CN109401538A - 一种高固体环氧耐磨涂料的制备方法 - Google Patents
一种高固体环氧耐磨涂料的制备方法 Download PDFInfo
- Publication number
- CN109401538A CN109401538A CN201811133365.6A CN201811133365A CN109401538A CN 109401538 A CN109401538 A CN 109401538A CN 201811133365 A CN201811133365 A CN 201811133365A CN 109401538 A CN109401538 A CN 109401538A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- epoxy resin
- epoxy
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明创造提供一种高固体环氧耐磨涂料的制备方法，包括主剂和固化剂。所述主剂由包括如下步骤的方法制备得到：将环氧树脂1、环氧树脂2、活性稀释剂、正丁醇、二甲苯、份防沉剂、分散剂依次加入反应釜中，进行高速搅拌得到混合液；在高速搅拌下，向混合液依次缓缓加入600目滑石粉、长石粉、云母粉、氧化铁红，搅拌30分钟，使其充分混合；向混合液依次加入环氧树脂1、偶联剂、正丁醇、二甲苯、非浮铝粉、分散剂、二甲苯，经高速剪切分散均匀，调配成主剂。本发明创造具有的优点和积极效果是：具有极好的耐腐蚀性，极好的防腐性能，可承受海水浸泡，极好的表面适应性能。
Description
技术领域
本发明创造涉及涂料制造领域，具体涉及一种高固体环氧耐磨涂料的制备方法。
背景技术
环氧树脂具有附着力强、硬度高、耐磨、耐酸碱等优点，因此在重防腐漆、船舶漆、集装箱漆等，特别是环氧漆得到广泛应用。随着经济的快速发展，现代工业、办公环境、医院等公共场所对环境的要求越来越高，传统涂料难以满足现代工业等的要求。传统的溶剂型环氧漆在生产、施工、固化过程中会排出大量有机溶剂(VOC)，造成环境污染，并影响人体健康。近几年，世界各国对涂料制定了相应的法规以限制溶剂的排放量。高固体分环氧防腐涂料具有低VOC排放、良好的附着力、较高防腐性、使用面广泛、大大提高施工效率等优点,在防腐要求高的施工领域得到广泛的应用。表述了高固体分涂料的配制设计及技术性能指标。
工程中各种金属结构所处的环境及运行工况十分复杂，大量建筑物、闸门、钢结构制件经常受到上游漂浮物、水中泥沙的冲刷和磨损，从而导致涂层的破坏和失效，涂料的耐磨性能直接影响到涂层的抗冲耐磨损性，同时在一定程度上也反映了涂料的使用寿命。
发明内容
本发明创造要解决的问题是提供一种高固体环氧耐磨涂料的制备方法，制得的涂料具有极好的耐腐蚀性，极好的防腐性能，可承受海水浸泡，极好的表面适应性能，漆膜坚韧强硬，极好的耐磨损性，用于海洋和工业腐蚀环境下高耐磨损要求部位。
为解决上述技术问题，本发明创造采用的技术方案是：一种高固体环氧耐磨涂料的制备方法，包括主剂和固化剂，其特征在于：
所述主剂由包括如下步骤的方法制备得到：
步骤1：将环氧树脂1、环氧树脂2、活性稀释剂、正丁醇、二甲苯、防沉剂、分散剂依次加入反应釜中，进行高速搅拌得到混合液；
步骤2：在高速搅拌下，向混合液依次缓缓加入600目滑石粉、长石粉、云母粉、氧化铁红，搅拌30分钟，使其充分混合；
步骤3：向混合液依次加入环氧树脂1、偶联剂、正丁醇、二甲苯、非浮铝粉、分散剂、二甲苯，经高速剪切分散均匀，调配成主剂；
所述固化剂由包括如下步骤的方法制备得到：按量将环氧树脂固化剂和环氧树脂促进剂两种反应液混合加入反应釜中，搅拌5-10min得到固化剂溶液；
所述主剂和固化剂的质量配比为9:1。
