CN109487971A - A kind of energy health decoration plate and preparation method thereof - Google Patents
A kind of energy health decoration plate and preparation method thereof Download PDFInfo
- Publication number
- CN109487971A CN109487971A CN201811639025.0A CN201811639025A CN109487971A CN 109487971 A CN109487971 A CN 109487971A CN 201811639025 A CN201811639025 A CN 201811639025A CN 109487971 A CN109487971 A CN 109487971A
- Authority
- CN
- China
- Prior art keywords
- oxygen ion
- negative oxygen
- ion powder
- energy
- decoration plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of energy health decoration plates and preparation method thereof, belong to decorative panel processing technique field.The UV finishing coat of UV bleeding agent, the UV seal coat and addition negative oxygen ion powder that add negative oxygen ion powder including the addition negative oxygen ion powder being painted in substrate;The UV bleeding agent for adding negative oxygen ion powder is the negative oxygen ion powder and UV bleeding agent of mass ratio 0.1-0.5:2, and negative oxygen ion powder diameter is 2000-5000 mesh;The UV seal coat for adding negative oxygen ion powder is the negative oxygen ion powder and UV seal coat of mass ratio 1-2:2, and negative oxygen ion powder diameter is 1000-2500 mesh;The UV finishing coat for adding negative oxygen ion powder is the negative oxygen ion powder and UV finishing coat of mass ratio 0.1-0.5:2, and negative oxygen ion powder diameter is 1500-5000 mesh.Decorative panel of the invention has the persistently excellent performances such as excitation releasing negative oxygen ion, high-efficiency antimicrobial, continuing purge air, high mechanical strength, good decorating effect.
Description
Technical field
The present invention relates to decorative panel processing technique field, a kind of energy health decoration plate and its preparation side are specifically disclosed
Method.
Background technique
Fiber cement board, fiber reinforced calcium silicate board are
Main body cementing material is made by slurrying, stream slurry (copy and take), at the processes such as base, precuring, demoulding, steam-cured, dry, sanding surface
Inorganic high-strength light material.In the UV field of coating of fiber cement board, fiber reinforced calcium silicate board product, in the market extensively
Using this kind of coated plate, it is mainly used in the inner wall decoration finishing of building, characteristic is that more pattern, inorganic environment-friendly, durability are good, resistance to
Delineation, energy conservation, cleaning etc., advantage performance obtains highly recognition.
Negative oxygen ion and far infrared have been affirmed fully in the recuperate effect of health care of human body, but fiber cement board, fiber increase
There are no this kind of healthcare functions currently on the market for strong calcium silicate board product, if developing a kind of coated plate with health care function, use
In improving people's lives working environment, not only have a vast market foreground, but also huge social benefit can be generated.
But negative oxygen ion powder is easy to influence the solidification and coating of UV coating in the prior art, and most by negative oxygen ion
Powder painting is attached in surface covering, is easy the dress that passage at any time causes to excite the decreased effectiveness of releasing negative oxygen ion, and prepares
The toxic burst size such as plaque volatile organic matter is larger.
Summary of the invention
To solve problems of the prior art, the present invention provides a kind of energy health decoration plate and preparation method thereof,
The decorative panel has the characteristics that natural, tasteless, nontoxic, safety is good, also has and persistently excites releasing negative oxygen ion, efficiently resists
The excellent performances such as bacterium, continuing purge air, high mechanical strength, water absorption rate be low, good weatherability, durable, good decorating effect.
In order to solve the above technical problems, present invention offer technical solution is as follows:
On the one hand, the present invention provides a kind of energy health decoration plate, including the addition negative oxygen ion powder being painted in substrate
UV bleeding agent, add negative oxygen ion powder UV seal coat and add negative oxygen ion powder UV finishing coat;
The negative oxygen ion powder and UV bleeding agent that the UV bleeding agent of the addition negative oxygen ion powder is mass ratio 0.1-0.5:2,
The negative oxygen ion powder diameter is 2000-5000 mesh;
The negative oxygen ion powder and UV seal coat that the UV seal coat of the addition negative oxygen ion powder is mass ratio 1-2:2, it is described
Negative oxygen ion powder diameter is 300-500 mesh;
The negative oxygen ion powder and UV finishing coat that the UV finishing coat of the addition negative oxygen ion powder is mass ratio 0.1-0.5:2, it is described
Negative oxygen ion powder diameter is 1500-2000 mesh.
