CN109384450A - Small cup and its method for cooking are built in magnetization - Google Patents
Small cup and its method for cooking are built in magnetization Download PDFInfo
- Publication number
- CN109384450A CN109384450A CN201811498548.8A CN201811498548A CN109384450A CN 109384450 A CN109384450 A CN 109384450A CN 201811498548 A CN201811498548 A CN 201811498548A CN 109384450 A CN109384450 A CN 109384450A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- magnetization
- raw material
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to porcelain technical fields, concretely relate to magnetization and build small cup and its method for cooking.It includes green body, glaze, reduction rod that it, which is formed,；The green body includes following raw material in parts by weight: 8 parts of kaolin, 5 parts of laterite, 2 parts of loess；The glaze includes following raw material in parts by weight: 13 ~ 15 parts of lime stone, 13 ~ 15 parts of plant ash, 5 ~ 7 parts of lithium carbonate, 5 ~ 7 parts of bauxite, 5 ~ 7 parts of dolomite, 20 ~ 30 parts of red glaze stone, 10 ~ 12 parts of magnetization material；The reduction rod includes: 3 ~ 5 parts of chitosan, 1 part of stearic acid, 15 parts of charcoal powder, 10 parts of turpentine oil, 5 parts of tea-seed oil in parts by weight.The present invention builds that a natural color development, glaze colours jade-like stone profit, glossiness be good, high yield rate, and magnetic efficiency is good.
Description
Technical field
The invention belongs to porcelain technical fields, concretely relate to magnetization and build small cup and its method for cooking.
Background technique
China has had the history of more than one thousand years using porcelain, and porcelain tool is a part that can not be lacked in common people's daily life,
In all age people's function possesses an exquisite porcelain tool and feels pleasing, in high spirits.With China's cultural life and
The continuous improvement of material life, requirement of the people to health and health care is higher and higher, and people are to drinking water, have tea in daily life
How the huge variation that equal living habits have occurred, solve tea quality of the people when drinking water, having tea, and is that people improve life
Bioplasm amount, enjoy life quality, pursues the serious hope demand of the way to keep in good health.But it is sold in current China market according to investigations each
Class porcelain tool, although kind is huge more without specific healthcare function, it is to adopt that reporting, which has most of the teapot of magnetizing function,
With setting magnetizing assembly, this can breaking teapot aesthetic feeling.
Building small cup is the Typical Representative in black glazed ware device, and China begins to fire black glazed ware very early, can trace back to earliest
The Eastern Han Dynasty reaches prosperous when building two Song of small cup.It builds small cup and originates in the Nanping City in Fujian province Jianyang town Qu Shuiji, it is simple and unsophisticated with its moulding to build small cup, glaze
Color is changeable, bright and colourful, and wonderful and deep by black porcelain shows incisively and vividly, occupy in Chinese porcelain a seat it
Ground.
Therefore, lack currently on the market it is a kind of can magnetized tea, the porcelain with health-preserving function, if small cup set will be built
Magnetizing function can satisfy modern to the needs, the overall aesthetic with holding porcelain, raising people of quality of life high request
The general level of the health.
Summary of the invention
The purpose of the present invention is to provide a kind of health magnetization to build small cup and its method for cooking.Its color development is natural, glaze colours jade-like stone moistens,
Glossiness is good, high yield rate, and magnetic efficiency is good.
To achieve the above object, the present invention adopts the following technical scheme:
Small cup is built in the magnetization, and composition includes green body, glaze, reduction rod.
The green body includes following raw material in parts by weight: 8 parts of kaolin, 5 parts of laterite, 2 parts of loess.
The glaze includes following raw material in parts by weight: 13 ~ 15 parts of lime stone, 13 ~ 15 parts of plant ash, lithium carbonate 5 ~
7 parts, 5 ~ 7 parts of bauxite, 5 ~ 7 parts of dolomite, 20 ~ 30 parts of red glaze stone, 10 ~ 12 parts of magnetization material.
