KR100989823B1 - Functional paint for wallpaper, method for manufacturing functional wallpaper and functional wallpaper - Google Patents

Functional paint for wallpaper, method for manufacturing functional wallpaper and functional wallpaper Download PDF

Info

Publication number
KR100989823B1
KR100989823B1 KR1020100027388A KR20100027388A KR100989823B1 KR 100989823 B1 KR100989823 B1 KR 100989823B1 KR 1020100027388 A KR1020100027388 A KR 1020100027388A KR 20100027388 A KR20100027388 A KR 20100027388A KR 100989823 B1 KR100989823 B1 KR 100989823B1
Authority
KR
South Korea
Prior art keywords
functional
wallpaper
paint
functional wallpaper
weight
Prior art date
Application number
KR1020100027388A
Other languages
Korean (ko)
Inventor
이윤영
Original Assignee
이윤영
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이윤영 filed Critical 이윤영
Priority to KR1020100027388A priority Critical patent/KR100989823B1/en
Application granted granted Critical
Publication of KR100989823B1 publication Critical patent/KR100989823B1/en

Abstract

PURPOSE: Functional wallpaper paints and a method for manufacturing the functional wallpaper using the same are provided to supply function of antibiosis, deodorization, humidity-resisting properties, oil-absorbing properties or far-infrared radiation radioactivity. CONSTITUTION: A first functional substance of 40~60 parts by weight, a second functional material of 0.5~10 parts by weights and dispersing agent of 0.5~4 parts by weights is mixed about the water soluble adhesive of 100 weight. Water of 5~25 parts by weights is mixed about the functional mixture liquid of 100 parts by weights. The first function material is one or more among red clay stone, elvan, rare earth, and corallite has 100~500 mesh of an average particle size. The second functional material has 100~500 mesh of average granularity. The second functional material is mineral including composite of the conductivity.

Description

기능성 벽지도료와 이를 이용한 기능성 벽지 제조방법 및 기능성 벽지 {Functional paint for wallpaper, method for manufacturing functional wallpaper and functional wallpaper}Functional wallpaper paint and functional wallpaper manufacturing method and functional wallpaper {Functional paint for wallpaper, method for manufacturing functional wallpaper and functional wallpaper}

본 발명은 기능성을 갖는 물질을 포함하는 기능성 벽지도료와 이를 이용한 기능성 벽지 제조방법 및 기능성 벽지에 관한 것으로서,The present invention relates to a functional wallpaper paint containing a material having a functional, a functional wallpaper manufacturing method and a functional wallpaper using the same,

구체적으로, 항균성, 탈취성, 항습성, 흡유성 또는 원적외선 방사성을 갖는 제1기능성물질과, 전도성을 갖는 조성물을 포함하는 광물로서 정전기 방지효과를 갖는 제2 기능성 물질과, 수용성접착제 및 분산제를 혼합한 기능성 혼합액과 상기 기능성 혼합액에 희석제로서 물을 일정 비율 혼합하여 구성한 기능성 벽지도료와; 상기 기능성 벽지도료를 준비하는 도료 준비공정과, 기능성 벽지도료를 펄프재질의 벽지에 코팅하는 코팅공정과, 기능성 벽지도료가 코팅된 벽지를 건조하는 건조공정과, 건조된 벽지를 귄취하는 권취공정으로 구성되는 기능성 벽지도료를 이용한 기능성 벽지 제조방법과; 상기 제조방법 중 건조공정 처리한 펄프재질 벽지를 내면지(1차 건조공정 처리한 벽지)로 하여, 내면지의 코팅면 또는 외면지인 한지 일측면 중 어느 하나의 표면에 수용성접착제를 도포하여 내면지와 외면지를 합지하는 합지공정과, 합지공정 처리한 기능성 벽지를 건조하는 2차 건조공정 및 상기 건조공정으로 건조된 기능성 벽지를 귄취하는 권취공정을 포함하여 구성되는 기능성 벽지도료를 이용한 기능성 벽지 제조방법과; 상기 기능성 벽지도료 및 기능성 벽지 제조방법으로 제조된 기능성 벽지에 관한 것이다.
Specifically, a first functional material having antimicrobial, deodorizing, hygroscopic, oil absorption or far infrared radiation, a second functional material having an antistatic effect as a mineral containing a conductive composition, and a water-soluble adhesive and a dispersant are mixed. A functional wallpaper paint composed of a predetermined ratio of water as a diluent in the functional mixture and the functional mixture; A paint preparation process for preparing the functional wallpaper paint, a coating process for coating the functional wallpaper paint on the pulp material wallpaper, a drying process for drying the wallpaper coated with the functional wallpaper paint, and a winding process for winding the dried wallpaper. A functional wallpaper manufacturing method using a functional wallpaper paint composed of; In the above manufacturing method, the pulp material wallpaper subjected to the drying process is used as the inner paper (the first drying process treated wallpaper), and the water-soluble adhesive is coated on any one surface of the coated paper or the outer paper of the inner paper. A method of manufacturing a functional wallpaper using a functional wallpaper paint comprising a lamination step of laminating outer paper, a secondary drying step of drying the laminated functional wallpaper and a winding step of winding the functional wallpaper dried by the drying step; ; It relates to a functional wallpaper produced by the functional wallpaper paint and a functional wallpaper manufacturing method.

주거 또는 사무용 건축물의 실내 벽체 및 천장에 시공되는 벽지는 재질에 따라, 종이벽지, 합성수지벽지, 섬유벽지 등으로 구분되고, 각 재질에 따른 특징도 다양하여 시공장소의 환경에 따라 각각에 맞는 재질의 벽지를 이용하고 있으나, 합성수지 재질의 벽지는 VOC물질을 포함하여 인체에 해롭다는 것이 널리 알려진 후 그 사용이 줄어들고 인체에 유해한 성분이 적게 포함되는 종이벽지에 관한 관심이 증대되고 있는 추세이다. 다음은 종이벽지(펄프재질의 벽지)와 벽지의 기능성을 다양화하기 위한 이중벽지에 관한 종래기술이다.Wallpapers installed on the interior walls and ceilings of residential or office buildings are classified into paper wallpaper, synthetic resin wallpaper, and fiber wallpaper, depending on the material.The characteristics of each material are also varied. Although wallpaper is used, synthetic resin wallpaper is known to be harmful to the human body, including VOC material, and its use is decreasing, and there is a trend of increasing interest in paper wallpaper containing less harmful components to the human body. The following is a prior art of paper wallpaper (pulp material wallpaper) and double wallpaper for diversifying the functionality of the wallpaper.

국내등록특허 제10-0481036호는 벽지용 천연소재 조성물과 이로부터 천연 벽지를 제조하는방법에 관한 것으로서, 토르말린 분말 71∼80 중량%, 천연 접착제 20∼29 중량%로 이루어진 것을 특징으로 하는 벽지용 천연소재 조성물을 제공하고, 상기 조성물을 이용하여, 벽지 원지에 도포하고, 이를 건조하는 것을 특징으로 하는 천연벽지의 제조방법을 제공하여, 인체에 유익한 음이온을 발생하고 원적외선을 다량 방출하며 인체에 유해한 휘발성 유기용제, 포름 알데히드, 중금속 등의 유해물질이 배출되지 않는 청정벽지를 제공하는 효과를 강조하고;Korean Patent No. 10-0481036 relates to a natural material composition for wallpaper and a method for manufacturing a natural wallpaper therefrom, comprising 71 to 80% by weight tourmaline powder, 20 to 29% by weight natural adhesive for wallpaper It provides a natural material composition, by using the composition, it is applied to the wallpaper base paper, and provides a method for producing a natural wallpaper, characterized in that it is dried, generates anion beneficial to the human body and emits a large amount of far infrared rays and harmful to the human body Emphasizing the effect of providing a clean wallpaper free of harmful substances such as volatile organic solvents, formaldehyde, heavy metals, etc .;

국내등록특허 제10-0636297호는 이중지 및 그 제조방법에 관한 것으로서, 제1초지기에서 초지되어 이송중인 습지의 일면에 기능성 물질 또는 잉크를 분포시킨 후 기능성 물질 또는 잉크가 분포된 종이의 일면이 내측이 되도록 제2초지기에 의해 초지된 습지와 합지하는 공정을 포함하여 이중지를 제조하는 이중지 제조방법을 제공하여, 기능성 물질을 분포시 별도의 바인더, 펄프 등이 요구되지 않아 제조공정이 간편하고 상대적으로 공정오염이 적으며, 또한 바인더, 펄프 등이 혼합되어 사용되지 않음으로 상대적으로 기능성 물질을 많이 도포시킬 수 있고 바인더, 펄프등이 기능성 물질의 기능을 저하시킬 우려가 없어 보다 효과적으로 기능성을 발휘할 수 있는 이중지를 제조할 수 있는 효과를 강조하고 있으나, 기능성을 갖는 물질이 제한적이고 보다 다양한 기능성을 추구하기 위한 구체적인 구성요소가 미미한 문제가 있어 그에 대한 지속적인 연구개발이 요구된다.
Korean Patent No. 10-0636297 relates to a duplex paper and a method for manufacturing the same, and after distributing a functional material or ink on one surface of a wetland which is papered and transported in a first paper machine, the surface of the paper on which the functional material or ink is distributed is It provides a double paper manufacturing method for manufacturing double paper including the process of laminating with the wetland paper made by the second paper machine so as to be inward. Relatively less process pollution, and because binders and pulp are not mixed and used, it is possible to apply a lot of functional materials.Binders, pulp, etc. do not have to worry about degrading the function of functional materials. It emphasizes the effect of making double paper that can be used, but functional materials are limited and more There is a variety of specific components for the pursuit of minor functional problems requires continuous research and development for them.

본 발명은 본 발명은 기능성을 갖는 물질을 포함하는 기능성 벽지도료와 이를 이용한 기능성 벽지 제조방법 및 기능성 벽지에 따른 문제들을 개선하고자 안출된 기술로써,The present invention provides a functional wallpaper paint comprising a material having a functional material, a method of manufacturing a functional wallpaper using the same, and a technique devised to improve the problems according to the functional wallpaper.

