CN109371703A - Conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement and preparation method and application - Google Patents
Conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement and preparation method and application Download PDFInfo
- Publication number
- CN109371703A CN109371703A CN201811289591.3A CN201811289591A CN109371703A CN 109371703 A CN109371703 A CN 109371703A CN 201811289591 A CN201811289591 A CN 201811289591A CN 109371703 A CN109371703 A CN 109371703A
- Authority
- CN
- China
- Prior art keywords
- parts
- aqueous
- rubber cement
- indsole
- sheaing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cements and preparation method and application, in parts by weight, including 167 parts of natural emulsions, 25 parts of titanium dioxides, 0.7 part of paregal O, 0.6 part of wetting agent JFC, 1.5 parts of aqueous defoamers, 75 parts of soft water, 5.0 parts of nano ATO dispersion liquids, 2.0 parts of mould inhibitor BCM, 0.9 part of anti-aging agent KY-405L, 4.0 parts of zinc oxide, 0.3 part of potassium hydroxide, 3.0 parts of sodium carboxymethylcelluloses, 1.5 parts of promotors, 3.0 parts of sulphur.The present invention screens the formula and preparation method of conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, optimizes, and makes it under the premise of adhesive strength is good, has excellent conducting function, and low in cost, asepsis environment-protecting can improve the quality of production.Simple production process of the invention, material source is extensive, is suitable for industrialized production.
Description
Technical field
The present invention relates to rubber processing, especially a kind of conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement and its system
Preparation Method and application.
Background technique
Currently, for the electric conductivity for realizing base fabric sheaing rubber cement in shoes use, most of gasoline using filling metal powder
Type rubber cement, adhesive property is good, and adhesive strength is high, but pollutes the disadvantage is that existing to environment, easy to cause fire, is good for operator
Health harm is larger.And since organic solvent is volatile, storage and transport are also not easy, storage life is very short, about on a week left side
The right side is not able to satisfy real production demand.And the rubber cement prepared using water as solvent, production technology are easy, it is not necessary to
It employs powerful device and energy saving, can reach one existing for technique and technical requirement and Gasoline rubber paste
A little disadvantages.However usually using the aqueous rubber cement of latex production since consistency is low, coated in being easy to produce seep through on rubber overshoes base fabric
Phenomenon, influences rubber overshoes presentation quality, and base fabric generates adhesion deformation in blanking process and seriously brings very big be stranded to actual production
It is difficult.And electrostatic charge cannot be exported successfully in vitro because conductive capability is limited, far can not eliminate particular surroundings by such rubber cement
Under due to itself static electricity and bring harm and security risk.
Therefore, it is the market demand for meeting particular surroundings and special population, guarantees rubber overshoes quality, improves cloth and sponge rubber
The bond properties and its electric conductivity of glue, it is ensured that cloth cover seep through and other issues will not be generated, shoes are eliminated with base fabric and scrape slurry process
In Electrostatic Fire, and the electrostatic of human body institute band can be successfully exported, so that invention waterborne conductive sheaing rubber cement is conductive in production
Have urgent reality unexpectedly adopted during rubber overshoes.
Summary of the invention
The technical problems to be solved by the present invention are: provide a kind of conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement and its
Preparation method and application, it has excellent conducting function, and low in cost, asepsis environment-protecting can improve the quality of production, with gram
Take the deficiencies in the prior art.
Of the invention is achieved in that conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, in parts by weight, packet
Include 160~170 parts of natural emulsions, 20~30 parts of titanium dioxides, 0.5~0.9 part of paregal O, 0.5~0.7 part of wetting agent JFC, 1~
2 parts of aqueous defoamers, 70~80 parts of soft water, 4~6 parts of nano ATO dispersion liquids, 1.5~2.5 parts of mould inhibitor BCM, 0.8~1.0 part
Anti-aging agent KY-405L, 3~5 parts of zinc oxide, 0.2~0.4 part of potassium hydroxide, 2~4 parts of sodium carboxymethylcelluloses, 1~2 part of promotion
Agent and 2.5~3.5 parts of sulphur.
Preferred mode is, in parts by weight, including 167 parts of natural emulsions, 25 parts of titanium dioxides, 0.7 part is average
Add O, 0.6 part of wetting agent JFC, 1.5 parts of aqueous defoamers, 75 parts of soft water, 5.0 parts of nano ATO dispersion liquids, 2.0 parts of mould inhibitors
BCM, 0.9 part of anti-aging agent KY-405L, 4.0 parts of zinc oxide, 0.3 part of potassium hydroxide, 3.0 parts of sodium carboxymethylcelluloses, 1.5 parts of rush
Into agent and 3.0 parts of sulphur.