Preferably, the negative oxygen ion powder is tourmaline, quartz, opal, wollastonite, Strange ice stone, medical stone, coral
Stone, six ring stones, Lei stone, hornblend, plagioclase, seaweed carbon etc., additive includes aluminum oxide, magnesia, iron oxide, dioxy
Change silicon, lithium potassium niobate, titanium dioxide, sodium oxide molybdena, calcium oxide, zirconium dioxide or yttrium oxide.
Preferably, the substrate is fiber cement board or fiber reinforced calcium silicate board.
On the other hand, the present invention also provides a kind of preparation methods of above-mentioned energy health decoration plate, comprising:
Step 1: by substrate sanding and dedusting;
Step 2: roller coating seal coat is simultaneously solidified into the first UV closing paint layer;
Step 3: again roller coating addition negative oxygen ion powder UV bleeding agent twice, two minor tick 4-5h;
Step 4: infrared ray carries out infiltration processing to the plate of penetrant treating;
Step 5: positive coating UV putty is cured as UV putty layer;
Step 6: the UV seal coat of roller coating three times addition negative oxygen ion powder simultaneously solidifies respectively, forms the 2nd UV and closes paint layer;
Step 7: washed ore light, dedusting;
Step 8: twice of white background priming paint of roller coating is formed by curing half-finished product plate;
Step 9: sanding dedusting, roller coating UV glue generate UV glue-line;
Step 10: roller coating UV F-C paint three times is simultaneously solidified into three layers of UV fluorocarbon layer, then applies the face UV of addition negative oxygen ion powder
Twice of paint is simultaneously solidified into two layers of protective paint layer, energy health decoration plate.
Preferably, in the step 2, the cured energy is 250-300mj/cm2。
Preferably, in the step 6, the solidification energy of the UV seal coat of roller coating three times addition negative oxygen ion powder is respectively
180-240mj/cm2、180-240mj/cm2、1200-2000mj/cm2。
Preferably, in the step 8, solidification energy 1200-2000mj/cm2;
In the step 9, the solidification energy of the UV glue is 50-80mj/cm2, keep UV glue not fully cured.
Preferably, in the step 10, the solidification energy that roller coating UV F-C paint is three times is respectively 100-600mj/cm2、
100-600mj/cm2、100-600mj/cm2。
Preferably, in the step 10, twice of UV finishing coat of solidification energy of Tu Tianjia negative oxygen ion powder is respectively 50-
80mj/cm2、1200-2000mj/cm2。
Further, the preparation method of above-mentioned energy health decoration plate can be with after the step 9 are as follows:
Step 11: the UV film with imitation stone effect being needed on decorative plate of outer wall, UV solidification, it is ensured that one time performance passes through
Energy 1200-2000mj/cm2, transfer, which is finished, is removed PET basement membrane with automatic film rolling machine;
Step 12: roller coating UV glue generates UV glue-line;
Step 13: the UV finishing coat of roller coating three times addition negative oxygen ion powder simultaneously solidifies, and solidification energy is respectively 180-240mj/
cm2、1200-2000mj/cm2。
Preferably, the substrate surface coating layer thickness is 100-110 μm.
Negative oxygen ion powder will select high-grade natural polar mineral, be divided refinement in superstructure technologies method, then
The high-performance that is combined with the inorganic antibacterial material formed by Assembling of Nanoparticles, multifunctional air purifying material, it has
There are lasting releasing negative oxygen ion, transmitting far infrared, the characteristic of high-efficiency antimicrobial, with dope for inner wall of architecture compound coating in decorative panel
On, there is air-cleaning function.Product is by negative oxygen ion to the physical absorption of pernicious gas, chemical breakdown, electrically neutralization etc.
Comprehensive function and purify the pernicious gases such as the formaldehyde discharged in indoor hardware fitting and furniture, ammonia, benzene, TVOC.
Negative oxygen ion material excites the ability of releasing negative oxygen ion related with the fineness of material and proportion, selects to be suitble to material
It is even more important.In terms of considering cost efficiency and UV coating compatibility, the present invention select the negative oxygen formed with multi mineral from
Sub- powder includes SiO as functional material, specific ingredient2、AL2O3、B2O3、MgO、Fe2O3、Na2O、CaO、K2O、TiO2、
Li2O、P2O5Equal microelements.And also different to the granularity requirements of negative oxygen ion powder in different technical process, fineness is being seeped
Saturating technique 2000-5000 mesh, in priming paint technique 1000-2500 mesh, in finishing coat technique 1500-5000 mesh.Negative oxygen ion powder adds
Add, the stability of coating function, the consistency of pattern and the duration for exciting releasing negative oxygen ion certainly will be influenced, so UV coating
Ingredient is used at different process nodes, and paint ingredient proportion is also different.