기능성 벽지를 제조하기 위하여 이용하는 종래 벽지도료는 항균성 또는 원적외선 방사성 등의 기능성을 갖는 특성이 있으나, 상기 기능성을 포함하는 동시에 탈취성, 항습성, 흡유성 및 벽지 자체에서 발생하는 정전기 또는 벽지가 시공된 공간의 공기 중에 존재하는 물질에 의하여 발생하는 정전기를 방지가능한 특성 등 보다 다양한 기능성이 요구되는 기능성 벽지도료 및 이를 이용한 기능성 벽지제조방법과 기능성 벽지가 요구되는 문제를 해결하는 해결점을 제공하는 것을 목적으로 한다.
Conventional wallpaper paint used to manufacture a functional wallpaper has the characteristics such as antibacterial or far-infrared radiation, but includes the above functionality and at the same time deodorizing, hygroscopic, oil absorption and static electricity generated from the wallpaper itself or wallpaper The purpose of the present invention is to provide a functional wallpaper paint that requires more various functionalities, such as a property capable of preventing static electricity generated by a material present in the air, and a solution for solving a problem requiring a functional wallpaper and a method of manufacturing a functional wallpaper using the same. do.

발명은 상기와 같은 소기의 목적을 실현하고자,The present invention is intended to realize the desired object as described above,

수용성접착제 100중량부에 대하여, 평균입도가 100~500mesh인 황토석, 자옥석, 맥반석, 희토, 산호석 등의 제1기능성물질 40~60중량부와; 평균입도가 100~500mesh이고 황동석, 금홍석, 티탄철석 등의 전도성을 갖는 조성물을 포함하는 광물인 제2기능성물질 0.5~10중량부와; 분산제 0.5~4중량부를 혼합한 기능성 혼합액과; 상기 기능성 혼합액 100중량부에 대하여, 물 5~25중량부를 더 포함하여 혼합한 기능성 벽지도료 및; 이를 이용한 기능성 벽지 제조방법 및 기능성 벽지를 제시한다.
40 to 60 parts by weight of a first functional material such as ocher, gemstone, elvan, rare earth and coral stone having an average particle size of 100 to 500 mesh based on 100 parts by weight of the water-soluble adhesive; 0.5 to 10 parts by weight of a second functional material, which is a mineral having an average particle size of 100 to 500 mesh and includes a composition having conductivity such as brass, rutile and titanium iron; Functional mixture liquid which mixed 0.5-4 weight part of dispersing agents; A functional wallpaper paint mixed with 100 to 5 parts by weight of the functional mixture, further comprising 5 to 25 parts by weight of water; A functional wallpaper manufacturing method and a functional wallpaper using the same are presented.

본 발명에 의한 기능성을 갖는 물질을 포함하는 기능성 벽지도료와 이를 이용한 기능성 벽지 제조방법 및 기능성 벽지는 상기의 과제 해결 수단으로써,Functional wallpaper paint comprising a material having a functional according to the present invention, a functional wallpaper manufacturing method and a functional wallpaper using the same as a means for solving the above problems,

종래 기능성 벽지를 제조하기 위하여 이용하는 벽지도료가 단순히 항균성, 원적외선 방사성 등의 기능성만을 갖는 것에 비하여 항균성, 탈취성, 항습성, 흡유성 또는 원적외선 방사성 등의 기능성뿐만 아니라 벽지 자체에서 발생하는 정전기 또는 벽지가 시공된 공간의 공기 중에 존재하는 물질에 의하여 발생하는 정전기를 방지가능한 기능성 벽지도료를 제시하고 그에 바람직한 기능성 벽지제조방법, 그로서 제조된 기능성 벽지를 제시하는 효과를 얻을 수 있다.
Compared to the conventional wall covering paints used to manufacture functional wallpaper, the antimicrobial, deodorizing, hygroscopic, oil absorption, or far-infrared radiation, as well as the antibacterial, far-infrared radiation, and the like, as well as the static electricity generated from the wallpaper itself It is possible to obtain an effect of presenting a functional wallpaper paint capable of preventing static electricity generated by a material present in the air of the constructed space, and presenting a preferable method of manufacturing the functional wallpaper, and the functional wallpaper manufactured thereby.

도 1은 본 발명의 바람직한 실시 예에 의한 기능성 벽지도료의 조성물 블럭도.
도 2는 본 발명의 바람직한 실시 예에 의한 기능성 벽지 제조방법의 블럭도.
도 3은 본 발명의 바람직한 다른 실시 예에 의한 기능성 벽지 제조방법의 블럭도.
도 4는 본 발명의 바람직한 실시 예에 의한 기능성 벽지 제조방법의 공정도.
도 5는 본 발명의 바람직한 다른 실시 예에 의한 기능성 벽지 제조방법의 공정도.1 is a block diagram of the composition of the functional wallpaper paint according to a preferred embodiment of the present invention.
Figure 2 is a block diagram of a functional wallpaper manufacturing method according to a preferred embodiment of the present invention.
Figure 3 is a block diagram of a functional wallpaper manufacturing method according to another embodiment of the present invention.
Figure 4 is a process diagram of a functional wallpaper manufacturing method according to a preferred embodiment of the present invention.
5 is a process chart of the functional wallpaper manufacturing method according to another embodiment of the present invention.

본 발명은 기능성을 갖는 물질을 포함하는 기능성 벽지도료와 이를 이용한 기능성 벽지 제조방법 및 기능성 벽지에 관한 것으로서,The present invention relates to a functional wallpaper paint containing a material having a functional, a functional wallpaper manufacturing method and a functional wallpaper using the same,

수용성접착제 100중량부에 대하여, 평균입도가 100~500mesh인 황토석, 자옥석, 맥반석, 희토, 산호석 등의 제1기능성물질 40~60중량부와; 평균입도가 100~500mesh이고 황동석, 금홍석, 티탄철석 등의 전도성을 갖는 조성물을 포함하는 광물인 제2기능성물질 0.5~10중량부와; 분산제 0.5~4중량부를 혼합한 기능성 혼합액과; 상기 기능성 혼합액 100중량부에 대하여, 물 5~25중량부를 더 포함하여 혼합한 기능성 벽지도료(30) 및;40 to 60 parts by weight of a first functional material such as ocher, gemstone, elvan, rare earth and coral stone having an average particle size of 100 to 500 mesh based on 100 parts by weight of the water-soluble adhesive; 0.5 to 10 parts by weight of a second functional material, which is a mineral having an average particle size of 100 to 500 mesh and includes a composition having conductivity such as brass, rutile and titanium iron; Functional mixture liquid which mixed 0.5-4 weight part of dispersing agents; Functional wallpaper paint 30, which further comprises 5 to 25 parts by weight of water with respect to 100 parts by weight of the functional mixture solution;

상기와 같은 조성물로 이루어진 기능성 벽지도료(30)를 준비하는 도료 준비공정(S100)과; 상기 기능성 벽지도료(30)를 펄프재질의 벽지(10)에 코팅하는 코팅공정(S200)과; 120~150℃의 온도로 기능성 벽지도료(30)가 코팅된 벽지를 건조하는 건조공정(S300) 및; 상기 건조공정(S300)으로 건조된 벽지를 귄취하는 권취공정(S400);을 포함하여 구성되는 기능성 벽지도료(30)를 이용한 기능성 벽지 제조방법 및;A paint preparation process (S100) for preparing a functional wallpaper paint (30) made of the composition as described above; A coating step (S200) of coating the functional wallpaper paint 30 on the wallpaper 10 of pulp material; A drying step of drying the wallpaper coated with the functional wallpaper paint 30 at a temperature of 120 to 150 ° C. (S300); A functional wallpaper manufacturing method using a functional wallpaper paint 30 comprising a winding step (S400) of winding up the wallpaper dried in the drying step (S300);

상기 제조방법 중 건조공정(S300) 처리한 펄프재질 벽지를 내면지(10')로 하여, 내면지(10')의 코팅면 또는 외면지(20)인 25~45g/㎡의 평량(坪量)을 갖는 한지 일측면 중 어느 하나의 표면에 수용성접착제(30')를 도포하여 내면지(10')와 외면지(20)를 합지하는 합지공정(S500)과; 상기 합지공정(S500) 처리한 기능성 벽지를 건조하는 2차 건조공정(S600) 및; 상기 건조공정(S300)으로 건조된 기능성 벽지를 귄취하는 권취공정(S400);을 포함하여 구성되는 기능성 벽지도료(30)를 이용한 기능성 벽지 제조방법에 관한 것이다.The pulp material wallpaper treated in the drying step (S300) of the manufacturing method as the inner paper 10 ', the basis weight of 25 ~ 45g / ㎡ that is the coated surface or the outer paper 20 of the inner paper (10') A lamination process (S500) of laminating the inner paper 10 'and the outer paper 20 by applying a water-soluble adhesive 30' on any one surface of the Korean paper with one side; A second drying step (S600) of drying the functional wallpaper treated with the laminating step (S500); It relates to a functional wallpaper manufacturing method using a functional wallpaper paint 30 comprising a; winding step (S400) for winding the functional wallpaper dried in the drying step (S300).

이하 본 발명을 적용한 실시예를 나타내는 첨부 도면 1내지 5를 참고하여 본 발명을 구체적으로 설명하면 다음과 같다.
Hereinafter, the present invention will be described in detail with reference to the accompanying drawings 1 to 5 showing an embodiment to which the present invention is applied.

