CN109421340A - A kind of weaving method of composite fibre thermal fabric - Google Patents
A kind of weaving method of composite fibre thermal fabric Download PDFInfo
- Publication number
- CN109421340A CN109421340A CN201710740116.2A CN201710740116A CN109421340A CN 109421340 A CN109421340 A CN 109421340A CN 201710740116 A CN201710740116 A CN 201710740116A CN 109421340 A CN109421340 A CN 109421340A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiber
- composite fibre
- fabric
- weaving method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of weaving method of composite fibre thermal fabric, include the following steps: that (1) raw material selects;(2) fiber pre-processes;(3) it spins;(4) it weaves;(5) final finishing.The present invention has the advantage that 1) design is novel, weaving method is easy, and easy to operate, exploitativeness is strong;2) the good thermal property of fabric is assigned at air layer structure using non-warmth retention property material knitting, while reduces fabric cost;3) blended and be woven into fabric with the different raw material of function by four kinds, so that fabric is had both the kind excellent properties such as warming, fashion, health care, pro-skin and one;4) fabric of this method braiding also has a variety of comprehensive performances on the basis of meeting thermal property, practical, can meet pursuit of the modern consumer to garment material, wide market.
Description
Technical field
The present invention relates to fabric technical fields, more particularly to a kind of weaving method of composite fibre thermal fabric.
Background technique
Currently, industry improve fabric thermal property main method be in fabric ingredient be added have thermal property at
Point, such as animal wool or animal suede etc., wherein this kind of fabric has good warming really using being at most wool, cashmere
Performance, but due to using the higher animal wool of price or animal down as raw material, the clothes for making such fabric and its being prepared
Price is also higher;In addition, such thermal fabric is to obtain better warming effect, pure animal wool or animal suede system are generallyd use
It is standby to form, since ingredient is single, it is functional also more single, it is not able to satisfy present people to garment material warmth retention property
The requirement of many-sided comprehensive performance such as the price and comprehensive health-care performance that can, be suitable for.
Summary of the invention
It is woven the invention mainly solves the technical problem of providing a kind of weaving method of composite fibre thermal fabric
Thermal fabric can satisfy requirement of the modern people to insulation garment fabric comprehensive performance.
In order to solve the above technical problems, one technical scheme adopted by the invention is that: a kind of composite fibre thermal surface is provided
The weaving method of material, includes the following steps:
(1) raw material selects: selecting soybean fiber, polyester fiber, jade silkworm fiber and medical stone, viscose fiber as blended needle
Knit the raw material of sweater;
(2) fiber pre-processes: spraying the pretreatment containing antistatic agent and antilubricant respectively in the raw material surface in step (1)
Then liquid sprays one layer of weaving lubricating oil again, set for 24 hours with plastic film covering is bored, then use wool opener shredding;
(3) it spins: including carding, drafting, rove, spun yarn, winder, doubling, double twisting and yarn steaming process, making to locate in advance in step (2)
Blended soybean fiber and medical stone, viscose fiber after reason are the first yarn, by polyester fiber and jade silkworm fiber it is blended be
Two yarns;
(4) it weaves: on two-sided circular knitting machine, using fixed knitting needle arrangement, triangle arrangement and mode of entrying by step (3)
In the first yarn and the second yarn be woven into two panels single-side fabric, then air is prepared by running-on, flatcar and machine tailor's sequence
Layer fabric;
(5) final finishing;Fabric in step (5) is prepared into finished product through soft treatment, open-width, washing, drying and fixating shape step
Composite fibre thermal fabric.
In a preferred embodiment of the present invention, in the step (1), the fineness of the soybean fiber is 3.13~
3.42dtex, average length 80mm;The fineness of the polyester fiber is 4.13~4.42dtex, average length 60mm;Institute
The fineness for stating jade silkworm fiber is 2.38~2.88dtex, average length 40mm;The fineness of the medical stone, viscose fiber is
1.71~1.93dtex, average length 40mm.
In a preferred embodiment of the present invention, in the step (2), the pretreatment fluid is to be containing mass fraction
0.5~0.6% antistatic agent and 0.2~0.3% antilubricant aqueous solution.
In a preferred embodiment of the present invention, in the step (3), soybean fiber and wheat in first yarn
The blending rate of meal stone viscose rayon is 75~85%: 15~25%;Polyester fiber and jade silkworm fiber in second yarn
Blending rate is 60~70%: 30~40%.
In a preferred embodiment of the present invention, the specification of first yarn is 16.9tex;The rule of second yarn
Lattice are 14.6tex.
In a preferred embodiment of the present invention, in the step (4), the specification of the two-sided circular knitting machine are as follows: 24
Needle/30mm, number 60F, barrel dliameter 755mm.
