CN109385112A - A kind of wear-resistant plastic formula - Google Patents
A kind of wear-resistant plastic formula Download PDFInfo
- Publication number
- CN109385112A CN109385112A CN201811416616.1A CN201811416616A CN109385112A CN 109385112 A CN109385112 A CN 109385112A CN 201811416616 A CN201811416616 A CN 201811416616A CN 109385112 A CN109385112 A CN 109385112A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- resistant plastic
- plasticizer
- benzotriazole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of wear-resistant plastic formula, the raw material including following parts by weight: 35-39 parts of thermoplastic resin masterbatch, 24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, 15-19 parts of triethylamine, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, 17-21 parts of benzotriazole, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water.On the basis of original thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and polyvinyl chloride resin, diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide and aluminium oxide are increased newly, the service life of plastics is improved, so that the wear-resisting property of plastics is greatly improved.
Description
Technical field
The present invention relates to the technical field of plastic production more particularly to a kind of wear-resistant plastic formulas.
Background technique
The Plastics Industry of China has formed the more industry body of class by long-term struggle and the opening towards the whole world
System becomes the basic material industry run neck and neck with steel, cement, timber.As a kind of new material, using field
Remote super above-mentioned three kinds of basic materials, Chinese Plastics Industry make remarkable achievements, and realize historic leap, but
It is that existing plastic wear-resisting is poor, therefore proposes a kind of wear-resistant plastic formula.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of wear-resistant plastic formulas.
A kind of wear-resistant plastic formula proposed by the present invention, the raw material including following parts by weight: thermoplastic resin masterbatch 35-39
Part, 24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, triethylamine
15-19 parts, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, benzotriazole
17-21 parts, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water.
Preferably, the raw material including following parts by weight: 36-38 parts of thermoplastic resin masterbatch, 25-27 parts of polyamide, poly- third
12-14 parts of alkene, 3-5 parts of plasticizer, 5-7 parts of polyvinyl chloride resin, 9-11 parts of diamond dust, 16-18 parts of triethylamine, tungsten disulfide 13-15
Part, 17-19 parts of white fused alumina micro mist, 9-11 parts of benzene sulfonic acid, 4-6 parts of polyimides, 18-20 parts of benzotriazole, 5-7 parts of titanium dioxide,
10-12 parts of aluminium oxide and suitable water.
Preferably, the raw material including following parts by weight: the raw material including following parts by weight: 37 parts of thermoplastic resin masterbatch,
26 parts of polyamide, 13 parts of polypropylene, 4 parts of plasticizer, 6 parts of polyvinyl chloride resin, 10 parts of diamond dust, 17 parts of triethylamine, tungsten disulfide 14
Part, 18 parts of white fused alumina micro mist, 10 parts of benzene sulfonic acid, 5 parts of polyimides, 19 parts of benzotriazole, 6 parts of titanium dioxide, 11 parts of aluminium oxide and
Suitable water.
Preferably, the plasticizer is made of polyvinyl chloride, dipentaerythritol, polyethylene glycol and polyvinyl alcohol of acetalization.
Preferably, preparation method includes the following steps:
S1: by diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide, oxygen
Change aluminium and suitable water is poured into mixing and blending machine and stirred evenly;
S2: thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and PVC tree are poured into mixing and blending machine described in S1
Rouge continues to stir;
After the completion of being stirred in S3:S2, gains are put into heater box and are heated;
S4: pouring into gains in mold after the completion of heating, is put into molding machine and carries out extrusion forming;
S5: being cooled to room temperature after extrusion forming, finally obtains the plastics with wear-resisting property.
Preferably, in the S1, the temperature setting of mixing and blending machine is 70-75 DEG C, and mixing time is set as 25-35min,
Mixing speed is set as 200-250r/min.
Preferably, in the S2, mixing time is set as 25-35min, and mixing speed is set as 200-250r/min.
