CN109355896A - A kind of softness and method for moisturizing of bamboo cotton - Google Patents
A kind of softness and method for moisturizing of bamboo cotton Download PDFInfo
- Publication number
- CN109355896A CN109355896A CN201811229920.5A CN201811229920A CN109355896A CN 109355896 A CN109355896 A CN 109355896A CN 201811229920 A CN201811229920 A CN 201811229920A CN 109355896 A CN109355896 A CN 109355896A
- Authority
- CN
- China
- Prior art keywords
- bamboo fiber
- bamboo
- resulting
- softness
- glycerol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of softness and method for moisturizing of bamboo cotton, according to the following steps: (1) bamboo fiber being combed into 15 microns of fineness, 20-80 millimeters of length；(2) it uses concentration to bleach for the ClO 2 bleaching liquid of 5000ppm step (1) resulting bamboo fiber, pulls drying out；(3) according to glycerol: water=2-5:98-95 ratio is configured to the aqueous solution of 2%-5% containing glycerol, stirs evenly；(4) step (2) resulting bamboo fiber is put among step (3) resulting glycerine water solution, the ratio of bamboo fiber and glycerine water solution is 1:5-1:10, is impregnated 2-4 hours；(5) by bamboo fiber obtained by step (4) pull out dewatered drying to get softness and humidity can be kept in 8-12% can be with the bamboo fiber of long-term preservation.The bamboo fiber manufactured by this method, feel is smooth, loose, is not bonded mutually, can keep the humidity of 8-12% for a long time, bamboo fiber is made not lose intensity because of dry and astringent, is conducive to subsequent spinning and weaving technique.
Description
Technical field
The present invention relates to a kind of bamboo cotton softness and method for moisturizing.
Background technique
Bamboo fiber is textile material best since the dawn of human civilization, it has moisture absorption hydrofuge, is breathed freely dry and comfortable, disinfection is killed
Bacterium, deodorization, the function that other textile materials of formaldehyde adsorption etc. do not have, textile is beautiful and generous, and drapability is good, does not contract
Water, it is well-pressed not wrinkle, it is the textile material that the mankind dream of, but the manufacture difficulty of bamboo fiber is quite high, with regard to one of them
Soft and moisturizing.
Summary of the invention
The object of the present invention is to provide the softnesses and method for moisturizing of a kind of bamboo cotton, it keeps bamboo fibre soft and with one
Fixed humidity improves textile performance.
The present invention is implemented as follows: a kind of softness and method for moisturizing of bamboo cotton, it is characterised in that: according to the following steps:
(1) bamboo fiber is combed into 15 microns of fineness, 20-80 millimeters of length；
(2) it uses concentration to bleach for the ClO 2 bleaching liquid of 5000ppm step (1) resulting bamboo fiber, pulls out
Drying；
(3) according to glycerol: water=2-5:98-95 ratio is configured to the aqueous solution of 2%-5% containing glycerol, stirs evenly；
(4) step (2) resulting bamboo fiber is put among step (3) resulting glycerine water solution, bamboo fiber and
The ratio of glycerine water solution is 1:5-1:10, is impregnated 2-4 hours；
(5) bamboo fiber obtained by step (4) is pulled out dewatered drying to get softness and humidity can be kept 8-12%'s
It can be with the bamboo fiber of long-term preservation.
The bamboo fiber manufactured by this method, feel is smooth, loose, is not bonded mutually, can keep for a long time
The humidity of 8-12%, makes bamboo fiber not lose intensity because of dry and astringent, is conducive to subsequent spinning and weaving technique.
Specific embodiment
The present invention will be further described below with reference to examples.
Embodiment 1
A kind of softness and method for moisturizing of bamboo cotton, according to the following steps:
(1) bamboo fiber is combed into 15 microns of fineness, 20-80 millimeters of length；
(2) it uses concentration to bleach for the ClO 2 bleaching liquid of 5000ppm step (1) resulting bamboo fiber, pulls out
Drying；
(3) according to glycerol: water=2-5:98-95 weight ratio is configured to the aqueous solution of 2%-5% containing glycerol, and stirring is equal
It is even；
(4) step (2) resulting bamboo fiber is put among step (3) resulting glycerine water solution, bamboo fiber and
The ratio of glycerine water solution is 1:5, is impregnated 2-4 hours；
(5) bamboo fiber obtained by step (4) is pulled out dewatered drying to get softness and humidity can be kept 8-12%'s
It can be with the bamboo fiber of long-term preservation.
Embodiment 2
A kind of softness and method for moisturizing of bamboo cotton, it is characterised in that: according to the following steps:
(1) bamboo fiber is combed into 15 microns of fineness, 20-80 millimeters of length；
(2) it uses concentration to bleach for the ClO 2 bleaching liquid of 5000ppm step (1) resulting bamboo fiber, pulls out
Drying；
(3) according to glycerol: water=2-5:98-95 ratio is configured to the aqueous solution of 2%-5% containing glycerol, stirs evenly；
(4) step (2) resulting bamboo fiber is put among step (3) resulting glycerine water solution, bamboo fiber and
The ratio of glycerine water solution is 1:10, is impregnated 2-4 hours；
(5) bamboo fiber obtained by step (4) is pulled out dewatered drying to get softness and humidity can be kept 8-12%'s
It can be with the bamboo fiber of long-term preservation.
Above-described is only preferred embodiments of the invention.It should be pointed out that for the ordinary skill of this field
For personnel, without departing from the principles of the present invention, it can also make several improvements and modification, this is also considered as of the invention
Protection scope.
Claims (1)
1. a kind of softness and method for moisturizing of bamboo cotton, it is characterised in that: according to the following steps:
(1) bamboo fiber is combed into 15 microns of fineness, 20-80 millimeters of length；
(2) it uses concentration to bleach for the ClO 2 bleaching liquid of 5000ppm step (1) resulting bamboo fiber, pulls drying out；
(3) according to glycerol: water=2-5:98-95 ratio is configured to the aqueous solution of 2%-5% containing glycerol, stirs evenly；
(4) step (2) resulting bamboo fiber is put among step (3) resulting glycerine water solution, bamboo fiber and glycerol
The ratio of aqueous solution is 1:5-1:10, is impregnated 2-4 hours；
(5) by bamboo fiber obtained by step (4) pull out dewatered drying to get softness and humidity can be kept in 8-12% can be with
The bamboo fiber of long-term preservation.