CN110387186A - A kind of antifouling anti-flaming dope and its construction method - Google Patents
A kind of antifouling anti-flaming dope and its construction method Download PDFInfo
- Publication number
- CN110387186A CN110387186A CN201910649614.5A CN201910649614A CN110387186A CN 110387186 A CN110387186 A CN 110387186A CN 201910649614 A CN201910649614 A CN 201910649614A CN 110387186 A CN110387186 A CN 110387186A
- Authority
- CN
- China
- Prior art keywords
- component
- flaming dope
- antifouling anti
- agent
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of antifouling anti-flaming dopes, it include the component of following parts by weight including component A and component B, the component A: 40~45 parts of fluorine silicon modified polyurethane resin, 0.1~1 part of antistatic agent, 0.1~5 part of fire retardant, 0.1~2 part of levelling agent, 0.1~2 part of wetting dispersing agent and 0.1~1 part of defoaming agent;The component B includes 40~50 parts of polyisocyanate prepolymers;The mass ratio of the component A and the component B are 1:4~10;Contain hydroxyl in the fluorine silicon modified polyurethane resin.The synergistic effect that the antifouling anti-flaming dope passes through the fluorine silicon modified polyurethane resin containing hydroxyl, polyisocyanate prepolymers and several functions auxiliary agent, while making coating that there are antifouling self-cleaning effects, the effect of fire-retardant fireproof can be reached again, the smoke amount of the antifouling anti-flaming dope is small, to environment and human body all without toxic action.The invention also discloses the construction methods of the antifouling anti-flaming dope.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of antifouling anti-flaming dope and its construction method.
Background technique
It is exactly coated on body surface and is formed by the fiery expanded by heating formation thermal insulation layer of coating chance by fireproof flame-retardant coating
Achieve the purpose that fire protection flame retarding.Fireproof flame-retardant coating be used for flammable substrates surface, can reduce by the combustibility of painting material surface,
Block the rapid sprawling of fire;For non-combustible substrate surface, to improve by a kind of extraordinary painting of painting material fire endurance
Material.Fireproof flame-retardant coating be coated in substrate surface, in addition to fire retardation, also have antirust, waterproof, anti-corrosion, it is wear-resisting and
Heat resistance, coating have toughness, coloring, adhesion, easy stemness and certain gloss.
The fire-retardant principle of fireproof flame-retardant coating is as follows: 1. fireproof flame-retardant coating itself has fire retardant or noninflammability, makes to be protected
The substrate of shield not direct contacted with air and postpone substrate ignition;2. fireproof flame-retardant coating is met, fire is heated to decomposite noninflammability
Inert gas, water down the oxygen in the inflammable gas and air decomposited by protection base material heated, inhibit burning;3. fire prevention resistance
Burning coating material heat can generate the free radical for slowing down and terminating combustion chain reaction;4. fireproof flame-retardant coating heat expand, formed every
The oxygen-impermeable expansion carbon-coating of heat, prevents substrate ignition.Fire retardant is the pass that fireproof flame-retardant coating can play the role of fire protection flame retarding
Key component.Fire retardant can absorb a large amount of heat when heated, release free radical and non-flammable gases that capture burning generates, or
Form the very low expansion carburization zone of heat-insulated oxygen barrier and thermal conductivity.Common fire retardant has following several: (1) halogenated flame retardant, such as
Chlorinated paraffin, decabromodiphenyl oxide, tetrabromobisphenol A etc.;(2) phosphorus flame retardant, such as phosphate, phosphite ester, phosphorus-containing polyol;
(3) halogen-phosphorus flame retardant, such as phosphoric acid trichloroacetaldehyde ester and other halogenated organophosphorus esters;(4) inorganic fire retardants, such as hydrogen-oxygen
Change magnesium, aluminium hydroxide, zinc borate, aluminium borate, antimony oxide, zirconium oxide, barium metaborate, zinc oxide, calcium carbonate, inorganic silicic acid