In a preferred embodiment of the present invention, in the step (4), the knitting needle is arranged as being ordered as dials knitting needle
AB, the cylinder knitting needle are ordered as AAAAAABBBBBB, are aligned using rib-loop, 12 pieces of one, knitting needle circulations;The triangle row
It is classified as 24F mono- circulation;The mode of entrying is that system-wide number penetrates the first yarn, and the is lining into the number of dials knitting needle lopping
Two yarns.
In a preferred embodiment of the present invention, in the step (4), the weaving are as follows: the first yarn is entried
Tension is 2.5cN, and the tension of entrying of the second yarn is 4.5cN;Sinking depth is 5.16mm;Coil length is 16.08mm;Loom
Revolving speed is 28r/min.
In a preferred embodiment of the present invention, the specification of the composite fibre thermal fabric of the preparation are as follows: breadth
190mm, grammes per square metre 245g/m2。
The beneficial effects of the present invention are: a kind of weaving method of composite fibre thermal fabric of the present invention, has the advantages that
1) design is novel, and weaving method is easy, and easy to operate, exploitativeness is strong;
2) the good thermal property of fabric is assigned at air layer structure using non-warmth retention property material knitting, while reduces fabric
Cost;
3) blended and be woven into fabric with the different raw material of function by four kinds, so that fabric is had both warming, fashion, health care, pro-skin
Deng kind of excellent properties and one;
4) fabric of this method braiding also has a variety of comprehensive performances on the basis of meeting thermal property, practical, can expire
Pursuit of the sufficient modern consumer to garment material, wide market.
Detailed description of the invention
Fig. 1 is a kind of cam chart of the weaving method of composite fibre thermal fabric of the present invention;
The components in the drawings are labeled as follows: Λ stitch cam,Tuck cam ,-flotation line triangle.
Specific embodiment
The preferred embodiments of the present invention will be described in detail with reference to the accompanying drawing, so that advantages and features of the invention energy
It is easier to be readily appreciated by one skilled in the art, so as to make a clearer definition of the protection scope of the present invention.
Referring to Fig. 1, the embodiment of the present invention includes:
Embodiment 1
A kind of weaving method of composite fibre thermal fabric, the specific steps are as follows:
(1) raw material selects: selecting soybean fiber, polyester fiber, jade silkworm fiber and medical stone, viscose fiber as blended needle
Knit the raw material of sweater;The fineness of the soybean fiber is 3.13~3.42dtex, average length 80mm;The terylene is fine
The fineness of dimension is 4.13~4.42dtex, average length 60mm;The fineness of the jade silkworm fiber is 2.38~2.88dtex, is put down
Equal length is 40mm;The fineness of the medical stone, viscose fiber is 1.71~1.93dtex, average length 40mm;
(2) fiber pre-processes: spraying the pretreatment containing antistatic agent and antilubricant respectively in the raw material surface in step (1)
Then liquid sprays one layer of weaving lubricating oil again, set for 24 hours with plastic film covering is bored, then use wool opener shredding;The pretreatment
Liquid be containing mass fraction be 0.5~0.6% antistatic agent and 0.2~0.3% antilubricant aqueous solution;
(3) it spins: including carding, drafting, rove, spun yarn, winder, doubling, double twisting and yarn steaming process, making to locate in advance in step (2)
Soybean fiber and medical stone, viscose fiber after reason is blended at the of 16.9tex with 75~85%: 15~25% ratio
One yarn, by polyester fiber and jade silkworm fiber with blended the second yarn at 14.6tex of 60~70%: 30~40% ratio;
(4) it weaves: including specification of equipment, knitting needle arrangement, triangle arrangement, mode of entrying and knitting technology;
Wherein, the specification of equipment are as follows: two-sided 24 needles of circular knitting machine/30mm, number 60F, barrel dliameter 755mm;
Knitting needle arrangement includes the sequence of dials knitting needle and cylinder knitting needle sequence, wherein dials knitting needle be ordered as AB, syringe is knitted
Needle is ordered as AAAAAABBBBBB, rib-loop contraposition, the knitting needle arrangement of 12 pieces of one, knitting needle circulations;
The triangle arrangement is as shown in Figure 1,24F mono- Weaving Cycle completed, and totally 5 recycle;
The mode of entrying are as follows: system-wide number penetrates the first yarn, and the second yarn is lining into the number of dials knitting needle lopping;
The knitting technology are as follows: the tension of entrying of the first yarn is 2.5cN, and the tension of entrying of the second yarn is 4.5cN;Kinking is deep
Degree is 5.16mm;Coil length is 16.08mm;Loom revolving speed is 28r/min;
(5) fabric in step (5) final finishing: is prepared into finished product through soft treatment, open-width, washing, drying and fixating shape step
Composite fibre thermal fabric.
