CN109353104A - The zero super net aldehyde board production technology of mirror surface of carbonization of one kind - Google Patents
The zero super net aldehyde board production technology of mirror surface of carbonization of one kind Download PDFInfo
- Publication number
- CN109353104A CN109353104A CN201810660126.XA CN201810660126A CN109353104A CN 109353104 A CN109353104 A CN 109353104A CN 201810660126 A CN201810660126 A CN 201810660126A CN 109353104 A CN109353104 A CN 109353104A
- Authority
- CN
- China
- Prior art keywords
- drying
- plate
- sorting
- carbonization
- net aldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The zero super net aldehyde board production technology of mirror surface of carbonization of one kind is disclosed in the present invention, what net aldehyde plate plate thickness produced can be stable after the present invention improves reaches 18cm, so prepared plank indeformable (structure designs 11 layers or 13 layers) does not rebound, water content is constant in the market 8-12%(plate water content all 14% or more, mutability), then passing through the stringent control of moisture, boiling timber, wood fibre is modified, drying time is lengthened, repeated drying is realized.In addition, plate prepared by the present invention is net aldehyde plate, the adhesive used between multi-layer board is net aldehyde glue, and antibacterial powder (chlorine dioxide) reaches insect-free, do not go mouldy nature antibacterial effect in addition;Moreover, plate is repaired layer by layer, scrape greasy, realizes that super flat mirror face is zero carbonization technique in industry.
Description
Technical field
The present invention relates to the productions of net aldehyde plate to prepare related fields, is especially the net aldehyde plate production of the zero super mirror surface of carbonization of one kind
Technique.
Background technique
Currently, indoor air quality status is a focal issue of social concerns, formaldehyde, TVOC, bacterial concentration are exceeded
Drastically influence the physical and mental health of people.Common wood-based plate Furniture panel reaches bonding using the adhesive of formaldehyde and urea synthesizing
Effect, although bonding property is excellent, wherein dissociate formaldehyde cause indoor air quality to deteriorate, to it is old children, weakling or
Pregnant woman breeds healthy hidden danger.Therefore, it can adsorb and the functional panels for decomposing formaldehyde in air are the demands of health of people,
It is the direction of Furniture panel development.Ecological board is using joiner plate core or normal plywood as substrate, and surface layer overlays melamine
Dipping decorative paper achievees the effect that exempt to paint and decorate, is one of biggish plate kind of furniture building material industry application amount.Net aldehyde plate at present
Become the plate first of people's decorate home.
Found by retrieval, a kind of net aldehyde antibacterial ecological board of the disclosure of the invention of patent No. CN201510408081.3 and
Its manufacturing method, it includes substrate layer, overlays the upper epidermis decorative film adhesive for being glued at substrate layer upper and lower surfaces respectively
Layer and layer decorative film adhesive layer;Upper epidermis decorative film adhesive layer and/or layer decorative film adhesive layer are to be impregnated with amino
The facing paper of resin adhesive liquid and Formaldehyde decomposition glue;Be impregnated with the facing paper of amino resins glue and Formaldehyde decomposition glue with a thickness of
0.08-0.12mm;Substrate layer is with a thickness of 2.5-25mm;Formaldehyde decomposition glue include Formaldehyde decomposition effective component, amino resins and
Nano silver;The mass ratio that Formaldehyde decomposition effective component accounts for Formaldehyde decomposition glue is 5-10%;Formaldehyde decomposition effective component includes crust
Element and nanometer silicon wafer;Amino resins is melamine resin or cyanurotriamide modified Lauxite;The concentration of nano silver
For 50-150ppm.
The patent of invention of patent No. CN201210250811.8 discloses a kind of bamboo carbon aldehyde-cleaning paraffin and manufacturing method and bamboo
The net aldehyde floor of carbon, belongs to ornament materials apparatus field.It is characterized in that, being uniform-distribution with bamboo carbon powder in the paraffin, contain
Amount is paraffin for the weight ratio with paraffin: bamboo carbon powder=100:(3 ~ 50), the granularity of the bamboo carbon powder is super for 8000 ~ 12000 purposes
Thin bamboo carbon powder.And it is produced using this aldehyde-cleaning paraffin and with waterproof and the timber floors of the pernicious gases such as formaldehyde can be absorbed.