Preferably, in the S3, heating temperature is set as 100-120 DEG C, keeps the temperature 15-20min.
Beneficial effects of the present invention: in original thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and polyvinyl chloride resin
On the basis of, increase diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium white newly
Powder and aluminium oxide improve the service life of plastics, so that the wear-resisting property of plastics is greatly improved.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Embodiment one
A kind of wear-resistant plastic formula is proposed in the present embodiment, the raw material including following parts by weight: thermoplastic resin masterbatch 35-39
Part, 24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, triethylamine
15-19 parts, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, benzotriazole
17-21 parts, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water;
Preparation method includes the following steps:
S1: by diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide, oxygen
Change aluminium and suitable water is poured into mixing and blending machine and stirred evenly;
S2: thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and PVC tree are poured into mixing and blending machine described in S1
Rouge continues to stir;
After the completion of being stirred in S3:S2, gains are put into heater box and are heated;
S4: pouring into gains in mold after the completion of heating, is put into molding machine and carries out extrusion forming;
S5: being cooled to room temperature after extrusion forming, finally obtains the plastics with wear-resisting property.
Embodiment two
A kind of wear-resistant plastic formula is proposed in the present embodiment, the raw material including following parts by weight: thermoplastic resin masterbatch 35-39
Part, 24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, triethylamine
15-19 parts, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, benzotriazole
17-21 parts, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water;
Preparation method includes the following steps:
S1: by diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide, oxygen
Change aluminium and suitable water is poured into mixing and blending machine and stirred evenly;
S2: thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and PVC tree are poured into mixing and blending machine described in S1
Rouge continues to stir;
After the completion of being stirred in S3:S2, gains are put into heater box and are heated;
S4: pouring into gains in mold after the completion of heating, is put into molding machine and carries out extrusion forming;
S5: being cooled to room temperature after extrusion forming, finally obtains the plastics with wear-resisting property.
Embodiment three
A kind of wear-resistant plastic formula is proposed in the present embodiment, the raw material including following parts by weight: thermoplastic resin masterbatch 35-39
Part, 24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, triethylamine
15-19 parts, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, benzotriazole
17-21 parts, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water;
Preparation method includes the following steps:
S1: by diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide, oxygen
Change aluminium and suitable water is poured into mixing and blending machine and stirred evenly;
S2: thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and PVC tree are poured into mixing and blending machine described in S1
Rouge continues to stir;
After the completion of being stirred in S3:S2, gains are put into heater box and are heated;
S4: pouring into gains in mold after the completion of heating, is put into molding machine and carries out extrusion forming;
S5: being cooled to room temperature after extrusion forming, finally obtains the plastics with wear-resisting property.
Example IV
A kind of wear-resistant plastic formula is proposed in the present embodiment, the raw material including following parts by weight: thermoplastic resin masterbatch 35-39
Part, 24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, triethylamine
15-19 parts, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, benzotriazole
17-21 parts, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water;
Preparation method includes the following steps:
S1: by diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide, oxygen
Change aluminium and suitable water is poured into mixing and blending machine and stirred evenly;
S2: thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and PVC tree are poured into mixing and blending machine described in S1
Rouge continues to stir;
After the completion of being stirred in S3:S2, gains are put into heater box and are heated;
S4: pouring into gains in mold after the completion of heating, is put into molding machine and carries out extrusion forming;
S5: being cooled to room temperature after extrusion forming, finally obtains the plastics with wear-resisting property.