<기능성 벽지용 코팅조성물><Coating composition for functional wallpaper>

본 발명은 송진, 천연라텍스, 아교, 카제인, 알긴산 나트륨, 젤라틴, 천연아스팔트 또는 일반적으로 사용되는 합성수지계의 수용성접착제 등의 수용성접착제 100중량부에 대하여, 평균입도가 100~500mesh인 황토석, 자옥석, 맥반석, 희토, 산호석 등의 제1기능성물질 40~60중량부와; 평균입도가 100~500mesh이고 황동석, 금홍석, 티탄철석 등의 전도성을 갖는 조성물을 포함하는 광물인 제2기능성물질 0.5~10중량부와; 분산제 0.5~4중량부를 혼합한 기능성 혼합액 및; 상기 기능성 혼합액 100중량부에 대하여, 물 5~25중량부를 더 포함하여 혼합한 것을 특징으로 하는 기능성 벽지도료(30)를 제시함으로서, 종래 기능성 벽지를 제조하기 위하여 이용하는 벽지도료가 항균성, 탈취성, 항습성, 흡유성 또는 원적외선 방사성 등의 기능성만을 갖는 것에 비하여 벽지 자체에서 발생하는 정전기 또는 벽지가 시공된 공간의 공기 중에 존재하는 물질에 의하여 발생하는 정전기를 방지가능한 효과를 얻을 수 있다.The present invention is a resin, such as rosin, natural latex, glue, casein, sodium alginate, gelatin, natural asphalt or synthetic resin-based water-soluble adhesives 40 to 60 parts by weight of a first functional material such as ocher, gemstone, elvan, rare earth and coral stone having an average particle size of 100 to 500 mesh based on 100 parts by weight of the water-soluble adhesive; 0.5 to 10 parts by weight of a second functional material, which is a mineral having an average particle size of 100 to 500 mesh and includes a composition having conductivity such as brass, rutile and titanium iron; Functional mixture liquid which mixed 0.5-4 weight part of dispersing agents; By presenting the functional wallpaper paint 30, characterized in that the mixture further comprises 5 to 25 parts by weight of water with respect to 100 parts by weight of the functional mixture solution, conventionally used for the production of functional wallpaper wallpaper antibacterial, deodorant, Compared to having only functions such as hygroscopicity, oil absorption or far-infrared radiation, it is possible to prevent the static electricity generated by the wallpaper itself or the static electricity generated by the material present in the air of the space where the wallpaper is constructed.

즉, 본 발명의 수용성접착제는 VOC물질을 포함하지 아니한 일반적인 송진, 천연라텍스, 아교, 카제인, 알긴산 나트륨, 젤라틴, 천연아스팔트 또는 일반적으로 사용되는 합성수지계의 수용성접착제(초산비닐계, 아크릴계, EVA계) 등과 같은 수용성접착제를 이용가능한데, 이는 하기 희석제로 이용하는 물과의 혼합성을 용이하게 유도하고, 인체에 유해한 물질의 방출을 줄이기 위함이다.That is, the water-soluble adhesive of the present invention is a common rosin, natural latex, glue, casein, sodium alginate, gelatin, natural asphalt or synthetic resin-based water-soluble adhesives (vinyl acetate-based, acrylic, EVA-based) that do not contain a VOC material A water-soluble adhesive such as) may be used to easily induce compatibility with water used as the following diluent and to reduce the release of substances harmful to the human body.

또한 제1기능성물질은 일반적으로 항균성, 탈취성, 항습성, 흡유성 또는 원적외선 방사성 등의 기능성을 갖는 물질로 알려진 황토석, 자옥석, 맥반석, 희토, 산호석 등의 물질로 이루어지는 것이 바람직하다.In addition, the first functional material is generally made of a material such as ocher, jadeite, elvan, rare earth, coral stone, etc., which are known as substances having functionality such as antibacterial, deodorant, hygroscopic, oil absorption or far infrared radiation.

구체적으로 상기 황토석은 항균성, 탈취성이 우수하고 벌집 형태로 이루어져 습도 조절이 용이하며 카탈라아제, 디페놀 옥시다이제, 사카라제, 프로테아제의 4가지 효소가 포함되어 있어서 상기 효소들이 벽지가 부착된 벽, 천장 또는 실내에서 발생하는 각종의 독소를 분해하여 제거함으로써 실내의 공기를 정화시키는 작용을 한다. 특히 카탈라이제는 황토석의 효소 중에 가장 높은 활성을 보여주고 있는 것으로 알려졌으며 이 효소는 생물에게 독소로써 영향을 미치는 과산화수소를 제거하는 기능을 하기 때문에 벽지가 부착된 벽, 천장 또는 실내에 포함된 과산화수소를 제거하는 효과를 갖는다.Specifically, the ocherite has excellent antibacterial and deodorizing properties and is made in a honeycomb form to easily control humidity, and includes four enzymes of catalase, diphenol oxidase, saccharase, and protease. By decomposing and removing various toxins generated from the ceiling or indoors, the indoor air is purified. In particular, catalase is known to have the highest activity among ocherite enzymes, which removes hydrogen peroxide that affects organisms as toxins. Has the effect of removing.

아울러 일반적으로 산화칼슘(CaO), 산화마그네슘(MgO), 이산화규소(SiO2), 알루미나(Al2O2), 산화칼륨(K2O), 산화철(Fe2O3), 산화나트륨(Na2O)), 납(Pb) 등의 혼합물로 구성된 황토석의 구성 요소와 본 발명을 연관하여 구체적으로 설명하면 다음과 같다.In general, calcium oxide (CaO), magnesium oxide (MgO), silicon dioxide (SiO 2 ), alumina (Al 2 O 2 ), potassium oxide (K 2 O), iron oxide (Fe 2 O 3 ), sodium oxide (Na 2 O)), lead (Pb) and the like will be described in detail with respect to the component of the loess composed of a mixture such as the present invention.

우선 알카리성 무기 화합물인 상기 산화칼슘(CaO)은 생석회라고 불리며 일반적으로 시멘트 재질로 구성된 벽체 또는 목재로 구성되는 천장에서 발생하는 균을 제거하여 실내공기를 청정하게 유지하는 효과가 있다. 즉 상기 구성의 벽체 또는 천장은 계절의 변화 혹은 실내외의 온도 차이에 의하여 온도 및 습도가 상승하면서 곰팡이가 발생하고, 이 곰팡이에 의해 악취가 발생하는데 상기 산화칼슘(CaO)은 강력한 수분 포집 능력을 가진 산화칼슘(CaO)이 수분을 포집하여 습도를 조절하고, 수분과 결합하면서 강 알카리성 물질로 변화되어 세정력을 발휘하여 곰팡이, 생균 및 각종 부패균을 제거하는 것이다. 또한 황토석 성분 중에 산화마그네슘(MgO), 이산화규소(SiO2), 알루미나(Al2O2), 산화칼륨(K2O), 산화철(Fe2O3), 산화나트륨(Na2O)), 납(Pb) 등의 기타 성분은 각각 흡착제, 건습도조절제, 온도조절제의 역할로써 독성 가스를 흡착하여 악취를 제거하고 수분을 억제하여 건습도를 조절하며, 습도를 조절함으로써 습도의 변화에 따라 영향을 받는 실내공기의 온도도 적절하게 조절하는 역할을 한다.First, the calcium oxide (CaO), which is an alkaline inorganic compound, is called quicklime and generally has an effect of keeping indoor air clean by removing germs generated from a wall made of cement or a ceiling made of wood. In other words, the wall or ceiling of the composition is a mold and the temperature and humidity increase due to seasonal changes or indoor and outdoor temperature difference, the odor is generated by the mold, the calcium oxide (CaO) has a strong moisture capture capacity Calcium oxide (CaO) captures moisture to control humidity, combines with moisture, changes to a strong alkaline material, exerts cleaning power, and removes mold, live bacteria and various decaying bacteria. In addition, in the clay component, magnesium oxide (MgO), silicon dioxide (SiO 2 ), alumina (Al 2 O 2 ), potassium oxide (K 2 O), iron oxide (Fe 2 O 3 ), sodium oxide (Na 2 O)), Other components such as lead (Pb) act as adsorbents, wet and dryness regulators, and temperature regulators, respectively, to remove odors by adsorbing toxic gases, to control moisture by controlling moisture, and to control humidity by changing humidity. It also plays a role in controlling the temperature of indoor air.

상기 자옥석은 변성작용에 의하여 일반 퇴적암보다 암석이 9배로 농축되어 있고, 주성분의 구성이 상기 황토석과 유사하여 황토석과 더불어 흡착제, 건습도조절제, 온도조절제의 역할로써 독성 가스를 흡착하여 악취를 제거하고 수분을 억제하여 건습도를 조절하며, 습도를 조절하여 납골함의 온도를 조절하는 역할을 할 뿐만 아니라 화학적 안정성과 흡유성이 높은 산화철(Fe2O3)을 많이 포함하고 있기 때문에 공기 중의 산화 물질과 기름성분으로부터 벽지 자체를 보호하는 효과가 있다.The jadeite is 9 times more concentrated than ordinary sedimentary rocks due to metamorphism, and the composition of the main component is similar to that of ocherite, which removes odors by adsorbing toxic gases as an adsorbent, a wet and dry conditioner, and a temperature regulator along with ocherite. Oxidizing substances in the air because it contains a lot of chemical stability and oil absorption (Fe 2 O 3 ), which not only plays a role of controlling moisture and humidity by controlling moisture, and controlling temperature of the ossuary by controlling humidity. It protects the wallpaper itself from oil and oil.

아울러 맥반석은 화성암류 중 석영반암에 속하는 암석으로써, 이산화규소(SiO2), 산화알루미늄(Al2O2), 산화철(Fe2O3)의 주성분으로 구성되고 1㎤당 3만~15만여 개의 많은 공극(다공질)을 갖는 특징이 있으며, 상기 특징을 갖는 맥반석은 강력한 흡착작용, 이온교환작용을 하기 때문에 습도를 조절하여 부패 원인균의 서식을 막고, 제거하는 효과가 있을 뿐만 아니라 원적외선 방사효과가 있어 인체에 유익한 효과도 얻을 수 있다.Elvanite is a rock belonging to quartz rock among igneous rocks. It is composed of main components of silicon dioxide (SiO 2 ), aluminum oxide (Al 2 O 2 ), and iron oxide (Fe 2 O 3 ). It is characterized by having many pores (porous), and because it has strong adsorption and ion exchange, it has the effect of controlling the humidity to prevent and eliminate the habitat of the causative bacteria, and also has far-infrared radiation effect. Benefits to the human body can also be obtained.

