CN109371747A - A kind of disposable degradable paper disc and preparation method thereof - Google Patents
A kind of disposable degradable paper disc and preparation method thereof Download PDFInfo
- Publication number
- CN109371747A CN109371747A CN201811130803.3A CN201811130803A CN109371747A CN 109371747 A CN109371747 A CN 109371747A CN 201811130803 A CN201811130803 A CN 201811130803A CN 109371747 A CN109371747 A CN 109371747A
- Authority
- CN
- China
- Prior art keywords
- parts
- disk body
- paper disc
- combined
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to disposable paper disc processing technique fields, specifically disclose a kind of disposable degradable paper disc, it includes disk body and the film layer coated in disk body inner surface, and the disk body includes following raw material: 25-35 parts of bamboo fibre, 18-25 parts of hemp stalk fiber, 20-30 parts of sugarcane fiber, 35-55 parts of cornstarch, condensation polysaccharide 15-25 parts, 5-10 parts of sodium alginate, 5-10 parts of chitosan, 170-190 parts of pure water；The film layer be by be coated on disk body inner surface be combined into film liquid it is dry after the film that is formed.Waterproof of the present invention, oil resistivity are good, and have excellent degradability.
Description
Technical field
The present invention relates to disposable paper disc processing technique field more particularly to a kind of disposable degradable paper disc and its preparations
Method.
Background technique
With the development of modern science and technology, rhythm of life is getting faster, and people require life simple and efficient, disposable to produce
Product enter people's lives, and paper disc has the advantages that convenient, healthy, and very big convenience is brought to our daily life.At present
A large amount of disposable plate is made of plastics, and the situation of China's up to the present white pollution has seriously threatened people
Daily life.Disposable plate made of previous used plastic material herein, can not adapt to current social development,
And since it has that degradation is difficult, also being abandoned by market slowly now.Therefore, the good paper of degradability is developed
Disk is just particularly important.
Summary of the invention
Based on background technique there are the problem of, the invention proposes a kind of disposable degradable paper disc and preparation method thereof,
Waterproof of the present invention, oil resistivity are good, and have excellent degradability.
The invention proposes a kind of disposable degradable paper discs, the film layer including disk body and coated in disk body inner surface,
The disk body includes following raw material: 25-35 parts of bamboo fibre, 18-25 parts of hemp stalk fiber, 20-30 parts of sugarcane fiber, corn
35-55 parts of starch, condensation polysaccharide 15-25 parts, 5-10 parts of sodium alginate, 5-10 parts of chitosan, 170-190 parts of pure water；
The film layer be by be coated on disk body inner surface be combined into film liquid it is dry after the film that is formed.
Preferably, it is described be combined into film liquid the preparation method comprises the following steps: cationic starch is uniformly mixed with deionized water, then
Under stirring conditions, it is warming up to 90-95 DEG C, is gelatinized 20-25min, it is standby that the gelatinization of starch solution that concentration is 5-10wt% is made
With；
Polyvinylalcohol solids powder is added in deionized water, is then heated to 92-96 DEG C, stirring to abundant dissolution, system
The poly-vinyl alcohol solution that concentration is 5-7wt% is obtained, it is spare；
Guar gum is added in deionized water, is then heated to 92-96 DEG C, stirring to abundant dissolution, it is 1- that concentration, which is made,
The guar gum solution of 2wt%, it is spare；
Gelatinization of starch solution, poly-vinyl alcohol solution, guar gum solution are added in container, stirred evenly, standing and defoaming,
It obtains being combined into film liquid.
Preferably, gelatinization of starch solution, poly-vinyl alcohol solution, guar gum solution volume ratio be 40-60:20-35:15-
30。
Preferably, being combined into film liquid coating thickness is 0.03-0.05mm.
Preferably, the invention also discloses the preparation method of the paper disc, include the following steps:
S1, bamboo fibre, hemp stalk fiber, sugarcane fiber are mixed, then acetic acid solution immersion treatment, is washed with clear water later
Only, it dries, crushes, obtain composite fibre powder；
S2, condensation polysaccharide, sodium alginate, chitosan are added in pure water and are stirred evenly, then water-bath is kept the temperature, and is obtained
Mix adhesive；
S3, composite fibre powder, mixing adhesive, cornstarch are added in batch mixer and are uniformly mixed, obtain mixture,
Then moulding press is fed the mixture into, it is hot-forming to get disk body；
S4, film liquid will be combined into be uniformly coated on disk body inner surface, then freeze-day with constant temperature, it is cooling after to get disposable
Degradable paper disc.
