CN109468544A - 高碳高铬冷作模具钢及其制备方法 - Google Patents
高碳高铬冷作模具钢及其制备方法 Download PDFInfo
- Publication number
- CN109468544A CN109468544A CN201811397092.6A CN201811397092A CN109468544A CN 109468544 A CN109468544 A CN 109468544A CN 201811397092 A CN201811397092 A CN 201811397092A CN 109468544 A CN109468544 A CN 109468544A
- Authority
- CN
- China
- Prior art keywords
- steel
- cold work
- high carbon
- work die
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (9)