Present inventor has found that UV coating must pass through ultraviolet photo-curing shape with negative oxygen ion powder by unremitting effort
At can excitated negative oxygen ion coating, coating by tens end production process complete, add negative oxygen ion powder must not influence UV
The normal UV of coating solidifies and the pattern of coating.At different production nodes, UV coating adds matching for negative oxygen ion powder
Than difference, it is 1-2:2 in priming paint technique, in finishing coat that negative oxygen ion powder and UV coating, which are added than being 0.1-0.5:2 in osmosis process,
Technique is 0.1-0.5:2.
Negative oxygen ion powder is mixed with dedicated UV bleeding agent, priming paint and finishing coat, potent dispersion 10-12 minutes respectively, is mixed
Uniformly, nanoscale negative oxygen ion powder is sent into the depths substrate 2-3mm using the powerful infiltration function of UV bleeding agent, realizes decorative panel
The excitation releasing negative oxygen ion healthcare function of material from inside to outside, after coated solidified decorative panel can have internal and surface it is antibacterial,
Bactericidal effect is purified decoration space, while breeding prevented also from decorative panel inside harmful bacteria, improves decorative panel and uses the longevity
Life.
Through test of many times, the coating layer thickness that negative oxygen ion powder is added is 100-110 μm the most reasonable, on the one hand meets protection
Finishing coat basic function, on the other hand enough thickness, enough negative oxygen ion powder dosages guarantee that decorative panel has and stablize purification function
Energy.
Selected negative oxygen ion powder not only has the function of exciting releasing negative oxygen ion, transmitting far infrared, if dosage
Excessively, it also has the side effect of radiation.Therefore meet in national A class finishing material standard and the room QB/T 2761-2006 in satisfaction
Under air clearing product standard requirements, negative oxygen ion powder gross mass is controlled in 8-15g/m2。
Compared with prior art, the invention has the following advantages:
By limiting granule size and materials ratio of the negative oxygen ion powder in different process, successfully prepare has the present invention
Persistently excitation releasing negative oxygen ion, high-efficiency antimicrobial, continuing purge air, good decorating effect energy health decoration plate;The present invention
The preparation method of the energy health decoration plate of offer is simple, by the solidification energy in regulation different process step, so that different
Step coating has different curing degree, convenient for being further processed with follow-up coating so that the decorative panel of preparation have compared with
High mechanical strength, preferable weatherability and durable property.
Specific embodiment
To keep the technical problem to be solved in the present invention, technical solution and advantage clearer, specific embodiment will be used below
It is described in detail, but the present invention is limited to absolutely not these examples.The following is only the preferred embodiment of the present invention, is only used to
Explain the present invention, it cannot be construed as a limitation to the scope of the present invention.It should be pointed out that all of the invention
Any modifications, equivalent replacements, and improvements etc. done within spirit and principle, should all be included in the protection scope of the present invention.
Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Except specified otherwise, component used in the present invention is commercial product.
The present invention provides a kind of energy health decoration plate and preparation method thereof, and specific embodiment is as follows.
Embodiment 1
A kind of energy health decoration plate, UV bleeding agent, addition including the addition negative oxygen ion powder being painted in substrate are negative
The UV seal coat of oxonium ion powder and the UV finishing coat of addition negative oxygen ion powder;
The negative oxygen ion powder and UV bleeding agent that the UV bleeding agent of the addition negative oxygen ion powder is mass ratio 0.1:2, it is described
Negative oxygen ion powder diameter is 2000-5000 mesh;
The negative oxygen ion powder and UV seal coat that the UV seal coat of the addition negative oxygen ion powder is mass ratio 1:2, it is described negative
Oxonium ion powder diameter is 1000-2500 mesh;
The negative oxygen ion powder and UV finishing coat that the UV finishing coat of the addition negative oxygen ion powder is mass ratio 0.1:2, the negative oxygen
Ion powder diameter is 1500-5000 mesh.
Preferably, the negative oxygen ion powder is tourmaline.