Salt etc.;(5) expansion type flame retardant, it is a fire protection flame retarding system, this system is by dehydrating agent (acid source), carbon forming agent (carbon
Source), foaming agent (heated decomposite non-flammable gases) composition.As fire protection flame retarding safety standard and environmental regulation are more and more tighter
Lattice have the shortcomings that smoke amount is big, halogenated flame retardant of toxicity is gradually replaced halogen-free flame retardants.Due to organic silicon fibre retardant
It is assigning except the excellent flame retardant property of substrate, moreover it is possible to improve other performances (such as processing performance, mechanical performance, heat-resisting of substrate
Performance etc.), ecology is friendly, and the recycling effect of fire proofing is preferable, is able to satisfy strict demand of the people to fire retardant, close several
Year organic silicon fibre retardant and its flame-retarded technology have obtained faster development.Organic silicon flame-retardant technology mainly there are several types of: (1) add
Add silicone powders;(2) macromolecule silicone oil is used in combination with metallic compound;(3) silicon rubber and organo-metallic compound, White Carbon black be simultaneously
With;(4) polysiloxane grafted or siloxanes containing active function groups and monomer copolymerizable, introduce silicon atom in the molecule.It is siliceous fire-retardant
After polymer introduces halogen or P, flame retardant effect is even more ideal, the reason is that halogen, P and Si have flame retardant synergistic effect.Under high temperature,
Halogen or P facilitate the production of charcoal, and Si increases the stability of layer of charcoal;Also, when replacing silane with siloxanes, the resistance of two element of P/Si
Combustion synergistic effect further strengthens.But there are the following problems for current fireproof flame-retardant coating: (1) fireproof flame-retardant coating does not have generally
Standby antifouling self-cleaning effect is not able to satisfy urban construction, required antifouling automatically cleaning and fire-retardant need in city management
It asks;Traditional fireproof flame-retardant coating generally added by flame retardant amount it is very big, and meet that fiery smoke amount is big, generates gas toxicity
Greatly, all harmful to environment and human body.
Therefore, it develops a kind of with antifouling automatically cleaning and more environmentally friendly anti-flaming dope has great importance.
Summary of the invention
It is an object of the invention to overcome above-mentioned technical deficiency, propose that a kind of antifouling anti-flaming dope, the anti-flaming dope have
Antifouling self-cleaning function, and to the injury very little of environment and human body, it is more environmentally-friendly;The purpose of another aspect of the present invention is,
It is proposed a kind of construction method of antifouling anti-flaming dope.
To reach above-mentioned technical purpose, technical solution of the present invention provides a kind of antifouling anti-flaming dope, including component A and group
Divide B, the component A includes the component of following parts by weight: 40~45 parts of fluorine silicon modified polyurethane resin, antistatic agent 0.1~1
Part, 0.1~5 part of fire retardant, 0.1~2 part of levelling agent, 0.1~2 part of wetting dispersing agent and 0.1~1 part of defoaming agent;The component B
Including 40~50 parts of polyisocyanate prepolymers;The mass ratio of the component A and the component B are 1:4~10;The fluorine silicon changes
Contain hydroxyl in property polyurethane resin.
The present invention also provides a kind of construction methods of antifouling anti-flaming dope, include the following steps:
S1, the surface of substrate is cleaned, removes the residual old paint film of substrate surface, iron rust, greasy dirt, oxide skin and miscellaneous
Object, it is ensured that substrate surface is rustless, without greasy dirt, without dust and without washmarking;
S2, each component is weighed respectively by the composition of component A and component B, after component A and component B are mixed respectively, then by group
Divide A and component B to mix according to the ratio that mass ratio is 1:4~10, obtains antifouling anti-flaming dope, antifouling anti-flaming dope is uniformly applied
It is overlying on substrate, until after dry solidification.
