CN109467843B - 一种用于制造医疗电线的pvc胶粒及其制备方法 - Google Patents
一种用于制造医疗电线的pvc胶粒及其制备方法 Download PDFInfo
- Publication number
- CN109467843B CN109467843B CN201811277103.7A CN201811277103A CN109467843B CN 109467843 B CN109467843 B CN 109467843B CN 201811277103 A CN201811277103 A CN 201811277103A CN 109467843 B CN109467843 B CN 109467843B
- Authority
- CN
- China
- Prior art keywords
- percent
- pvc
- materials
- rubber mixing
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:PVC树脂粉40~48%、可塑剂20~28%、轻钙8~10%、重钙16~20%、稳定剂1.8~2.4%、高岭土2~4%、PVC润滑剂0.25~0.4%、阻燃剂0.5~1%、碳黑0.35~0.5%;该用于制造医疗电线的PVC胶粒安全环保无毒,达到了食品级,符合RoHS和REACH的环保要求,并且能够通过12KV的高压测试以及400KHz的高频测试,制造成本低,经济效益好,可靠性高。
Description
技术领域
本发明涉及化工材料技术领域,尤其涉及一种用于制造医疗电线的PVC胶粒及其制备方法。
背景技术
医疗电线是一种用于传输高频高压信号的电线,其结构包括芯线和外皮。其中,对于医疗电线的外皮要求具备以下性能:1、达到食品级;2、能够通过12KV的高压测试;3、能够通过400KHz的高频测试。
然而,目前市场上的医疗电线的外皮并不能完全符合上述要求,因此存在改进的必要。
发明内容
本发明为克服上述缺陷而提供了一种用于制造医疗电线的PVC胶粒及其制备方法,该用于制造医疗电线的PVC胶粒安全环保无毒,达到了食品级,符合RoHS和REACH的环保要求,并且能够通过12KV的高压测试以及400KHz的高频测试,制造成本低,经济效益好,可靠性高;该用于制造医疗电线的PVC胶粒的制备方法工艺简单,生产效率高,产品合格率高,适合于大规模推广应用。
为实现上述目的,本发明采用如下的技术方案。
一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 40~48%
可塑剂 20~28%
轻钙 8~10 %
重钙 16~20 %
稳定剂 1.8~2.4 %
高岭土 2~4%。
其中,所述用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 40~44%
可塑剂 24~28%
轻钙 8~9%
重钙 18~20 %
稳定剂 1.8~2.1 %
高岭土 3~4%。
其中,所述用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 44~48%
可塑剂 20~24%
轻钙 9~10 %
重钙 16~18 %
稳定剂 2.1~2.4 %
高岭土 2~3%。
PVC树脂,物理外观为白色粉末,无毒、无臭。相对密度1.35-1.46,折射率1.544(20℃),不溶于水,汽油,酒精和氯乙烯,溶于丙酮,二氯乙烷,二甲苯等溶剂,化学稳定性很高,具有良好的可塑性。除少数有机溶剂外,常温下可耐任何浓度的盐酸、90% 以下的硫酸、50-60%的硝酸及20%以下的烧碱,此外,对于盐类亦相当稳定;PVC在火焰上能燃烧并放出氯化氢(HCl),但离开火焰即自熄,是一种“自熄性”、“难燃性”物质;PVC在100℃以上开始分解并缓慢放出HCl,随着温度上升,分解与释放HCl速度加快,致使PVC变色。
可塑剂,是一种增加材料的柔软性或是材料液化的添加剂。其添加对象包含了塑胶、混凝土、干壁材料、水泥与石膏等等。同一种可塑剂常常使用在不同的对象上,但其效果往往并不相同。可塑剂种类多达百余种,但使用得最普遍的即是一群称为邻苯二甲酸酯类的化合物。
轻钙是轻质碳酸钙,又称沉淀碳酸钙,简称轻钙。可用作橡胶、塑料 、造纸、涂料和油墨等行业的填料。广泛用于有机合成、冶金、玻璃和石棉等生产中。
重钙,就是方解石粉,是重质碳酸钙的简称,是由天然碳酸盐矿物如方解石、大理石、石灰石磨碎而成。是常用的粉状无机填料,具有化学纯度高、惰性大、不易化学反应、热稳定性好、在400℃以下不会分解、白度高、吸油率低、折光率低、质软、干燥、不含结晶水、硬度低磨耗值小、无毒、无味、无臭、分散性好等优点。
广义地讲,能增加溶液、胶体、固体、混合物的稳定性能的化学物都叫稳定剂。它可以减慢反应,保持化学平衡,降低表面张力,防止光、热分解或氧化分解等作用。狭义地讲,主要是指保持高聚物塑料、橡胶、合成纤维等稳定,防止其分解、老化的试剂。