The preparation method of above-mentioned energy health decoration plate, comprising:
Step 1: by the sanding of fiber cement board substrate and dedusting, guaranteeing that UV seal coat is spread evenly across on substrate;
Step 2: roller coating seal coat is simultaneously solidified into the first UV closing paint layer, solidification energy 250mj/cm2;
Step 3: roller coating adds the UV bleeding agent of negative oxygen ion powder twice, two minor tick 4h, is conducive to fully penetrated: will permeate
Agent roller coating can penetrate into inside plate on the back of the panel, on the one hand ensure that flatness, cleaning and the drying at the back side, make plate with it is Nian Jie
Cohesive force between agent greatly improves, and another aspect negative oxygen ion powder also penetrates into inside substrate;
Step 4: infrared ray carries out infiltration processing to the plate of penetrant treating;
Step 5: positive coating UV putty is cured as UV putty layer: eliminating board surface defect;
Step 6: three times UV addition negative oxygen ion powder seal coats of roller coating simultaneously solidify respectively, form the 2nd UV and close paint layer, Gu
Changing energy is respectively 180mj/cm2、180mj/cm2、1200mj/cm2;
Step 7: washed ore light, dedusting;
Step 8: twice of white background priming paint of roller coating is formed by curing half-finished product plate, solidification energy 1200mj/cm2;
Step 9: sanding dedusting, roller coating UV glue generate UV glue-line, solidification energy 50mj/cm2, keep UV glue not fully cured;
Step 10: roller coating UV F-C paint three times is simultaneously solidified into three layers of UV fluorocarbon layer, and solidification energy is respectively 100mj/cm2、
100mj/cm2、100mj/cm2, then apply twice of the UV finishing coat of addition negative oxygen ion powder and be solidified into two layers of protective paint layer, solidify energy
Amount is respectively 50mj/cm2、1200mj/cm2, energy health decoration plate.
Embodiment 2
A kind of energy health decoration plate, UV bleeding agent, addition including the addition negative oxygen ion powder being painted in substrate are negative
The UV seal coat of oxonium ion powder and the UV finishing coat of addition negative oxygen ion powder;
The negative oxygen ion powder and UV bleeding agent that the UV bleeding agent of the addition negative oxygen ion powder is mass ratio 0.5:2, it is described
Negative oxygen ion powder diameter is 2000-5000 mesh;
The negative oxygen ion powder and UV seal coat that the UV seal coat of the addition negative oxygen ion powder is mass ratio 2:2, it is described negative
Oxonium ion powder diameter is 300-2500 mesh;
The negative oxygen ion powder and UV finishing coat that the UV finishing coat of the addition negative oxygen ion powder is mass ratio 0.5:2, the negative oxygen
Ion powder diameter is 1500-5000 mesh.
Preferably, the negative oxygen ion powder is quartz.
The preparation method of above-mentioned energy health decoration plate, comprising:
Step 1: by the sanding of fiber cement board substrate and dedusting, guaranteeing that UV seal coat is spread evenly across on substrate;
Step 2: roller coating seal coat is simultaneously solidified into the first UV closing paint layer, and solidification can 300mj/cm2;
Step 3: roller coating adds the UV bleeding agent of negative oxygen ion powder twice, two minor tick 5h, is conducive to fully penetrated: will permeate
Agent roller coating can penetrate into inside plate on the back of the panel, on the one hand ensure that flatness, cleaning and the drying at the back side, make plate with it is Nian Jie
Cohesive force between agent greatly improves, and another aspect negative oxygen ion powder also penetrates into inside substrate;
Step 4: infrared ray carries out infiltration processing to the plate of penetrant treating;
Step 5: positive coating UV putty is cured as UV putty layer: eliminating board surface defect;
Step 6: three times UV addition negative oxygen ion powder seal coats of roller coating simultaneously solidify respectively, form the 2nd UV and close paint layer, Gu
Changing energy is respectively 240mj/cm2、240mj/cm2、2000mj/cm2;
Step 7: washed ore light, dedusting;
Step 8: twice of white background priming paint of roller coating is formed by curing half-finished product plate, solidification energy 2000mj/cm2;
Step 9: roller coating UV glue generates UV glue-line, solidification energy 80mj/cm2, keep UV glue not fully cured;
Step 11: the UV film with imitation stone effect being needed on decorative plate of outer wall, UV solidification, it is ensured that one time performance passes through
Energy 2000mj/cm2, transfer, which is finished, is removed PET basement membrane with automatic film rolling machine;
Step 12: roller coating UV glue generates UV glue-line;
Step 13: the UV finishing coat of roller coating three times addition negative oxygen ion powder simultaneously solidifies, and solidification energy is respectively 240mj/cm2、
2000mj/cm2。
Embodiment 3
A kind of energy health decoration plate, UV bleeding agent, addition including the addition negative oxygen ion powder being painted in substrate are negative
The UV seal coat of oxonium ion powder and the UV finishing coat of addition negative oxygen ion powder;
The negative oxygen ion powder and UV bleeding agent that the UV bleeding agent of the addition negative oxygen ion powder is mass ratio 0.2:2, it is described
Negative oxygen ion powder diameter is 2000-5000 mesh;
The negative oxygen ion powder and UV seal coat that the UV seal coat of the addition negative oxygen ion powder is mass ratio 1.5:2, it is described
Negative oxygen ion powder diameter is 1000-2500 mesh;
The negative oxygen ion powder and UV finishing coat that the UV finishing coat of the addition negative oxygen ion powder is mass ratio 0.4:2, the negative oxygen
Ion powder diameter is 1500-5000 mesh.