Compared with prior art, the beneficial effect comprise that
1, antifouling anti-flaming dope provided by the invention uses the fluorine silicon modified polyurethane resin for containing hydroxyl as main body tree
Rouge, fluorine silicon modified polyurethane resin and polyisocyanate prepolymers crosslinking curing containing hydroxyl, generating, there is extremely strong hydrophobic to hate
The self-cleaning coating of oiliness, soil resistant;Pass through the antistatic agent of addition special ratios, fire retardant and other functional aids again
Synergistic effect, while making coating that there are antifouling self-cleaning effects, and the effect of fire-retardant fireproof can be reached, the antifouling anti-flaming dope
Smoke amount it is small, to environment and human body all without toxic action;
2, antifouling anti-flaming dope provided by the invention is applied widely, all kinds of conventional bases suitable for urban operating mechanism
Material, such as concrete, cement, marble, metal, timber, wood fibre board, glass, acrylic, plastics, synthetic material;
3, construction method provided by the invention is easy to operate, requires construction equipment and execution conditions lower, suitable scene
Construction, and antifouling anti-flaming dope of the invention is easily constructed, and surface drying is fast, substantially increases construction efficiency, coating do solid work rear acid resistance,
Alkali resistance, solvent resistance, moisture-proof cold cycling are excellent, and the 3000h of resistance to artificial weathering aging performance is without significant changes, resistant protection
Performance is still fine.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that embodiment described herein is only used to explain the present invention, it is not used to limit
The present invention.
The embodiment provides a kind of antifouling anti-flaming dopes, including component A and component B, and wherein component A includes such as
The component of lower parts by weight: 40~45 parts of fluorine silicon modified polyurethane resin, 0.1~1 part of antistatic agent, 0.1~5 part of fire retardant, stream
0.1~2 part of flat agent, 0.1~2 part of wetting dispersing agent and 0.1~1 part of defoaming agent;Component B include polyisocyanate prepolymers 40~
50 parts;The mass ratio of component A and component B are 1:4~10;Contain hydroxyl in fluorine silicon modified polyurethane resin.
Fluorine silicon modified polyurethane resin is the resin that fluorine silicon resin is modified polyurethane;Of the invention some
In preferred embodiment, fluorinated silicone modified polyester resin is gathered by the branched chain type of hydroxyl fluorine silicon resin and hydroxyl active group
The fluorine silicon modified polyurethane resin containing hydroxyl that urethane resin is joined together to form by being dehydrated dealcoholysis, this is fluorinated silicone modified poly-
The hydroxyl value of urethane resin is 150~250mg KOH/g.To hydroxyl fluorinated silicone modified resin and hydroxyl activity in the present invention
The specific type of the branch type polyurethane resin of group is not particularly limited, and those skilled in the art can be according to practical feelings
Condition selects both resins, and adjusts relevant preparation method according to the raw material of selection, as long as can guarantee final fluorine silicon obtained
Contain hydroxyl in modified polyurethane resin.
In some preferred embodiments of the invention, antistatic agent is the fluorinated silicone modified hydrophobic antistatic agent of special type;Resistance
Firing agent is DCRM47105 silica white and/or DCRM47081 silica white;Both fire retardants are by generating cracking layer of charcoal and raising
The inoxidizability of layer of charcoal realizes flame retardant efficiency, by optimizing the type of fire retardant, to be further reduced smoke amount, reduces to environment
With the injury of human body;Levelling agent is esters of acrylic acid levelling agent;Wetting dispersing agent is esters of acrylic acid wetting dispersing agent;Defoaming agent
For organic silicon defoaming agent;The present invention does not limit the specific type of levelling agent, wetting dispersing agent and defoaming agent particularly, this
The technical staff in field can select corresponding auxiliary agent commonly used in the art, such as: isothiazolinone can select 4,5- bis-
Chloro- 2- n-octyl -3- isothiazolinone;Benzimidazole can select benzimidazole methyl carbamate;Iodine propargyl class can
To select iodo- 2 propargyl butyl carbamate of 3-;Esters of acrylic acid levelling agent can select polyethyl acrylate and polypropylene
Acid butyl ester etc.;Organic silicon defoaming agent can select dimethyl silicone polymer etc., as long as can guarantee that corresponding auxiliary agent plays accordingly
Effect.
In some preferred embodiments of the invention, polyisocyanate prepolymers be HDI trimer, MDI tripolymer,
One of IPDI tripolymer and TDI tripolymer.
In some preferred embodiments of the invention, also contain solvent, and component A and component B in component A and component B
Middle solubilizer polishing respectively is to 100 parts;The solvent is ethyl acetate, in butyl acetate, toluene, dimethylbenzene, butyl glycol ether
One or more of mixing.
It is highly preferred that it is 1:1 mixing that solvent, which is ethyl acetate and dimethylbenzene according to mass ratio,.
