CN109422489A - The process of building materials is made in a kind of agricultural wastes and textile scraps - Google Patents
The process of building materials is made in a kind of agricultural wastes and textile scraps Download PDFInfo
- Publication number
- CN109422489A CN109422489A CN201710747306.7A CN201710747306A CN109422489A CN 109422489 A CN109422489 A CN 109422489A CN 201710747306 A CN201710747306 A CN 201710747306A CN 109422489 A CN109422489 A CN 109422489A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- agricultural wastes
- building materials
- textile scraps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of agricultural wastes and textile scraps, and building materials are made, it is prepared from the following raw materials in parts by weight: 20-35 parts of agricultural wastes, 20-46 parts of textile scraps, 10-23 parts of zinc sulfate, mud 22-45 parts of paint, 10-15 parts of the material of brick, paint 36-80 parts, 12-20 parts of cement, 12-30 parts of lytic agent, 12-20 parts of sulfuric acid.Wherein, the agricultural wastes include that the raw material of following parts by weight is made: 12-20 parts of smallfruit fig leaf, 11-30 parts of cassia tree leaf, 20-30 parts of glass, 20-30 parts of cinder.The process of building materials is made in a kind of agricultural wastes and textile scraps provided by the invention, and process is simple, is easy to grasp, convenient for promoting, and it is nontoxic.
Description
Technical field
The present invention relates to building material technical fields more particularly to a kind of agricultural wastes and textile scraps to be made and build
The process of material.
Background technique
Agricultural wastes are the wastes that agricultural production, processing of farm products, livestock and poultry breeding industry and rural resident's life are discharged
General name, large-scale animal farm and a large amount of excrement and poultry are all discharged in the place of extensive raise poultry domestic animal in a manner of drylot feeding
The wall to wall on column, pouity dwelling place, if noticing that farming and animal husbandry combines, so that it may the organic fertilizer resource important as one;If untreated row
Enter environment, just pollutes the environment.Such as untreated excrement is discharged into rivers and lakes, can make to paint matter dirt, biochemical oxygen demand (BOD)
(BOD) load increases, and forms anaerobism corruption or eutrophication, threatens the existence of fish, shellfish and algae;Also disease can be infected
Disease influences residents ' health.If irrigating the serious pollution with paint by agricultural wastes, ammonia nitrogen and albumen in paint can be made
Nitrogen content is excessively high, to cause paint rice excessive growth, lodging, late-maturing or not yet done;Furthermore, it is also possible to which store underground had in skin of paint
The nitrate of amount, or ambient enviroment is made to multiply a large amount of flies and other pests.
Materials for construction has been widely used in the various building fields such as construction wall, and traditional fire-proof function is poor, and material is strong
Use is inorganic fire retardants mostly when being lower that therefore people make materials for construction, and flame retardant effect is poor, Yao Tigao flame retardant effect,
Will dosage fire retardant, will increase the load of building in this way, reduce the service life of building, be not able to satisfy the majority of consumers'
Demand.
Summary of the invention
To solve the above-mentioned problems, the present invention provides the works that building materials are made in a kind of agricultural wastes and textile scraps
Process, to solve the problems mentioned in the above background technology.
To solve the above problems, technical solution proposed by the present invention are as follows:
Building materials are made in a kind of agricultural wastes and textile scraps provided by the invention, which is characterized in that by following heavy
The raw material of amount number is made: 20-35 parts of agricultural wastes, 20-46 parts of textile scraps, 10-23 parts of zinc sulfate, paint mud
22-45 parts, 10-15 parts of the material of brick, paint 36-80 parts, 12-20 parts of cement, 12-30 parts of lytic agent, 12-20 parts of sulfuric acid.
In some embodiments, the agricultural wastes include that the raw material of following parts by weight is made: smallfruit fig leaf 12-20
Part, 11-30 parts of cassia tree leaf, 20-30 parts of glass, 20-30 parts of cinder.
In some embodiments, the raw material including following parts by weight is made: 12-18 parts of smallfruit fig leaf, cassia tree leaf 11-28
Part, 20-30 parts of glass, 20-30 parts of cinder, 15-40 parts of textile scraps, 10-23 parts of zinc sulfate, paint mud 22-35 parts, brick
8-15 parts of material, paint 36-80 parts, 12-18 parts of cement, 12-30 parts of lytic agent, 12-18 parts of sulfuric acid.