质纯的高岭土呈洁白细腻、松软土状,具有良好的可塑性和耐火性等理化性质。其矿物成分主要由高岭石、埃洛石、水云母、伊利石、蒙脱石以及石英、长石等矿物组成。高岭土用途十分广泛,主要用于造纸、陶瓷和耐火材料,其次用于涂料、橡胶填料、搪瓷釉料和白水泥原料,少量用于塑料、油漆、颜料、砂轮、铅笔、日用化妆品、肥皂、农药、医药、纺织、石油、化工、建材、国防等工业部门。
其中,所述用于制造医疗电线的PVC胶粒还包括PVC润滑剂,所述PVC润滑剂占总原料质量百分比的0.25~0.4%。
PVC润滑剂的作用是在塑料加工中改善树脂的流动性和制品的脱模性,防止在机内或模具内因粘着而产生缺陷。
其中,所述用于制造医疗电线的PVC胶粒还包括阻燃剂,所述阻燃剂占总原料质量百分比的0.5~1%。
阻燃剂,赋予易燃聚合物难燃性的功能性助剂,主要是针对高分子材料的阻燃设计的;阻燃剂有多种类型,按使用方法分为添加型阻燃剂和反应型阻燃剂。
其中,所述用于制造医疗电线的PVC胶粒还包括碳黑,所述碳黑占总原料质量百分比的0.35~0.5%。
碳黑,又名炭黑,是一种无定形碳。轻、松而极细的黑色粉末,表面积非常大,范围从10~3000m2/g,是含碳物质(煤、天然气、重油、燃料油等)在空气不足的条件下经不完全燃烧或受热分解而得的产物。比重1.8-2.1。由天然气制成的称“气黑”,由油类制成的称“灯黑”,由乙炔制成的称“乙炔黑”。此外还有“槽黑”、“炉黑”。按炭黑性能区分有“补强炭黑”、“导电炭黑”、“耐磨炭黑”等。可作黑色染料,用于制造中国墨、油墨、油漆等,也用于做橡胶的补强剂。
其中,所述稳定剂包括以下质量百分比的原料:
氯化钙 10~15%
氯化锌 5~10%
氯化钡 5~10%
硬脂酸钠 30~40%
水 10~15%
乙醇 15~20%
亚磷酸酯 6~8%
抗氧剂 3~5%。
本发明的稳定剂稳定性高,其与高岭土共混,能够大大提高复合稳定剂性能,使PVC老化后的抗张残留率和伸长残留率提高30%,同时由于复合稳定剂与高岭土化合后,形成绝缘性能更高的物质,其绝缘电阻比高岭土加入一般的稳定剂高约100%,同时使得PVC的耐电压强度提高了约50%。
其中,所述轻钙为纳米级轻钙,所述重钙为毫米级重钙。
其中,所述可塑剂包括以下质量百分比的原料:
DOTP 60~70%
PE蜡 10~15%
β-二酮 5~10%
水滑石 5~10%
乙撑双硬脂酰胺 6~8%。
本发明的可塑剂与PVC胶粒混炼以后,化合形成的PVC混合胶粒能够比使用常规可塑剂的耐热性能提高约50%,耐紫外光的性能提高约30%,机械强度提高约20%。
一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至60-70℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌1-2分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌2-3分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌1-2分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌3-5分钟,使物料混合均匀,得到PVC胶料;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
优选地,所述步骤E 和步骤F 之间还包括有步骤E1,往炼胶机依次加入PVC润滑剂、阻燃剂、碳黑,搅拌5-10分钟,使物料混合均匀。
本发明的有益效果为:
1、本发明的配方根据用于制造医疗电线的PVC胶粒的各项技术要求配制,通过正交法筛选,通过DSC热分析法和NMR核磁共振,研究塑胶和配合剂链段结合程度,并通过红外光谱、气相色谱,分析交联结构,由此获得能够通过12KV的高压及400KHz的高频、符合食品级、且制造成本低的PVC胶粒;
2、高岭土的使用增加了PVC胶粒的绝缘性能,便于通过高压高频测试;
3、本发明的最特别之处在于,高岭土与稳定剂混合以后,能够大大提高复合稳定剂性能,使PVC老化后的抗张残留率和伸长残留率提高30%,同时由于复合稳定剂与高岭土化合后,形成绝缘性能更高的物质,其绝缘电阻比高岭土加入一般的稳定剂高约100%,同时使得PVC的耐电压强度提高了约50%;
4、该PVC胶粒的产品硬度达到80±3 (23℃),平均比重达到1.35 ± 0.100,适合于制造医疗电线;
5、本申请使用的复配可塑剂与PVC胶粒混炼以后,化合形成的PVC混合胶粒能够比使用常规可塑剂的耐热性能提高约50%,耐紫外光的性能提高约30%,机械强度提高约20%;
6、使用纳米级轻钙和毫米级重钙相结合,纳米级的轻钙颗粒填充到毫米级的重钙颗粒的间隙中,形成了结构更加稳固的轻钙重钙结合体,利用该轻钙重钙结合体作为本申请的PVC胶粒补强剂,能够提高该PVC胶粒的机械强度约30%。
具体实施方式
下面结合实施例对本发明作进一步的说明,这是本发明的较佳实施例。
实施例1。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 48%
可塑剂 20%
轻钙 8 %
重钙 17 %
稳定剂 1.8%
高岭土 4%
PVC润滑剂 0.25%
阻燃剂 0.55%
碳黑 0.4%。