The preparation method of conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, takes each component by above-mentioned weight fraction；1) match
CMC swelling body processed: 65 parts of soft water, sodium carboxymethylcellulose and mould inhibitor BCM mixing are added into blender, is slowly stirred and adds
Enter potassium hydroxide, stir to sodium carboxymethylcellulose the thick shape liquid for no clustering phenomena that is uniformly dispersed, obtains CMC swelling body；
2) vulcanizing agent aqueous dispersions are prepared:
A) canned small ball weight is 8 kilograms, and wherein the small ball weight of diameter 20-40mm is 6.0 kilograms, diameter 10-
The small ball weight of 15mm is 2.0 kilograms, is replenished in time after abrasion；
B) tinning sequence: 5 parts of soft water are added into tank, anti-aging agent KY-405L, zinc oxide, promotor, sulphur, aqueous disappear
Infusion is eventually adding remaining soft water, and various compounding agents are stirred evenly, upper cover sealing → labelling, ball milling；
C) Ball-milling Time adds up whole for 10 hours, and tank cannot be washed with water when tank out, and tinning must use soft water；
D) ball milling liquid shows enchashment use, cannot go out tank and park deposit；
3) rubber cement manufactures: vulcanizing agent aqueous dispersions being added into CMC swelling body, nano ATO dispersion liquid, wetting agent JFC, put down
Flat plus O and titanium dioxide, stirring to powder it is fully dispersed uniformly after, obtain mixing mother liquor；Under agitation, to mixing mother liquor in by
Natural emulsion is gradually added, continues that it is fully dispersed to be stirred to each compounding agent to be uniform viscous body, pulp is got product, with imitative Baume
Densimeter measures rubber cement concentration, and concentration is 13~18 seconds.
A kind of application of conduction rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, it is characterised in that: 48 prepared in rubber cement
In hour, the glue that a layer thickness is 0.2~0.4mm is equably scraped on base fabric in the rubber overshoes sponge that resistance value tends to 0.000K Ω
Pulp layer guarantees that the gap of fabric fibre is filled up completely by rubber cement, takes the middle base fabric for the sheaing rubber cement covering that length and width is 25cm or so
Be put into vulcanizing tank, vulcanize under conditions of 130 DEG C × 40min it is primary, after parking one day, base fabric surface dirt and miscellaneous in cleaning
Object, with resistance apparatus measure in base fabric resistance value.
Nano ATO dispersion liquid --- water fluid conductive material, resistivity 106-108(Ω.cm)
Natural emulsion --- it is bonded with measuring fiber.
Wetting agent JFC --- increase bonding rubber cement to the penetrating power of woven design, to improve bonding intensity.
Paregal O --- increase the stability of rubber cement system, improves the greasy property that sole cloth scrapes slurry, it is ensured that pulp layer is thick
Degree.
Aqueous defoamer --- eliminate the insoluble gas in rubber cement.
Potassium hydroxide --- alkaline medium prevents from going bad.
Mould inhibitor BCM --- prevent mucilage layer and sole cloth from going mouldy.
Hydroxymethyl cellulose --- for the thickening stabilizing agent in rubber cement body, prevent rubber cement to the through performance of woven design.
Titanium dioxide --- woven design filler.
Nano ATO dispersion liquid performance parameter
Interconnection of the evenly dispersed nano ATO conducting particles in insulating body is to reach the effect of electrically conducting transparent
Fruit, and stablize without easy to knot groups.
In order to further verify effect of the invention, following experiment has been carried out:
One, optimum proportion of materials research
Table 1
Table 1 is continuous
Table 1 continuous 2
Table 1 continuous 3
According to 1 test result of table, optimum formula are as follows: 167 parts of natural emulsions, 25 parts of titanium dioxides, 0.7 part of paregal O, 0.6
Part wetting agent JFC, 1.5 parts of aqueous defoamers, 75 parts of soft water, 5.0 parts of nano ATO dispersion liquids, 2.0 parts of mould inhibitor BCM, 0.9 part
Anti-aging agent KY-405L, 4.0 parts of zinc oxide, 0.3 part of potassium hydroxide, 3.0 parts of sodium carboxymethylcelluloses, 1.5 parts of promotors, 3.0 parts
Sulphur.
Two, pulping process is studied
Table 2
It show that optimum manufacturing process is by several comparison of process flow in table 2: first manufacturing CMC swelling body, vulcanizing agent
Aqueous dispersions, then each compounding agent is added thereto and is fabricated to titanium dioxide mixing liquid, it is finally gradually added into natural emulsion again, prepares
Sheaing rubber cement quality be just able to satisfy and scrape base fabric requirement.