The raw material of the magnetization material includes: 10 ~ 15 parts of iron ore powder, 5 parts of bombax cotton, alginic acid the third two in parts by weight
5 parts of alcohol ester, 20 parts of isopropanol.
It is described to magnetize expecting the preparation method comprises the following steps: mixing and stirring iron ore powder, bombax cotton, propylene glycol alginate, isopropanol
1 ~ 2h is mixed, it is spare.
The reduction rod includes: 3 ~ 5 parts of chitosan, 1 part of stearic acid, 15 parts of charcoal powder, turpentine oil 10 in parts by weight
Part, 5 parts of tea-seed oil.
The reduction rod mixes the preparation method comprises the following steps: each raw material will be formulated, and mixture into strips, is cut using shaping mechanism
It is disconnected, obtain strip stick.
It is described to magnetize the method for cooking for building small cup,
(1) by kaolin, laterite, loess mix, be added blank raw material total weight 20-30% water, ball milling for 24 hours, aging 48h, mistake
250 meshes, dehydration obtain base slurry；
(2) water is added to mix each raw material in glaze formula, wet-milling obtains the glaze slip that mass concentration is 50 ~ 60%；Glaze slip reaches rule
It is taken out from ball mill after fixed fineness；Cross 250 meshes, aging 48h；
(3) base prepared in step (1) is starched in injection mold, takes out, dries after blank forming, modified, in green body
One layer of glaze slip made in advance is coated in outer surface, dries, time 2-3 hour；It takes out spare；
(4) green body obtained in step (3) immerses in step (1) to 10 ~ 15min takes out in glaze slip obtained again, is again dipped into
5min takes out, and glaze slip is made uniformly to be attached to billet surface；
(5) it is sent into stove to fire, firing program is: opening fire door after igniting, is gradually warmed up, makes furnace temperature from room temperature in 8 hours
700 DEG C are risen to, realizes hydrofuge process；Fire door is closed, furnace temperature is made to be gradually heated to 1250 ~ 1300 DEG C, it is primary every 15min investment
Reduction rod, investment reduction rod dosage are that every cubic metre of kiln launches 500g, the firing time 3 hours；Furnace temperature is controlled after the completion of firing
900 DEG C are cooled to, fire door, the cooling kiln discharge of Temperature fall are opened.
Remarkable advantage of the invention is:
(1) present invention is adsorbed Armco magnetic iron ore by bombax cotton, is added in glaze by adding magnetization material in glaze,
Iron ore can be prevented because of the problem of magnetic attraction causes other ore sinterings to be unevenly distributed, so that iron ore dispersion is more equal
After even, magnetic efficiency is more significant, and the crystal boundary that introduces after high temperature sintering of the addition of bombax cotton and stomata facilitate
Influence of the phase reducing atmosphere to glaze, facilitates the formation of glaze color.
(2) present invention uses homemade reduction rod, and the addition of chitosan stablizes its property, flammable strong, is not likely to produce
The fluctuation of reducing atmosphere ensure that the stability for building a final product quality.
(3) the of the invention iron ore for building small cup by being added in glaze Jing Guo modification, can make water after being filled with water
It is more preferable that qualitative change obtains mouthfeel, kills various bacteria and virus in water and realizes health-care effect, can meet in water containing mineral composition
People's lives require and standard, and Sheng can make vinosity more preferable after drinking, and mouthfeel is more preferable, and porcelain tool can make having for tea after containing tea
Beneficial ingredient is not lost, and mouthfeel is more preferable.
Specific embodiment
Further to disclose rather than the present invention is limited, the present invention is described in further detail below in conjunction with example.
Embodiment 1
Small cup is built in the magnetization, and composition includes green body, glaze, reduction rod.
The green body includes following raw material in parts by weight: 8 parts of kaolin, 5 parts of laterite, 2 parts of loess.
The glaze includes following raw material in parts by weight: 13 parts of lime stone, 13 parts of plant ash, 5 parts of lithium carbonate, aluminium alum
5 parts of soil, 5 parts of dolomite, 20 parts of red glaze stone, 10 parts of magnetization material.