本实施例的稳定剂包括以下质量百分比的原料:
氯化钙 10%
氯化锌 10%
氯化钡 5%
硬脂酸钠 40%
水 10%
乙醇 15%
亚磷酸酯 6%
抗氧剂 4%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙。
本实施例的可塑剂包括以下质量百分比的原料:
DOTP 60%
PE蜡 15%
β-二酮 9%
水滑石 10%
乙撑双硬脂酰胺 6%。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至60℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌1分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌3分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌1分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌5分钟,使物料混合均匀,得到PVC胶料;
步骤E1、往炼胶机依次加入PVC润滑剂、阻燃剂、碳黑,搅拌5分钟,使物料混合均匀;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-0级。
其中,RoHS是《电气、电子设备中限制使用某些有害物质指令》(the Restrictionof the use of certain hazardous substances in electrical and electronicequipment)的英文缩写。
其中,REACH是欧盟法规《化学品的注册、评估、授权和限制》(REGULATIONconcerning the Registration, Evaluation,Authorization and Restriction ofChemicals)的简称,是欧盟建立的,并于2007年6月1日起实施的化学品监管体系。
实施例2。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 48%
可塑剂 20%
轻钙 9 %
重钙 16 %
稳定剂 2.1 %
高岭土 3%
PVC润滑剂 0.4%
阻燃剂 1%
碳黑 0.5%。
本实施例的稳定剂包括以下质量百分比的原料:
氯化钙 12%
氯化锌 7%
氯化钡 7%
硬脂酸钠 35%
水 12%
乙醇 15%
亚磷酸酯 7%
抗氧剂 5%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙。
本实施例的可塑剂包括以下质量百分比的原料:
DOTP 65%
PE蜡 12%
β-二酮 8%
水滑石 8%
乙撑双硬脂酰胺 7%。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至65℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌2分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌2分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌2分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌3分钟,使物料混合均匀,得到PVC胶料;
步骤E1、往炼胶机依次加入PVC润滑剂、阻燃剂、碳黑,搅拌6分钟,使物料混合均匀;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-0级。
实施例3。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 44%
可塑剂 24%
轻钙 8 %
重钙 18 %
稳定剂 2.4 %
高岭土 2%
PVC润滑剂 0.4%
阻燃剂 0.8%
碳黑 0.4%。
本实施例的稳定剂包括以下质量百分比的原料:
氯化钙 15%
氯化锌 5%
氯化钡 10%
硬脂酸钠 30%
水 15%
乙醇 15%
亚磷酸酯 7%
抗氧剂 3%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙。
本实施例的可塑剂包括以下质量百分比的原料:
DOTP 70%
PE蜡 10%
β-二酮 7%
水滑石 5%
乙撑双硬脂酰胺 8%。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至70℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌1分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌3分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌1分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌5分钟,使物料混合均匀,得到PVC胶料;