Preferably, S1 concrete operations are as follows: bamboo fibre, hemp stalk fiber, sugarcane fiber are mixed, are then 10- with concentration
The acetic acid solution immersion treatment 3-4h of 17wt% is cleaned with clear water later, is dried, and is crushed, is obtained composite fibre powder.
Preferably, in S2, bath temperature is 92-97 DEG C, and water-bath soaking time is 15-25min.
Preferably, in S3, hot pressing temperature is 150-165 DEG C, hot pressing time 3-5min.
Preferably, in S4, at 75-85 DEG C, the time is controlled in 1.5-3.5h for temperature control when freeze-day with constant temperature.
After the present invention mixes bamboo fibre, hemp stalk fiber, sugarcane fiber, with acetic acid solution immersion treatment, it is fine that mixing is made
Powder is tieed up, fiber can remove the harmful toxic matter of fiber surface after acetic acid solution immersion treatment, while can also remove part half
The ingredients such as cellulose, siliceous, make the cross-linked structure on its surface by partial destruction, to reduce fiber surface contact angle, change
Kind fiber wetness, allows fiber preferably in conjunction with auxiliary agent, improves processing performance, and then improve the stability of paper disc；And
Bamboo fibre, hemp stalk fiber, sugarcane fiber, which are used cooperatively, has the effect of enhancing paper disc hardness, and discarded rear degradable.The present invention
Condensation polysaccharide, sodium alginate, chitosan are added in pure water by a certain percentage, compounding obtains mixing adhesive, the mixing
Adhesive is more environmentally-friendly, degradable and safe and non-toxic compared to traditional Organic adhesive.Cationic starch is added the present invention
In deionized water, heating gelatinization is configured to certain density gelatinization of starch solution, then by gelatinization of starch solution and polyvinyl alcohol
Solution, guar gum solution compound by a certain percentage, are made and are combined into film liquid, polyvinyl alcohol, guar gum make to make with compounding for starch
The viscosity for being combined into film liquid obtained is significantly improved compared to common starch solution, will be combined into film liquid and is applied in disk body inner surface
Cloth can generate uniformly and the film layer of densification in disk body inner surface after drying, can play barrier action to grease and water, Jin Erji
The earth improves paper disc waterproof oil resistance.Degradability laboratory test results show, disposable degradable paper prepared by the present invention
The weightlessness that the weightlessness that disk soil buries 30 days is more than 18%, soil buries 60 days is more than that the weightlessness buried 120 days of 40%, soil is more than 84%, is shown
It writes and is higher than commercially available common disposable degradable paper disc, it is seen then that degradability of the present invention is excellent.In short, waterproof of the present invention, oil resistivity
It is good, and there is excellent degradability.
Specific embodiment
Technical solution of the present invention is described in detail combined with specific embodiments below.
Embodiment 1
A kind of disposable degradable paper disc, the film layer including disk body and coated in disk body inner surface, the disk body include
Following raw material: 25 parts of bamboo fibre, 25 parts of hemp stalk fiber, 20 parts of sugarcane fiber, 55 parts of cornstarch, condensation polysaccharide 15
Part, 10 parts of sodium alginate, 5 parts of chitosan, 190 parts of pure water；
The film layer be by be coated on disk body inner surface be combined into film liquid it is dry after the film that is formed.
Embodiment 2
A kind of disposable degradable paper disc, the film layer including disk body and coated in disk body inner surface, the disk body include
Following raw material: 35 parts of bamboo fibre, 18 parts of hemp stalk fiber, 30 parts of sugarcane fiber, 35 parts of cornstarch, condensation polysaccharide 25
Part, 5 parts of sodium alginate, 10 parts of chitosan, 170 parts of pure water；
The film layer be by be coated on disk body inner surface be combined into film liquid it is dry after the film that is formed.
Embodiment 3
A kind of disposable degradable paper disc, the film layer including disk body and coated in disk body inner surface, the disk body include
Following raw material: 30 parts of bamboo fibre, 22 parts of hemp stalk fiber, 25 parts of sugarcane fiber, 45 parts of cornstarch, condensation polysaccharide 19
Part, 7 parts of sodium alginate, 8 parts of chitosan, 180 parts of pure water；
The film layer be by be coated on disk body inner surface be combined into film liquid it is dry after the film that is formed；It is combined into film liquid painting
Cloth is with a thickness of 0.03mm.