또한 희토는 화학원소 주기율표상의 란탄계 15개 원소인 La, Ce, Pr, Nd, Pm, Eu, Gd, Tb, Dy, Er, Tm, Tb, Lu 및 이들과 성질이 유사한 2개 원소인 Y와 Sc를 합한 17개의 희토류원소를 주성분으로 하는 산화물광물로써 대부분 희토류원소 간의 화학적 성질이 비슷하고 섞여서 산출되므로 이를 분리하는 공정 및 절차는 매우 까다로우며, 원자로에서의 열 중성자 흡수체의 경우와 같이 원소 하나하나의 특유한 성질을 이용하는 경우를 제외하고는 일반적으로 혼합 상태로 사용하는 경우가 많은 특성이 있다. 또한 희토의 주성분인 희토류원소는 살균과 항균성이 뛰어나고 원적외선을 방사율이 높기 때문에 본 발명의 제1기능성물질인 상기 황토석, 자옥석 및 희토와 더불어 벽체 또는 천장 등에서 발생가능한 세균의 번식을 방지하고, 실내공기의 악취를 제거하며, 세균을 살균하는 효과가 있다.In addition, rare earths include La, Ce, Pr, Nd, Pm, Eu, Gd, Tb, Dy, Er, Tm, Tb, Lu, which are lanthanide 15 elements in the chemical element periodic table, and Y, Y It is an oxide mineral composed mainly of 17 rare earth elements including Sc, and the chemical properties of most rare earth elements are similar and mixed, so the process and procedure for separating them are very difficult, and as in the case of thermal neutron absorbers in a reactor, Except in the case of using one unique property, there are many characteristics that are generally used in a mixed state. In addition, the rare earth element, which is a main component of rare earths, has excellent sterilization and antibacterial properties, and has high emissivity for far infrared rays, and thus prevents breeding of bacteria that may occur in walls or ceilings, as well as the first functional material of the present invention, such as ocher, gemstone and rare earth. Eliminates bad smell of air, and sterilizes germs.

산호석은 산호초와 산호사 등과 같은 산호류를 다량함유하는 석회암의 일종으로서, CaCO3를 주성분으로 하여 SiO2, MgO, K2O, AL2O3 등을 포함하고 원적외선 방출(3.690×102(W/m2), FT-IR분석법, 조건-40℃)하는 특성을 갖는 광물로 알려져 있어 상기 희토와 더불어 인체에 유익한 효과를 얻을 수 있다.Coral stone is a kind of limestone that contains a large amount of corals such as coral reefs and coral sands. It contains CaCO 3 as a main component and contains SiO 2 , MgO, K 2 O, AL 2 O 3 , and emits far infrared rays (3.690 × 10 2 (W / m 2 ), FT-IR analysis, the condition -40 ℃) is known as a mineral having a characteristic can be obtained a beneficial effect on the human body with the rare earth.

아울러 본 발명의 제1기능성물질에 포함되는 물질들의 평균입도 크기는 100~500mesh가 바람직한데, 이는 제1기능성물질의 입자가 100mesh 초과의 크기를 갖으면 입자크기가 지나치게 작아 수용성접착제와의 혼합시 분산력이 떨어지는 문제가 발생하고, 입자의 크기가 500mesh를 미만이면 입자의 크기가 지나치게 커서 제1기능성물질을 포함하는 본 발명에 의한 기능성 벽지도료(30)가 펄프재질의 벽지(10, 10')에 효과적으로 코팅되지 못하여 제조완료된 기능성 벽지에서 제1기능성물질이 박리되거나, 제1기능성물질의 큰 입자로 인하여 기능성 벽지 표면이 지나치게 거칠어지는 문제가 발생하기 때문이다.In addition, the average particle size of the materials included in the first functional material of the present invention is preferably 100 ~ 500mesh, when the particles of the first functional material has a size of more than 100 mesh when the particle size is too small when mixed with a water-soluble adhesive When the problem of dispersing is lowered and the size of the particles is less than 500 mesh, the size of the particles is so large that the functional wallpaper paint 30 according to the present invention including the first functional material is a pulp material wallpaper (10, 10 '). This is because the first functional material is peeled off from the manufactured functional wallpaper because it is not effectively coated, or the surface of the functional wallpaper is excessively rough due to the large particles of the first functional material.

또한 기능성 혼합액의 제1기능성물질의 함량비는 수용성접착제 100중량부에 대하여 40~60중량부를 갖는 것이 바람직한데, 제1기능성물질의 함량비가 60중량부를 초과하면 무기질 재질의 제1기능성물질이 지나치게 많이 포함되어 기능성 혼합액의 혼합이 어려운 문제와 수용성접착제의 접착력이 떨어져 벽지에 코팅된 기능성 혼합액을 포함하는 기능성 벽지도료(30)가 박리되는 문제가 발생하고, 40중량부 미만으로 함유되면 기능적 효과가 미미해지는 문제가 발생하기 때문이다.In addition, the content ratio of the first functional material of the functional mixture is preferably 40 to 60 parts by weight with respect to 100 parts by weight of the water-soluble adhesive. When the content ratio of the first functional material exceeds 60 parts by weight, the first functional material of the inorganic material is excessively It is difficult to mix the functional mixture solution because it contains a lot of problems and the problem of peeling off the functional wallpaper paint 30, including the functional mixture solution coated on the wallpaper due to the poor adhesion of the water-soluble adhesive, if contained less than 40 parts by weight functional effect This is because a problem occurs that becomes insignificant.

평균입도가 100~500mesh(제1기능성물질의 평균입도와 동일한 원리에 의함)이고 황동석, 금홍석, 티탄철석 등의 전도성을 갖는 조성물을 포함하는 광물인 제2기능성물질은 본 발명의 주된 기술적 사상으로서, Cu, Ti 또는 Fe 등을 포함하는 다량함유하는 광물을 이용하여 벽지 자체에서 발생하는 정전기 또는 벽지가 시공된 공간의 공기 중에 존재하는 물질에 의하여 발생하는 정전기를 방지가능한 효과를 얻을 수 있다.The second functional material, which is a mineral having an average particle size of 100 to 500 mesh (based on the same principle as the average particle size of the first functional material) and having a conductive composition such as brass, rutile, or titanium iron, is a main technical idea of the present invention. By using a large amount of minerals including Cu, Ti or Fe, it is possible to prevent the static electricity generated by the wallpaper itself or the static electricity generated by the material present in the air of the space where the wallpaper is constructed.

즉, 정전기는 물질을 구성하는 분자가 갖는 외곽전자에 여러 가지 원인에 의하여 에너지가 가해져 자유전자로 변화하고 상기 자유전자가 순간적으로 이동하면서 발생하게 되는데, 이러한 정전기는 발생원인에 따라 접촉대전, 마찰대전, 박리대전, 유동대전, 분출대전, 충돌대전, 파괴대전 및 기타의 대전원인으로 구분하며, 일상적인 환경에서는 서로 다른 물체가 접촉-분리하였을 때 자유전자의 이동이 발생하여 (+)와 (-)의 전하가 상대를 향하여 병행하는 전기 이중충이 형성되고, 이후 물체들이 분리하게 되면 이중층의 전하분리(전기적 편극)가 일어나 서로 다른 물체는 각각 다른 극성을 갖게 되는 접촉대전과 서로 다른 물체가 마찰을 일으켰을 때나 마찰에 의하여 접촉위치가 이동하여 전하분리가 일어나 서로 다른 물체가 각각 다른 극성을 갖게 되는 마찰대전에 의하여 발생하는 정전기가 많이 발생한다.In other words, static electricity is generated as energy is applied to the outer electrons of molecules constituting a material and is changed to free electrons and the free electrons are momentarily moved. It is divided into charging, exfoliating charging, floating charging, ejecting charging, collision charging, destroying charging and other charging powers.In ordinary environments, free electron movement occurs when different objects are contact-separated. An electric double charge is formed in which the charges of-) are parallel to each other. Then, when the objects are separated, a double layer of charge separation (electric polarization) occurs, so that the contact charge and the different objects have different polarities. Contact point is moved by friction and charge separation occurs and different objects have different polarity. Generates a lot of static electricity by friction charging.

이를 본 발명과 연관하여 살펴보면, 본 발명에 의한 제2기능성물질의 황동석은 CuFeS2의 화학식을 갖는 구리와 철의 황화광물이고 전기전도성이 우수하기 때문에 전기공업에서 이용하는 구리의 원료 광물로 이용되고, 금홍석(TiO2) 및 티탄철석(FeTiO2)은 티타늄의 중요한 원료 광물로서 광물로서의 자체가 전도성을 갖지는 못하지만 광물을 구성하는 조성물 중에 전도성을 갖는 Cu, Ti 또는 Fe 등의 조성물을 다량함유하고 있기 때문에 접촉 또는 마찰대전에 의하여 발생가능한 자유전자를 제2기능성물질의 전도성 조성물 간으로 용이하게 이동-분산시킬 수 있어 전기적 편극을 예방하여 정전기 발생을 방지할 수 있으며, 벽지와 외부물체와의 접촉-마찰에 의하여 벽지 자체에서 발생하는 정전기 또는 벽지가 시공된 공간의 공기 중에 존재하는 물질에 의하여 발생하는 정전기를 제2기능성물질로 접지가능한 효과를 발휘하여 여러 가지 원인에 의하여 발생한 정전기를 쉽게 분산시는 효과를 얻을 수 있다. 또한 당업자는 본 발명에 의한 제2기능성물질을 상기에서 언급한 종류의 광물뿐만 아니라 전도성을 갖는 조성물(Cu, Ag, Al 등)을 다량 함유하는 어느 광물을 이용하여도 무방할 것임을 인지할 것이다.Looking at this in connection with the present invention, the brass stone of the second functional material according to the present invention is a sulfide mineral of copper and iron having the formula of CuFeS 2 and is used as a raw material mineral of copper used in the electrical industry because of its excellent electrical conductivity, Rutile (TiO 2 ) and titanium iron (FeTiO 2 ) are important raw minerals of titanium, but because they do not have conductivity as minerals themselves, they contain a large amount of conductive compositions such as Cu, Ti, or Fe. Free electrons that can be generated by contact or triboelectric charge can be easily transferred and dispersed between the conductive compositions of the second functional material, thereby preventing electric polarization, thereby preventing static electricity, and contact-friction between the wallpaper and external objects. Due to the static electricity generated by the wallpaper itself or the material present in the air of the space where the wallpaper is constructed. The static electricity generated by the second functional material can be grounded, and thus, the static electricity generated by various causes can be easily dispersed. Those skilled in the art will also recognize that the second functional material according to the present invention may use any mineral containing a large amount of conductive compositions (Cu, Ag, Al, etc.) as well as minerals of the aforementioned kind.