Preferably, the negative oxygen ion powder is tourmaline.
The preparation method of above-mentioned energy health decoration plate, comprising:
Step 1: by the sanding of fiber cement board substrate and dedusting, guaranteeing that UV seal coat is spread evenly across on substrate;
Step 2: roller coating seal coat is simultaneously solidified into the first UV closing paint layer, solidification energy 250-300mj/cm2;
Step 3: roller coating adds the UV bleeding agent of negative oxygen ion powder twice, two minor tick 4h, is conducive to fully penetrated: will permeate
Agent roller coating can penetrate into inside plate on the back of the panel, on the one hand ensure that flatness, cleaning and the drying at the back side, make plate with it is Nian Jie
Cohesive force between agent greatly improves, and another aspect negative oxygen ion powder also penetrates into inside substrate;
Step 4: infrared ray carries out infiltration processing to the plate of penetrant treating;
Step 5: positive coating UV putty is cured as UV putty layer: eliminating board surface defect;
Step 6: three times UV addition negative oxygen ion powder seal coats of roller coating simultaneously solidify respectively, form the 2nd UV and close paint layer, Gu
Changing energy is respectively 200mj/cm2、200mj/cm2、1800mj/cm2;
Step 7: washed ore light, dedusting;
Step 8: twice of white background priming paint of roller coating is formed by curing half-finished product plate, solidification energy 1800mj/cm2;
Step 9: roller coating UV glue generates UV glue-line, solidification energy 60mj/cm2, keep UV glue not fully cured;
Step 10: roller coating UV F-C paint three times is simultaneously solidified into three layers of UV fluorocarbon layer, and solidification energy is respectively 400mj/cm2、
400mj/cm2、400mj/cm2, then apply twice of the UV finishing coat of addition negative oxygen ion powder and be solidified into two layers of protective paint layer, solidify energy
Amount is respectively 60mj/cm2、1600mj/cm2, energy health decoration plate.
For the beneficial effect for further illustrating energy health decoration plate prepared by the present invention, because length is limited, only to implement
It is as follows that comparative example is constructed for example 1.
Comparative example 1
During the preparation process, negative oxygen ion powder is not added, remaining condition is same as Example 1.
Comparative example 2
The negative oxygen ion powder in step 3 is omitted in this comparative example, remaining condition is same as Example 1.
Comparative example 3
The negative oxygen ion powder in step 6 is omitted in this comparative example, remaining condition is same as Example 1.
Comparative example 4
The negative oxygen ion powder in step 3 and step 6 is omitted in this comparative example, and the dosage of negative oxygen ion powder in step 10 is increased
Add in embodiment 1 that all negative oxygen ion powder dosages are equal, remaining condition is same as Example 1.
The performance of above-described embodiment 1-3 and comparative example 1-4 decorative panel prepared is measured, measurement is according to JC/
T2040-2010 " anion function indoor decoration material ", and be four sides inner wall surface to above-mentioned decorative panel decoration area is used
Room inner air performance detected, according to " the indoor air purification product clean-up effect measurement side QB/T2761-2006
Method ", it the results are shown in Table 1.
Table 1
In summary, energy health decoration plate prepared by the present invention has the function of persistently exciting releasing negative oxygen ion, together
When the energy health decoration plate formaldehyde for preparing and VOC burst size it is lower.
When negative oxygen ion powder diameter used herein is 1000 mesh, the plaque surface dicoration of preparation is poor.
After the range that negative oxygen ion additive amount is limited beyond the application, on the one hand it is unfavorable for the stabilization of coating, on the other hand, generation
Negative oxygen ion concentration will not significantly improve, and radiativity significantly improves 10% or more.
