CN109504209A - A kind of preparation method for removing decomposing formaldehyde preparation - Google Patents
A kind of preparation method for removing decomposing formaldehyde preparation Download PDFInfo
- Publication number
- CN109504209A CN109504209A CN201811223884.1A CN201811223884A CN109504209A CN 109504209 A CN109504209 A CN 109504209A CN 201811223884 A CN201811223884 A CN 201811223884A CN 109504209 A CN109504209 A CN 109504209A
- Authority
- CN
- China
- Prior art keywords
- added
- stirred
- preparation
- titanium dioxide
- lopon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods for removing decomposing formaldehyde preparation, including following raw material: titanium dioxide optical catalyst powder, silicone acrylic emulsion, talcum powder, Texanol lipidol, LOPON dispersing agent, defoaming agent；Talcum powder, Texanol lipidol, LOPON dispersing agent, defoaming agent are added in ball-milling dispersion machine, suitable water is added to be stirred, mixing time 4-5h, mixed liquor is made, above-mentioned mixed liquor is heated in agitator tank, and silicone acrylic emulsion is added and is stirred 1-2h, it adds titanium dioxide optical catalyst powder and stirs 0.5-1h in the case where revolving speed is the revolving speed of 2000-3000r/min, neutralizer is added and neutralizes to PH7-7.5；The application preparation can adhere to the body surface of emitting formaldehyde, distributing for formaldehyde can be effectively prevented, and titanium dioxide optical catalyst can be by Formaldehyde decomposition, so that formaldehyde emission is just absorbed less than in air, newly-decorated house is quickly moved in, people's lives are facilitated.
Description
Technical field
The present invention relates to formaldehyde remover production technology method and technology field, in particular to a kind of removing decomposing formaldehyde preparation
Preparation method.
Background technique
Formaldehyde is essential harmful substance in newly-decorated house, and formaldehyde has seriously endangered the health of people.
Therefore, newly-decorated house is needed to dry for a long time just to can be carried out and be moved in, but formaldehyde can persistently distribute very in later life
Long a period of time, therefore it is particularly significant to research and develop a kind of preparation for removing decomposing formaldehyde.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of preparation methods of preparation for being able to produce removing formaldehyde.
In order to solve the above-mentioned technical problem, the technical solution of the present invention is as follows: a kind of preparation side for removing decomposing formaldehyde preparation
Method, including following raw material: titanium dioxide optical catalyst powder, silicone acrylic emulsion, talcum powder, Texanol lipidol, LOPON®890
Dispersing agent, defoaming agent；Talcum powder, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added to ball-milling dispersion machine
In, suitable water is added and is stirred, mixing time 4-5h is made mixed liquor, above-mentioned mixed liquor is heated in agitator tank, and
Silicone acrylic emulsion is added and is stirred 1-2h, adding titanium dioxide optical catalyst powder in revolving speed is turning for 2000-3000r/min
Speed is lower to stir 0.5-1h, and neutralizer is added and neutralizes to PH7-7.5.
Embodiment as one preferred, the component including following mass fraction: titanium dioxide optical catalyst powder 40, silicon
Acrylic emulsion 400, talcum powder 30, Texanol lipidol 20, LOPON®890 dispersing agent 3, defoaming agent 1；By talcum powder, Texanol
Lipidol, LOPON®890 dispersing agent, defoaming agent are added in ball-milling dispersion machine, are added in the water of suitable 2000 score and are carried out
Stirring, mixing time 4-5h are made mixed liquor, above-mentioned mixed liquor are heated in agitator tank, and silicone acrylic emulsion is added and is stirred
1-2h is mixed, titanium dioxide optical catalyst powder is added and stirs 0.5-1h in the case where revolving speed is the revolving speed of 2000-3000r/min, add
Enter neutralizer to neutralize to PH7-7.5.