아울러 제2기능성물질의 함량비는 수용성접착제 100중량부에 대하여 0.5~10중량부를 갖는 것이 바람직한데, 제1기능성물질의 함량비가 0.5중량부 미만으로 포함되면 정전기 방지효과를 갖는 전도성 조성물의 함량이 미미하여 제2기능성물질이 갖는 정전기 방지효과가 떨어지고, 10중량부를 초과하여 포함되면 제1기능성물질이 갖는 자연색의 발현효과가 제2기능성물질이 갖는 조흔색(황동석-녹흑색, 금홍석-황갈색, 티탄척설-흑색)에 의하여 탁해지는 문제가 발생하며, 10중량부 정도의 함량비만으로도 일반적인 환경에 놓인 벽지에서 발생가능한 정전기를 충분히 방지가능한 효과를 얻을 수 있기 때문이다.In addition, the content ratio of the second functional material is preferably 0.5 to 10 parts by weight with respect to 100 parts by weight of the water-soluble adhesive, when the content ratio of the first functional material is less than 0.5 parts by weight of the conductive composition having an antistatic effect The antistatic effect of the second functional material is insignificant, and if it is included in an amount exceeding 10 parts by weight, the natural color expression effect of the first functional material is streaked with that of the second functional material (brassite-green black, rutile-yellow-brown, titanium) (Black) is caused by the problem of turbidity, and even if the content ratio of about 10 parts by weight can be sufficiently prevented the static electricity generated in the wallpaper placed in the general environment.

또한 본 발명은 기능성 혼합액의 제조에 있어서, 제1기능성물질 및 제2기능성물을 수용성접착제에 혼합시킴에 있어서 보다 우수한 분산효과를 얻기 위하여 분산제를 이용하는데, 상기의 제1, 2기능성물질은 평균입도가 100~500mesh인 비교적 큰 입자를 갖는 것이 가능하기 때문에 수용성의 일반적인 분산제를 이용가능하고, 이때 분산제의 함량이 수용성접착제 100중량부에 대하여 분산제를 0.5중량부 미만으로 기능성 혼합액에 함유되면 기능성물질(제1, 2)의 분산력이 떨어질 수 있으며 4중량부를 초과하여 함유되면 수용성접착제의 접착력이 떨이질 수 있는 문제가 있기 때문에 수용성접착제 100중량부에 대하여 0.5~4중량부를 함유하는 것이 바람직하다.In addition, the present invention uses a dispersant in the production of the functional mixture, in order to obtain a better dispersing effect in mixing the first functional material and the second functional material in the water-soluble adhesive, the first, the second functional material is an average Since it is possible to have relatively large particles having a particle size of 100 to 500 mesh, a water-soluble general dispersant may be used, and when the content of the dispersant is contained in the functional mixture with less than 0.5 parts by weight of the dispersant based on 100 parts by weight of the water-soluble adhesive, a functional material It is preferable to contain 0.5 to 4 parts by weight with respect to 100 parts by weight of the water-soluble adhesive because there is a problem that the dispersing force of (1, 2) may be reduced and the content of more than 4 parts by weight may cause the adhesive force of the water-soluble adhesive to fall.

상기 수용성접착제, 제1기능성물질, 제2기능성물질 및 분산제로 구성되는 기능성 혼합액은 수용성접착제의 종류 및 수용성접착제 자체의 점도에 따라서 기능성 혼합액 100중량부에 대하여, 희석제인 물 5~25중량부를 혼합하여 기능성 벽지도료(30)를 제조되는데, 제조완료된 기능성 벽지도료(30)를 일정의 방법으로 분사, 도포 또는 흡착하는 방법으로 벽지에 코팅처리하기 위해서는 일정의 접착력과 점도가 요구되고 본 발명에서 제시한 수용성접착제에 있어서는 물을 5중량부 미만으로 함유하면 기능성 벽지도료(30)의 점도가 지나치게 강하여 기능성 벽지도료(30)의 벽지에 대한 코팅처리가 난해하고, 물을 25중량부를 초과하여 희석하면 수용성접착제의 접착력이 떨어져 기능성 벽지도료(30) 코팅된 기능성 벽지를 건조시 벽지에서 기능성 벽지도료(30)가 박리되는 현상이 발생하기 때문이다.The functional mixture consisting of the water-soluble adhesive, the first functional material, the second functional material, and the dispersant is mixed with 5 to 25 parts by weight of water, which is a diluent, based on 100 parts by weight of the functional mixture according to the type of the water-soluble adhesive and the viscosity of the water-soluble adhesive itself. In order to manufacture a functional wallpaper paint 30, in order to coating the wallpaper by spraying, applying or adsorbing the finished functional wallpaper paint 30 in a predetermined method requires a certain adhesive strength and viscosity is presented in the present invention In one water-soluble adhesive, when the water content is less than 5 parts by weight, the viscosity of the functional wallpaper paint 30 is too strong, so that the coating treatment of the functional wallpaper paint 30 is difficult, and when water is diluted more than 25 parts by weight. Functional wallpaper paint (30) when drying the coated functional wallpaper due to the poor adhesion of the water-soluble adhesive, the functional wallpaper paint (30) This phenomenon is due to be re-generated.

이상의 본 발명에 의한 기능성 벽지도료(30)는 황토석, 자옥석,또는 희토가 갖는 색을 갖기 때문에 각각의 제1기능성물질 및 제2기능성물질의 물리-화학적 특성뿐만 아니라 자연미를 느낄 수 있는 기능성 벽지의 색상 구현이 가능한 효과가 있다.Since the functional wallpaper paint 30 according to the present invention has a color of ocher, gemstone, or rare earth, the functional wallpaper which can feel natural beauty as well as the physico-chemical properties of each of the first and second functional materials. Color implementation of the effect is possible.

아울러 본 발명은 상기 기능성 벽지도료를 이용하여 다음과 같은 벽지 제조방법으로서 기능성 벽지 제조가 가능하다.
In addition, the present invention is capable of producing a functional wallpaper as the following wallpaper manufacturing method using the functional wallpaper paint.

<기능성 벽지 제조방법><Functional wallpaper manufacturing method>

[실시예 1]Example 1

본 발명의 실시 예1에 의한 기능성 벽지 제조방법은 상기 기능성 벽지도료(30)를 준비하는 도료 준비공정(S100)과; 상기 기능성 벽지도료(30)를 펄프재질의 벽지(10)에 코팅하는 코팅공정(S200)과; 120~150℃의 온도로 기능성 벽지도료(30)가 코팅된 벽지를 건조하는 건조공정(S300) 및; 상기 건조공정(S300)으로 건조된 벽지를 귄취하는 권취공정(S400);을 포함하여 구성된다.Functional wallpaper manufacturing method according to the first embodiment of the present invention comprises a paint preparation step (S100) for preparing the functional wallpaper paint (30); A coating step (S200) of coating the functional wallpaper paint 30 on the wallpaper 10 of pulp material; A drying step of drying the wallpaper coated with the functional wallpaper paint 30 at a temperature of 120 to 150 ° C. (S300); It comprises a; winding step (S400) for winding the wallpaper dried in the drying step (S300).

기능성 벽지도료(30)를 준비하는 도료 준비공정(S100)은 상기에서 언급한 기능성 벽지도료(30)에 관한 기재로 갈음한다.The paint preparation step (S100) of preparing the functional wallpaper paint (30) is replaced with the description of the functional wallpaper paint (30) mentioned above.

준비된 기능성 벽지도료(30)를 펄프재질의 벽지(10)에 코팅하는 코팅공정(S200)은 일반적으로 알려진 롤러코팅, 스크린코팅, 스프레이코팅 등의 방법 중 어느 것을 채택하여 수행하여도 무방하나, 본 발명에 있어서는 기능성 벽지도료(30)를 코팅용 흡착롤러(40)의 표면에 흡착시키고 흡착롤러(40)에 흡착된 기능성 벽지도료(30)를 이송라인에 의하여 이송되는 펄프재질의 벽지(10)의 일측면에 코팅시키고 기능성 벽지도료(30)가 코팅되는 펄프재질의 벽지(10)의 반대측면은 압력롤러(50)로써 일정의 압력을 가하여 코팅두께를 조절하고 가해지는 일정의 압력에 의하여 기능성 벽지도료(30)가 펄프재질 벽지(10)의 내부 소정까지 흡착(침투)가능한 롤러코팅 방법을 이용하는 것이 바람직하다.The coating process (S200) for coating the prepared functional wallpaper paint 30 on the pulp material wallpaper 10 is generally known roller coating, screen coating, spray coating In the present invention, the functional wallpaper paint 30 is adsorbed on the surface of the coating roller 40 for coating and the functional wallpaper paint 30 is adsorbed on the roller 40. ) Is coated on one side of the pulp material wallpaper 10 transferred by the transfer line, and the opposite side of the pulp material wallpaper 10 on which the functional wallpaper paint 30 is coated is a pressure roller 50. It is preferable to use a roller coating method in which the functional wallpaper paint 30 is adsorbed (infiltrated) to a predetermined inside of the pulp material wallpaper 10 by adjusting the coating thickness by applying a predetermined pressure.

이때 기능성 벽지도료(30)를 흡착롤러(40)에 흡착시키는 방법에 있어서는 도4와 같이 지능성 벽지도료를 내재하는 수조에 롤러의 일부를 침적시켜 흡착롤러(40)의 표면에 기능성 벽지도료(30)가 흡착되도록 하는 방법 또는 분사체를 이용하여 기능성 벽지도료(30)를 흡착롤러(40)의 표면에 분사하여 흡착시키는 방법 등 일반적으로 이용하는 롤러코팅의 도료 흡착방법을 이용하는 것이 가능하다.At this time, in the method of adsorbing the functional wallpaper paint 30 to the adsorption roller 40, a portion of the roller is deposited on the surface of the adsorption roller 40 by depositing a part of the roller in the water tank containing the intelligent wallpaper paint as shown in FIG. It is possible to use a roller coating material adsorption method that is generally used, such as a method of adsorbing a) or by spraying the functional wallpaper paint 30 on the surface of the adsorption roller 40 by using an injector.