The preparation for being combined into film liquid: cationic starch is uniformly mixed with deionized water, then in the condition of stirring
Under, 90 DEG C are warming up to, 25min is gelatinized, it is spare that the gelatinization of starch solution that concentration is 5wt% is made；
Polyvinylalcohol solids powder is added in deionized water, is then heated to 92 DEG C, stirring is made dense to abundant dissolution
Degree is the poly-vinyl alcohol solution of 7wt%, spare；
Guar gum is added in deionized water, is then heated to 92 DEG C, stirring to abundant dissolution, it is 2wt% that concentration, which is made,
Guar gum solution, it is spare；
By gelatinization of starch solution, poly-vinyl alcohol solution, guar gum solution, 40:35:15 is added in container by volume, is stirred
It mixes uniformly, standing and defoaming obtains being combined into film liquid.
The preparation method of the paper disc, includes the following steps:
S1, by bamboo fibre, hemp stalk fiber, sugarcane fiber mix, then with concentration be 10wt% acetic acid solution immersion at
4h is managed, is cleaned later with clear water, is dried, crushes, obtains composite fibre powder；
S2, condensation polysaccharide, sodium alginate, chitosan are added in pure water and are stirred evenly, then water-bath is kept the temperature, and is obtained
Mix adhesive；Bath temperature is 92 DEG C, and water-bath soaking time is 25min；
S3, composite fibre powder, mixing adhesive, cornstarch are added in batch mixer and are uniformly mixed, obtain mixture,
Then moulding press is fed the mixture into, it is hot-forming to get disk body；Hot pressing temperature is 150 DEG C, hot pressing time 5min；
S4, it film liquid will be combined into will be uniformly coated on disk body inner surface, then the freeze-day with constant temperature 3.5h at 75 DEG C, it is cooling
Afterwards to get disposable degradable paper disc.
Embodiment 4
A kind of disposable degradable paper disc, the film layer including disk body and coated in disk body inner surface, the disk body include
Following raw material: 35 parts of bamboo fibre, 18 parts of hemp stalk fiber, 30 parts of sugarcane fiber, 35 parts of cornstarch, condensation polysaccharide 25
Part, 5 parts of sodium alginate, 10 parts of chitosan, 170 parts of pure water；
The film layer be by be coated on disk body inner surface be combined into film liquid it is dry after the film that is formed；It is combined into film liquid painting
Cloth is with a thickness of 0.05mm.
The preparation for being combined into film liquid: cationic starch is uniformly mixed with deionized water, then in the condition of stirring
Under, 95 DEG C are warming up to, 20min is gelatinized, it is spare that the gelatinization of starch solution that concentration is 10wt% is made；
Polyvinylalcohol solids powder is added in deionized water, is then heated to 96 DEG C, stirring is made dense to abundant dissolution
Degree is the poly-vinyl alcohol solution of 5wt%, spare；
Guar gum is added in deionized water, is then heated to 96 DEG C, stirring to abundant dissolution, it is 1wt% that concentration, which is made,
Guar gum solution, it is spare；
By gelatinization of starch solution, poly-vinyl alcohol solution, guar gum solution, 60:20:30 is added in container by volume, is stirred
It mixes uniformly, standing and defoaming obtains being combined into film liquid.
The preparation method of the paper disc, includes the following steps:
S1, by bamboo fibre, hemp stalk fiber, sugarcane fiber mix, then with concentration be 17wt% acetic acid solution immersion at
3h is managed, is cleaned later with clear water, is dried, crushes, obtains composite fibre powder；
S2, condensation polysaccharide, sodium alginate, chitosan are added in pure water and are stirred evenly, then water-bath is kept the temperature, and is obtained
Mix adhesive；Bath temperature is 97 DEG C, and water-bath soaking time is 15min；
S3, composite fibre powder, mixing adhesive, cornstarch are added in batch mixer and are uniformly mixed, obtain mixture,
Then moulding press is fed the mixture into, it is hot-forming to get disk body；Hot pressing temperature is 165 DEG C, hot pressing time 3min；
S4, it film liquid will be combined into will be uniformly coated on disk body inner surface, then the freeze-day with constant temperature 1.5h at 85 DEG C, it is cooling
Afterwards to get disposable degradable paper disc.
