CN109457487A - 面料用防蚊材料、穿戴品及面料用防蚊材料的制备方法 - Google Patents
面料用防蚊材料、穿戴品及面料用防蚊材料的制备方法 Download PDFInfo
- Publication number
- CN109457487A CN109457487A CN201810805573.XA CN201810805573A CN109457487A CN 109457487 A CN109457487 A CN 109457487A CN 201810805573 A CN201810805573 A CN 201810805573A CN 109457487 A CN109457487 A CN 109457487A
- Authority
- CN
- China
- Prior art keywords
- mosquito
- vinyl
- fabric
- solution
- ionic liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种面料用防蚊材料、穿戴品及面料用防蚊材料的制备方法，该面料用防蚊材料的制备方法是：S1.制备1‑乙烯基‑3‑庚基咪唑六氟磷酸离子液体单体；S2.将苯乙烯、丙烯晴、对二乙烯基苯和安息香乙醚与S1中制得的离子液体单体混合振动得到均相溶液A；将驱蚊酯和乳化剂加入均相溶液A中得到均相溶液B；用紫外光灯照射溶液B聚合得到高分子1‑乙烯基‑3‑庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊；S3.用致孔剂在微胶囊的囊壁上生成孔；再用溶胀剂将孔扩大，使驱蚊酯释放顺畅。本发明提供的穿戴品，由面料制成，面料由纱线制成，纱线由面料用防蚊材料与粘胶和植物粉混合通过喷丝然后纺纱制成。在使用时防蚊效果好。
Description
技术领域
本发明涉及面料和穿戴品。
背景技术
面料是用来制作服装的材料，面料不仅可以诠释服装的风格和特性，而且直接左右着服装的色彩、造型的表现效果。随着人们生活水平和文化品位的日益提高，着装理念也跟随着发生变化，由远古时代的防寒保暖到传统的注重结实耐穿再到当今的崇尚时尚自由、运动休闲，强调环保抗污染、保健、舒适合体、随意自然又美丽大方的服装。随着高科技的迅猛发展，新材料、新技术和新工艺被大量应用到衣服面料上，因而出现了抗菌防螨、吸汗透气、吸热保温、抗紫外线、防水防静电、耐火阻燃等形形色色的功能性服装面料。因此，无论在工作还是生活中，功能性面料将成为人们不可缺少的亲密助手。
蚊子在世界十大公害动物中排行第三位，可见其对人类的危害程度，蚊子在叮咬人畜的同时还可传播很多疾病，如疟疾、登革热等，蚊虫防治技术种类繁多，主要有物理防治、化学防治、生物防治等。各种技术的作用原理和使用方式均不同，各有各的优劣，如物理防治中的蚊香、灭害灵等会危害人体健康；化学防治会使蚊虫产生抗药性等。而且如果是在野外行军打仗或施工作业，以上方法都发挥不出很大的功效，因此有必要研究一种穿戴品，穿戴上就能防蚊虫，而且防蚊虫的效果能持久。
随着微胶囊技术的发展，微胶囊技术已经深入到了纺织领域，在申请号为CN200810200955.6申请日为2008.10.09的专利文件中公开了一种缓释驱杀蚊整理剂的制备方法，其先制备水包油乳液在通过包覆和固化制得缓释驱杀蚊整理剂，通过使用高分子材料作为壁材，将有效成分包裹其中，使得驱虫杀蚊虫的有效成分恒速挥发缓慢释放，达到长时间驱赶蚊虫的效果。但这种制备方法得到的微胶囊是将驱蚊酯完全包覆，这样，驱蚊酯需要在微胶囊经过挤压发生破裂后，驱蚊酯才能释放，在正常使用时无法使得驱蚊酯从微胶囊中释放出来，影响驱蚊效果。
发明内容
为解决现有技术中存在的问题，本发明提供一种面料用防蚊材料、穿戴品及面料用防蚊材料的制备方法，本发明的面料用防蚊材料的制备方法能在微胶囊的壁上生成微孔并进行扩孔，使得驱蚊酯从孔中释出顺畅；本发明的面料用防蚊材料防蚊效果好。
为达到上述目的，本发明提供一种防蚊材料的制备方法：包括以下步骤：
S1.制备1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体；
S2.将苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚与S1步骤中制得的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体混合振动得到均相溶液A；
将驱蚊酯和乳化剂加入均相溶液A中，搅拌均匀后得到均相溶液B；
用紫外光灯照射均相溶液B引发聚合反应，反应完成后用乙醇反复超声波振动洗涤后得到高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊；
S3.将质量分数为25％的十二烷基硫酸钠水溶液、高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊和致孔剂充分混合，在25℃～35℃下搅拌9h～11h后得到溶液D，向溶液D中加入摩尔比为1:0.02～0.03的1-乙烯基 -3-庚基咪唑六氟磷酸离子液体单体和溶胀剂，在25℃～35℃下搅拌9h～11h，得到溶液C；