按重量份数计所述主剂包括如下组份：步骤1中环氧树脂1是12.5-29.5份，环氧树脂2是3.5-5.5份，活性稀释剂3.0-5.5份，正丁醇1.2-2.7份，二甲苯2.0-7.0份，防沉剂1.0-2.0份，分散剂0.1-0.34份；步骤2中滑石粉600目7.3-14.5份，长石粉15.0-37.0份，云母粉5.0-9.0份，氧化铁红1.0-2.0份；步骤3中环氧树脂1是4.5-8.5份，偶联剂0.6-0.8份，正丁醇2.41-4.55份，二甲苯0.5-1.5份，非浮铝粉2.0-4.0份，分散剂0.1-0.3份、二甲苯1.23-2.35份。
按重量份数计所述固化剂包括如下组份：环氧树脂固化剂95.3-99.75份，环氧树脂促进剂1.25-4.70份。
进一步，环氧树脂1是E51，环氧树脂2是E44。
进一步，所述分散剂为脂肪族酰胺类分散剂，所述防沉剂是聚烯烃蜡。
进一步，所述环氧树脂固化剂是通过腰果油改性酚醛胺技术合成制得。
进一步，所述环氧树脂促进剂是DMP-30。
进一步，所述活性稀释剂是腰果酚改性环氧树脂类活性稀释剂。
进一步，所述偶联剂为硅烷偶联剂。
本发明创造具有的优点和积极效果是：1、涂料主剂主要作用于海洋和工业腐蚀环境下高耐磨损要求部位，可作为底漆或中间漆使用，具有漆膜坚韧，极佳的耐磨损性，极好的防腐性能，可承受海水浸泡，极好的表面适应性能。2、在主剂制备中环氧稀释剂作为溶剂，能将在搅拌过程中降低涂料中的树脂粘度，以便于和各组分更加充分的溶解，改善其工艺性能。3、二甲苯作为溶剂，起稀释作用；防沉助剂使涂料具有触变性，粘度大大提高，增强其涂膜性能，方便施工；氧化铁红作为一种防锈颜料，有耐高温，可以代替高价的红丹漆，节约有色金属。4、云母粉具有活性羟基基团使其容易与乳液有机地结合起来，云母片状颗粒在乳液及水的混合物中极易分散悬浮，在涂膜中平行排列、搭接和重叠，成一种叠层结构，增加了涂膜的致密性，从而提高了涂膜强度、耐洗刷性、抗透水性、防止龟、延迟粉化，延长涂膜的使用寿命；减少树脂的用量，从而降低生产成本。5、非浮铝粉作为填料，在涂料中可接触金属表面形成致密的保护膜，起到良好的耐磨耐腐防锈功能。氧化铁红作为一种防锈颜料，有耐高温，可以代替高价的红丹漆，节约有色金属。6、在涂料固化剂制备过程，DMP-30作为环氧树脂促进剂，使环氧树脂体系加速固化。
具体实施方式
下面对本发明创造的具体实施例做详细说明。
原料来源如下：
| 原料名称 | 型号 |
| 去离子水 | 工业级 |
| 防沉剂 | 聚烯烃蜡 |
| 分散剂 | 脂肪族酰胺类分散剂 |
| 润湿分散剂 | AFCONA-4598 |
| 消泡剂 | TEGO 810 |
| 环氧树脂1 | E51 |
| 环氧树脂2 | E44 |
| 活性稀释剂 | 腰果酚改性环氧树脂类活性稀释剂 |
| 偶联剂 | 硅烷偶联剂 |
| 环氧树脂固化剂 | 通过腰果油改性酚醛胺技术合成 |
| 环氧树脂促进剂 | DMP-30 |
实施例1：
本发明创造的一种高固体环氧耐磨涂料的制备方法，包括主剂和固化剂。
所述主剂由包括如下步骤的方法制备得到：
步骤1：将12.5份环氧树脂1、5.5份环氧树脂2、5.5份活性稀释剂、2.7份正丁醇、7.0份二甲苯、2.0份防沉剂、0.30份分散剂依次加入反应釜中，进行高速搅拌得到混合液。
步骤2：在高速搅拌下，向混合液依次缓缓加入600目滑石粉12.5份、长石粉25.0份、云母粉9.0份、氧化铁红2.0份，搅拌30分钟，使其充分混合。
步骤3：向混合液依次加入环氧树脂1为4.5份、偶联剂0.8份、4.55份正丁醇、二甲苯1.5份、非浮铝粉2.0份、分散剂0.3份、二甲苯2.35份，经高速剪切分散均匀，调配成主剂。
所述固化剂由包括如下步骤的方法制备得到：按量将环氧树脂固化剂和环氧树脂促进剂两种反应液混合加入反应釜中，搅拌5-10min得到固化剂溶液。
所述主剂和固化剂的质量配比为9:1。
实施例2：
所述主剂由包括如下步骤的方法制备得到：
步骤1：将29.5份环氧树脂1、3.5份环氧树脂2、3.0份活性稀释剂、1.2份正丁醇、5份二甲苯、1.0份防沉剂、0.1份分散剂依次加入反应釜中，进行高速搅拌得到混合液。
步骤2：在高速搅拌下，向混合液依次缓缓加入600目滑石粉10.3份、长石粉15.0份、云母粉8.0份、氧化铁红1.0份，搅拌30分钟，使其充分混合。
