CN109382283A - A kind of Ceramo-steel calcium plate and coating construction process - Google Patents
A kind of Ceramo-steel calcium plate and coating construction process Download PDFInfo
- Publication number
- CN109382283A CN109382283A CN201811028300.5A CN201811028300A CN109382283A CN 109382283 A CN109382283 A CN 109382283A CN 201811028300 A CN201811028300 A CN 201811028300A CN 109382283 A CN109382283 A CN 109382283A
- Authority
- CN
- China
- Prior art keywords
- plate
- ceramo
- steel
- steel calcium
- panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Ceramo-steel calcium plate and coating construction process, including panel, middle layer, bottom plate, composite layer；Its coating construction process, comprising the following steps: shear, fluting, bending, welding, bottom surface sheet metal forming select galvanized steel plain sheet to pass through bending, slot, bottom surface sheet metal forming after welding processing；By galvanized steel plain sheet and the bottom plate, the clear water after degreasing degreasing rinses surface well, is dried after surface washing is clean, dries up water stain substrate surface and moisture, any particle and external contaminant in substrate surface and gap of removal with air cannon after drying；Steel calcium plate base paint special is sprayed to the panel, after the completion of basecoat paint, is tested, the dedicated finishing coat of steel calcium plate is sprayed to the panel after qualified.Beneficial effect is: the Ceramo-steel calcium plate has high rigidity, self-cleaning anti-pollution, heatproof, fire-retardant, weather-proof, environmentally friendly characteristic.
Description
Technical field
The present invention relates to Ceramo-steel calcium plate technique fields, more particularly to a kind of Ceramo-steel calcium plate and coating construction process.
Background technique
In recent years, with the Large scale construction in the development of large public building, especially subway city throughout the country, with
Preceding common construction material is not able to satisfy the requirement of these public buildings increasingly, and the adhesion strength of these public buildings is prevented
Fiery performance and self-cleaning antifouling property have requirements at the higher level, so promoting the adhesion strength of construction material, fire protecting performance and self-cleaning anti-
Dirty performance has become the development trend of present construction material, and steel calcium plate is to apply and give birth in this trend, and steel calcium is compound
Plate, aluminium calcium composite plate are using environment-friendly materials fiber reinforced calcium silicate board (fiber reinforced cement board) as substrate, and in substrate
On one side or intrinsic stainless steel installation component is clamped on four sides, then passes through height with 0.4-0.6MM zinc/aluminum-plated steel plate, 0.4-0.6MM aluminium sheet
The advanced process combining such as temperature, high pressure forms, and applies roasting upper multilayer weather resistance, color in zinc/aluminum-plated steel plate or surface of aluminum plate
The new material of extremely stable F-C paint or inorganic coating, but this material is primarily present following problem: hardness is not high,
The disadvantages of fire protecting performance is poor, and self-cleaning antifouling property is bad.
Summary of the invention
The object of the invention is that providing a kind of Ceramo-steel calcium plate and coating construction process to solve the above-mentioned problems.
The present invention through the following technical solutions to achieve the above objectives:
A kind of Ceramo-steel calcium plate, the Ceramo-steel calcium plate include panel, middle layer, bottom plate, composite layer；
Its coating construction process, comprising the following steps:
S1, shear, fluting, bending, welding, bottom surface sheet metal forming select galvanized steel plain sheet to pass through bending, slot, bottom after welding processing
Panel forming；
After work in S2, completion step S1, by galvanized steel plain sheet and the bottom plate, the clear water after degreasing degreasing rinses table well
Face is dried after surface washing is clean, it is dry after with air cannon drying substrate surface is water stain and moisture, removal are any in substrate
Particle and external contaminant in surface and gap；
S3, after completing work in step S2, steel calcium plate base paint special is sprayed to the panel, after the completion of basecoat paint, is carried out
It examines, the dedicated finishing coat of steel calcium plate is sprayed to the panel after qualified；
After spray coating operations in S4, completion step S3, to the bottom plate sprayed fire proofing coating, fire resistant coating carries out after spraying
Examine, it is qualified after in the bottom plate and be bonded complex fiber cement plate respectively on the panel, be to complete the pottery after qualified
The coating decoration of porcelain steel calcium plate.
Preferably, the substrate of the panel be galvanized steel plain sheet, galvanized steel plain sheet with a thickness of 0.5 millimeter, the panel accounts for institute
The mass percent for stating Ceramo-steel calcium plate is 16.15%.
Preferably, the middle layer is high-density fiber cement plate, the middle layer with a thickness of 10 millimeters, the centre
The mass percent that layer accounts for the Ceramo-steel calcium plate is 67%.
Preferably, the substrate of the bottom plate be galvanized steel plain sheet, galvanized steel plain sheet with a thickness of 0.5 millimeter, the bottom plate accounts for institute
The mass percent for stating Ceramo-steel calcium plate is 16.15%.
