CN109401455A - Phenylpropyl alcohol expanding fire-proof paint - Google Patents
Phenylpropyl alcohol expanding fire-proof paint Download PDFInfo
- Publication number
- CN109401455A CN109401455A CN201811232345.4A CN201811232345A CN109401455A CN 109401455 A CN109401455 A CN 109401455A CN 201811232345 A CN201811232345 A CN 201811232345A CN 109401455 A CN109401455 A CN 109401455A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- phenylpropyl alcohol
- proof paint
- expanding fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention proposes a kind of phenylpropyl alcohol expanding fire-proof paints, according to parts by weight, including following components: 50~70 parts of styrene-acrylic emulsion, 4~8 parts of ammonium polyphosphate, 2~6 parts of dipentaerythritol, 8~16 parts of expanded perlite, 5~10 parts of hydroxyethyl cellulose, 0.4~0.8 part of wetting dispersing agent, 0.3~0.6 part of levelling agent, 2~6 parts of coalescing agent and 6~12 parts of modified Nano carborundum;Wherein, the modified Nano carborundum is mainly prepared by nanometer silicon carbide, starch and silane coupling agent.Not only coating expansion multiplying power is high for the fireproof coating, also improves its heat-insulated and refractory ability.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of phenylpropyl alcohol expanding fire-proof paint.
Background technique
Fireproof coating is exactly by that on the surface of those combustible materials, can improve the refractory ability of material, subtract paint brush
Slow propagation of flame spread speed, or can prevent to burn within a certain period of time, this kind of coating are known as fireproof coating, or are called fire-retardant
Coating.Fireproof coating is to reduce by the combustibility of painting material surface for flammable substrates surface, block the rapid climing of fire
Prolong, to improve by a kind of sapecial coating of painting material fire endurance.It is applied to flammable substrates surface, to change material table
Face combustion characteristics, retardance fire are spread rapidly;Or be applied on building element, the extraordinary of fire endurance to improve component applies
Material claims fireproof coating.
Although steel do not have combustibility, its thermal coefficient is big, and fire resistance is poor, in the case where flameproof protection is not added,
Generally there was only the fire endurance of 15min under the direct calcination of thermal-flame.More than 15min, steel construction intensity is reduced rapidly and very
Bearing capacity is lost fastly.When the temperature of structure reaches 350,500,600 DEG C, intensity declines 1/3,1/2,2/3 respectively, works as knot
When structure temperature reaches 600 DEG C or more, steel construction will lose bearing capacity completely.Just because of this, effective guarantor is taken to steel member
Shield measure protects it from the direct calcination of thermal-flame, delays the time of collapsing, providing valuable time for fire control just seems
It is particularly significant.Fireproof coating is coated on steel surface, in addition to there is decoration and protective effect, due to the noninflammability of coating itself
And flame retardancy, the sprawling of flame when fire can be prevented to occur delay the extension of the intensity of a fire.
Summary of the invention
The present invention proposes a kind of phenylpropyl alcohol expanding fire-proof paint, and not only coating expansion multiplying power is high for the fireproof coating, also improves
Its heat-insulated and refractory ability.
The technical scheme of the present invention is realized as follows:
A kind of phenylpropyl alcohol expanding fire-proof paint, according to parts by weight, including following components:
50~70 parts of styrene-acrylic emulsion, 4~8 parts of ammonium polyphosphate, 2~6 parts of dipentaerythritol, 8~16 parts of expanded perlite, hydroxyl
5~10 parts of ethyl cellulose, 0.4~0.8 part of wetting dispersing agent, 0.3~0.6 part of levelling agent, 2~6 parts of coalescing agent and modification
6~12 parts of nanometer silicon carbide;Wherein, the modified Nano carborundum is mainly by nanometer silicon carbide, starch and silane coupling agent system
It is standby to obtain.