The utility model of patent No. CN201720061640.2 discloses a kind of net aldehyde antibacterial floor, including floor body,
Floor body includes bottom, and the top contact surface of bottom is successively bonded with cold touching coal keriotheca, middle layer and activity from bottom to top
Layer of charcoal, and there are two net aldehyde antibacterials to impregnate layer for package in cold touching coal keriotheca, is bonded with branch between two net aldehyde antibacterial dipping layers
Frame.
Due to net aldehyde plate become people's decorate home firstly, its application is very common, then for existing net aldehyde plate
For net aldehyde plate prepared by preparation process, have the following disadvantages;First, plank is in the preparation since drying controls not
It is good, then plate can be made to be easily deformed during use;Second, existing net aldehyde plate be easy to appear it is infested, mildew etc. it is existing;Its
Three, net aldehyde plate prepared by prior art is difficult to realize zero carbonization technique in super flat mirror face.
Summary of the invention
Therefore, in order to solve above-mentioned deficiency, the present invention provides one kind the zero super net aldehyde board production technology of mirror surface of carbonization herein, this
What net aldehyde plate plate thickness produced can be stable after invention improves reaches 18cm, then the indeformable (knot of prepared plank
Structure design 11 layers or 13 layers), do not rebound, water content is constant in the market 8-12%(plate water content all 14% or more, mutability), that
By the stringent control of moisture, boiling timber is modified by wood fibre, lengthens drying time, and repeated drying is realized.In addition, this
The prepared plate of invention is net aldehyde plate, and the adhesive used between multi-layer board is net aldehyde glue, and in addition antibacterial powder (titanium dioxide
Chlorine) reach insect-free, do not go mouldy nature antibacterial effect;Moreover, plate is repaired layer by layer, scrape greasy, realizes super flat mirror face in industry
Zero carbonization technique.
The invention is realized in this way the zero super net aldehyde board production technology of mirror surface of carbonization of one kind is constructed, it is real in the following way
It applies,
(1) firstly, sorting properly in plate, drying ungrease treatment then is carried out to the middle plate of sorting, after drying carry out in plate splicing
Operation;
(2) core plate is formed after plate splicing in, then core plate is smeared without aldehyde glue, plate-laying assembly is carried out to it later, is cold-pressed, cuts
Core, hot press operation;It is carried out once to saw side, once scrapes greasy and carries out natural Health preservation 3 days after the completion of hot pressing;
(3) sorting, the fixed thickness of sanding of carry out for sorting qualification, the underproof progress of sorting are carried out after preliminary health 3 days to it
It reprocesses and carries out scraping again greasy;
(4) plate after thick operation fixed to sanding in step (3) carries out sorting operation again, and sorting is underproof to be returned again
It repairs, then to the plate cloth of sorting qualification without aldehyde glue, is then cold-pressed, cuts core, hot pressing and scrape again greasy, carried out again later
Health, conditioned time is one week at this time;
(5) plate completed to health in step (4) carries out the operation of saw side, and carries out the secondary fixed thick processing of sanding therewith, simultaneously
It is underproof to sorting to be reprocessed and carry out scraping again greasy;
The qualified plate of fixed thick processing secondary to sanding carries out substrate inspection, carries out cloth sticker material later, is then divided again
Inspection, sorting is underproof to be reprocessed and carries out scraping again greasy;
(6) to sorting behind the secondary saw side of plate of sorting qualification in step (5), sorting is underproof to be reprocessed and is carried out again
It scrapes greasy;The carry out health of sorting qualification 2 days;
(7) plate after health is carried out pasting net aldehyde paper hot pressing, product inspection, packing.
As an improvement of the above technical solution, the super net aldehyde board production technology of mirror surface of a kind of zero carbonization, for step (1)
Properly the requirement of middle plate is that will have movable joint, cavity, thin skin detection to middle sorting.
As an improvement of the above technical solution, the super net aldehyde board production technology of mirror surface of a kind of zero carbonization, for step (1)
When middle drying operation, 120 DEG C of temperature, zero pressure, drying time is 60 minutes, it is required that being that moisture content is maintained at 8-12%.
As an improvement of the above technical solution, the super net aldehyde board production technology of mirror surface of a kind of zero carbonization, for step (2)
For step (4), when hot press operation;Temperature is 125 DEG C -135 DEG C, pressure 15-18 megapascal;Hot pressing time are as follows: 38-45 points
Clock;
For the cold pressing described in the step (2) and step (4), the pressure 12-15 megapascal of cold pressing, the time 120 minutes.
As an improvement of the above technical solution, the super net aldehyde board production technology of mirror surface of a kind of zero carbonization, for step (2)
It is corresponding cut core for, 1 millimeter or more gap will all repair.