步骤3：向混合液依次加入环氧树脂1为8.5份、偶联剂0.6份、2.41份正丁醇、二甲苯0.5份、非浮铝粉4.0份、分散剂0.1份、二甲苯2.24份，经高速剪切分散均匀，调配成主剂。
所述固化剂由包括如下步骤的方法制备得到：按量将环氧树脂固化剂和环氧树脂促进剂两种反应液混合加入反应釜中，搅拌5-10min得到固化剂溶液。
所述主剂和固化剂的质量配比为9:1。
实施例3
所述主剂由包括如下步骤的方法制备得到：
步骤1：将20.36份环氧树脂1、4.5份环氧树脂2、4.0份活性稀释剂、2.0份正丁醇、2.0份二甲苯、1.5份防沉剂、0.15份分散剂依次加入反应釜中，进行高速搅拌得到混合液。
步骤2：在高速搅拌下，向混合液依次缓缓加入600目滑石粉7.3份、长石粉37.0份、云母粉5.0份、氧化铁红1.5份，搅拌30分钟，使其充分混合。
步骤3：向混合液依次加入环氧树脂1为6.5份、偶联剂0.7份、2.61份正丁醇、二甲苯0.5份、非浮铝粉3.0份、分散剂0.15份、二甲苯1.23份，经高速剪切分散均匀，调配成主剂。
所述固化剂由包括如下步骤的方法制备得到：按量将环氧树脂固化剂和环氧树脂促进剂两种反应液混合加入反应釜中，搅拌5-10min得到固化剂溶液。
所述主剂和固化剂的质量配比为9:1。
将以上实施例制得的高固体环氧耐磨涂料进行性能检测，检测数据如下表所示。
从上表中可以看出，制得的高固体环氧耐磨涂料，具有极好的耐腐蚀性，极好的防腐性能，可承受海水浸泡，极好的表面适应性能，漆膜坚韧强硬，极好的耐磨损性，用于海洋和工业腐蚀环境下高耐磨损要求部位。
以上对本发明创造的实施例进行了详细说明，但所述内容仅为本发明创造的较佳实施例，不能被认为用于限定本发明的实施范围。凡依本发明创造范围所作的均等变化与改进等，均应仍归属于本专利涵盖范围之内。
Claims (8)
1.一种高固体环氧耐磨涂料的制备方法，包括主剂和固化剂，其特征在于：
所述主剂由包括如下步骤的方法制备得到：
步骤1：将环氧树脂1、环氧树脂2、活性稀释剂、正丁醇、二甲苯、防沉剂、分散剂依次加入反应釜中，进行高速搅拌得到混合液；
步骤2：在高速搅拌下，向混合液依次缓缓加入600目滑石粉、长石粉、云母粉、氧化铁红，搅拌30分钟，使其充分混合；
步骤3：向混合液依次加入环氧树脂1、偶联剂、正丁醇、二甲苯、非浮铝粉、分散剂、二甲苯，经高速剪切分散均匀，调配成主剂；
所述固化剂由包括如下步骤的方法制备得到：按量将环氧树脂固化剂和环氧树脂促进剂两种反应液混合加入反应釜中，搅拌5-10min得到固化剂溶液；
所述主剂和固化剂的质量配比为9:1。
2.根据权利要求1所述的一种高固体环氧耐磨涂料的制备方法，其特征在于：
按重量份数计所述主剂包括如下组份：步骤1中环氧树脂1是12.5-29.5份，环氧树脂2是3.5-5.5份，活性稀释剂3.0-5.5份，正丁醇1.2-2.7份，二甲苯2.0-7.0份，防沉剂1.0-2.0份，分散剂0.1-0.34份；步骤2中滑石粉600目7.3-14.5份，长石粉15.0-37.0份，云母粉5.0-9.0份，氧化铁红1.0-2.0份；步骤3中环氧树脂1是4.5-8.5份，偶联剂0.6-0.8份，正丁醇2.41-4.55份，二甲苯0.5-1.5份，非浮铝粉2.0-4.0份，分散剂0.1-0.3份、二甲苯1.23-2.35份；
按重量份数计所述固化剂包括如下组份：环氧树脂固化剂95.3-99.75份，环氧树脂促进剂1.25-4.70份。
3.根据权利要求1所述的一种高固体环氧耐磨涂料的制备方法，其特征在于：环氧树脂1是E51，环氧树脂2是E44。
4.根据权利要求1所述的一种高固体环氧耐磨涂料的制备方法，其特征在于：所述分散剂为脂肪族酰胺类分散剂，所述防沉剂是聚烯烃蜡。
5.根据权利要求1所述的一种高固体环氧耐磨涂料，其特征在于：所述环氧树脂固化剂是通过腰果油改性酚醛胺技术合成制得。
6.根据权利要求1所述的一种高固体环氧耐磨涂料，其特征在于：所述环氧树脂促进剂是DMP-30。
7.根据权利要求1的所述的一种高固体环氧耐磨涂料，其特征在于：所述活性稀释剂是腰果酚改性环氧树脂类活性稀释剂。
8.根据权利要求1所述的一种高固体环氧耐磨涂料，其特征在于：所述偶联剂为硅烷偶联剂。