Preferably, the composite layer with a thickness of 1 millimeter, the composite layer accounts for the quality hundred of the Ceramo-steel calcium plate
Divide than being 0.5%.
Preferably, in the step S3 to the panel spray steel calcium plate base paint special, before spraying with 200 mesh~
250 mesh filter screens or high-quality filter cloth are filtered steel calcium plate base paint special, and selecting bore is 2.5 millimeters~3.5 millis
The spray gun of rice, 2.5 kilograms~5.0 kilograms of air pressure carry out spraying steel calcium plate base paint special after adjusting atomizing effect.
Preferably, the dedicated finishing coat of steel calcium plate is sprayed to the panel in the step S3, is filtered with 300 mesh~350 mesh
Net or high-quality filter cloth are filtered the dedicated finishing coat of steel calcium plate, select bore be 1.5 millimeters~2.0 millimeters spray gun,
2.5 kilograms~5.0 kilograms of air pressure, the spraying dedicated finishing coat of steel calcium plate is carried out after adjusting atomizing effect, sprays any coating
It is preceding all to carry out the protection of periphery workpiece, prevent extraneous contamination.
Preferably, compound to the bottom plate and the panel be bonded complex fiber cement plate respectively in the step S4
It should be noted that the bonding force between the coating uniformity of compound adhesive and fibre cement plate and the bottom plate and the panel when bonding
Whether securely, gap between composite glue and fibre cement plate and the bottom plate and the panel, generate bubble it is more few more
It is good.
A kind of coating construction process of Ceramo-steel calcium plate proposed by the present invention is carrying out base paint special and the spraying of dedicated finishing coat
It requires to carry out it stringent filtering before, be sprayed with the spray gun of go-no-go, certain air pressure, ensure that spraying
Quality and effect, a kind of Ceramo-steel calcium plate proposed by the present invention has high rigidity, self-cleaning anti-pollution, heatproof, fire-retardant, weather-proof, ring
The characteristic of guarantor.
Specific embodiment
A kind of Ceramo-steel calcium plate proposed by the present invention, including panel, middle layer, bottom plate, composite layer, wherein panel
Substrate is galvanized steel plain sheet, galvanized steel plain sheet with a thickness of 0.5 millimeter, the mass percent that panel accounts for Ceramo-steel calcium plate is 16.15%,
Middle layer be high-density fiber cement plate, middle layer with a thickness of 10 millimeters, middle layer accounts for the mass percent of Ceramo-steel calcium plate
Be 67%, the substrate of bottom plate is galvanized steel plain sheet, galvanized steel plain sheet with a thickness of 0.5 millimeter, bottom plate accounts for the quality percentage of Ceramo-steel calcium plate
Than being 16.15%, composite layer with a thickness of 1 millimeter, the mass percent that composite layer accounts for Ceramo-steel calcium plate is 0.5%.
Its coating construction process, comprising the following steps:
S1, shear, fluting, bending, welding, bottom surface sheet metal forming select galvanized steel plain sheet to pass through bending, slot, bottom after welding processing
Panel forming；
After work in S2, completion step S1, by galvanized steel plain sheet and bottom plate, clear water rinses surface, table well after degreasing degreasing
Face is dried after rinsing well, it is dry after with air cannon drying substrate surface is water stain and moisture, removal are any in substrate surface
And particle and external contaminant in gap；
After work in S3, completion step S2, steel calcium plate base paint special is sprayed to panel, with 200 mesh~250 mesh mistakes before spraying
Strainer or high-quality filter cloth are filtered steel calcium plate base paint special, and selecting bore is 2.5 millimeters~3.5 millimeters of spray
2.5 kilograms~5.0 kilograms of rifle, air pressure carry out spraying steel calcium plate base paint special after adjusting atomizing effect, and basecoat paint is complete
Cheng Hou tests, and the dedicated finishing coat of steel calcium plate is sprayed to panel after qualified, with 300 mesh~350 mesh before spraying dedicated finishing coat
Filter screen or high-quality filter cloth are filtered the dedicated finishing coat of steel calcium plate, and selecting bore is 1.5 millimeters~2.0 millimeters of spray
2.5 kilograms~5.0 kilograms of rifle, air pressure carry out the spraying dedicated finishing coat of steel calcium plate after adjusting atomizing effect, spray any painting
Workpiece protection in periphery should be all carried out before layer, prevent extraneous contamination.
After spray coating operations in S4, completion step S3, to bottom plate sprayed fire proofing coating, fire resistant coating carries out after spraying
It examines, should be noted that the painting of compound adhesive after qualified in bottom plate and be bonded complex fiber cement plate respectively on panel, compound sticking
Whether the bonding force between the cloth uniformity and fibre cement plate and bottom plate and panel is secured, composite glue and fibre cement plate
And gap between bottom plate and panel, generate that the fewer bubble the better, the coating decoration of Ceramo-steel calcium plate is completed after qualified.