As an improvement of the above technical solution, the super net aldehyde board production technology of mirror surface of a kind of zero carbonization, for step (4)
It for corresponding cloth is operated without aldehyde glue, is realized using cloth glue machine, the operation of cloth glue machine is soft rod rubber stick in 40-60m guarantee cloth
The glue uniformity, every layer of cloth glue is in 1-1.1 kilograms of glue.
As an improvement of the above technical solution, a kind of super net aldehyde board production technology of mirror surface of zero carbonization, described scraping are greasy
Operation is all scraped greasy according to 0.1 millimeter or more gap.
As an improvement of the above technical solution, the super net aldehyde board production technology of mirror surface of a kind of zero carbonization, for step (3)
In a sanding for, the abrasive band 60-80m is used when operation, sand to plate face does not remain putty without being recessed;
For the secondary sanding in step (5), use the abrasive band 80-120m when operation, sand to plate face without be recessed do not remain it is greasy
Son.
As an improvement of the above technical solution, the super net aldehyde board production technology of mirror surface of a kind of zero carbonization, for step (1)
For, using following drying equipment carry out drying operation, the drying equipment include drying shell, drying seat, top drying cylinder,
Upper drying heat-generating pipe, upper drying heat shield, plate transporting reticulation belt;Drying seat is fixed on the inside of drying shell, dries shell
Inside is provided with the drying seat supports seat for being used to support drying seat, and cylinder, upper drying heat-generating pipe, upper drying heat shield are dried in top
Respectively multiple groups, top drying cylinder are fixed on the top of drying shell, and upper drying heat-generating pipe is mounted on top drying cylinder
Retractable ends, upper drying heat shield are located at the top of upper drying heat-generating pipe;The front and back sides of drying shell have plate baking
Dry import and plate drying outlet;Plate transporting reticulation belt is horizontally through behind plate drying import and plate drying outlet and corresponds to
It dries above seat,
The inside of drying seat, which is equipped under multiple groups, dries heat-generating pipe, is provided with temperature detector on the inside of drying shell;
The drying operation of the drying equipment is as follows;Start plate transporting reticulation belt first, while the middle plate dried will be needed to be put into
In plate transporting reticulation belt, rear stopping in drying shell is sent into from plate drying import by plate in the drive of plate transporting reticulation belt;Starting
Cylinder is dried on top, and drying cylinder in control top stretches out, upper drying heat-generating pipe is transferred to lowest point;And it is dried in starting simultaneously
Heat-generating pipe and the fever of lower drying heat-generating pipe make drying interior of shell temperature be maintained at 120 DEG C, dry to drying interior of shell heating
It is dry to restart plate transporting reticulation belt after sixty minutes for plate from plate drying outlet removal, it is required that being that moisture content is maintained at 8-
12%。
The present invention has the advantage that the present invention provides one kind the zero super net aldehyde board production technology of mirror surface of carbonization herein, have
Following improvement and benefit;Firstly, net aldehyde plate plate thickness produced can be stable reach 18cm, then prepared plank
Indeformable (structure design 11 layers or 13 layers) does not rebound, and water content is constant in the market 8-12%(plate water content all 14% or more,
Mutability), then boiling timber is modified by wood fibre by moisture stringent control, drying time is lengthened, repeated drying is real
It is existing.In addition, plate prepared by the present invention is net aldehyde plate, the adhesive used between multi-layer board is net aldehyde glue, and anti-in addition
Bacterium powder (chlorine dioxide) reaches insect-free, do not go mouldy nature antibacterial effect;Moreover, plate is repaired layer by layer, greasy, the super flat mirror of realization is scraped
Face is zero carbonization technique in industry.