By adopting the above-described technical solution, compared with prior art, the present invention is to rubber overshoes sponge indsole fabric aqueous sheaing
The formula and preparation method of rubber cement are screened, are optimized, and make it under the premise of adhesive strength is good, have good conductive function
Can, asepsis environment-protecting can improve the quality of production.Simple production process of the invention, material source is extensive, is suitable for industrial metaplasia
It produces.The invention is simple and feasible, low in cost, and the using effect of product is good.
Specific embodiment
The embodiment of the present invention 1: conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, in parts by weight, including 167
Part natural emulsion, 25 parts of titanium dioxides, 0.7 part of paregal O, 0.6 part of wetting agent JFC, 1.5 parts of aqueous defoamers, 75 parts of soft water,
5.0 parts of nano ATO dispersion liquids, 2.0 parts of mould inhibitor BCM, 0.9 part of anti-aging agent KY-405L, 4.0 parts of zinc oxide, 0.3 part of hydroxide
Potassium, 3.0 parts of sodium carboxymethylcelluloses, 1.5 parts of promotors, 3.0 parts of sulphur.
The preparation method of conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, takes each component by above-mentioned weight fraction；1) match
CMC swelling body processed: 65 parts of soft water, 3 parts of sodium carboxymethylcelluloses and 2.0 parts of mould inhibitor BCM mixing are added into blender, slowly
0.3 part of potassium hydroxide is stirred and be added, the thick shape liquid for no clustering phenomena that is uniformly dispersed is stirred to sodium carboxymethylcellulose, is obtained
CMC swelling body；2) prepare vulcanizing agent aqueous dispersions: a) canned small ball weight is 8 kilograms, wherein the bead weight of diameter 20-40mm
Amount is 6.0 kilograms, and the small ball weight that diameter is 10-15mm is 2.0 kilograms, is replenished in time after abrasion.B) tinning sequence: into tank
Be added 5 parts of soft water, 0.9 part of anti-aging agent KY-405L, 4.0 parts of zinc oxide, 1.5 parts of promotors, 3.0 parts of sulphur, 1.5 parts aqueous disappear
Infusion is eventually adding 5.0 parts of soft water, various compounding agents is stirred evenly, upper cover sealing → labelling, ball milling.C) Ball-milling Time
Add up whole for 10 hours, tank cannot be washed with water when tank out, tinning must use soft water.D) ball milling liquid shows enchashment use, forbids tank out
Park deposit.3) rubber cement manufactures: vulcanizing agent aqueous dispersions, 5.0 parts of nano ATO dispersion liquids, 0.6 part being added into CMC swelling body
Wetting agent JFC, 0.75 part of paregal O, 25 parts of titanium dioxides, stirring to powder it is fully dispersed uniformly after, obtain mixing mother liquor；It is stirring
Under the conditions of, 167 parts of natural emulsions are gradually added into mixing mother liquor, continue that it is fully dispersed to be stirred to each compounding agent to be uniform viscous
Thick body, pulp are got product, and measure rubber cement concentration with imitative Baumé areometer, it is qualification that concentration, which is 13~18 seconds,.
The application of conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, it is characterised in that: 48 hours prepared in rubber cement
It is interior, the rubber cement that a layer thickness is 0.2~0.4mm is equably scraped on base fabric in the rubber overshoes sponge that resistance value tends to 0.000K Ω
Layer, guarantees that the gap of fabric fibre is filled up completely by rubber cement, and the indsole for the sheaing rubber cement covering that length and width is 25cm or so is taken to lay
Enter in vulcanizing tank, vulcanize under conditions of 130 DEG C × 40min it is primary, after parking one day, base fabric surface dirt and miscellaneous in cleaning
Object, with resistance apparatus measure in base fabric resistance value.
The embodiment of the present invention 2: conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, in parts by weight, including 167
Part natural emulsion, 30 parts of titanium dioxides, 0.7 part of paregal O, 0.6 part of wetting agent JFC, 1.5 parts of aqueous defoamers, 75 parts of soft water,
8.0 parts of nano ATO dispersion liquids, 2.0 parts of mould inhibitor BCM, 0.9 part of anti-aging agent KY-405L, 4.0 parts of zinc oxide, 0.3 part of hydroxide
Potassium, 3.0 parts of sodium carboxymethylcelluloses, 1.5 parts of promotors, 3.0 parts of sulphur.
Preparation method and application is the same as embodiment 1.
The embodiment of the present invention 3: conductive rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, in parts by weight, including 167
Part natural emulsion, 25 parts of titanium dioxides, 0.7 part of paregal O, 0.6 part of wetting agent JFC, 1.5 parts of aqueous defoamers, 85 parts of soft water,
5.0 parts of nano ATO dispersion liquids, 2.0 parts of mould inhibitor BCM, 0.9 part of anti-aging agent KY-405L, 4.0 parts of zinc oxide, 0.3 part of hydroxide
Potassium, 4.0 parts of sodium carboxymethylcelluloses, 1.5 parts of promotors, 3.0 parts of sulphur.Preparation method and application is the same as embodiment 1.