Embodiment as one preferred, the component including following mass fraction: titanium dioxide optical catalyst powder 45, silicon
Acrylic emulsion 430, talcum powder 35, Texanol lipidol 25, LOPON®890 dispersing agent 4, defoaming agent 1；By talcum powder, Texanol
Lipidol, LOPON®890 dispersing agent, defoaming agent are added in ball-milling dispersion machine, are added in the water of suitable 3000 score and are carried out
Stirring, mixing time 4-5h are made mixed liquor, above-mentioned mixed liquor are heated in agitator tank, and silicone acrylic emulsion is added and is stirred
1-2h is mixed, titanium dioxide optical catalyst powder is added and stirs 0.5-1h in the case where revolving speed is the revolving speed of 2000-3000r/min, add
Enter neutralizer to neutralize to PH7-7.5.
Embodiment as one preferred, the component including following mass fraction: titanium dioxide optical catalyst powder 50, silicon
Acrylic emulsion 450, talcum powder 40, Texanol lipidol 30, LOPON®890 dispersing agent 5, defoaming agent 1.5；By talcum powder,
Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added in ball-milling dispersion machine, and suitable 4000 score is added
It is stirred in water, mixing time 4-5h, mixed liquor is made, above-mentioned mixed liquor is heated in agitator tank, and the third cream of silicon is added
Liquid is stirred 1-2h, adds titanium dioxide optical catalyst powder and stirs in the case where revolving speed is the revolving speed of 2000-3000r/min
0.5-1h is added neutralizer and neutralizes to PH7-7.5.
What the present invention obtained by adopting the above technical scheme has the beneficial effect that the application preparation can adhere to the object of emitting formaldehyde
Body surface face can effectively prevent distributing for formaldehyde, and titanium dioxide optical catalyst can be by Formaldehyde decomposition, so that formaldehyde emission
It is just absorbed less than in air, newly-decorated house is quickly moved in, people's lives are facilitated.
Specific embodiment
Below with reference to embodiment, the invention will be further described.It should be noted that for these embodiments
Explanation be used to help understand the present invention, but and do not constitute a limitation of the invention.In addition, invention described below is each
Technical characteristic involved in embodiment can be combined with each other as long as they do not conflict with each other.
Embodiment 1
A kind of preparation method for removing decomposing formaldehyde preparation, the component including following mass fraction: optically catalytic TiO 2
Agent powder 40, silicone acrylic emulsion 400, talcum powder 30, Texanol lipidol 20, LOPON®890 dispersing agent 3, defoaming agent 1；It will slide
Mountain flour, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added in ball-milling dispersion machine, are added suitable 2000 points
It is stirred in several water, mixing time 4-5h, mixed liquor is made, above-mentioned mixed liquor is heated in agitator tank, and silicon is added
Acrylic emulsion is stirred 1-2h, adds titanium dioxide optical catalyst powder and stirs in the case where revolving speed is the revolving speed of 2000-3000r/min
0.5-1h is mixed, neutralizer is added and neutralizes to PH7-7.5.
Embodiment 2
A kind of preparation method for removing decomposing formaldehyde preparation, the component including following mass fraction: optically catalytic TiO 2
Agent powder 45, silicone acrylic emulsion 430, talcum powder 35, Texanol lipidol 25, LOPON®890 dispersing agent 4, defoaming agent 1；It will slide
Mountain flour, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added in ball-milling dispersion machine, are added suitable 3000 points
It is stirred in several water, mixing time 4-5h, mixed liquor is made, above-mentioned mixed liquor is heated in agitator tank, and silicon is added
Acrylic emulsion is stirred 1-2h, adds titanium dioxide optical catalyst powder and stirs in the case where revolving speed is the revolving speed of 2000-3000r/min
0.5-1h is mixed, neutralizer is added and neutralizes to PH7-7.5.
Embodiment 3
A kind of preparation method for removing decomposing formaldehyde preparation, the component including following mass fraction: optically catalytic TiO 2
Agent powder 50, silicone acrylic emulsion 450, talcum powder 40, Texanol lipidol 30, LOPON®890 dispersing agent 5, defoaming agent 1.5；It will
Talcum powder, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added in ball-milling dispersion machine, are added suitable 4000
It is stirred in the water of score, mixing time 4-5h, mixed liquor is made, above-mentioned mixed liquor is heated in agitator tank, and is added
Silicone acrylic emulsion is stirred 1-2h, adds titanium dioxide optical catalyst powder in the case where revolving speed is the revolving speed of 2000-3000r/min
0.5-1h is stirred, neutralizer is added and neutralizes to PH7-7.5.