In some preferred embodiments of the invention, component A includes the group of following parts by weight in the antifouling anti-flaming dope
Point: 45 parts of fluorine silicon modified polyurethane resin, 0.5 part of antistatic agent, 2 parts of fire retardant, 1 part of levelling agent, 1 part of wetting dispersing agent and disappear
1 part of infusion, solubilizer is mended to 100 parts;Component B includes 50 parts of polyisocyanate prepolymers, and solubilizer is mended to 100 parts;Component A and
The mass ratio of component B is 1:4.
The embodiments of the present invention also provide a kind of construction methods of antifouling anti-flaming dope, include the following steps:
(1) surface of substrate is cleaned, removes the residual old paint film of substrate surface, iron rust, greasy dirt, oxide skin and miscellaneous
Object, it is ensured that substrate surface is rustless, without greasy dirt, without dust and without washmarking;
(2) each component is weighed respectively by the composition of component A and component B, after component A and component B are mixed respectively, then by group
Divide A and component B to mix according to the ratio that mass ratio is 1:4~10, obtains antifouling anti-flaming dope, antifouling anti-flaming dope is uniformly applied
It is overlying on substrate, until after dry solidification.
Wherein, component A is prepared with the following method: by fluorine silicon modified polyurethane resin, antistatic agent, fire retardant, levelling
Agent, wetting dispersing agent, defoaming agent and solvent mixing, and be dispersed with stirring uniformly to get to component A.
Component B is prepared with the following method: polyisocyanate prepolymers and solvent are mixed, be dispersed with stirring uniformly to get
To component B.
In some preferred embodiments of the invention, the thickness of dry film of antifouling anti-flaming dope is 2~5mm, spray viscosity
For 60~80s;Spray pressure is 2~4bar, and spray distance is 15~20cm, sprayable 3~4 rifle.
In some preferred embodiments of the invention, which is 10~35 DEG C, and air is relatively wet
Degree≤75%.
In order to which the present invention will be described in further detail, the present invention is carried out below in conjunction with specific embodiment further
Explanation.Experimental method used in embodiment in the present invention is conventional method unless otherwise specified;Reality in the present invention
Apply material used in example, reagent etc., unless otherwise specified, be it is commercially available, wherein DCRM47105 silica white and
DCRM47081 silica white derives from Dow corning company.
Embodiment 1:
The embodiment of the present invention 1 provides a kind of antifouling anti-flaming dope, including component A and component B, and wherein component A includes
The component of following parts by weight: 45 parts of the fluorine silicon modified polyurethane resin of hydroxyl, the fluorinated silicone modified hydrophobic antistatic agent 0.5 of special type
Part, 1 part of DCRM47105 silica white, 1 part of DCRM47081 silica white, 1 part of acrylate leveling agent, acrylate wetting dispersing agent
1 part and 1 part of organic silicon defoamer, 49.5 parts of solvent (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);Component B includes
50 parts of HDI trimer, 50 parts of solvent (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);The quality of component A and component B
Than for 1:4.
The present embodiment 1 additionally provides a kind of construction method of antifouling anti-flaming dope, includes the following steps:
(1) surface of substrate is cleaned, removes the residual old paint film of substrate surface, iron rust, greasy dirt, oxide skin and miscellaneous
Object, it is ensured that substrate surface is rustless, without greasy dirt, without dust and without washmarking;
(2) temperature be 10~35 DEG C, relative air humidity less than 75% under conditions of construct, the fluorine silicon of hydroxyl is changed
Property polyurethane resin, the hydrophobic antistatic agent of fluorinated silicone modified special type, DCRM47105 silica white, DCRM47081 silica white, propylene
Acid esters levelling agent, acrylate wetting dispersing agent, organic silicon defoamer and solvent mixing, and be dispersed with stirring uniformly, obtain component
A;HDI trimer and solvent are mixed, is dispersed with stirring uniformly, obtains component B;By component A and component B according to mass ratio be 1:4
It is uniformly mixed, after curing 15min, obtains antifouling anti-flaming dope, it is antifouling fire-retardant by antifouling anti-flaming dope even application on substrate
The thickness of dry film of coating is 3.5mm, until after antifouling anti-flaming dope dry solidification.