The raw material of the magnetization material includes: 10 parts of iron ore powder, 5 parts of bombax cotton, alginate propylene glycol in parts by weight
5 parts of ester, 20 parts of isopropanol.
It is described to magnetize expecting the preparation method comprises the following steps: mixing and stirring iron ore powder, bombax cotton, propylene glycol alginate, isopropanol
1h is mixed, it is spare.
The reduction rod include: in parts by weight 3 parts of chitosan, 1 part of stearic acid, 15 parts of charcoal powder, 10 parts of turpentine oil,
5 parts of tea-seed oil.
The reduction rod mixes the preparation method comprises the following steps: each raw material will be formulated, and mixture into strips, is cut using shaping mechanism
It is disconnected, obtain strip stick.
It is described to magnetize the method for cooking for building small cup,
(1) kaolin, laterite, loess are mixed, the water of blank raw material total weight 20% is added, for 24 hours, aging 48h crosses 250 to ball milling
Mesh, dehydration obtain base slurry；
(2) water is added to mix each raw material in glaze formula, wet-milling obtains the glaze slip that mass concentration is 50%；Glaze slip reaches regulation
Fineness after taken out from ball mill；Cross 250 meshes, aging 48h；
(3) base prepared in step (1) is starched in injection mold, takes out, dries after blank forming, modified, in green body
One layer of glaze slip made in advance is coated in outer surface, dries, time 2 h；It takes out spare；
(4) green body obtained in step (3) immerses in step (1) to 10min takes out in glaze slip obtained again, is again dipped into 5min
It takes out, glaze slip is made uniformly to be attached to billet surface；
(5) it is sent into stove to fire, firing program is: opening fire door after igniting, is gradually warmed up, makes furnace temperature from room temperature in 8 hours
700 DEG C are risen to, realizes hydrofuge process；Fire door is closed, furnace temperature is made to be gradually heated to 1250 DEG C, puts into primary reduction every 15min
Stick, investment reduction rod dosage are that every cubic metre of kiln launches 500g, the firing time 3 hours；Control furnace temperature cooling after the completion of firing
To 900 DEG C, fire door, the cooling kiln discharge of Temperature fall are opened.
Embodiment 2
Small cup is built in the magnetization, and composition includes green body, glaze, reduction rod.
The green body includes following raw material in parts by weight: 8 parts of kaolin, 5 parts of laterite, 2 parts of loess.
The glaze includes following raw material in parts by weight: 14 parts of lime stone, 15 parts of plant ash, 6 parts of lithium carbonate, aluminium alum
6 parts of soil, 6 parts of dolomite, 25 parts of red glaze stone, 11 parts of magnetization material.
The raw material of the magnetization material includes: 10 parts of iron ore powder, 5 parts of bombax cotton, alginate propylene glycol in parts by weight
5 parts of ester, 20 parts of isopropanol.
It is described to magnetize expecting the preparation method comprises the following steps: mixing and stirring iron ore powder, bombax cotton, propylene glycol alginate, isopropanol
1h is mixed, it is spare.
The reduction rod include: in parts by weight 3 parts of chitosan, 1 part of stearic acid, 15 parts of charcoal powder, 10 parts of turpentine oil,
5 parts of tea-seed oil.
The reduction rod mixes the preparation method comprises the following steps: each raw material will be formulated, and mixture into strips, is cut using shaping mechanism
It is disconnected, obtain strip stick.