In summary, the preparation method of energy health decoration plate provided by the invention is simple, has high-efficiency antimicrobial, continues only
The advantages that changing air, good decorating effect.
The above is a preferred embodiment of the present invention, it is noted that for those skilled in the art
For, without departing from the principles of the present invention, it can also make several improvements and retouch, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (10)
1. a kind of energy health decoration plate, which is characterized in that including the UV infiltration for the addition negative oxygen ion powder being painted in substrate
Agent, the UV seal coat for adding negative oxygen ion powder and the UV finishing coat for adding negative oxygen ion powder;
The negative oxygen ion powder and UV bleeding agent that the UV bleeding agent of the addition negative oxygen ion powder is mass ratio 0.1-0.5:2, it is described
Negative oxygen ion powder diameter is 2000-5000 mesh;
The negative oxygen ion powder and UV seal coat that the UV seal coat of the addition negative oxygen ion powder is mass ratio 1-2:2, the negative oxygen
Ion powder diameter is 1000-2500 mesh;
The negative oxygen ion powder and UV finishing coat that the UV finishing coat of the addition negative oxygen ion powder is mass ratio 0.1-0.5:2, the negative oxygen
Ion powder diameter is 1500-5000 mesh.
2. energy health decoration plate according to claim 1, which is characterized in that the negative oxygen ion powder is tourmaline, stone
Diamond stone, opal, wollastonite, Strange ice stone, medical stone, corallite, six ring stones, Lei stone, hornblend, plagioclase or seaweed carbon.
3. energy health decoration plate according to claim 1, which is characterized in that the substrate is fiber cement board or fiber
Enhance calcium silicate board.
4. the preparation method of any energy health decoration plate of claim 1-3 characterized by comprising
Step 1: by substrate sanding and dedusting;
Step 2: roller coating seal coat is simultaneously solidified into the first UV closing paint layer;
Step 3: again roller coating addition negative oxygen ion powder UV bleeding agent twice, two minor tick 4-5h;
Step 4: infrared ray carries out infiltration processing to the plate of penetrant treating;
Step 5: positive coating UV putty is cured as UV putty layer;
Step 6: the UV seal coat of roller coating three times addition negative oxygen ion powder simultaneously solidifies respectively, forms the 2nd UV and closes paint layer;
Step 7: washed ore light, dedusting;
Step 8: twice of white background priming paint of roller coating is formed by curing half-finished product plate;
Step 9: sanding dedusting, roller coating UV glue generate UV glue-line;
Step 10: roller coating UV F-C paint three times is simultaneously solidified into three layers of UV fluorocarbon layer, then applies the UV finishing coat two of addition negative oxygen ion powder
All over and be solidified into two layers of protective paint layer, energy health decoration plate.
5. the preparation method of energy health decoration plate according to claim 4, which is characterized in that described in the step 2
Cured energy is 250-300mj/cm2。
6. the preparation method of energy health decoration plate according to claim 4, which is characterized in that in the step 6, roller coating
The solidification energy of the UV seal coat of three times addition negative oxygen ion powder is respectively 180-240mj/cm2、180-240mj/cm2、1200-
2000mj/cm2。
7. the preparation method of energy health decoration plate according to claim 4, which is characterized in that in the step 8, solidification
Energy is 1200-2000mj/cm2;
In the step 9, the solidification energy of the UV glue is 50-80mj/cm2, keep UV glue not fully cured.
8. the preparation method of energy health decoration plate according to claim 4, which is characterized in that in the step 10, rolling
The solidification energy for applying UV F-C paint three times is respectively 100-600mj/cm2、100-600mj/cm2、100-600mj/cm2;
Twice of UV finishing coat of solidification energy for applying addition negative oxygen ion powder is respectively 50-80mj/cm2、1200-2000mj/cm2。
9. the preparation method of energy health decoration plate according to claim 4, which is characterized in that can after the step 9
With are as follows:
Step 11: the UV film with imitation stone effect being needed on decorative plate of outer wall, UV solidification, it is ensured that one time performance passes through energy
1200-2000mj/cm2, transfer, which is finished, is removed PET basement membrane with automatic film rolling machine;
Step 12: roller coating UV glue generates UV glue-line;
Step 13: the UV finishing coat of roller coating three times addition negative oxygen ion powder simultaneously solidifies, and solidification energy is respectively 180-240mj/cm2、
1200-2000mj/cm2。
10. according to the preparation method of any energy health decoration plate of claim 4-9, which is characterized in that the substrate
Surface covering is with a thickness of 100-110 μm.