Secondly, the present invention for step (1), is dried when implementing using such as Fig. 2-drying equipment shown in Fig. 3
Dry run, the drying equipment include drying shell, drying seat, top drying cylinder, upper drying heat-generating pipe, upper drying heat shield,
Plate transporting reticulation belt;Drying seat is fixed on the inside of drying shell, dries to be provided with to be used to support on the inside of shell and dries seat
Seat supports seat is dried, top drying cylinder, upper drying heat-generating pipe, upper drying heat shield are respectively multiple groups, and it is solid that cylinder is dried on top
It is scheduled on the top of drying shell, upper drying heat-generating pipe is mounted on the retractable ends of top drying cylinder, and upper drying heat shield is located at
The top of upper drying heat-generating pipe;The front and back sides of drying shell have plate drying import and plate drying outlet;Plate
Transporting reticulation belt is horizontally through behind plate drying import and plate drying outlet and corresponds to above drying seat, dries the inside peace of seat
Equipped with heat-generating pipe is dried under multiple groups, temperature detector is provided on the inside of drying shell.The drying operation of the drying equipment is as follows;
Start plate transporting reticulation belt first, while the middle plate dried will be needed to be put into plate transporting reticulation belt, by plate transporting reticulation belt band
Plate stops after being sent into drying shell from plate drying import in dynamic;Start top and dry cylinder, drying cylinder in control top is stretched
Out, upper drying heat-generating pipe is transferred to lowest point;And heat-generating pipe and the fever of lower drying heat-generating pipe are dried in starting simultaneously, to drying
Interior of shell heating makes drying interior of shell temperature be maintained at 120 DEG C, and drying restarts plate transporting reticulation belt for plate after sixty minutes
Material is dried outlet from plate and is removed, it is required that being that moisture content is maintained at 8-12%.
Detailed description of the invention
Fig. 1 is the super net aldehyde board production technology flow diagram of mirror surface of zero carbonization of the present invention;
Fig. 2 is drying equipment overall schematic according to the present invention;
Fig. 3 is drying equipment schematic internal view according to the present invention.
Wherein: drying shell 1 dries seat 2, and cylinder 3, upper drying heat-generating pipe 4, upper drying heat shield 5, plate are dried in top
Transporting reticulation belt 6, dries seat supports seat 7, and plate dries import 8, plate drying outlet 9, lower drying heat-generating pipe 10, temperature detector
11。
Specific embodiment
Below in conjunction with attached drawing 1- Fig. 3, the present invention is described in detail, technical solution in the embodiment of the present invention into
Row clearly and completely describes, it is clear that described embodiments are only a part of the embodiments of the present invention, rather than whole realities
Apply example.Based on the embodiments of the present invention, those of ordinary skill in the art are obtained without making creative work
Every other embodiment, shall fall within the protection scope of the present invention.
The present invention provides one kind the zero super net aldehyde board production technology of mirror surface of carbonization herein by improving, and makes in the following way
It is standby, as shown in Figure 1, implement in the following way,
(1) firstly, sorting properly in plate, drying ungrease treatment then is carried out to the middle plate of sorting, after drying carry out in plate splicing
Operation;For sorting in step (1), properly the requirement of middle plate is that will have movable joint, cavity, thin skin detection;For in step (1)
When drying operation, 120 DEG C of temperature, zero pressure, drying time is 60 minutes, it is required that being that moisture content is maintained at 8-12%.
(2) in plate splicing after form core plate, then to core plate smear without aldehyde glue, it is carried out later plate-laying assembly, cold pressing,
Cut core, hot press operation;It is carried out once to saw side, once scrapes greasy and carries out natural Health preservation 3 days after the completion of hot pressing;Hot press operation
When;Temperature is 125 DEG C -135 DEG C, pressure 15-18 megapascal;Hot pressing time are as follows: 38-45 minutes;When cold press operation, the pressure of cold pressing
Power 12-15 megapascal, the time 120 minutes;For cutting core, 1 millimeter or more gap will all be repaired.
(3) sorting is carried out after preliminary health 3 days to it, sanding of carry out for sorting qualification is fixed thick, and sorting is underproof
It is reprocessed and carries out scraping again greasy;For a sanding, use the abrasive band 60-80m when operation, sand to plate face without
Recess does not remain putty;
(4) plate after thick operation fixed to sanding in step (3) carries out sorting operation again, and sorting is underproof to be returned again
It repairs, then to the plate cloth of sorting qualification without aldehyde glue, is then cold-pressed, cuts core, hot pressing and scrape again greasy, carried out again later
Health, conditioned time is one week at this time;
When hot press operation;Temperature is 125 DEG C -135 DEG C, pressure 15-18 megapascal;Hot pressing time are as follows: 38-45 minutes;Cold press operation
When, the pressure 12-15 megapascal of cold pressing, the time 120 minutes;Wherein, it for cloth is without the operation of aldehyde glue, is realized using cloth glue machine, cloth
The operation of glue machine is soft rod rubber stick in the 40-60m guarantee cloth glue uniformity, and every layer of cloth glue is in 1-1.1 kilograms of glue.