Embodiment five
A kind of wear-resistant plastic formula is proposed in the present embodiment, the raw material including following parts by weight: thermoplastic resin masterbatch 35-39
Part, 24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, triethylamine
15-19 parts, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, benzotriazole
17-21 parts, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water;
Preparation method includes the following steps:
S1: by diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide, oxygen
Change aluminium and suitable water is poured into mixing and blending machine and stirred evenly;
S2: thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and PVC tree are poured into mixing and blending machine described in S1
Rouge continues to stir;
After the completion of being stirred in S3:S2, gains are put into heater box and are heated;
S4: pouring into gains in mold after the completion of heating, is put into molding machine and carries out extrusion forming;
S5: being cooled to room temperature after extrusion forming, finally obtains the plastics with wear-resisting property.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of wear-resistant plastic formula, which is characterized in that the raw material including following parts by weight: 35-39 parts of thermoplastic resin masterbatch,
24-28 parts of polyamide, 11-15 parts of polypropylene, 2-6 parts of plasticizer, 4-8 parts of polyvinyl chloride resin, 8-12 parts of diamond dust, triethylamine 15-19
Part, 12-16 parts of tungsten disulfide, 16-20 parts of white fused alumina micro mist, 8-12 parts of benzene sulfonic acid, 3-7 parts of polyimides, benzotriazole 17-21
Part, 4-8 parts of titanium dioxide, 9-13 parts of aluminium oxide and suitable water.
2. a kind of wear-resistant plastic formula according to claim 1, which is characterized in that the raw material including following parts by weight: heat
36-38 parts of plastic resin masterbatch, 25-27 parts of polyamide, 12-14 parts of polypropylene, 3-5 parts of plasticizer, 5-7 parts of polyvinyl chloride resin, Buddha's warrior attendant
9-11 parts of sand, 16-18 parts of triethylamine, 13-15 parts of tungsten disulfide, 17-19 parts of white fused alumina micro mist, 9-11 parts of benzene sulfonic acid, polyamides are sub-
4-6 parts of amine, 18-20 parts of benzotriazole, 5-7 parts of titanium dioxide, 10-12 parts of aluminium oxide and suitable water.
3. a kind of wear-resistant plastic formula according to claim 1, which is characterized in that the raw material including following parts by weight: heat
37 parts of plastic resin masterbatch, 26 parts of polyamide, 13 parts of polypropylene, 4 parts of plasticizer, 6 parts of polyvinyl chloride resin, 10 parts of diamond dust, triethylamine
17 parts, 14 parts of tungsten disulfide, 18 parts of white fused alumina micro mist, 10 parts of benzene sulfonic acid, 5 parts of polyimides, 19 parts of benzotriazole, titanium dioxide 6
Part, 11 parts of aluminium oxide and suitable water.
4. a kind of wear-resistant plastic formula according to claim 1, which is characterized in that the plasticizer is by polyvinyl chloride, two
Pentaerythrite, polyethylene glycol and polyvinyl alcohol of acetalization composition.
5. a kind of wear-resistant plastic formula according to claim 1, which is characterized in that preparation method includes the following steps:
S1: by diamond dust, triethylamine, tungsten disulfide, white fused alumina micro mist, benzene sulfonic acid, polyimides, benzotriazole, titanium dioxide, oxygen
Change aluminium and suitable water is poured into mixing and blending machine and stirred evenly;
S2: thermoplastic resin masterbatch, polyamide, polypropylene, plasticizer and PVC tree are poured into mixing and blending machine described in S1
Rouge continues to stir;
After the completion of being stirred in S3:S2, gains are put into heater box and are heated;
S4: pouring into gains in mold after the completion of heating, is put into molding machine and carries out extrusion forming;
S5: being cooled to room temperature after extrusion forming, finally obtains the plastics with wear-resisting property.
6. a kind of wear-resistant plastic formula according to claim 5, which is characterized in that in the S1, the temperature of mixing and blending machine
Degree is set as 70-75 DEG C, and mixing time is set as 25-35min, and mixing speed is set as 200-250r/min.
7. a kind of wear-resistant plastic formula according to claim 5, which is characterized in that in the S2, mixing time is set as
25-35min, mixing speed are set as 200-250r/min.
8. a kind of wear-resistant plastic formula according to claim 5, which is characterized in that in the S3, heating temperature is set as
100-120 DEG C, keep the temperature 15-20min.