Preferably, the modified Nano carborundum the preparation method comprises the following steps:
1) starch is added to the water and is stirred dispersion, amylase is then added and is digested, heating is gone out after enzymatic hydrolysis
It is living, obtain enzymolysis liquid;
2) nanometer silicon carbide and silane coupling agent are added into the enzymolysis liquid of step 1) and is stirred dispersion, warm to 60 DEG C~
70 DEG C, be stirred to react 2~6h, after centrifugal vacuum it is dry.
Preferably, the mass ratio of the starch and the nanometer silicon carbide is 10~20:1, the nanometer silicon carbide with
The mass ratio of the silane coupling agent is 25~35:1.
Preferably, the silane coupling agent is aminopropyl triethoxysilane, glycidol fan's oxygroup propyl trimethoxy
Silane, methacryloxypropyl trimethoxy silane, vinyltriethoxysilane, vinyltriethoxysilane, mercapto
Propyl front three (second) one or more of oxysilane and ethylenediaminepropyltriethoxysilane.
Preferably, the wetting dispersing agent is calgon wetting agent;The levelling agent selects water-and acrylate total
Polymers, fluorine richness polyacrylate copolymer or Siloxane-Oxyalkylene Copolymers polymer are one such.
Preferably, the coalescing agent be propylene glycol phenylate, dipropylene glycol n-butyl ether, Lauryl Alcohol ester, methoxybutanol,
At least one of ethylene glycol monobutyl ether and dipropylene glycol propyl ether.
The preparation method of phenylpropyl alcohol expanding fire-proof paint of the invention:
After mixing the above components evenly according to the proportion.
Beneficial effects of the present invention:
Phenylpropyl alcohol expanding fire-proof paint of the invention, which is added to, mainly to be prepared by nanometer silicon carbide, starch and silane coupling agent
Obtained nanometer silicon carbide, it is high with matrix resin binding force, it is not easy to be precipitated, improves the water resistance and fire insulation of coating
Energy.
Specific embodiment
Embodiment 1
Modified Nano carborundum the preparation method comprises the following steps:
1) starch is added to the water and is stirred dispersion, amylase is then added and is digested, heating is gone out after enzymatic hydrolysis
It is living, obtain enzymolysis liquid;
2) nanometer silicon carbide is added into the enzymolysis liquid of step 1) and aminopropyl triethoxysilane is stirred dispersion, temperature
To 60 DEG C DEG C, be stirred to react 6h, after centrifugal vacuum it is dry.
The mass ratio of starch and nanometer silicon carbide is 20:1, the quality of nanometer silicon carbide and aminopropyl triethoxysilane
The ratio between be 25:1.
Embodiment 2
Modified Nano carborundum the preparation method comprises the following steps:
1) starch is added to the water and is stirred dispersion, amylase is then added and is digested, heating is gone out after enzymatic hydrolysis
It is living, obtain enzymolysis liquid;
2) be added into the enzymolysis liquid of step 1) nanometer silicon carbide and methacryloxypropyl trimethoxy silane into
Row is dispersed with stirring, and temperature is stirred to react 2h to 70 DEG C, after centrifugal vacuum it is dry.
Embodiment 3
A kind of phenylpropyl alcohol expanding fire-proof paint, according to parts by weight, including following components:
60 parts of styrene-acrylic emulsion, 6 parts of ammonium polyphosphate, 7 parts of dipentaerythritol, 12 parts of expanded perlite, hydroxyethyl cellulose 7
The modification of part, 0.6 part of calgon wetting agent, 0.5 part of water-borne acrylate copolymer, 4 parts of propylene glycol phenylate and embodiment 1
8 parts of nanometer silicon carbide.
Embodiment 4
A kind of phenylpropyl alcohol expanding fire-proof paint, according to parts by weight, including following components:
50 parts of styrene-acrylic emulsion, 4 parts of ammonium polyphosphate, 8 parts of dipentaerythritol, 8 parts of expanded perlite, 5 parts of hydroxyethyl cellulose,
0.4 part of calgon wetting agent, 0.3 part of Siloxane-Oxyalkylene Copolymers polymer, 3 parts of Lauryl Alcohol ester and embodiment 2 change
6 parts of nanometer silicon carbide of property.