아울러 상기 코팅공정(S200) 처리된 펄프재질 벽지를 120~150℃의 온도로 건조하는 건조공정(S300) 은 기능성 벽지도료(30)가 흡착된 벽지를 건조하기 위한 공정으로서, 일반적인 벽지 제조의 건조방법 중 어느 것이나 이용가능하나, 고온의 건조풍을 발생시켜 기능성 벽지도료(30)가 흡착된 벽지를 건조하면 벽지 이외의 공간으로 유출되는 건조풍이 많아 에너지 효율이 떨어지는 문제가 발생하기 때문에 본 발명에 의한 건조공정(S300)은 내부에 고온의 스팀을 내재하여 외부의 표면이 120~150℃로 가열된 가열롤러(60)를 이용하는 것이 바람직하다. 이때, 건조공정(S300)에서 이용하는 가열롤러(60)는 한 개만을 이용하여도 무방하나 도4와 같이 다 수개로 구성되는 건조롤러를 이용함으로써 이송라인의 속도를 빠르게 하여 생산성을 향상시킬 수도 있고, 건조롤러의 표면온도가 120℃미만이면 기능성 벽지도료(30)가 미흡하게 건조되어 기능성 벽지도료(30)와 펄프재질의 벽지(10)가 어울어진 자연미가 높은 색상과 문향의 기능성 벽지를 제조하기 어려운 문제와 하기 권취공정(S400)으로 다수 층을 형성하며 권취된 기능성 벽지의 상하면이 붙거나 기능성 벽지도료(30)의 색상 및 문향이 손상되는 문제가 발생하며, 150℃을 초과한 온도로 건조하면 수용성접착제가 급격하게 경화되어 기능성 벽지도료(30) 코팅층이 갈라지거나 수용성접착제의 색이 변색되어 황변현상이 일어나기 때문이다.In addition, the drying step of drying the pulp material wallpaper treated with the coating step (S200) at a temperature of 120 ~ 150 ℃ (S300) Silver is a process for drying the wallpaper to which the functional wallpaper paint 30 is adsorbed, and any of the general drying methods for manufacturing wallpaper can be used, but drying the wallpaper to which the functional wallpaper paint 30 is adsorbed by generating a high temperature drying wind. When the drying air flows out into the space other than the wallpaper, there is a problem that the energy efficiency is low, so the drying step (S300) according to the present invention has a high temperature steam in the interior and the external surface is heated to 120 ~ 150 ℃ It is preferable to use the roller 60. At this time, the heating roller 60 used in the drying step (S300) may use only one, but by using a drying roller composed of a plurality of as shown in Figure 4 may be used to improve the productivity of the transfer line to increase the speed If the surface temperature of the drying roller is less than 120 ° C., the functional wallpaper paint 30 is insufficiently dried to produce a functional wallpaper having a high natural beauty color and aroma of the functional wallpaper paint 30 and the pulp material wallpaper 10. Problems that are difficult to do and forming a plurality of layers in the following winding process (S400) and the upper and lower surfaces of the wound functional wallpaper is attached or the color and taste of the functional wallpaper paint (30) is damaged, and at a temperature exceeding 150 ℃ This is because when dried, the water-soluble adhesive is rapidly cured, and the coating layer of the functional wallpaper paint 30 is cracked or the color of the water-soluble adhesive is discolored to cause yellowing.

상기 건조공정(S300)으로 건조된 벽지를 권취롤러(90)로서 귄취하는 권취공정(S400)은 도4와 같이 벽지 이송라인에 연계된 권취롤러에 의하여 수행한다.
Winding step (S400) of winding the wallpaper dried in the drying step (S300) as the winding roller 90 is performed by a winding roller connected to the wallpaper transfer line as shown in FIG.

[실시예 2][Example 2]

상기 실시예 1에 의한 기능성 벽지 제조방법은 펄프재질 벽지(10)의 일측면에 기능성 벽지도료(30)를 코팅하는 방법으로 제조하는 것을 특징으로 하나, 본 실시예는 기능성 벽지도료(30)를 준비하는 도료 준비공정(S100)과; 상기 기능성 벽지도료(30)를 펄프재질의 내면지(10', 실시 예1의 펄프재질 벽지(10)과 동일)의 일측면에 코팅하는 코팅공정(S200)과; 120~150℃의 온도로 기능성 벽지도료(30)가 코팅된 벽지를 건조하는 1차 건조공정(S300')과; 상기 1차 건조공정(S300') 처리한 내면지(10')의 코팅면 또는 외면지(20)인 25~45g/㎡의 평량(坪量)을 갖는 한지 일측면 중 어느 하나의 표면에 수용성접착제(30')를 도포하여 내면지(10')와 외면지(20)를 합지하는 합지공정(S500)과; 상기 합지공정(S500) 처리한 기능성 벽지를 건조하는 2차 건조공정(S600) 및; 상기 2차 건조공정(S600)으로 건조된 기능성 벽지를 귄취하는 권취공정(S400);을 포함하여 구성된다.The functional wallpaper manufacturing method according to the first embodiment is characterized in that the manufacturing method by coating the functional wallpaper paint 30 on one side of the pulp material wallpaper 10, the present embodiment is a functional wallpaper paint (30) A paint preparation step (S100) to prepare; A coating step (S200) of coating the functional wallpaper paint 30 on one side of an inner surface paper 10 'of pulp material (the same as the pulp material wallpaper 10 of Example 1); A first drying step (S300 ') of drying the wallpaper coated with the functional wallpaper paint 30 at a temperature of 120 to 150 ° C .; Water-soluble on any one of the surface of the paper surface of the inner surface paper 10 'treated with the primary drying step (S300') or one side of the Hanji having a basis weight of 25 ~ 45g / ㎡ that is the outer paper 20 A lamination process (S500) of applying the adhesive 30 'and laminating the inner sheet 10' and the outer sheet 20; A second drying step (S600) of drying the functional wallpaper treated with the laminating step (S500); It comprises a; winding step (S400) for winding the functional wallpaper dried in the secondary drying step (S600).

기능성 벽지도료(30)를 준비하는 도료 준비공정(S100), 코팅공정(S200) 및 1차건조공정(S300)(실시예 1의 건조공정(S300)과 동일함)은 상기에서 언급한 실시예 1의 각 공정에 관한 기재로 갈음한다.The paint preparation process (S100), the coating process (S200) and the primary drying process (S300) (same as the drying process (S300) of Example 1) for preparing the functional wallpaper paint 30 are the above-mentioned embodiments. It replaces with description about each process of 1.

상기 1차 건조공정(S300') 처리한 내면지(10')의 코팅면 또는 외면지(20)인 25~45g/㎡의 평량(坪量)을 갖는 한지 일측면 중 어느 하나의 표면에 수용성접착제(30')를 도포하여 내면지(10')와 외면지(20)를 합지하는 합지공정(S500)은 도5와 같이 수용성접착제(30', 제조의 용이성을 위하여 기능성 벽지도료(30)의 수용성접착제와 동일한 것을 이용하는 것이 바람직함)를 내면지(10')의 코팅면 또는 외면지(20)의 일측면에 도포(또는 분사)하고, 서로 대응하는 고정롤러(70)와 압력롤러(80, 합지용)를 이용하여 내면지(10')와 외면지(20)를 합지하는 공정이다. 본 공정은 내면지(10')에 비교적 적은 평량(25~45g/㎡의 평량(坪量))을 갖아 일정의 투명성을 갖는 펄프재질의 벽지(한지, 외면지(20))를 결착시킴으로서 내면지(10')에 코팅된 기능성 벽지도료(30)의 제1기능성물질과 제2기능성물질이 직접적으로 외부에 노출되어 벽지시공 이후 가해질 수 있는 외부의 물리적인 요인에 의하여 손상(이탈)되는 것을 방지하는 효과, 기능성물질(제1 및 제2)이 갖는 기능성을 장기간 지속시키는 효과 및 기능성물질(제1 및 제2)이 갖는 자연의 색상을 보다 부드럽게 연출가능한 효과가 있다.Water-soluble on any one of the surface of the paper surface of the inner surface paper 10 'treated with the primary drying step (S300') or one side of the Hanji having a basis weight of 25 ~ 45g / ㎡ that is the outer paper 20 The lamination process (S500) of laminating the inner paper 10 'and the outer paper 20 by applying the adhesive 30' is performed by the water-soluble adhesive 30 ', as shown in FIG. It is preferable to use the same as the water-soluble adhesive of the () is applied (or sprayed) on one side of the coated surface or the outer paper 20 of the inner paper (10 '), and the fixed roller 70 and the pressure roller (corresponding to each other) 80, the inner paper (10 ') and the outer paper 20 is a step of laminating using. This process has a relatively small basis weight (25 to 45 g / m2 basis weight) on the inner paper 10 'and binds the wallpaper of pulp material (Hanji, outer paper 20) with a certain transparency. The first functional material and the second functional material of the functional wallpaper paint 30 coated on the paper 10 'are directly exposed to the outside and damaged (departed) by external physical factors that may be applied after the wallpaper construction. There is an effect of preventing, long-lasting the functionality of the functional materials (first and second), and the effect of rendering the natural color of the functional materials (first and second) more smoothly.

아울러 상기 고정롤러(70)와 압력롤러(80) 사이로 인입되는 외면지(20)와 내면지(10')는 압력롤러(80)에 의하여 합지에 요구되는 압력을 전달받는데, 이때 압력롤러(80)에 의하여 전달되는 압력의 세기에 의하여 합지되는 기능성 벽지의 두께 및 내면지(10')에 코팅된 기능성 벽지도료(30)에 의한 자연의 색상을 외면지(20) 표면에 표출 정도를 조절할 수 있는 효과를 얻을 수 있다.In addition, the outer surface paper 20 and the inner surface paper 10 'drawn between the fixed roller 70 and the pressure roller 80 receive the pressure required for lamination by the pressure roller 80, in this case the pressure roller 80 The thickness of the functional wallpaper laminated by the strength of the pressure delivered by the) and the natural color by the functional wallpaper paint 30 coated on the inner paper (10 ') can adjust the degree of expression on the surface of the outer paper (20) You can get the effect.