Claims (7)
1. a kind of conduction rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, it is characterised in that: in parts by weight, including 160~
170 parts of natural emulsions, 20~30 parts of titanium dioxides, 0.5~0.9 part of paregal O, 0.5~0.7 part of wetting agent JFC, 1~2 part aqueous
Defoaming agent, 70~80 parts of soft water, 4~6 parts of nano ATO dispersion liquids, 1.5~2.5 parts of mould inhibitor BCM, 0.8~1.0 part of anti-aging agent
KY-405L, 3~5 parts of zinc oxide, 0.2~0.4 part of potassium hydroxide, 2~4 parts of sodium carboxymethylcelluloses, 1~2 part of promotor and
2.5~3.5 parts of sulphur.
2. base fabric sheaing rubber cement in antistatic rubber overshoes sponge according to claim 1, it is characterised in that: according to parts by weight
It calculates, including 167 parts of natural emulsions, 25 parts of titanium dioxides, 0.7 part of paregal O, 0.6 part of wetting agent JFC, 1.5 parts of aqueous defoamers,
75 parts of soft water, 5.0 parts of nano ATO dispersion liquids, 2.0 parts of mould inhibitor BCM, 0.9 part of anti-aging agent KY-405L, 4.0 parts of zinc oxide, 0.3
Part potassium hydroxide, 3.0 parts of sodium carboxymethylcelluloses, 1.5 parts of promotors and 3.0 parts of sulphur.
3. conduction rubber overshoes sponge indsole fabric aqueous sheaing rubber cement according to claim 1 or 2, it is characterised in that: genuine milk
Glue solid is content 60%.
4. conduction rubber overshoes sponge indsole fabric aqueous sheaing rubber cement according to claim 1 or 2, it is characterised in that: nano ATO
Dispersion liquid is water fluid conductive material.
5. conduction rubber overshoes sponge indsole fabric aqueous sheaing rubber cement according to claim 1 or 2, it is characterised in that: 1.5 parts of rush
It is 1.5 parts of promotor TT into agent.
6. a kind of preparation method of conduction rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, it is characterised in that: press above-mentioned weight fraction
Take each component；
1) it prepares CMC swelling body: 65 parts of soft water, sodium carboxymethylcellulose and mould inhibitor BCM mixing being added into blender, slowly
Potassium hydroxide is stirred and be added, the thick shape liquid for no clustering phenomena that is uniformly dispersed is stirred to sodium carboxymethylcellulose, obtains CMC swelling
Body；
2) vulcanizing agent aqueous dispersions are prepared:
A) canned small ball weight is 8 kilograms, and wherein the small ball weight of diameter 20-40mm is 6.0 kilograms, and diameter is 10-15mm's
Small ball weight is 2.0 kilograms, is replenished in time after abrasion；
B) tinning sequence: 5 parts of soft water, anti-aging agent KY-405L, zinc oxide, promotor, sulphur, aqueous defoamer being added into tank,
It is eventually adding remaining soft water, various compounding agents are stirred evenly, upper cover sealing → labelling, ball milling；
C) Ball-milling Time adds up whole for 10 hours, and tank cannot be washed with water when tank out, and tinning must use soft water；
D) ball milling liquid shows enchashment use, cannot go out tank and park deposit；
3) rubber cement manufactures: vulcanizing agent aqueous dispersions, nano ATO dispersion liquid, wetting agent JFC, peregal being added into CMC swelling body
O and titanium dioxide, stirring to powder it is fully dispersed uniformly after, obtain mixing mother liquor；Under agitation, gradually add into mixing mother liquor
Enter natural emulsion, continues that it is fully dispersed to be stirred to each compounding agent to be uniform viscous body, pulp is got product, with imitative Baume degree
Meter measurement rubber cement concentration, concentration are 13~18 seconds.
7. a kind of application of conduction rubber overshoes sponge indsole fabric aqueous sheaing rubber cement, it is characterised in that: prepared in rubber cement 48 small
When it is interior, the rubber cement that a layer thickness is 0.2~0.4mm is equably scraped on base fabric in the rubber overshoes sponge that resistance value tends to 0.000K Ω
Layer, guarantees that the gap of fabric fibre is filled up completely by rubber cement, and the indsole for the sheaing rubber cement covering that length and width is 25cm or so is taken to lay
Enter in vulcanizing tank, vulcanize under conditions of 130 DEG C × 40min it is primary, after parking one day, base fabric surface dirt and miscellaneous in cleaning
Object, with resistance apparatus measure in base fabric resistance value.