(5) plate completed to health in step (4) carries out the operation of saw side, and carries out the secondary fixed thick processing of sanding therewith,
It is underproof to sorting simultaneously to be reprocessed and carry out scraping again greasy;The qualified plate of fixed thick processing secondary to sanding carries out substrate
It examines, carries out cloth sticker material later, then carry out sorting again, sorting is underproof to be reprocessed and carry out scraping again greasy;This
When for secondary sanding, the abrasive band 80-120m is used when operation, sand to plate face does not remain putty without being recessed.
(6) to sorting behind the secondary saw side of plate of sorting qualification in step (5), sorting is underproof reprocess and again
Scrape greasy;The carry out health of sorting qualification 2 days;
(7) plate after health is carried out pasting net aldehyde paper hot pressing, product inspection, packing.
For scraped described in the above process greasy operation all scrape according to 0.1 millimeter or more gap it is greasy.
So, for a kind of super net aldehyde board production technology of mirror surface of zero carbonization of the present invention, net aldehyde plate produced
Plate thickness can be stable reach 18cm, then prepared plank indeformable (structure designs 11 layers or 13 layers), do not rebound,
Water content is constant in the market 8-12%(plate water content all 14% or more, mutability), then by the stringent control of moisture, boiling wood
Material, wood fibre is modified, drying time is lengthened, repeated drying is realized.In addition, plate prepared by the present invention is net aldehyde plate,
The adhesive used between multi-layer board is net aldehyde glue, and antibacterial powder (chlorine dioxide) reaches insect-free, do not go mouldy nature in addition
Antibacterial effect;Moreover, plate is repaired layer by layer, scrape greasy, realizes that super flat mirror face is zero carbonization technique in industry.
The present invention for step (1), carries out drying behaviour using such as Fig. 2-drying equipment shown in Fig. 3 when implementing
Make, the drying equipment include drying shell 1, drying seat 2, top drying cylinder 3, upper drying heat-generating pipe 4, upper drying heat shield 5,
Plate transporting reticulation belt 6;Drying seat 2 is fixed on the inside of drying shell 1, and the inside of drying shell 1, which is provided with, is used to support drying
The drying seat supports seat 7 of seat 2, it is respectively multiple groups that cylinder 3, upper drying heat-generating pipe 4, upper drying heat shield 5 are dried in top, and top is dried
Dry gas cylinder 3 is fixed on the top of drying shell 1, and upper drying heat-generating pipe 4 is mounted on the retractable ends of top drying cylinder 3, upper baking
Dry heat shield 5 is located at the top of upper drying heat-generating pipe 4;The front and back sides of drying shell 1 have plate drying import 8 and plate
Material drying outlet 9;Plate transporting reticulation belt 6 is horizontally through behind plate drying import 8 and plate drying outlet 9 and corresponds to drying seat
2 tops, the inside of drying seat 2 are equipped with drying heat-generating pipe 10 under multiple groups, dry and are provided with temperature detector 11 on the inside of shell 1.
The drying operation of the drying equipment is as follows;Start plate transporting reticulation belt 6, while the middle plate that needs are dried first
It is put into plate transporting reticulation belt 6, stops after being sent into drying shell 1 by plate in the drive of plate transporting reticulation belt 6 from plate drying import 8
Only;Start top and dry cylinder 3, drying cylinder 3 in control top stretches out, by upper drying heat-generating pipe 4 decentralization to lowest point;And simultaneously
Heat-generating pipe 4 and the fever of lower drying heat-generating pipe 10 are dried in starting, to heating inside drying shell 1, make to dry 1 internal temperature of shell
120 DEG C are maintained at, drying restarts plate transporting reticulation belt 6 after sixty minutes and removes plate from plate drying outlet 9, it is required that being
Moisture content is maintained at 8-12%.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (9)
1. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind, it is characterised in that: implement in the following way,
(1) firstly, sorting properly in plate, drying ungrease treatment then is carried out to the middle plate of sorting, after drying carry out in plate splicing
Operation;
(2) core plate is formed after plate splicing in, then core plate is smeared without aldehyde glue, plate-laying assembly is carried out to it later, is cold-pressed, cuts
Core, hot press operation;It is carried out once to saw side, once scrapes greasy and carries out natural Health preservation 3 days after the completion of hot pressing;
(3) sorting, the fixed thickness of sanding of carry out for sorting qualification, the underproof progress of sorting are carried out after preliminary health 3 days to it
It reprocesses and carries out scraping again greasy;
(4) plate after thick operation fixed to sanding in step (3) carries out sorting operation again, and sorting is underproof to be returned again
It repairs, then to the plate cloth of sorting qualification without aldehyde glue, is then cold-pressed, cuts core, hot pressing and scrape again greasy, carried out again later
Health, conditioned time is one week at this time;
(5) plate completed to health in step (4) carries out the operation of saw side, and carries out the secondary fixed thick processing of sanding therewith, simultaneously
It is underproof to sorting to be reprocessed and carry out scraping again greasy;
The qualified plate of fixed thick processing secondary to sanding carries out substrate inspection, carries out cloth sticker material later, is then divided again
Inspection, sorting is underproof to be reprocessed and carries out scraping again greasy;
(6) to sorting behind the secondary saw side of plate of sorting qualification in step (5), sorting is underproof to be reprocessed and is carried out again
It scrapes greasy;The carry out health of sorting qualification 2 days;
(7) plate after health is carried out pasting net aldehyde paper hot pressing, product inspection, packing.
2. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that: for step (1)
Properly the requirement of middle plate is that will have movable joint, cavity, thin skin detection to middle sorting.
3. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that: for step (1)
When middle drying operation, 120 DEG C of temperature, zero pressure, drying time is 60 minutes, it is required that being that moisture content is maintained at 8-12%.
4. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that: for step (2)
For step (4), when hot press operation;Temperature is 125 DEG C -135 DEG C, pressure 15-18 megapascal;Hot pressing time are as follows: 38-45 points
Clock;
For the cold pressing described in the step (2) and step (4), the pressure 12-15 megapascal of cold pressing, the time 120 minutes.
5. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that: for step (2)
It is corresponding cut core for, 1 millimeter or more gap will all repair.
6. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that: for step (4)
It for corresponding cloth is operated without aldehyde glue, is realized using cloth glue machine, the operation of cloth glue machine is soft rod rubber stick in 40-60m guarantee cloth
The glue uniformity, every layer of cloth glue is in 1-1.1 kilograms of glue.
7. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that: described scrapes greasy behaviour
Work is all scraped greasy according to 0.1 millimeter or more gap.
8. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that:
For a sanding in step (3), use the abrasive band 60-80m when operation, sand to plate face without be recessed do not remain it is greasy
Son;
For the secondary sanding in step (5), use the abrasive band 80-120m when operation, sand to plate face without be recessed do not remain it is greasy
Son.
9. the zero super net aldehyde board production technology of mirror surface of carbonization of one kind according to claim 1, it is characterised in that: for step (1)
For, drying operation is carried out using following drying equipment, which includes drying shell (1), drying seat (2), top baking
Dry gas cylinder (3), upper drying heat-generating pipe (4), upper drying heat shield (5), plate transporting reticulation belt (6);Drying seat (2) is fixed on drying
The inside of shell (1),
The drying seat supports seat (7) for being used to support drying seat (2) is provided on the inside of drying shell (1), cylinder is dried on top
(3), upper drying heat-generating pipe (4), upper drying heat shield (5) are respectively multiple groups, and top drying cylinder (3) is fixed on drying shell
(1) top, upper drying heat-generating pipe (4) are mounted on the retractable ends of top drying cylinder (3), and upper drying heat shield (5) is located at
The top of upper drying heat-generating pipe (4);
The front and back sides of drying shell (1) have plate drying import (8) and plate drying outlet (9);
Plate transporting reticulation belt (6) is horizontally through plate drying import (8) and plate drying outlet (9) afterwards and corresponds to drying seat
(2) top,
The inside of drying seat (2) is equipped with drying heat-generating pipe (10) under multiple groups, is provided with temperature detector on the inside of drying shell (1)
(11);
The drying operation of the drying equipment is as follows;
Start plate transporting reticulation belt (6) first, while the middle plate dried will be needed to be put into plate transporting reticulation belt (6), by plate
Plate is sent into rear stopping in drying shell (1) from plate drying import (8) in transporting reticulation belt (6) drive;Start top and dries cylinder
(3), control top drying cylinder (3) is stretched out, by upper drying heat-generating pipe (4)
It transfers to lowest point;And heat-generating pipe (4) and the fever of lower drying heat-generating pipe (10) are dried in starting simultaneously, to drying shell
(1) internal heating makes drying shell (1) internal temperature be maintained at 120 DEG C, and plate transporting reticulation belt is restarted in drying after sixty minutes
(6) plate is dried outlet (9) from plate to remove, it is required that being that moisture content is maintained at 8-12%.