상기와 연관하여 본 실시예 2에 의한 기능성 벽지 제조방법은 기능성 벽지도료(30)가 코팅된 기능성 벽지(내면지, 10')를 1차 건조하여 기능성 벽지도료(30)를 안정화시킨 후, 합지공정-2차 건조공정-권취공정을 수행하기 때문에 기능성 벽지도료(30)가 포함하는 기능성물질(제1 및 제2)이 수용성접착제와 함께 완전히 경화되어 기능성물질(제1 및 제2)이 합지공정 중에 압력롤러(80)에 의하여 가해지는 압력에 의하여 유동(가해지는 압력에 의하여 일측으로 몰리는 현상)되는 종래 이중벽지 제조방법의 문제를 해결함으로써, 기능성물질(제1 및 제2)이 고르게 분산된 기능성 벽지 제조를 가능하게 하는 효과가 있다.In connection with the above, the method for manufacturing a functional wallpaper according to the second embodiment of the present invention stabilizes the functional wallpaper paint 30 by first drying the functional wallpaper coated with the functional wallpaper paint 30 (inner paper, 10 '), and then laminating it. Since the process-second drying process-winding process is performed, the functional materials (first and second) included in the functional wallpaper paint 30 are completely cured together with the water-soluble adhesive, and the functional materials (first and second) are laminated. By solving the problem of the conventional double wall paper manufacturing method, which flows due to the pressure applied by the pressure roller 80 during the process (the phenomenon of being driven to one side by the applied pressure), the functional materials (first and second) are evenly dispersed. There is an effect of enabling the production of functional wallpaper.

또한 합지공정(S500) 처리한 기능성 벽지에 처리된 수용성접착제를 경화시켜 외면지(20)와 내면지(10')를 완고하게 결착시키기 위한 2차 건조공정(S600)은 건조롤러(60')로서 1차 건조공정(S300', 실시 예1의 건조공정(S300)과 동일)과 동일한 원리 및 방법으로 수행가능하고, 2차 건조공정(S600) 이후 수행하는 권취공정(S400) 역시 실시 예1의 권취롤러(90)를 이용한 권취공정(S400)과 동일하게 수행가능하다.In addition, the secondary drying step (S600) for hardening the outer paper 20 and the inner paper 10 'by curing the water-soluble adhesive treated on the functional wallpaper treated with the lamination process (S500) is a drying roller (60'). As a primary drying step (S300 ', the same as the drying step (S300) of Example 1) can be carried out in the same principle and method, the winding step (S400) performed after the second drying step (S600) is also Example 1 It can be carried out in the same manner as the winding step (S400) using the winding roller (90).

다음은 본 발명의 바람직한 실시 예1 및 2에 의한 각각의 실험 예이고, 하기의 실험 예뿐만 아니라 상기에서 언급한 기능성 벽지도료(30)를 포함하는 다양한 제조방법에 의한 기능성 벽지의 제조가 가능할 것이다.
The following is an experimental example of each of the preferred embodiments 1 and 2 of the present invention, and the functional wallpaper can be manufactured by various manufacturing methods including the above-mentioned functional wallpaper paint 30 as well as the following experimental examples. .

[실험 예1] - 실시 예1에 의한 기능성 벽지제조방법Experimental Example 1-Method of manufacturing functional wallpaper according to Example 1

1. 도료 준비공정(S100)1. Paint preparation process (S100)

(1) 재료준비(1) Material Preparation

- 수용성접착제(Y사, YP-900, 초산비닐계) 10kg과;10 kg of a water-soluble adhesive (Y company, YP-900, vinyl acetate type);

- 평균입도 450mesh인 황토석(내몽고산) 4kg과 자옥석(경북, 예천산) 0.5kg 및 희토(내몽고산) 0.5kg을 혼합한 제1기능성물질 5kg과;-5 kg of the first functional material mixed with 4 kg of yellow clay (Inner Mongolia), 0.5 kg of jadeite (Gyeongbuk, Yecheon) and 0.5 kg of rare earth (Inner Mongolia);

- 평균입도 450mesh인 황동석(충북 제천산) 0.5kg과;0.5kg of brass stone (Jecheonsan, Chungbuk) with an average particle size of 450mesh;

- 분산제(Y사, NANOX DSP) 0.5kg을 교반 혼합하여 기능성 혼합액을 준비하고;0.5 kg of a dispersant (Y Company, NANOX DSP) was stirred and mixed to prepare a functional mixture;

- 상기 준비된 기능성 혼합액 16kg에 물 1.5kg을 혼합(희석)하여 기능성 벽지도료를 준비한다.
-Prepare the functional wallpaper paint by mixing (diluted) 1.5kg of water with 16kg of the prepared functional mixture solution.

2. 코팅공정(S200), 건조공정(S300) 및 권취공정(S400)2. Coating process (S200), drying process (S300) and winding process (S400)

- 준비한 기능성 벽지도료를 수조에 넣고, 권취된 한지(전북, 전주산)를 이송라인에 인입시킨 후 코팅공정(S200), 건조공정(S300) 및 권취공정(S400)을 수행한다.-Put the prepared functional wallpaper paint in the water tank, insert the rolled Hanji (Jeonbuk, Jeonjusan) into the transfer line and then perform the coating process (S200), drying process (S300) and winding process (S400).

- 이때, 흡착롤러, 건조롤러, 권취롤러 및 벽지이송라인의 속도는 60m/min으로 하고;At this time, the speed of the adsorption roller, drying roller, take-up roller and wallpaper transfer line is 60m / min;

- 코팅롤러에 대응하는 압력롤러의 기준압력은 2kgf/cm2으로 하고;The reference pressure of the pressure roller corresponding to the coating roller is 2 kgf / cm 2 ;

- 건조롤러의 히팅온도는 130℃로 한다.
-The heating temperature of the drying roller is 130 ℃.

[실험 예2] - 실시 예2에 의한 기능성 벽지제조방법Experimental Example 2-Method of manufacturing functional wallpaper according to Example 2

1. 도료 준비공정(S100)1. Paint preparation process (S100)

(1) 재료준비(1) Material Preparation

- 실험 예1과 동일한 기능성 벽지도료를 준비한다.
-Prepare the same functional wallpaper paint as in Experiment 1.

2. 코팅공정(S200), 1차 건조공정(S300'), 합지공정(S500), 2차 건조공정(S600) 및 권취공정(S400)2. Coating process (S200), primary drying process (S300 '), lamination process (S500), secondary drying process (S600) and winding process (S400)

- 준비한 기능성 벽지도료를 수조에 넣고, 권취된 한지(내면지, 전북, 전주산)를 이송라인에 인입시킨 후 코팅공정(S200), 1차 건조공정(S300')을 진행하고;-Put the prepared functional wallpaper paint in the water tank, insert the wound Hanji (inner paper, Jeonbuk, Jeonju) into the transfer line, and then proceed with the coating process (S200) and the first drying process (S300 ');

- 수용성접착제(Y사, YP-900, 초산비닐계) 5kg을 접착제 도포용기에 넣고 1차 건조공정(S300') 완료된 내면지의 코팅면 표면에 수용성접착제를 도포시키고;5 kg of a water soluble adhesive (Y, YP-900, vinyl acetate) was placed in an adhesive coating container and a water soluble adhesive was applied to the surface of the coated surface of the inner paper which had been subjected to the first drying step (S300 ');

- 상기 수용성접착제가 도포된 내면지의 상면에 평량이 35g/㎡인 한지(외면지)를 합지용 고정롤러와 압력롤러 사이로 인입시켜 합지공정(S500)을 수행하고;Performing a lamination process (S500) by introducing a Korean paper (outer paper) having a basis weight of 35 g / m 2 onto the upper surface of the inner paper to which the water-soluble adhesive is applied, between the fixing roller and the pressure roller for lamination;

- 합지완료된 기능성 벽지를 건조롤러를 이용하여 건조시키고, 권취공정(S400)을 수행한다.The laminated functional wallpaper is dried using a drying roller, and a winding process (S400) is performed.

- 이때, 코팅공정(S200), 1차 건조공정(S300'), 합지공정(S500), 2차 건조공정(S600) 및 권취공정(S400)은 일체의 벽지 이송라인에 의하여 수행하므로 전체 흡착롤러, 1차 건조롤러, 합지용 고정롤러, 2차 건조롤러, 권취롤러 및 벽지이송라인의 속도는 60m/min으로 동일하게 하고;-At this time, the coating process (S200), the first drying process (S300 '), the lamination process (S500), the second drying process (S600) and the winding process (S400) is performed by a single wallpaper transfer line, so the entire adsorption roller , The speed of the primary drying roller, the fixed roller for lamination, the secondary drying roller, the winding roller and the wallpaper transfer line is the same at 60 m / min;

- 코팅롤러에 대응하는 압력롤러의 기준압력은 2kgf/cm2으로 하고;The reference pressure of the pressure roller corresponding to the coating roller is 2 kgf / cm 2 ;

- 1차 건조롤러의 히팅온도는 130℃로 하고;The heating temperature of the primary drying roller is 130 ° C .;

- 합지용 압력롤러의 기준압력은 3kgf/cm2으로 하고;The reference pressure of the pressure roller for lamination is 3 kgf / cm 2 ;

- 2차 건조롤러의 히팅온도는 130℃로 한다.
-Heating temperature of secondary drying roller shall be 130 ℃.

또한 상기 실험 예1 및 2를 통하여 제조한 기능성 벽지의 항균성 및 탈취성 시험을 하여 표1과 같은 결과를 얻었고, 정전기 방지 효과를 시험하여 표2와 같은 결과를 얻었다.(벽지에 관한 규정(KS M 7305) 중 정전기에 관한 특별히 정한 규정이 없어, 일반 섬유의 마찰 대전압에 관한 규정(KS K 0555;2005 B법)으로 대체 시험함)In addition, the antimicrobial and deodorant test of the functional wallpaper prepared through Experimental Examples 1 and 2 obtained the results shown in Table 1, and the results of the antistatic effect were obtained to obtain the results shown in Table 2. (Regulation on wallpaper (KS) M 7305) There is no specific regulation on static electricity, and it is replaced by the regulation on frictional electrification of general fiber (KS K 0555; 2005 B method).