将表面活性剂加入水中，在85℃～95℃加热搅拌0.5h～1.5h得到表面活性剂溶液，并将表面活性剂溶液加入到溶液C中，65℃～75℃搅拌9h～11h后静置分层，去掉水层得到溶液E，用甲醇清洗溶液E，得到微孔高分子1-乙烯基-3- 庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。
以上步骤得到的微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，由于通过1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成微胶囊膜，然后通过苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚与1-乙烯基-3- 庚基咪唑六氟磷酸离子液体单体形成溶液并对驱蚊酯进行包覆形成高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，然后通过致孔剂形成微孔微胶囊，并利用溶胀剂进行扩孔，最后形成微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，从而该方法形成的微胶囊上具有孔结构且孔进行进一步扩大，从而能有效地使得微胶囊中的驱蚊酯得到很好的释放，从而提高防蚊效果；
另外1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体化学稳定性高、不溶于水、绿色、环保无毒，且1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体中的阳离子部分具有抗菌性，选用苯乙烯和丙烯腈作为单体是因为聚-(苯乙烯-丙烯腈) 具有高化学稳定性和易成膜性；乳化剂将驱蚊酯细化后与均相溶液A混合均匀，在紫外光灯照射下发生聚合反应生成高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。
进一步的，S1步骤中制备的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体的步骤为：将摩尔比为1:1～1.5的乙烯基咪唑和溴代正庚烷在0℃下混合搅拌反应6.5h～7.5h，将得到的粘稠液体用乙醚反复洗涤后，旋转蒸发得到溴代1- 乙烯基-3-庚基咪唑离子液体单体，将摩尔比为1:1的溴代1-乙烯基-3-庚基咪唑离子液体单体和六氟磷酸钾加入水溶液中，70℃～80℃旋转2h～3h，冷却，静置分层，除去水层得到有机层，将有机层用水和乙醚交替洗涤，70℃～80℃旋转蒸发1h～2h,得到1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体。此摩尔比的乙烯基咪唑和溴代正庚烷能使乙烯基咪唑反应更充分；乙醚能除去未完全反应的原料；鉴于溴离子的亲水性，因此用六氟磷酸钾中的钾离子替换掉溴代1-乙烯基-3-庚基咪唑离子液体单体中的溴离子，防止吸水受潮。
进一步的，S2步骤中1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体、苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚的摩尔比为90～110:140～160:190～ 210:2.5～4.5:1.5～1.8。此比例能使成膜率最高。
进一步的，S2步骤中所述乳化剂为脂肪酸甘油酯。脂肪酸甘油酯将驱蚊酯的粒径控制在650～750nm，以利于被包覆。
进一步的，S2步骤中所述紫光灯的紫外光波长λ＝220～280nm。此波段范围的紫外光能使聚合反应更完全。
进一步的，S3步骤中所述致孔剂为摩尔比为25～28:1的正庚烷和邻苯二甲酸二丁酯的混合溶液。此比例范围的混合溶液致孔效果最好，能使在微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊囊壁上生成的孔的孔径在0.1～0.2nm范围内的比例最大。
进一步的，S3步骤中所述表面活性剂溶液为聚乙烯醇溶液，所述溶胀剂为过氧化二苯甲酰。以上设置能将上一步形成的孔进一步扩大，使得孔径在0.5～ 0.8nm的范围内，扩孔后的孔径比驱蚊酯分子的直径稍大，从而进一步提高微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊释放驱蚊酯的量，防蚊材料释放驱蚊酯持久性长。