The specification of the composite fibre thermal fabric of above method preparation are as follows: breadth 190mm, grammes per square metre 245g/m2。
Soybean fiber is a kind of new Regenerated Protein Fiber, and smooth appearance has mercerising, soft, pendency
Appropriateness, light specific gravity, moisture absorption moisture-inhibiting, strength is high, and elasticity is good, and the moisture absorption of gloss, cotton with feel, silk as cashmere is ventilative
With the warmth retention property of wool, it is known as " artificial cashmere ";Jade silkworm fiber is a kind of protein modified cellulose fibre, is had splendid
Soft glutinous skating sense and comfortable Moisture absorption & moisture conductivity are imitated containing the amino acid that ten several needed by human body are wanted with special pro-skin
Answer, it is emitting far-infrared and excitation anion many advantages, such as, especially suitable for weave contact skin textile;Medical stone is viscous
Glue fiber has far-infrared health care function;The fabric of polyester fiber preparation is well-pressed, smooth, conformality is good.
The blended preparation of above-mentioned four kinds of raw materials is had the fabric of air layer structure by the present invention, on the one hand warming in raising fabric
While performance, the cost of fabric is reduced;On the other hand, blended using the fibrous raw material of different function, improve fabric
Comprehensive performance makes it have both the kind excellent properties and one such as warming, fashion, health care, pro-skin, practical, can meet the modern times and disappear
Pursuit of the person of expense to garment material, wide market.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification and accompanying drawing content is applied directly or indirectly in other relevant skills
Art field, is included within the scope of the present invention.
Claims (9)
1. a kind of weaving method of composite fibre thermal fabric, which comprises the steps of:
(1) raw material selects: selecting soybean fiber, polyester fiber, jade silkworm fiber and medical stone, viscose fiber as blended needle
Knit the raw material of sweater;
(2) fiber pre-processes: spraying the pretreatment containing antistatic agent and antilubricant respectively in the raw material surface in step (1)
Then liquid sprays one layer of weaving lubricating oil again, set for 24 hours with plastic film covering is bored, then use wool opener shredding;
(3) it spins: including carding, drafting, rove, spun yarn, winder, doubling, double twisting and yarn steaming process, making to locate in advance in step (2)
Blended soybean fiber and medical stone, viscose fiber after reason are the first yarn, by polyester fiber and jade silkworm fiber it is blended be
Two yarns;
(4) it weaves: on two-sided circular knitting machine, using fixed knitting needle arrangement, triangle arrangement and mode of entrying by step (3)
In the first yarn and the second yarn be woven into two panels single-side fabric, then air is prepared by running-on, flatcar and machine tailor's sequence
Layer fabric;
(5) fabric in step (5) final finishing: is prepared into finished product through soft treatment, open-width, washing, drying and fixating shape step
Composite fibre thermal fabric.
2. the weaving method of composite fibre thermal fabric according to claim 1, which is characterized in that in the step (1),
The fineness of the soybean fiber is 3.13~3.42dtex, average length 80mm;The fineness of the polyester fiber is
4.13~4.42dtex, average length 60mm;The fineness of the jade silkworm fiber is 2.38~2.88dtex, and average length is
40mm;The fineness of the medical stone, viscose fiber is 1.71~1.93dtex, average length 40mm.
3. the weaving method of composite fibre thermal fabric according to claim 1, which is characterized in that in the step (2),
The pretreatment fluid be containing mass fraction be 0.5~0.6% antistatic agent and 0.2~0.3% antilubricant aqueous solution.
4. the weaving method of composite fibre thermal fabric according to claim 1, which is characterized in that in the step (3),
The blending rate of soybean fiber and medical stone, viscose fiber is 75~85%: 15~25% in first yarn;It is described
Polyester fiber and the blending rate of jade silkworm fiber are 60~70%: 30~40% in second yarn.
5. the weaving method of composite fibre thermal fabric according to claim 4, which is characterized in that first yarn
Specification is 16.9tex;The specification of second yarn is 14.6tex.
6. the weaving method of composite fibre thermal fabric according to claim 1, which is characterized in that in the step (4),
The specification of the two-sided circular knitting machine are as follows: 24 needles/30mm, number 60F, barrel dliameter 755mm.
7. the weaving method of composite fibre thermal fabric according to claim 1, which is characterized in that in the step (4),
The knitting needle is arranged as the AB that is ordered as of dials knitting needle, and the cylinder knitting needle is ordered as AAAAAABBBBBB, using rib-loop pair
Position, 12 pieces of one, knitting needle circulations;The triangle arrangement is 24F mono- circulation;The mode of entrying is that system-wide number penetrates the first yarn
Line is lining into the second yarn in the number of dials knitting needle lopping.
8. the weaving method of composite fibre thermal fabric according to claim 1, which is characterized in that in the step (4),
The weaving are as follows: the tension of entrying of the first yarn is 2.5cN, and the tension of entrying of the second yarn is 4.5cN;Sinking depth is
5.16mm;Coil length is 16.08mm;Loom revolving speed is 28r/min.
9. according to claim 1 to the weaving method of composite fibre thermal fabric described in one of 8, which is characterized in that the system
The specification of standby composite fibre thermal fabric are as follows: breadth 190mm, grammes per square metre 245g/m2。