[표1]Table 1

Figure 112010019449899-pat00001

Figure 112010019449899-pat00001

[표2][Table 2]

Figure 112010019449899-pat00002

Figure 112010019449899-pat00002

[결과][result]

본 발명에 의한 기능성 벽지도료(30), 기능성 벽지의 제조방법에 의하여 제조된 기능성 벽지는 표1의 항곰팡이 시험과 탈취시험에 관한 결과에서 알 수 있듯이 제1기능성물질을 포함하고 있어 항균성, 탈취성을 갖아 우수한 항균성 및 탈취성을 갖는 것을 알 수 있고, 정전기의 발생가능성을 알 수 있는 대전성 시험의 결과를 나타내는 표2와 같이 본 발명의 제2기능성물질을 포함하지 아니한 종래 기능성 벽지에 비하여 매우 우수한 정전기 방지효과를 갖는 것을 알 수 있다. 또한 당업자는 비록 본 발명의 실험 예에서는 언급하지는 아니하였으나 본 발명에 의한 제1기능성물질을 포함하는 기능성 벽지도료(30)는 혼합 및 준비과정에서 제1기능성물질의 화학-물리적인 변형을 가할만한 특별한 처리조건(온도, pH 등)을 가하지 않아 일반적인 제1기능성물질이 갖는 항습성, 흡유성 또는 원적외선 방사성 등의 효과는 변함없이 발휘 가능한 것을 용이하게 인지가능할 것이다.
Functional wallpaper paint 30 according to the present invention, the functional wallpaper produced by the manufacturing method of the functional wallpaper, as can be seen from the results relating to the antifungal test and deodorization test of Table 1, the antibacterial, deodorizing Compared with the conventional functional wallpaper which does not contain the second functional material of the present invention, as shown in Table 2 showing the results of the chargeability test, which can be seen that it has excellent antibacterial and deodorizing properties, and the possibility of generating static electricity. It can be seen that it has a very good antistatic effect. Also, those skilled in the art, although not mentioned in the experimental examples of the present invention, the functional wallpaper paint 30 including the first functional material according to the present invention is capable of adding chemical-physical modification of the first functional material in the mixing and preparation process. By not applying special treatment conditions (temperature, pH, etc.), the effects such as anti-humidity, oil absorption or far-infrared radiation of the first primary functional material will be easily recognized.

<기능성 벽지><Functional wallpaper>

상기에서 언급한 본 발명에 의한 기능성 벽지도료(30) 및 이를 이용한 기능성 벽지의 제조방법에 의한 기능성 벽지는 기능성 벽지도료(30)의 기술적 사상과 기능성 벽지 제조방법의 기술적 사상을 통하여 제조된 것을 특징으로 하여 항균성, 탈취성, 항습성, 흡유성 또는 원적외선 방사성 등의 비롯하여, 정전기 방지의 효과를 얻을 수 있다.The functional wallpaper paint 30 according to the present invention mentioned above and the functional wallpaper by the manufacturing method of the functional wallpaper using the same are manufactured through the technical idea of the functional wallpaper paint 30 and the technical idea of the manufacturing method of the functional wallpaper. The antistatic effect can be obtained, including antibacterial, deodorizing, hygroscopic, oil absorption or far-infrared radiation.

또한 상기는 본 발명의 바람직한 실시예를 참고로 설명하였으며, 본 발명은 상기의 실시예에 한정되지 아니하고, 상기의 실시예를 통해 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명의 요지를 벗어나지 않는 범위에서 다양한 변경으로 실시할 수 있는 것이다.
In addition, the above has been described with reference to a preferred embodiment of the present invention, the present invention is not limited to the above embodiment, the person having ordinary skill in the art to which the present invention pertains through the above embodiment the gist of the present invention Various changes can be made without departing from the scope of the invention.

10 : 펄프재질의 벽지 10' : 내면지
20 : 외면지 30 : 기능성 벽지도료
40 : 흡착롤러 50 : 압력롤러(코팅용)
60 : 가열롤러 70 : 고정롤러
80 : 압력롤러(합지용) 90 : 권취롤러
S100 : 도료 준비공정 S200 : 코팅공정
S300 : 건조공정 S400 : 권취공정
S500 : 합지공정 S600 : 2차 건조공정10: pulp material wallpaper 10 ': inner paper
20: exterior paper 30: functional wallpaper paint
40: adsorption roller 50: pressure roller (for coating)
60: heating roller 70: fixed roller
80: pressure roller (for lamination) 90: winding roller
S100: Paint preparation process S200: Coating process
S300: drying process S400: winding process
S500: Lamination process S600: Second drying process

Claims (9)

수용성접착제 100중량부에 대하여,
평균입도가 100~500mesh인 황토석, 자옥석, 맥반석, 희토, 산호석 중 어느 하나 이상의 제1기능성물질 40~60중량부와;
평균입도가 100~500mesh이고 전도성을 갖는 조성물을 포함하는 광물인 제2기능성물질 0.5~10중량부와;
분산제 0.5~4중량부를 혼합한 기능성 혼합액 및;
상기 기능성 혼합액 100중량부에 대하여, 물 5~25중량부를 더 포함하여 혼합한 것을 특징으로 하는 기능성 벽지도료.
Per 100 parts by weight of a water-soluble adhesive,
40 to 60 parts by weight of any one or more of the first functional material of ocher, gemstone, elvan, rare earth and coral stone having an average particle size of 100 to 500 mesh;
0.5 to 10 parts by weight of the second functional material, which is a mineral containing a composition having an average particle size of 100 to 500 mesh;
Functional mixture liquid which mixed 0.5-4 weight part of dispersing agents;
A functional wallpaper paint, characterized by further comprising 5 to 25 parts by weight of water with respect to 100 parts by weight of the functional mixture solution.
제1항에 있어서,
상기 제2기능성물질은 황동석, 금홍석, 티탄철석 중 어느 하나 이상의 광물인 것을 특징으로 하는 기능성 벽지도료.
The method of claim 1,
The second functional material is a functional wallpaper paint, characterized in that any one or more minerals of brass, rutile, titanium iron.
제1항 내지 제2항 중 어느 한 항의 기능성 벽지도료(30)를 준비하는 도료 준비공정(S100)과;
상기 기능성 벽지도료(30)를 펄프재질의 벽지(10)에 코팅하는 코팅공정(S200)과;
120~150℃의 온도로 기능성 벽지도료(30)가 코팅된 벽지를 건조하는 건조공정(S300) 및;
상기 건조공정(S300)으로 건조된 벽지를 귄취하는 권취공정(S400);을 포함하여 구성되는 것을 특징으로 하는 기능성 벽지도료를 이용한 기능성 벽지 제조방법.
A paint preparation step (S100) for preparing the functional wallpaper paint of any one of claims 1 to 2;
A coating step (S200) of coating the functional wallpaper paint 30 on the wallpaper 10 of pulp material;
Drying process of drying the wallpaper coated with the functional wallpaper paint (30) at a temperature of 120 ~ 150 ℃ (S300) And ;
Method of manufacturing a functional wallpaper using a functional wallpaper paint, characterized in that comprises ;; winding step of winding the wallpaper dried in the drying step (S300) (S400).
제1항 내지 제2항 중 어느 한 항의 기능성 벽지도료(30)를 준비하는 도료 준비공정(S100)과;
상기 기능성 벽지도료(30)를 펄프재질의 내면지(10')의 일측면에 코팅하는 코팅공정(S200)과;
120~150℃의 온도로 기능성 벽지도료(30)가 코팅된 벽지를 건조하는 1차 건조공정(S300')과;
상기 1차 건조공정(S300') 처리한 내면지(10')의 코팅면 또는 외면지(20)인 일정 평량(坪量)을 갖는 한지 일측면 중 어느 하나의 표면에 수용성접착제를 도포하여 내면지(10')와 외면지(20)를 합지하는 합지공정(S500)과;
상기 합지공정(S500) 처리한 기능성 벽지를 건조하는 2차 건조공정(S600) 및;
상기 2차 건조공정(S600)으로 건조된 기능성 벽지를 귄취하는 권취공정(S400);을 포함하여 구성되는 것을 특징으로 하는 기능성 벽지도료를 이용한 기능성 벽지 제조방법.
A paint preparation step (S100) for preparing the functional wallpaper paint of any one of claims 1 to 2;
A coating step (S200) of coating the functional wallpaper paint 30 on one side of the inner surface paper 10 'of pulp material;
A first drying step (S300 ') of drying the wallpaper coated with the functional wallpaper paint 30 at a temperature of 120 to 150 ° C .;
The inner surface by applying the water-soluble adhesive to any one surface of the coated surface of the inner surface paper 10 'subjected to the primary drying step (S300') or one side having a certain basis weight (坪 量) A lamination process (S500) for laminating the paper 10 ′ and the outer paper 20;
A second drying step (S600) of drying the functional wallpaper treated with the laminating step (S500);
Method of manufacturing a functional wallpaper using a functional wallpaper paint, characterized in that it comprises a; winding step (S400) for winding the functional wallpaper dried in the secondary drying step (S600).
제4항에 있어서,
상기 외면지(20)인 한지의 일정 평량(坪量)은 25~45g/㎡인 것을 특징으로 하는 기능성 벽지도료를 이용한 기능성 벽지 제조방법.
The method of claim 4, wherein
Method of manufacturing a functional wallpaper using a functional wallpaper paint, characterized in that the predetermined basis weight of the paper that is the outer paper (20) is 25 ~ 45g / ㎡.
제1항 내지 제2항 중 어느 한 항의 기능성 벽지도료로 제조된 것을 특징으로 하는 기능성 벽지.
The functional wallpaper, which is made of the functional wallpaper paint of any one of claims 1 to 2.
제3항의 기능성 벽지 제조방법으로 제조된 것을 특징으로 하는 기능성 벽지.
Functional wallpaper, characterized in that produced by the functional wallpaper manufacturing method of claim 3.
제4항의 기능성 벽지 제조방법으로 제조된 것을 특징으로 하는 기능성 벽지.
Functional wallpaper, characterized in that produced by the functional wallpaper manufacturing method of claim 4.
제5항의 기능성 벽지 제조방법으로 제조된 것을 특징으로 하는 기능성 벽지.Functional wallpaper, characterized in that produced by the functional wallpaper manufacturing method of claim 5.
KR1020100027388A 2010-03-26 2010-03-26 Functional paint for wallpaper, method for manufacturing functional wallpaper and functional wallpaper KR100989823B1 (en)