It is described to magnetize the method for cooking for building small cup,
(1) kaolin, laterite, loess are mixed, the water of blank raw material total weight 30% is added, for 24 hours, aging 48h crosses 250 to ball milling
Mesh, dehydration obtain base slurry；
(2) water is added to mix each raw material in glaze formula, wet-milling obtains the glaze slip that mass concentration is 50 ~ 60%；Glaze slip reaches rule
It is taken out from ball mill after fixed fineness；Cross 250 meshes, aging 48h；
(3) base prepared in step (1) is starched in injection mold, takes out, dries after blank forming, modified, in green body
One layer of glaze slip made in advance is coated in outer surface, dries, and the time 3 hours；It takes out spare；
(4) green body obtained in step (3) immerses in step (1) to 15min takes out in glaze slip obtained again, is again dipped into 5min
It takes out, glaze slip is made uniformly to be attached to billet surface；
(5) it is sent into stove to fire, firing program is: opening fire door after igniting, is gradually warmed up, makes furnace temperature from room temperature in 8 hours
700 DEG C are risen to, realizes hydrofuge process；Fire door is closed, furnace temperature is made to be gradually heated to 1280 DEG C, puts into primary reduction every 15min
Stick, investment reduction rod dosage are that every cubic metre of kiln launches 500g, the firing time 3 hours；Control furnace temperature cooling after the completion of firing
To 900 DEG C, fire door, the cooling kiln discharge of Temperature fall are opened.
Embodiment 3
Small cup is built in the magnetization, and composition includes green body, glaze, reduction rod.
The green body includes following raw material in parts by weight: 8 parts of kaolin, 5 parts of laterite, 2 parts of loess.
The glaze includes following raw material in parts by weight: 15 parts of lime stone, 15 parts of plant ash, 7 parts of lithium carbonate, aluminium alum
7 parts of soil, 7 parts of dolomite, 30 parts of red glaze stone, 12 parts of magnetization material.
The raw material of the magnetization material includes: 15 parts of iron ore powder, 5 parts of bombax cotton, alginate propylene glycol in parts by weight
5 parts of ester, 20 parts of isopropanol.
It is described to magnetize expecting the preparation method comprises the following steps: mixing and stirring iron ore powder, bombax cotton, propylene glycol alginate, isopropanol
1 ~ 2h is mixed, it is spare.
The reduction rod include: in parts by weight 5 parts of chitosan, 1 part of stearic acid, 15 parts of charcoal powder, 10 parts of turpentine oil,
5 parts of tea-seed oil.
The reduction rod mixes the preparation method comprises the following steps: each raw material will be formulated, and mixture into strips, is cut using shaping mechanism
It is disconnected, obtain strip stick.
It is described to magnetize the method for cooking for building small cup,
(1) kaolin, laterite, loess are mixed, the water of blank raw material total weight 30% is added, for 24 hours, aging 48h crosses 250 to ball milling
Mesh, dehydration obtain base slurry；
(2) water is added to mix each raw material in glaze formula, wet-milling obtains the glaze slip that mass concentration is 60%；Glaze slip reaches regulation
Fineness after taken out from ball mill；Cross 250 meshes, aging 48h；
(3) base prepared in step (1) is starched in injection mold, takes out, dries after blank forming, modified, in green body
One layer of glaze slip made in advance is coated in outer surface, dries, and the time 3 hours；It takes out spare；
(4) green body obtained in step (3) immerses in step (1) to 15min takes out in glaze slip obtained again, is again dipped into 5min
It takes out, glaze slip is made uniformly to be attached to billet surface；
(5) it is sent into stove to fire, firing program is: opening fire door after igniting, is gradually warmed up, makes furnace temperature from room temperature in 8 hours
700 DEG C are risen to, realizes hydrofuge process；Fire door is closed, furnace temperature is made to be gradually heated to 1300 DEG C, puts into primary reduction every 15min
Stick, investment reduction rod dosage are that every cubic metre of kiln launches 500g, the firing time 3 hours；Control furnace temperature cooling after the completion of firing
To 900 DEG C, fire door, the cooling kiln discharge of Temperature fall are opened.
Comparative example 1
Magnetization material is directlyed adopt into iron ore, is not added other；Other components and method for cooking are same as Example 1.
Comparative example 2
Reduction rod is directly replaced with by weight, 15 parts of charcoal powder, 10 parts of turpentine oil, 5 parts of tea-seed oil；Other components and
Method for cooking is identical with embodiment 1.
Product testing:
Embodiment 1 builds a glaze light, in bright gay color, builds small cup using the embodiment of the present invention 1 and purifies water (48h), water-quality constituents
Testing result, it is exceeded (≤0.005mg/L) to be not detected cadmium, and lead doping (≤0.01mg/L) is not detected, formaldehyde, pH is not detected
7.20, water hardness 150mg/L.