步骤E1、往炼胶机依次加入PVC润滑剂、阻燃剂、碳黑,搅拌7分钟,使物料混合均匀;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-0级。
实施例4。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 44%
可塑剂 24%
轻钙 9 %
重钙 17 %
稳定剂 1.9 %
高岭土 3%
PVC润滑剂 0.3%
阻燃剂 0.8%。
本实施例的稳定剂包括以下质量百分比的原料:
氯化钙 10%
氯化锌 10%
氯化钡 5%
硬脂酸钠 40%
水 10%
乙醇 15%
亚磷酸酯 6%
抗氧剂 4%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙。
本实施例的可塑剂包括以下质量百分比的原料:
DOTP 70%
PE蜡 10%
β-二酮 7%
水滑石 5%
乙撑双硬脂酰胺 8%。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至60℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌2分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌2分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌2分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌3分钟,使物料混合均匀,得到PVC胶料;
步骤E1、往炼胶机依次加入PVC润滑剂、阻燃剂、碳黑,搅拌8分钟,使物料混合均匀;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-0级。
实施例5。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 44%
可塑剂 24%
轻钙 9 %
重钙 18 %
稳定剂 2.1 %
高岭土 2.6%
PVC润滑剂 0.3%。
本实施例的稳定剂包括以下质量百分比的原料:
氯化钙 15%
氯化锌 5%
氯化钡 10%
硬脂酸钠 30%
水 15%
乙醇 15%
亚磷酸酯 7%
抗氧剂 3%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙。
本实施例的可塑剂包括以下质量百分比的原料:
DOTP 60%
PE蜡 15%
β-二酮 9%
水滑石 10%
乙撑双硬脂酰胺 6%。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至65℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌1分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌3分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌1分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌5分钟,使物料混合均匀,得到PVC胶料;
步骤E1、往炼胶机依次加入PVC润滑剂、阻燃剂、碳黑,搅拌9分钟,使物料混合均匀;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-0级。
实施例6。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 44%
可塑剂 24%
轻钙 9 %
重钙 18 %
稳定剂 2.1 %
高岭土 2.9%。
本实施例的稳定剂包括以下质量百分比的原料:
氯化钙 12%
氯化锌 7%
氯化钡 7%
硬脂酸钠 35%
水 12%
乙醇 15%
亚磷酸酯 7%
抗氧剂 5%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙。
本实施例的可塑剂包括以下质量百分比的原料:
DOTP 62%
PE蜡 14%
β-二酮 8%
水滑石 8%
乙撑双硬脂酰胺 8%。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至70℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌2分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌2分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌2分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌3分钟,使物料混合均匀,得到PVC胶料;