为达到上述目的，本发明提供一种面料用防蚊材料，包括由所述的面料用防蚊材料的制备方法制得的微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。该微胶囊由于通过1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成微胶囊膜，然后通过苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚与1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成溶液并对驱蚊酯进行包覆形成高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，然后通过致孔剂形成微孔微胶囊，并利用溶胀剂进行扩孔，最后形成微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，从而该方法形成的微胶囊上具有孔结构且孔进行进一步扩大，从而能有效地使得微胶囊中的驱蚊酯得到很好的释放，从而提高防蚊效果。
为达到上述目的，本发明提供一种穿戴品，穿戴品由面料制成，面料由纱线制成，纱线由所述的面料用防蚊材料与粘胶和植物粉混合通过喷丝然后纺纱制成。面料用防蚊材料与粘胶和植物粉混合后通过喷丝然后纺纱制成纱线，纱线编制成面料，面料制成穿戴品，而防蚊材料中采用微孔高分子1-乙烯基-3- 庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，该微胶囊由于通过1-乙烯基-3- 庚基咪唑六氟磷酸离子液体单体形成微胶囊膜，然后通过苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚与1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成溶液并对驱蚊酯进行包覆形成高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，然后通过致孔剂形成微孔微胶囊，并利用溶胀剂进行扩孔，最后形成微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，从而该方法形成的微胶囊上具有孔结构且孔进行进一步扩大，从而能有效地使得微胶囊中的驱蚊酯得到很好的释放，从而提高防蚊效果。
具体实施方式
下面通过具体实施方式对本发明做进一步详细说明。
实施例1。
本发明提供了一种面料用防蚊材料的制备方法，面料用防蚊材料的制备方法包括以下实施方式：
实施方式一：面料用防蚊材料的制备方法，包括以下步骤：
S1.将摩尔比为1:1的乙烯基咪唑和溴代正庚烷在0℃下混合搅拌反应6.5h，将得到的粘稠液体用乙醚反复洗涤后，旋转蒸发得到溴代1-乙烯基-3-庚基咪唑离子液体单体，将摩尔比为1:1的溴代1-乙烯基-3-庚基咪唑离子液体单体和六氟磷酸钾加入水溶液中，70℃旋转2h，冷却，静置分层，除去水层得到有机层，将有机层用水和乙醚洗涤，70℃旋转蒸发1h,得到1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体，主要反应关系式如下所示：
S2.将摩尔比为90:140:190:2.5:1.5的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体、苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚混合振动得到均相溶液A；其中安息香乙醚为光敏剂；
将驱蚊酯和脂肪酸甘油酯加入均相溶液A中,搅拌均匀，得到均相溶液B；
用波长λ＝220nm的紫外光灯照射溶液B引发聚合反应，反应完成后用乙醇反复超声波振动洗涤后得到高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，主要反应关系式如下所示：
式(2)中为式(1)中的
S3.将质量分数为25％的十二烷基硫酸钠水溶液、高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊和摩尔比为25:1的正庚烷和邻苯二甲酸二丁酯的混合溶液充分混合，在25℃下搅拌9h后得到溶液D，向溶液D中加入摩尔比为1:0.02的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体和过氧化二苯甲酰，在25℃下搅拌9h，得到溶液C。
将聚乙烯醇加入到水中，85℃加热搅拌0.5h形成聚乙烯醇溶液，并将聚乙烯醇溶液加入到溶液C中，65℃搅拌9h后静置分层，去掉水层得到溶液E，用甲醇清洗溶液E，得到微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。
实施方式二：面料用防蚊材料的制备方法，包括以下步骤：
S1.将摩尔比为1:1的乙烯基咪唑和溴代正庚烷在0℃下混合搅拌反应7h，将得到的粘稠液体用乙醚反复洗涤后，旋转蒸发得到溴代1-乙烯基-3-庚基咪唑离子液体单体，将摩尔比为1:1的溴代1-乙烯基-3-庚基咪唑离子液体单体和六氟磷酸钾加入水溶液中，75℃旋转2.5h，冷却，静置分层，除去水层得到有机层，将有机层用水和乙醚洗涤，75℃旋转蒸发1.5h,得到1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体，主要反应关系式如下所示：