Comparative example 1 builds a glaze light, and color is dim compared with embodiment 1, builds small cup using comparative example 1 and purifies water (48h), water
Matter composition detection is not detected lead doping (≤0.01mg/L), formaldehyde is not detected as a result, to be not detected cadmium exceeded (≤0.005mg/L),
PH 7.56, water hardness 250mg/L.
Comparative example 2 builds that a glaze is unstable, and color is uneven, builds small cup using comparative example 1 and purifies water (48h), water quality at
Sorting is surveyed as a result, to be not detected cadmium exceeded (≤0.005mg/L), and lead doping (≤0.01mg/L) is not detected, formaldehyde, pH is not detected
7.33, water hardness 200mg/L.
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification, is all covered by the present invention.
Claims (5)
1. small cup is built in magnetization, it is characterised in that: it includes green body, glaze, reduction rod that it, which is formed,；The green body includes in parts by weight
Following raw material: 8 parts of kaolin, 5 parts of laterite, 2 parts of loess；The glaze includes following raw material in parts by weight: lime stone 13 ~
15 parts, 13 ~ 15 parts of plant ash, 5 ~ 7 parts of lithium carbonate, 5 ~ 7 parts of bauxite, 5 ~ 7 parts of dolomite, 20 ~ 30 parts of red glaze stone, magnetization material 10
~ 12 parts；The reduction rod include: in parts by weight 3 ~ 5 parts of chitosan, 1 part of stearic acid, 15 parts of charcoal powder, 10 parts of turpentine oil,
5 parts of tea-seed oil.
2. small cup is built in magnetization according to claim 1, it is characterised in that: the raw material of the magnetization material wraps in parts by weight
It includes: 10 ~ 15 parts of iron ore powder, 5 parts of bombax cotton, 5 parts of propylene glycol alginate, 20 parts of isopropanol.
3. small cup is built in magnetization according to claim 2, it is characterised in that: it is described magnetization material the preparation method comprises the following steps: by iron ore
1 ~ 2h is mixed in powder, bombax cotton, propylene glycol alginate, isopropanol, spare.
4. small cup is built in magnetization according to claim 1, it is characterised in that: the reduction rod the preparation method comprises the following steps: will formula it is each
A raw material mixing, into strips using shaping mechanism, cutting obtains strip stick to mixture.
5. the method for cooking that small cup is built in a kind of magnetization as described in claim 1, it is characterised in that: the following steps are included:
(1) by kaolin, laterite, loess mix, be added blank raw material total weight 20-30% water, ball milling for 24 hours, aging 48h, mistake
250 meshes, dehydration obtain base slurry；
(2) water is added to mix each raw material in glaze formula, wet-milling obtains the glaze slip that mass concentration is 50 ~ 60%；Glaze slip reaches rule
It is taken out from ball mill after fixed fineness；Cross 250 meshes, aging 48h；
(3) base prepared in step (1) is starched in injection mold, takes out, dries after blank forming, modified, in green body
One layer of glaze slip made in advance is coated in outer surface, dries, time 2-3 hour；It takes out spare；
(4) green body obtained in step (3) immerses in step (1) to 10 ~ 15min takes out in glaze slip obtained again, is again dipped into
5min takes out, and glaze slip is made uniformly to be attached to billet surface；
(5) it is sent into stove to fire, firing program is: opening fire door after igniting, is gradually warmed up, makes furnace temperature from room temperature in 8 hours
700 DEG C are risen to, realizes hydrofuge process；Fire door is closed, furnace temperature is made to be gradually heated to 1250 ~ 1300 DEG C, it is primary every 15min investment
Reduction rod, investment reduction rod dosage are that every cubic metre of kiln launches 500g, the firing time 3 hours；Furnace temperature is controlled after the completion of firing
900 DEG C are cooled to, fire door, the cooling kiln discharge of Temperature fall are opened.