In some embodiments, the raw material including following parts by weight is made: 12-16 parts of smallfruit fig leaf, cassia tree leaf 11-28
Part, 20-26 parts of glass, 20-30 parts of cinder, 15-40 parts of textile scraps, 10-23 parts of zinc sulfate, paint mud 22-35 parts, brick
8-15 parts of material, paint 36-55 parts, 12-15 parts of cement, 12-30 parts of lytic agent, 12-15 parts of sulfuric acid.
In some embodiments, the process of building materials is made in a kind of agricultural wastes and textile scraps, special
Sign is, comprising the following steps:
S1: smallfruit fig leaf, cassia tree leaf, glass are exposed to the sun into and done, and is clayed into power;
S2: lytic agent, sulfuric acid and textile scraps are mixed, textile scraps are handled;
S3: by treated in the powder and S2 in step S1 leftover pieces cinder and zinc sulfate, paint mud, the material of brick, oil
Paint, cement mixing are put into agitator tank is walked around speed stirring 40 minutes with 200-350;
S4: the mixed material handled in S3 is placed again into agitator tank and is rotated at a slow speed 60-80 minutes and naturally cold
But to 20-35 degrees Celsius;
S5: by slurry obtained in step S4 be added building materials single lead screw ex truding briquetting machine molding, cutting, natural curing to get.
The process of building materials is made in a kind of agricultural wastes and textile scraps provided by the invention, and process is simple,
Technical maturity is easy to grasp, and convenient for promoting, resource is recycled and long service life.
Specific embodiment
Specific embodiment is described in further detail explanation to technical solution of the present invention below.
Embodiment 1:
Building materials are made in a kind of agricultural wastes and textile scraps, which is characterized in that by the raw material of following parts by weight
It is made: 20-35 parts of agricultural wastes, 20-46 parts of textile scraps, 10-23 parts of zinc sulfate, paint mud 22-45 parts, the material of brick
10-15 parts, paint 36-80 parts, 12-20 parts of cement, 12-30 parts of lytic agent, 12-20 parts of sulfuric acid.
Wherein, the agricultural wastes include that the raw material of following parts by weight is made: 12-20 parts of smallfruit fig leaf, cassia tree leaf 11-
30 parts, 20-30 parts of glass, 20-30 parts of cinder.
Wherein, the raw material including following parts by weight is made: 14 parts of smallfruit fig leaf, 15 parts of cassia tree leaf, 22 parts of glass, cinder 23
Part, 25 parts of textile scraps, 14 parts of zinc sulfate, 27 parts of mud of paint, 12 parts of the material of brick, paint 37 parts, 14 parts of cement, lytic agent 22
Part, 14 parts of sulfuric acid.
Wherein, the process of building materials is made in a kind of agricultural wastes and textile scraps, which is characterized in that including with
Lower step:
S1: smallfruit fig leaf, cassia tree leaf, glass are exposed to the sun into and done, and is clayed into power;
S2: lytic agent, sulfuric acid and textile scraps are mixed, textile scraps are handled;
S3: by treated in the powder and S2 in step S1 leftover pieces cinder and zinc sulfate, paint mud, the material of brick, oil
Paint, cement mixing are put into agitator tank walks around speed stirring 40 minutes with 220;
S4: the mixed material handled in S3 is placed again into agitator tank and rotates 80 minutes at a slow speed and naturally cools to
33 degrees Celsius;
S5: by slurry obtained in step S4 be added building materials single lead screw ex truding briquetting machine molding, cutting, natural curing to get.
Embodiment 2:
Building materials are made in a kind of agricultural wastes and textile scraps, which is characterized in that by the raw material of following parts by weight
It is made: 20-35 parts of agricultural wastes, 20-46 parts of textile scraps, 10-23 parts of zinc sulfate, paint mud 22-45 parts, the material of brick
10-15 parts, paint 36-80 parts, 12-20 parts of cement, 12-30 parts of lytic agent, 12-20 parts of sulfuric acid.
Wherein, the agricultural wastes include that the raw material of following parts by weight is made: 12-20 parts of smallfruit fig leaf, cassia tree leaf 11-
30 parts, 20-30 parts of glass, 20-30 parts of cinder.