S2.将摩尔比为100:150:200:3:1.6的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体、苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚混合振动得到均相溶液A；其中安息香乙醚为光敏剂；
将驱蚊酯和脂肪酸甘油酯加入均相溶液A中，搅拌均匀后得到均相溶液B；
用波长λ＝250nm的紫外光灯照射溶液B引发聚合反应，反应完成后用乙醇反复超声波振动洗涤后得到高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，主要反应关系式如下所示：
式(2)中为式(1)中的
S3.将质量分数为25％的十二烷基硫酸钠水溶液、高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊和摩尔比为26.5:1的正庚烷和邻苯二甲酸二丁酯的混合溶液充分混合，在27.5℃下搅拌10h后得到溶液D，向溶液D 中加入摩尔比为1:0.025的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体和过氧化二苯甲酰，在30℃下搅拌10h，得到溶液C。
将聚乙烯醇加入水中在90℃加热搅拌1h配成聚乙烯醇溶液，并将聚乙烯醇溶液加入到溶液C中，70℃搅拌10h后静置分层，去掉水层得到溶液E，用甲醇清洗溶液E，得到微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。
实施方式三：面料用防蚊材料的制备方法，包括以下步骤：
S1.将摩尔比为1:1的乙烯基咪唑和溴代正庚烷在0℃下混合搅拌反应7.5h，将得到的粘稠液体用乙醚反复洗涤后，旋转蒸发得到溴代1-乙烯基-3-庚基咪唑离子液体单体，将摩尔比为1:1的溴代1-乙烯基-3-庚基咪唑离子液体单体和六氟磷酸钾加入水溶液中，80℃旋转3h，冷却，静置分层，除去水层得到有机层，将有机层用水和乙醚洗涤，80℃旋转蒸发2h,得到1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体，主要反应关系式如下所示：
S2.将摩尔比为110:160:210:4.5:1.8的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体、苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚混合振动得到均相溶液A；其中安息香乙醚为光敏剂；
将驱蚊酯和脂肪酸甘油酯加入均相溶液A中，搅拌均匀后得到均相溶液B；
用波长λ＝280nm的紫外光灯照射溶液B引发聚合反应，反应完成后用乙醇反复超声波振动洗涤后得到高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，主要反应关系式如下所示：
式(2)中为式(1)中的
S3.将质量分数为25％的十二烷基硫酸钠水溶液、高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊和摩尔比为28:1的正庚烷和邻苯二甲酸二丁酯的混合溶液充分混合，在30℃下搅拌11h后得到溶液D，向溶液D中加入摩尔比为1:0.03的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体和过氧化二苯甲酰，在35℃下搅拌11h，得到溶液C。
将聚乙烯醇加入水中95℃加热搅拌1.5h配成聚乙烯醇溶液，并将聚乙烯醇溶液加入到溶液C中，75℃搅拌11h后静置分层，去掉水层得到溶液E，用甲醇清洗溶液E，得到微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。
实施例2。
本发明提供一种面料用防蚊材料，包括由实施例1中制备方法制得的微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。该微胶囊由于通过1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成微胶囊膜，然后通过苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚与1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成溶液并对驱蚊酯进行包覆形成高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，然后通过致孔剂形成微孔微胶囊，并利用溶胀剂进行扩孔，最后形成微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，从而该方法形成的微胶囊上具有孔结构且孔进行进一步扩大，从而能有效地使得微胶囊中的驱蚊酯得到很好的释放，从而提高防蚊效果。
实施例3