After the completion of antifouling anti-flaming dope construction in the present embodiment, surface drying time of the paint film at 25 DEG C is about 30min, table
There are super-hydrophobic automatic cleaning and flame retarding and smoke suppressing properties after dry 1h, rear paint film is fully cured for 24 hours, and 72h coating performance reaches best.It applies
The performance of antifouling anti-flaming dope in this example is tested after work 72h, test result is shown in Table 1.
Embodiment 2:
The embodiment of the present invention 2 provides a kind of antifouling anti-flaming dope, including component A and component B, and wherein component A includes
The component of following parts by weight: 43 parts of the fluorine silicon modified polyurethane resin of hydroxyl, the fluorinated silicone modified hydrophobic antistatic agent 0.6 of special type
Part, 3 parts of DCRM47105 silica white, 1 part of acrylate leveling agent, 1 part of acrylate wetting dispersing agent and organic silicon defoamer
0.5 part, 50.9 parts of solvent (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);Component B includes 45 parts of MDI tripolymer, molten
55 parts of agent (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);The mass ratio of component A and component B are 1:7.
The construction method of the antifouling anti-flaming dope of the present embodiment 2 is identical as the construction method in embodiment 1, and difference is:
The thickness of dry film of antifouling anti-flaming dope is 2.5mm, and component A and component B is mixed for 1:7 according to mass ratio when preparing antifouling anti-flaming dope
It closes.
The performance of antifouling anti-flaming dope in the present embodiment is tested after construction 72h, test result is shown in Table 1.
Embodiment 3:
The embodiment of the present invention 3 provides a kind of antifouling anti-flaming dope, including component A and component B, and wherein component A includes
The component of following parts by weight: 45 parts of the fluorine silicon modified polyurethane resin of hydroxyl, the fluorinated silicone modified hydrophobic antistatic agent 1 of special type
Part, 5 parts of DCRM47081 silica white, 2 parts of acrylate leveling agent, 2 parts of acrylate wetting dispersing agent and organic silicon defoamer 1
Part, 44 parts of solvent (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);Component B includes 50 parts of IPDI tripolymer, solvent 50
Part (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);The mass ratio of component A and component B are 1:10.
The construction method of the antifouling anti-flaming dope of the present embodiment 3 is identical as the construction method in embodiment 1, and difference is:
The thickness of dry film of antifouling anti-flaming dope is 5mm, and component A and component B is mixed for 1:10 according to mass ratio when preparing antifouling anti-flaming dope
It closes.
The performance of antifouling anti-flaming dope in the present embodiment is tested after construction 72h, test result is shown in Table 1.
Embodiment 4:
The embodiment of the present invention 4 provides a kind of antifouling anti-flaming dope, including component A and component B, and wherein component A includes
The component of following parts by weight: 40 parts of the fluorine silicon modified polyurethane resin of hydroxyl, the fluorinated silicone modified hydrophobic antistatic agent 0.1 of special type
Part, 0.1 part of DCRM47105 silica white, 0.1 part of acrylate leveling agent, 0.1 part of acrylate wetting dispersing agent and organosilicon disappear
0.1 part of infusion, 59.5 parts of solvent (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);Component B includes TDI tripolymer 40
Part, 60 parts of solvent (solvent is that ethyl acetate and dimethylbenzene are mixed according to 1:1);The mass ratio of component A and component B are 1:5.
The construction method of the antifouling anti-flaming dope of the present embodiment 4 is identical as the construction method in embodiment 1, and difference is:
The thickness of dry film of antifouling anti-flaming dope is 2mm, and component A and component B is mixed for 1:5 according to mass ratio when preparing antifouling anti-flaming dope
It closes.
The performance of antifouling anti-flaming dope in the present embodiment is tested after construction 72h, test result is shown in Table 1.
Comparative example 1:
This example provides a kind of antifouling anti-flaming dope, in the composition and construction method and embodiment 1 of the antifouling anti-flaming dope
It is identical, difference is, in this example the mass ratio of component A and component B be 1:3.The performance of antifouling anti-flaming dope in this example is tested,
The contact angle that the antifouling anti-flaming dope is found after test is 85 °, does not have antifouling self-cleaning effect.