The application preparation can adhere to the body surface of emitting formaldehyde, can effectively prevent distributing for formaldehyde, and dioxy
Newly-decorated house can be enabled by Formaldehyde decomposition, so that formaldehyde emission is just absorbed less than in air by changing titanium photochemical catalyst
It is enough quickly to move in, facilitate people's lives.
Above the embodiments of the present invention are described in detail, but the present invention is not limited to described embodiments.It is right
For those skilled in the art, in the case where not departing from the principle of the invention and spirit, these embodiments are carried out more
Kind change, modification, replacement and modification, still fall in protection scope of the present invention.
Claims (4)
1. a kind of preparation method for removing decomposing formaldehyde preparation, which is characterized in that including following raw material: titanium dioxide optical catalyst
Powder, silicone acrylic emulsion, talcum powder, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent；By talcum powder, Texanol rouge
Alcohol, LOPON®890 dispersing agent, defoaming agent are added in ball-milling dispersion machine, and suitable water is added and is stirred, mixing time
4-5h is made mixed liquor, above-mentioned mixed liquor is heated in agitator tank, and silicone acrylic emulsion is added and is stirred 1-2h, is added
Titanium dioxide optical catalyst powder stirs 0.5-1h in the case where revolving speed is the revolving speed of 2000-3000r/min, and neutralizer neutralization is added and arrives
PH7-7.5。
2. the preparation method according to claim 1 for removing decomposing formaldehyde preparation, which is characterized in that including following quality point
Several component: titanium dioxide optical catalyst powder 40, silicone acrylic emulsion 400, talcum powder 30, Texanol lipidol 20, LOPON&
Reg890 dispersing agent 3, defoaming agent 1；Talcum powder, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added to ball
It grinds in dispersion machine, is added in the water of suitable 2000 score and is stirred, mixed liquor is made in mixing time 4-5h, will be above-mentioned mixed
It closes liquid to be heated in agitator tank, and silicone acrylic emulsion is added and is stirred 1-2h, add titanium dioxide optical catalyst powder and turning
0.5-1h is stirred under the revolving speed that speed is 2000-3000r/min, neutralizer is added and neutralizes to PH7-7.5.
3. the preparation method according to claim 1 for removing decomposing formaldehyde preparation, which is characterized in that including following quality point
Several component: titanium dioxide optical catalyst powder 45, silicone acrylic emulsion 430, talcum powder 35, Texanol lipidol 25, LOPON&
Reg890 dispersing agent 4, defoaming agent 1；Talcum powder, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added to ball
It grinds in dispersion machine, is added in the water of suitable 3000 score and is stirred, mixed liquor is made in mixing time 4-5h, will be above-mentioned mixed
It closes liquid to be heated in agitator tank, and silicone acrylic emulsion is added and is stirred 1-2h, add titanium dioxide optical catalyst powder and turning
0.5-1h is stirred under the revolving speed that speed is 2000-3000r/min, neutralizer is added and neutralizes to PH7-7.5.
4. the preparation method according to claim 1 for removing decomposing formaldehyde preparation, it is characterised in that: including following quality point
Several component: titanium dioxide optical catalyst powder 50, silicone acrylic emulsion 450, talcum powder 40, Texanol lipidol 30, LOPON&
Reg890 dispersing agent 5, defoaming agent 1.5；Talcum powder, Texanol lipidol, LOPON®890 dispersing agent, defoaming agent are added to
It in ball-milling dispersion machine, is added in the water of suitable 4000 score and is stirred, mixed liquor is made in mixing time 4-5h, will be above-mentioned
Mixed liquor is heated in agitator tank, and silicone acrylic emulsion is added and is stirred 1-2h, is added titanium dioxide optical catalyst powder and is existed
0.5-1h is stirred under the revolving speed that revolving speed is 2000-3000r/min, neutralizer is added and neutralizes to PH7-7.5.