CN109351915A - 一种提高砂芯质量的方法 - Google Patents
一种提高砂芯质量的方法 Download PDFInfo
- Publication number
- CN109351915A CN109351915A CN201811300437.1A CN201811300437A CN109351915A CN 109351915 A CN109351915 A CN 109351915A CN 201811300437 A CN201811300437 A CN 201811300437A CN 109351915 A CN109351915 A CN 109351915A
- Authority
- CN
- China
- Prior art keywords
- core box
- core
- wire cutting
- air discharge
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种提高砂芯质量的方法，芯盒在制芯时，当芯盒腔体内部为复杂曲面以及狭小型腔，不适于使用排气塞或顶芯杆排气的情况下，在芯盒设计和制作过程中使用线切割，对芯盒这些狭小位置进行处理，形成连通芯盒腔体内外的线切割排气槽。本发明在芯盒设计和制作过程中使用线切割，对这些狭小位置进行处理，采用线切割机的好处是其钼丝直径可选择0.14‑0.16mm，这样的缝隙选用小于此直径的覆膜砂规格，可以保证砂粒不能通过而气体可以通过，从而达到引导气体流向的目的，保证砂芯质量。
Description
技术领域
本发明属于芯盒设计与制作技术领域，尤其是涉及一种提高砂芯质量的方法。
背景技术
我公司由于生产零件的复杂程度不同，芯盒也是各式各样的。特别是形状非常复杂的芯盒，存在很多排气死角，导致型芯充砂不实、缺肉、强度不够等缺陷。为了避免出现上述缺陷，提高型芯质量，我们考虑人为引导气体走向，使气体催化剂均匀地分布在整个型芯芯盒中，使砂芯均匀固化，从而提高型芯的强度，提高砂芯的合格率及制芯效率。
芯盒在制芯时需要通过设计出的排气减小型腔内的压力，引导气携带砂的流动，从而充满型腔，保证射砂完整和致密，一般的排气结构设计是在分型面上加工排气槽，型腔内加顶芯杆、排气塞等方式实现。
但是由于零件的复杂程度不同，芯盒也是各式各样的。特别是形状非常复杂的芯盒，存在很多复杂曲面以及狭小型腔，这些位置属于排气死角，如果这些区域无排气结构，就会产生涡流导致砂芯出现充砂不实、缺肉、强度不够等缺陷。为了避免出现上述缺陷，提出了一种针对这些排气死角位置的排气方案。
现有技术的缺点：
排气塞上表面是一个平面，因此一般只能设置在砂芯平面上；顶芯杆与砂芯接触部位可以是平面或者曲面，但对于一些狭小位置，尖角位置也无法实现。
发明内容
本发明旨在克服现有技术的缺陷，提供一种提高砂芯质量的方法，芯盒在制芯时，当芯盒腔体内部为复杂曲面以及狭小型腔，不适于使用排气塞或顶芯杆排气的情况下，在芯盒设计和制作过程中使用线切割，对芯盒这些狭小位置进行处理，形成连通芯盒腔体内外的线切割排气槽。
优选地，所述排气槽为钼丝切割形成的缝隙，缝隙的宽度为0.14-0.16mm。
优选地，所述排气槽位于腔体内部尖角位置。
优选地，所述排气槽位于圆角或芯盒拐角位置。
针对现有技术存在的问题，本发明在芯盒设计和制作过程中使用线切割，对这些狭小位置进行处理，采用线切割机的好处是其钼丝直径可选择0.14-0.16mm，这样的缝隙选用小于此直径的覆膜砂规格，可以保证砂粒不能通过而气体可以通过，从而达到引导气体流向的目的，保证砂芯质量。
附图说明
下面结合附图和具体实施方式进一步说明：
图1为本发明实施例1的一种提高砂芯质量的方法的示意图；
图2为本发明实施例2的一种提高砂芯质量的方法的示意图；
图中：1-上模板，2-砂芯型腔，3-下模板，4-线切割排气槽。
具体实施方式
实施例1：
如图1所示：本发明公开了一种提高砂芯质量的方法，芯盒在制芯时，当芯盒腔体内部为复杂曲面以及狭小型腔，不适于使用排气塞或顶芯杆排气的情况下，在芯盒设计和制作过程中使用线切割，对芯盒这些狭小位置进行处理，形成连通芯盒腔体内外的线切割排气槽4。
所述排气槽4为钼丝切割形成的缝隙，缝隙的宽度为0.14-0.16mm。
排气槽4位于腔体内部尖角位置，这些位置无法设置排气塞和顶芯杆。
实施例2：
如图2所示，实施例2与实施例1不同的是，排气槽位于圆角或芯盒拐角位置，这些位置无法设置排气塞和顶芯杆。
本发明的工作原理：
芯盒排气是必须的，排气的方法有多种，如常见的顶杆排气，气塞排气，排气片排气等，此专利与现有技术芯盒排气原理是相同的，即设计一些孔隙让砂粒无法通过，而气体可以通过，达到排气目的；此专利的关键点在于，解决了现有技术无法解决的一些特殊位置的排气问题(如尖角，圆角，直角等部位)。
本发明针对一些特殊产品，可提高其砂芯局部质量。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (4)
1.一种提高砂芯质量的方法，其特征在于，芯盒在制芯时，当芯盒腔体内部为复杂曲面以及狭小型腔，不适于使用排气塞或顶芯杆排气的情况下，在芯盒设计和制作过程中使用线切割，对芯盒这些狭小位置进行处理，形成连通芯盒腔体内外的线切割排气槽。
2.根据权利要求1所述的提高砂芯质量的方法，其特征在于，所述排气槽为钼丝切割形成的缝隙，缝隙的宽度为0.14-0.16mm。
3.根据权利要求1所述的一种提高砂芯质量的方法，其特征在于：所述排气槽位于腔体内部尖角位置。
4.根据权利要求1所述的一种提高砂芯质量的方法，其特征在于：所述排气槽位于圆角或芯盒拐角位置。