Comparative example 2:
This example provides a kind of antifouling anti-flaming dope, in the composition and construction method and embodiment 1 of the antifouling anti-flaming dope
It is identical, difference is, the mass ratio of component A and component B is 1:12.
The performance for testing antifouling anti-flaming dope in this example, finds that the antifouling anti-flaming dope is more sticky, can not be successfully after test
Construction.
The performance test results of the antifouling anti-flaming dope of 1 Examples 1 to 4 of table
The above described specific embodiments of the present invention are not intended to limit the scope of the present invention..Any basis
Any other various changes and modifications that technical concept of the invention is made should be included in the guarantor of the claims in the present invention
It protects in range.
Claims (9)
1. a kind of antifouling anti-flaming dope, which is characterized in that including component A and component B, the component A include following parts by weight
Component: 40~45 parts of fluorine silicon modified polyurethane resin, 0.1~1 part of antistatic agent, 0.1~5 part of fire retardant, levelling agent 0.1~2
Part, 0.1~2 part of wetting dispersing agent and 0.1~1 part of defoaming agent;The component B includes 40~50 parts of polyisocyanate prepolymers;
The mass ratio of the component A and the component B are 1:4~10;Contain hydroxyl in the fluorine silicon modified polyurethane resin.
2. antifouling anti-flaming dope according to claim 1, which is characterized in that the fluorine silicon modified polyurethane resin is by band
What the branch type polyurethane resin of the fluorine silicon resin of hydroxyl and hydroxyl active group was joined together to form by being dehydrated dealcoholysis
Fluorine silicon modified polyurethane resin containing hydroxyl, the hydroxyl value of the fluorine silicon modified polyurethane resin are 150~250mg KOH/g.
3. antifouling anti-flaming dope according to claim 1, which is characterized in that the antistatic agent is fluorinated silicone modified special type
Hydrophobic antistatic agent;The fire retardant is DCRM47105 silica white and/or DCRM47081 silica white;The levelling agent is propylene
Esters of gallic acid levelling agent;The wetting dispersing agent is esters of acrylic acid wetting dispersing agent;The defoaming agent is organic silicon defoaming agent.
4. antifouling anti-flaming dope according to claim 1, which is characterized in that the polyisocyanate prepolymers are HDI tri-
One of aggressiveness, MDI tripolymer, IPDI tripolymer and TDI tripolymer.
5. antifouling anti-flaming dope according to claim 1, which is characterized in that also containing molten in the component A and component B
Agent, and solubilizer polishing is distinguished in component A and component B to 100 parts;The solvent is ethyl acetate, butyl acetate, toluene, two
The mixing of one or more of toluene, butyl glycol ether.
6. antifouling anti-flaming dope according to claim 1, which is characterized in that component A includes in the antifouling anti-flaming dope
The component of following parts by weight: 45 parts of fluorine silicon modified polyurethane resin, 0.5 part of antistatic agent, 2 parts of fire retardant, 1 part of levelling agent, profit
1 part and 1 part of defoaming agent of hygroscopic water powder, solubilizer is mended to 100 parts;The component B includes 50 parts of polyisocyanate prepolymers, solubilization
Agent is mended to 100 parts;The mass ratio of the component A and the component B are 1:4.
7. a kind of construction method of antifouling anti-flaming dope as described in any one of claims 1 to 6, which is characterized in that including such as
Lower step:
S1, the surface of substrate is cleaned, removes residual old paint film, iron rust, greasy dirt, oxide skin and the sundries of substrate surface, really
Protect substrate surface it is rustless, without greasy dirt, without dust and without washmarking;
S2, each component is weighed respectively by the composition of component A and component B, after component A and component B are mixed respectively, then by component A
It is mixed with component B according to the ratio that mass ratio is 1:4~10, obtains antifouling anti-flaming dope, antifouling anti-flaming dope is uniformly coated
In on substrate, until after dry solidification.
8. the construction method of antifouling anti-flaming dope according to claim 7, which is characterized in that the antifouling anti-flaming dope
Thickness of dry film is 2~5mm, and spray viscosity is 60~80s.
9. the construction method of antifouling anti-flaming dope according to claim 7, which is characterized in that construction temperature is 10~35
DEG C, relative air humidity≤75%.