A kind of coating construction process of Ceramo-steel calcium plate proposed by the present invention is carrying out base paint special and the spraying of dedicated finishing coat
It requires to carry out it stringent filtering before, be sprayed with the spray gun of go-no-go, certain air pressure, ensure that spraying
Quality and effect, a kind of Ceramo-steel calcium plate proposed by the present invention has high rigidity, self-cleaning anti-pollution, heatproof, fire-retardant, weather-proof, ring
The characteristic of guarantor.
The basic principles, main features and advantages of the invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, and the above embodiments and description only describe originals of the invention
Reason, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes and improvements
It all fall within the protetion scope of the claimed invention.
Claims (8)
1. a kind of Ceramo-steel calcium plate, it is characterised in that: the Ceramo-steel calcium plate includes panel, middle layer, bottom plate, composite layer；
Its coating construction process, comprising the following steps:
S1, shear, fluting, bending, welding, bottom surface sheet metal forming select galvanized steel plain sheet to pass through bending, slot, bottom after welding processing
Panel forming；
After work in S2, completion step S1, by galvanized steel plain sheet and the bottom plate, the clear water after degreasing degreasing rinses table well
Face is dried after surface washing is clean, it is dry after with air cannon drying substrate surface is water stain and moisture, removal are any in substrate
Particle and external contaminant in surface and gap；
S3, after completing work in step S2, steel calcium plate base paint special is sprayed to the panel, after the completion of basecoat paint, is carried out
It examines, the dedicated finishing coat of steel calcium plate is sprayed to the panel after qualified；
After spray coating operations in S4, completion step S3, to the bottom plate sprayed fire proofing coating, fire resistant coating carries out after spraying
Examine, it is qualified after in the bottom plate and be bonded complex fiber cement plate respectively on the panel, be to complete the pottery after qualified
The coating decoration of porcelain steel calcium plate.
2. a kind of Ceramo-steel calcium plate according to claim 1, it is characterised in that: the substrate of the panel is galvanized steel plain sheet,
Galvanized steel plain sheet with a thickness of 0.5 millimeter, the mass percent that the panel accounts for the Ceramo-steel calcium plate is 16.15%.
3. a kind of Ceramo-steel calcium plate according to claim 1, it is characterised in that: the middle layer is high-density fiber cement
Plate, the middle layer with a thickness of 10 millimeters, the mass percent that the middle layer accounts for the Ceramo-steel calcium plate is 67%.
4. a kind of Ceramo-steel calcium plate according to claim 1, it is characterised in that: the substrate of the bottom plate is galvanized steel plain sheet,
Galvanized steel plain sheet with a thickness of 0.5 millimeter, the mass percent that the bottom plate accounts for the Ceramo-steel calcium plate is 16.15%.
5. a kind of Ceramo-steel calcium plate according to claim 1, it is characterised in that: the composite layer with a thickness of 1 millimeter,
The mass percent that the composite layer accounts for the Ceramo-steel calcium plate is 0.5%.
6. a kind of coating construction process of Ceramo-steel calcium plate according to claim 1, it is characterised in that: in the step S3
To the panel spray steel calcium plate base paint special, with 200 mesh~250 mesh filter screens or high-quality filter cloth pair before spraying
Steel calcium plate base paint special is filtered, and selects the spray gun that bore is 2.5 millimeters~3.5 millimeters, air pressure 2.5 kilograms~5.0
Kilogram, spraying steel calcium plate base paint special is carried out after adjusting atomizing effect.
7. a kind of coating construction process of Ceramo-steel calcium plate according to claim 1, it is characterised in that: in the step S3
To the panel spray the dedicated finishing coat of steel calcium plate, it is special to steel calcium plate with 300 mesh~350 mesh filter screens or high-quality filter cloth
It is filtered with finishing coat, selects the spray gun that bore is 1.5 millimeters~2.0 millimeters, 2.5 kilograms~5.0 kilograms of air pressure, adjustment
The spraying dedicated finishing coat of steel calcium plate is carried out after good atomizing effect, should all be carried out the protection of periphery workpiece before spraying any coating, be prevented outer
To pollute.
8. a kind of coating construction process of Ceramo-steel calcium plate according to claim 1, it is characterised in that: in the step S4
To the bottom plate and the panel be bonded complex fiber cement plate respectively, when compound sticking, should be noted that the coating of compound adhesive is uniform
Whether degree and the bonding force between fibre cement plate and the bottom plate and the panel are secured, and composite glue and fibre cement are flat
The fewer gap, generation bubble between plate and the bottom plate and the panel the better.