Embodiment 5
A kind of phenylpropyl alcohol expanding fire-proof paint, according to parts by weight, including following components:
55 parts of styrene-acrylic emulsion, 8 parts of ammonium polyphosphate, 5 parts of dipentaerythritol, 16 parts of expanded perlite, hydroxyethyl cellulose 8
Part, 0.5 part of calgon wetting agent, 0.6 part of Siloxane-Oxyalkylene Copolymers polymer, 2 parts of ethylene glycol monobutyl ether and embodiment 1
10 parts of modified Nano carborundum.
Embodiment 6
A kind of phenylpropyl alcohol expanding fire-proof paint, according to parts by weight, including following components:
70 parts of styrene-acrylic emulsion, 5 parts of ammonium polyphosphate, 10 parts of dipentaerythritol, 14 parts of expanded perlite, hydroxyethyl cellulose 10
Part, 0.8 part of calgon wetting agent, 0.6 part of fluorine richness polyacrylate copolymer, 6 parts of dipropylene glycol propyl ether and embodiment 2
12 parts of modified Nano carborundum.
Test example
The phenylpropyl alcohol expanding fire-proof paint that embodiment 3~6 obtains is tested for the property according to GB14907-2002, as a result
It is shown in Table 1:
The performance test results of the phenylpropyl alcohol expanding fire-proof paint of the invention of table 1
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of phenylpropyl alcohol expanding fire-proof paint, which is characterized in that according to parts by weight, including following components:
50~70 parts of styrene-acrylic emulsion, 4~8 parts of ammonium polyphosphate, 2~6 parts of dipentaerythritol, 8~16 parts of expanded perlite, ethoxy
5~10 parts of cellulose, 0.4~0.8 part of wetting dispersing agent, 0.3~0.6 part of levelling agent, 2~6 parts of coalescing agent and modified Nano
6~12 parts of silicon carbide;Wherein, the modified Nano carborundum is mainly prepared by nanometer silicon carbide, starch and silane coupling agent
It arrives.
2. phenylpropyl alcohol expanding fire-proof paint according to claim 1, which is characterized in that the system of the modified Nano carborundum
Preparation Method are as follows:
1) starch is added to the water and is stirred dispersion, amylase is then added and is digested, heat up inactivation after enzymatic hydrolysis, obtains
To enzymolysis liquid;
2) nanometer silicon carbide is added into the enzymolysis liquid of step 1) and silane coupling agent is stirred dispersion, temperature to 60 DEG C~70
DEG C, be stirred to react 2~6h, after centrifugal vacuum it is dry.
3. phenylpropyl alcohol expanding fire-proof paint according to claim 2, which is characterized in that the starch and the nano silicon carbide
The mass ratio of silicon is 10~20:1, and the mass ratio of the nanometer silicon carbide and the silane coupling agent is 25~35:1.
4. phenylpropyl alcohol expanding fire-proof paint according to claim 2, which is characterized in that the silane coupling agent is aminopropyl
Triethoxysilane, glycidyl ester oxy propyl trimethoxysilane, methacryloxypropyl trimethoxy silane, second
Alkenyl triethoxysilane, three ethoxy of vinyltriethoxysilane, mercapto propyl front three (second) oxysilane and ethylenediamine propyl
One or more of base silane.
5. phenylpropyl alcohol expanding fire-proof paint according to claim 1, which is characterized in that the wetting dispersing agent is six inclined phosphorus
Sour sodium wetting agent;The levelling agent selects water-borne acrylate copolymer, fluorine richness polyacrylate copolymer or polyether-modified
Polysiloxane polymer is one such.
6. phenylpropyl alcohol expanding fire-proof paint according to claim 1, which is characterized in that the coalescing agent is propylene glycol phenyl
At least one in ether, dipropylene glycol n-butyl ether, Lauryl Alcohol ester, methoxybutanol, ethylene glycol monobutyl ether and dipropylene glycol propyl ether
Kind.