Degradation property test
According to the standard of GB/T 20197-2006 to the embodiment 1-4 disposable degradable paper disc prepared and commercially available general
Logical disposable degradable paper disc carries out Degrading experiment, and each experimental group correspondence is denoted as experimental group 1-4 and control group, experimental result
It is as shown in the table:
| Soil buries 30 days weightless (%) | Soil buries 60 days weightless (%) | Soil buries 120 days weightless (%) | |
| Control group | 12.6 | 26.7 | 61.9 |
| Experimental group 1 | 18.3 | 40.8 | 84.1 |
| Experimental group 2 | 19.2 | 41.5 | 84.9 |
| Experimental group 3 | 19.8 | 43.2 | 86.3 |
| Experimental group 4 | 19.5 | 41.9 | 85.8 |
As can be seen from the above table, the disposable degradable paper disc soil of 1-4 of embodiment of the present invention preparation buries 30 days weightlessness, soil
The weightlessness and the native weightlessness for burying 120 days for burying 60 days, are all remarkably higher than commercially available common disposable degradable paper disc, it is seen then that this
Invention degradability is excellent.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of disposable degradable paper disc, which is characterized in that the paper disc includes disk body and coated in disk body inner surface
Film layer, the disk body include following raw material: 25-35 parts of bamboo fibre, 18-25 parts of hemp stalk fiber, sugarcane fiber 20-30
Part, 35-55 parts of cornstarch, condensation polysaccharide 15-25 parts, 5-10 parts of sodium alginate, 5-10 parts of chitosan, pure water 170-190
Part；
The film layer be by be coated on disk body inner surface be combined into film liquid it is dry after the film that is formed.
2. paper disc according to claim 1, which is characterized in that it is described be combined into film liquid the preparation method comprises the following steps: by cationic
Starch is uniformly mixed with deionized water, then under stirring conditions, is warming up to 90-95 DEG C, is gelatinized 20-25min, concentration is made
It is spare for the gelatinization of starch solution of 5-10wt%；
Polyvinylalcohol solids powder is added in deionized water, is then heated to 92-96 DEG C, stirring is made dense to abundant dissolution
Degree is the poly-vinyl alcohol solution of 5-7wt%, spare；
Guar gum is added in deionized water, is then heated to 92-96 DEG C, stirring to abundant dissolution, it is 1-2wt% that concentration, which is made,
Guar gum solution, it is spare；
Gelatinization of starch solution, poly-vinyl alcohol solution, guar gum solution are added in container, stirred evenly, standing and defoaming obtains
It is combined into film liquid.
3. paper disc according to claim 2, which is characterized in that gelatinization of starch solution, poly-vinyl alcohol solution, guar gum solution
Volume ratio be 40-60:20-35:15-30.
4. paper disc according to claim 1-3, which is characterized in that being combined into film liquid coating thickness is 0.03-
0.05mm。
5. a kind of preparation method of any one of -4 paper discs according to claim 1, which comprises the steps of:
S1, bamboo fibre, hemp stalk fiber, sugarcane fiber are mixed, then acetic acid solution immersion treatment, is cleaned with clear water later, is dried
It is dry, it crushes, obtains composite fibre powder；
S2, condensation polysaccharide, sodium alginate, chitosan are added in pure water and are stirred evenly, then water-bath is kept the temperature, and is mixed
Adhesive；
S3, composite fibre powder, mixing adhesive, cornstarch are added in batch mixer and are uniformly mixed, obtain mixture, then
Moulding press is fed the mixture into, it is hot-forming to get disk body；
S4, film liquid will be combined into be uniformly coated on disk body inner surface, then freeze-day with constant temperature, it is cooling after to get can disposably drop
Solve paper disc.
6. preparation method according to claim 5, which is characterized in that S1 concrete operations are as follows: by bamboo fibre, hemp stalk fiber,
Sugarcane fiber mixing, the acetic acid solution immersion treatment 3-4h for being then 10-17wt% with concentration are cleaned with clear water later, drying,
It crushes, obtains composite fibre powder.
7. preparation method according to claim 5 or 6, which is characterized in that in S2, bath temperature is 92-97 DEG C, and water-bath is protected
The warm time is 15-25min.
8. according to the described in any item preparation methods of claim 5-7, which is characterized in that in S3, hot pressing temperature 150-165
DEG C, hot pressing time 3-5min.
9. according to the described in any item preparation methods of claim 5-8, which is characterized in that in S4, temperature is controlled when freeze-day with constant temperature
At 75-85 DEG C, the time is controlled in 1.5-3.5h.