本发明提供一种穿戴品，穿戴品由面料制成，面料由纱线制成，纱线由面料用防蚊材料与粘胶和植物粉混合通过喷丝然后纺纱制成。面料用防蚊材料与粘胶和植物粉混合后通过喷丝然后纺纱制成纱线。纱线编制成面料，面料制成穿戴品。
由于纱线中含有防蚊材料，且防蚊材料中采用微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，该微胶囊由于通过1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成微胶囊膜，然后通过苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚与1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体形成溶液并对驱蚊酯进行包覆形成高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，然后通过致孔剂形成微孔微胶囊，并利用溶胀剂进行扩孔，最后形成微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊，从而该方法形成的微胶囊上具有孔结构且孔进行进一步扩大，从而能有效地使得微胶囊中的驱蚊酯得到很好的释放，从而提高防蚊效果。
Claims (9)
1.面料用防蚊材料的制备方法，其特征在于，包括以下步骤：
S1.制备1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体；
S2.将苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚与S1步骤中制得的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体混合振动得到均相溶液A；
将驱蚊酯和乳化剂加入均相溶液A中,搅拌均匀后得到均相溶液B；
用紫外光灯照射均相溶液B引发聚合反应，反应完成后用乙醇反复超声波振动洗涤后得到高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊；
S3.将质量分数为25％的十二烷基硫酸钠水溶液、高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊和致孔剂充分混合，在25℃～35℃下搅拌9h～11h后得到溶液D，向溶液D中加入摩尔比为1:0.02～0.03的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体和溶胀剂，在25℃～35℃下搅拌9h～11h，得到溶液C；
将表面活性剂加入水中，在85℃～95℃加热搅拌0.5h～1.5h得到表面活性剂溶液，并将表面活性剂溶液加入到溶液C中，65℃～75℃搅拌9h～11h后静置分层，去掉水层得到溶液E，用甲醇清洗溶液E，得到微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。
2.根据权利要求1所述的面料用防蚊材料的制备方法，其特征在于：S1步骤中制备的1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体的步骤为：将摩尔比为1:1～1.5的乙烯基咪唑和溴代正庚烷在0℃下混合搅拌反应6.5h～7.5h，将得到的粘稠液体用乙醚反复洗涤后，旋转蒸发得到溴代1-乙烯基-3-庚基咪唑离子液体单体，将摩尔比为1:1的溴代1-乙烯基-3-庚基咪唑离子液体单体和六氟磷酸钾加入水溶液中，70℃～80℃旋转2h～3h，冷却，静置分层，除去水层得到有机层，将有机层用水和乙醚交替洗涤，70℃～80℃旋转蒸发1h～2h,得到1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体。
3.根据权利要求1所述的面料用防蚊材料的制备方法，其特征在于：S2步骤中1-乙烯基-3-庚基咪唑六氟磷酸离子液体单体、苯乙烯、丙烯腈、对二乙烯基苯和安息香乙醚的摩尔比为90～110:140～160:190～210:2.5～4.5:1.5～1.8。
4.根据权利要求1所述的面料用防蚊材料的制备方法，其特征在于：S2步骤中所述乳化剂为脂肪酸甘油酯。
5.根据权利要求1所述的面料用防蚊材料的制备方法，其特征在于：S2步骤中所述紫光灯的紫外光波长λ＝220～280nm。
6.根据权利要求1所述的面料用防蚊材料的制备方法，其特征在于：S3步骤中所述致孔剂为摩尔比为25～28:1的正庚烷和邻苯二甲酸二丁酯的混合溶液。
7.根据权利要求1所述的面料用防蚊材料的制备方法，其特征在于：S3步骤中所述表面活性剂溶液为聚乙烯醇溶液，所述溶胀剂为过氧化二苯甲酰。
8.一种面料用防蚊材料，其特征在于：包括由权利要求1至7中任意一项所述的面料用防蚊材料的制备方法制得的微孔高分子1-乙烯基-3-庚基咪唑六氟磷酸离子液体聚合膜防蚊微胶囊。
9.一种穿戴品，其特征在于：穿戴品由面料制成，面料由纱线制成，纱线由权利要求8所述的面料用防蚊材料与粘胶和植物粉混合通过喷丝然后纺纱制成。