步骤E1、往炼胶机依次加入PVC润滑剂、阻燃剂、碳黑,搅拌10分钟,使物料混合均匀;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-0级。
实施例7。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 40%
可塑剂 28%
轻钙 10 %
重钙 16 %
稳定剂 2.5 %
高岭土 3.5%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙,所述稳定剂为钙锌稳定剂,所述可塑剂对苯二甲酸二辛酯。对苯二甲酸二辛酯环保无毒,满足环境管理有害物质含量管控标准HL-00259的要求。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至70℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌2分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌2分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌2分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌3分钟,使物料混合均匀,得到PVC胶料;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-1级。
实施例8。
本实施例的一种用于制造医疗电线的PVC胶粒,包括以下质量百分比的原料:
PVC树脂粉 48%
可塑剂 20%
轻钙 9%
重钙 19 %
稳定剂 2 %
高岭土 2%。
本实施例的轻钙为纳米级轻钙,所述重钙为毫米级重钙,所述稳定剂为钙锌稳定剂,所述可塑剂对苯二甲酸二辛酯。对苯二甲酸二辛酯环保无毒,满足环境管理有害物质含量管控标准HL-00259的要求。
本实施例的一种用于制造医疗电线的PVC胶粒的制备方法,包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至70℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌1分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌3分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌1分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌5分钟,使物料混合均匀,得到PVC胶料;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。
本实施例制得的PVC胶粒的绝缘等级达到C级,硬度为80±3 (23℃),平均比重达到1.35 ± 0.100,能够通过12KV的高压及400KHz的高频,符合食品级要求,符合RoHS和REACH的环保要求,阻燃等级达到V-0级。
本发明的PVC胶粒安全环保无毒,达到了食品级,符合RoHS和REACH的环保要求,制造成本低,经济效益好,可靠性高。
最后应当说明的是,以上实施例仅用以说明本发明的技术方案,而非对本发明保护范围的限制,尽管参照较佳实施例对本发明作了详细地说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的实质和范围。
Claims (3)
1.一种用于制造医疗电线的PVC胶粒,其特征在于:包括以下质量百分比的原料:
PVC树脂粉 40~48%
可塑剂 20~28%
轻钙 8~10 %
重钙 16~20 %
稳定剂 1.8~2.4 %
高岭土 2~4%
PVC润滑剂 0.25~0.4%
阻燃剂 0.5~1%
碳黑 0.35~0.5%;
其中,所述稳定剂包括以下质量百分比的原料:
氯化钙 10~15%
氯化锌 5~10%
氯化钡 5~10%
硬脂酸钠 30~40%
水 10~15%
乙醇 15~20%
亚磷酸酯 6~8%
抗氧剂 3~5%;
其中,所述可塑剂包括以下质量百分比的原料:
DOTP 60~70%
PE蜡 10~15%
β-二酮 5~10%
水滑石 5~10%
乙撑双硬脂酰胺 6~8%。
2.根据权利要求1所述的一种用于制造医疗电线的PVC胶粒,其特征在于:所述轻钙为纳米级轻钙,所述重钙为毫米级重钙。
3.如权利要求1-2任意一项所述的一种用于制造医疗电线的PVC胶粒的制备方法,其特征在于:包括以下加工步骤:
步骤A、根据配方称取适量的物料,分别放置到不同的容器中;
步骤B、将炼胶机的温度调节至60-70℃,然后将PVC树脂粉加入到炼胶机,接着往炼胶机缓慢加入可塑剂,搅拌1-2分钟,使物料混合均匀;
步骤C、往炼胶机同时加入轻钙和重钙,搅拌2-3分钟,使物料混合均匀;
步骤D、往炼胶机缓慢加入稳定剂,搅拌1-2分钟,使物料混合均匀;
步骤E、往炼胶机缓慢加入高岭土,搅拌3-5分钟,使物料混合均匀,得到PVC胶料;
步骤F、将所述PVC胶料倒入造粒机造粒,即得成品。