans epoxy resin, 15 parts of Corvic, 40 parts of sodium alginate, 5 parts of talcum powder, 12 parts of peppermint, 25 parts of paraffin, carbonic acid
3 parts of ammonium, 50 parts of water.
The degree of polymerization of the Corvic is 700~1200.
The preparation method of environment-friendly type peppermint thermal insulation material, comprising the following steps: peppermint is dried, crushes, then will own
Raw material mixing, hot-forming, hot pressing pressure 16Mpa, hot pressing temperature are 400~4200 DEG C.
Embodiment 2
Environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 40 parts of flyash, 140 parts of blast-furnace cinder, big
30 parts of beans epoxy resin, 10 parts of Corvic, 30 parts of sodium alginate, 1 part of talcum powder, 10 parts of peppermint, 20 parts of paraffin, carbonic acid
1 part of ammonium, 30 parts of water.
The degree of polymerization of the Corvic is 700~1200.
The preparation method of environment-friendly type peppermint thermal insulation material, comprising the following steps: peppermint is dried, crushes, then will own
Raw material mixing, hot-forming, hot pressing pressure 15Mpa, hot pressing temperature are 400~4200 DEG C.
Embodiment 3
Environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 80 parts of flyash, 180 parts of blast-furnace cinder, big
40 parts of beans epoxy resin, 20 parts of Corvic, 60 parts of sodium alginate, 10 parts of talcum powder, 15 parts of peppermint, 30 parts of paraffin, carbon
5 parts of sour ammonium, 80 parts of water.
The degree of polymerization of the Corvic is 700~1200.
The preparation method of environment-friendly type peppermint thermal insulation material, comprising the following steps: peppermint is dried, crushes, then will own
Raw material mixing, hot-forming, hot pressing pressure 17Mpa, hot pressing temperature are 400~4200 DEG C.
Embodiment 4
Environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 50 parts of flyash, 150 parts of blast-furnace cinder, big
33 parts of beans epoxy resin, 18 parts of Corvic, 50 parts of sodium alginate, 7 parts of talcum powder, 13 parts of peppermint, 22 parts of paraffin, carbonic acid
4 parts of ammonium, 40 parts of water.
The degree of polymerization of the Corvic is 700~1200.
The preparation method of environment-friendly type peppermint thermal insulation material, comprising the following steps: peppermint is dried, crushes, then will own
Raw material mixing, hot-forming, hot pressing pressure 16Mpa, hot pressing temperature are 400~4200 DEG C.
Reference examples 1
The difference from embodiment 1 is that: not plus peppermint.
Environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 60 parts of flyash, 160 parts of blast-furnace cinder, big
35 parts of beans epoxy resin, 15 parts of Corvic, 40 parts of sodium alginate, 5 parts of talcum powder, 25 parts of paraffin, 3 parts of ammonium carbonate, water
50 parts.
The degree of polymerization of the Corvic is 700~1200.
The preparation method of environment-friendly type peppermint thermal insulation material, comprising the following steps: mix all raw materials, hot-forming, heat
Pressure pressure is 16Mpa, and hot pressing temperature is 400~4200 DEG C.
Reference examples 2
The difference from example 2 is that: not plus sodium alginate.
Environment-friendly type peppermint thermal insulation material, the raw material including following parts by weight meter: 40 parts of flyash, 140 parts of blast-furnace cinder, big
30 parts of beans epoxy resin, 10 parts of Corvic, 1 part of talcum powder, 10 parts of peppermint, 20 parts of paraffin, 1 part of ammonium carbonate, 30 parts of water.
The degree of polymerization of the Corvic is 700~1200.
The preparation method of environment-friendly type peppermint thermal insulation material, comprising the following steps: peppermint is dried, crushes, then will own
Raw material mixing, hot-forming, hot pressing pressure 15Mpa, hot pressing temperature are 400~4200 DEG C.
Performance test:
Thermal coefficient w/mk | Compression strength (28d) MPa | |
Embodiment 1 | 0.025 | 47.6 |
Embodiment 2 | 0.027 | 46.1 |
Embodiment 3 | 0.029 | 43.2 |
Embodiment 4 | 0.023 | 46.5 |
Reference examples 1 | 0.033 | 44.3 |
Reference examples 2 | 0.028 | 32.1 |
Peppermint has a certain impact to heating conduction, can slightly improve thermal insulation property.Heat preservation can be improved in sodium alginate
The compression strength of material.
The above, preferable specific embodiment only of the invention, the scope of protection of the present invention is not limited to this, any ripe
Know those skilled in the art within the technical scope of the present disclosure, the letter for the technical solution that can be become apparent to
Altered or equivalence replacement are fallen within the protection scope of the present invention.
Claims (8)
1. environment-friendly type peppermint thermal insulation material, which is characterized in that the raw material including following parts by weight meter: 40~80 parts of flyash, height
140~180 parts of furnace slag, 30~40 parts of soybean epoxy resin, 10~20 parts of Corvic, 30~60 parts of sodium alginate,
1~10 part of talcum powder, 10~15 parts of peppermint, 20~30 parts of paraffin, 1~5 part of ammonium carbonate, 30~80 parts of water.
2. environment-friendly type peppermint thermal insulation material according to claim 1, which is characterized in that the original including following parts by weight meter
Material: 60 parts of flyash, 35 parts of soybean epoxy resin, 15 parts of Corvic, 40 parts of sodium alginate, is slided 160 parts of blast-furnace cinder
5 parts of mountain flour, 12 parts of peppermint, 25 parts of paraffin, 3 parts of ammonium carbonate, 50 parts of water.
3. environment-friendly type peppermint thermal insulation material according to claim 1, which is characterized in that the original including following parts by weight meter
Material: 40 parts of flyash, 30 parts of soybean epoxy resin, 10 parts of Corvic, 30 parts of sodium alginate, is slided 140 parts of blast-furnace cinder
1 part of mountain flour, 10 parts of peppermint, 20 parts of paraffin, 1 part of ammonium carbonate, 30 parts of water.
4. environment-friendly type peppermint thermal insulation material according to claim 1, which is characterized in that the original including following parts by weight meter
Material: 80 parts of flyash, 40 parts of soybean epoxy resin, 20 parts of Corvic, 60 parts of sodium alginate, is slided 180 parts of blast-furnace cinder
10 parts of mountain flour, 15 parts of peppermint, 30 parts of paraffin, 5 parts of ammonium carbonate, 80 parts of water.
5. environment-friendly type peppermint thermal insulation material according to claim 1, which is characterized in that the original including following parts by weight meter
Material: 50 parts of flyash, 33 parts of soybean epoxy resin, 18 parts of Corvic, 50 parts of sodium alginate, is slided 150 parts of blast-furnace cinder
7 parts of mountain flour, 13 parts of peppermint, 22 parts of paraffin, 4 parts of ammonium carbonate, 40 parts of water.
6. environment-friendly type peppermint thermal insulation material according to claim 1-5, which is characterized in that the polyvinyl chloride tree
The degree of polymerization of rouge is 700~1200.
7. the preparation method based on environment-friendly type peppermint thermal insulation material described in claim 1, which is characterized in that including following step
It is rapid: peppermint is dried, crushes, then mixes all raw materials, it is hot-forming.
8. the preparation method of environment-friendly type peppermint thermal insulation material according to claim 7, which is characterized in that the hot pressing pressure
Power is 15~17Mpa, and hot pressing temperature is 400~4200 DEG C.