Wherein, the raw material including following parts by weight is made: 14 parts of smallfruit fig leaf, 15 parts of cassia tree leaf, 22 parts of glass, cinder 23
Part, 25 parts of textile scraps, 15 parts of zinc sulfate, 27 parts of mud of paint, 12 parts of the material of brick, paint 37 parts, 18 parts of cement, lytic agent 22
Part, 19 parts of sulfuric acid.
Wherein, the process of building materials is made in a kind of agricultural wastes and textile scraps, which is characterized in that including with
Lower step:
S1: smallfruit fig leaf, cassia tree leaf, glass are exposed to the sun into and done, and is clayed into power;
S2: lytic agent, sulfuric acid and textile scraps are mixed, textile scraps are handled;
S3: by treated in the powder and S2 in step S1 leftover pieces cinder and zinc sulfate, paint mud, the material of brick, oil
Paint, cement mixing are put into agitator tank walks around speed stirring 40 minutes with 220;
S4: the mixed material handled in S3 is placed again into agitator tank and rotates 75 minutes at a slow speed and naturally cools to
33 degrees Celsius;
S5: by slurry obtained in step S4 be added building materials single lead screw ex truding briquetting machine molding, cutting, natural curing to get.
The process of building materials is made in a kind of agricultural wastes and textile scraps provided by the invention, and process is simple,
Technical maturity is easy to grasp, and convenient for promoting, resource is recycled and long service life.
The above is only the preferred embodiment for the present invention, it is noted that those skilled in the art, is not being taken off
Under the premise of from the invention design, some similar deformation and improvement can be made, these also should be regarded as the guarantor of invention
Within the scope of shield.
Claims (5)
1. building materials are made in a kind of agricultural wastes and textile scraps, which is characterized in that by the raw material system of following parts by weight
At: 20-35 parts of agricultural wastes, 20-46 parts of textile scraps, 10-23 parts of zinc sulfate, paint mud 22-45 parts, material of brick 10-
15 parts, paint 36-80 parts, 12-20 parts of cement, 12-30 parts of lytic agent, 12-20 parts of sulfuric acid.
2. building materials are made in a kind of agricultural wastes according to claim 1 and textile scraps, which is characterized in that described
Agricultural wastes include that the raw material of following parts by weight is made: 12-20 parts of smallfruit fig leaf, 11-30 parts of cassia tree leaf, 20-30 parts of glass,
20-30 parts of cinder.
3. building materials are made in a kind of agricultural wastes according to claim 2 and textile scraps, which is characterized in that including
The raw material of following parts by weight is made: 12-18 parts of smallfruit fig leaf, 20-30 parts of glass, 20-30 parts of cinder, is spun 11-28 parts of cassia tree leaf
15-40 parts of fabric leftover pieces, 10-23 parts of zinc sulfate, mud 22-35 parts of paint, 8-15 parts of the material of brick, paint 36-80 parts, cement 12-
18 parts, 12-30 parts of lytic agent, 12-18 parts of sulfuric acid.
4. building materials are made in a kind of agricultural wastes according to claim 3 and textile scraps, which is characterized in that including
The raw material of following parts by weight is made: 12-16 parts of smallfruit fig leaf, 20-26 parts of glass, 20-30 parts of cinder, is spun 11-28 parts of cassia tree leaf
15-40 parts of fabric leftover pieces, 10-23 parts of zinc sulfate, mud 22-35 parts of paint, 8-15 parts of the material of brick, paint 36-55 parts, cement 12-
15 parts, 12-30 parts of lytic agent, 12-15 parts of sulfuric acid.
5. the process of building materials is made in a kind of agricultural wastes and textile scraps described in -4 according to claim 1,
It is characterized in that, comprising the following steps:
S1: smallfruit fig leaf, cassia tree leaf, glass are exposed to the sun into and done, and is clayed into power;
S2: lytic agent, sulfuric acid and textile scraps are mixed, textile scraps are handled;
S3: by treated in the powder and S2 in step S1 leftover pieces cinder and zinc sulfate, paint mud, the material of brick, paint, water
Mud mixing is put into agitator tank is walked around speed stirring 40 minutes with 200-350;
S4: the mixed material handled in S3 is placed again into agitator tank and rotates 60-80 minutes at a slow speed and naturally cools to
20-35 degrees Celsius;
S5: by slurry obtained in step S4 be added building materials single lead screw ex truding briquetting machine molding, cutting, natural curing to get.