CN109337519A - A kind of aqueous glass flake paint and preparation method thereof - Google Patents
A kind of aqueous glass flake paint and preparation method thereof Download PDFInfo
- Publication number
- CN109337519A CN109337519A CN201811229325.1A CN201811229325A CN109337519A CN 109337519 A CN109337519 A CN 109337519A CN 201811229325 A CN201811229325 A CN 201811229325A CN 109337519 A CN109337519 A CN 109337519A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- glass flake
- aqueous
- aqueous glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous glass flake paints, and according to parts by weight include component A and B component: wherein component A includes: one 5~10 parts of reactive diluent, 2~5 parts of auxiliary rheological agents, 1~2 part of wetting dispersing agent, 50~60 parts of epoxy resin, 5~30 parts of glass flake；Wherein B component includes: 40~60 parts of polyamide curing agent, 40~60 parts of water.The features such as flexibility of the present invention is good, surface drying is fast, low VOC can be used for bridge steel structure, the outdoor corrosion-inhibiting coating of the steels structure such as petroleum pipeline.
Description
Technical field
The invention belongs to heavy-duty anticorrosive coating technical field, it is related to a kind of aqueous glass flake paint and preparation method thereof.
Background technique
Heavy-duty anticorrosive coating is one of the important development of current China's anticorrosive coating, it is widely used in ship, petrochemical industry, bridge
China's key areas such as beam, container, electric power railway, construction steel structure.However heavy-duty anticorrosive coating China at present there is also
Some problems: surface treatment requires height, and project amount is big, and the used big multiple stiffness of epoxy type coating is had a surplus, and toughness is insufficient.Sternly
The cold time, it is some need on the marine engineering made short work of such as the flat field of drilling well often after coating on the day of will load and unload, therefore
It is required that coating can rapid curing meet these production requirements, another importance is exactly cannot in coating system used
Contain the heavy metal being harmful to the human body.
Summary of the invention
The problem to be solved in the present invention is to provide a kind of aqueous glass flake paints and preparation method thereof, can quickly apply
Solidify after dress, meet some particular application demands, and without the heavy metal being harmful to the human body in coating
In order to solve the above technical problems, the technical solution adopted by the present invention is that: a kind of aqueous glass flake paint, by weight
Number meter includes component A and B component:
Wherein component A includes: one 5~10 parts of reactive diluent, 2~5 parts of auxiliary rheological agents, 1~2 part of wetting dispersing agent, ring
50~60 parts of oxygen resin, 5~30 parts of scale；
Wherein B component includes: 40~60 parts of polyamide curing agent, 40~60 parts of deionized water.
Further, reactive diluent one is one or more of isopropanol, propylene glycol monomethyl ether, butyl glycol ether.
Further, one or more of auxiliary rheological agents DC828, PU65；Wetting dispersing agent be DC365,
One or more of BYK2055, ELNT3660.
Further, epoxy resin WPE-51-60.
Further, glass flake is 800 mesh glass flakes, using this glass flake as the corrosion-inhibiting coating of filler, tool
There are very high cohesive force and excellent chemical-resistant resistance and anti-aging property.Since glass flake is overlapping arrangement in the coating
, therefore great role has been risen to the permeability resistance of film.Coating process can be used brushing, airless spraying or roller and apply
Dress.
Further, aqueous polyamide curing agent is BS901, AB-HGF-100, BS906 one of or several.Epoxy
General performance is excellent when resin hot setting, but the coating used in civil construction and bonding agent etc. are difficult due to heating,
Normal temperature cure is needed, at this moment just needs to be added curing agent, distance between aqueous polyamide curing agent functional group has good soft
It is soft.
The present invention also provides the preparation methods of above-mentioned aqueous glass flake paint, include the following steps:
Step 1: epoxy resin, reactive diluent, wetting dispersing agent are added to the container by formula rate, it is stirred
Uniformly；
Step 2: auxiliary rheological agents are added in the mixture that the first step obtains, stir, is uniformly mixed；
Step 3: pigments and fillers are added in the mixture that second step obtains, stir, is uniformly mixed and obtains component A；
Step 5: in proportion mixing aqueous polyamide curing agent, water, high-speed stirred obtains B component after mixing；
Step 6: the component A that the 4th step obtains is mixed with the B component that the 5th step obtains, stir evenly to get product.
Further, the speed of agitator of second step is 400~600rpm, and mixing time is 0.5~1h；The stirring of third step
Revolving speed is 1500~2000rpm, and mixing time is 0.5~1h.
The advantages and positive effects of the present invention are: toughness of the present invention is good, solidification is quick, environmental protection, it can be used for marine worker
The outdoor anti-corrosion primer of the steels structures such as steel structure, bridge, pipeline and petroleum and petrochemical industry steel construction.The present invention is to surface treatment
Of less demanding, project amount is small, can reach requirement in rigidity and toughness in performance, even if coating also can be fast in the severe cold time
Speed solidification, meets production requirement, another importance is exactly in coating system used without containing the huge sum of money being harmful to the human body
Belong to.
Specific embodiment
Technical solution of the present invention is described in detail below, but protection scope of the present invention is not limited to the implementation
Example.
Embodiment 1
A kind of aqueous glass flake paint, it is characterised in that: according to parts by weight include component A and B component:
Wherein component A includes: 8 parts of propylene glycol monomethyl ether, 4 parts of PU65 auxiliary rheological agents, 1 part of DC365 wetting dispersing agent, WPE-
58 parts of 51-60 epoxy resin, 29 parts of 800 mesh glass flake；Propylene glycol monomethyl ether has faint ether taste, but does not have strong and stimulating gas
Taste keeps its purposes more safe extensively.Since existing ether has hydroxyl in its molecular structure again, thus its solubility property is very
It is excellent, and have the features such as suitable rate of volatilization and reactivity.
Wherein B component include: aqueous polyamide curing agent BS901 be 55 parts, deionized water is 45 parts.
The preparation method of above-mentioned aqueous glass flake paint, includes the following steps:
Hold step 1: WPE-51-60 epoxy resin, propylene glycol monomethyl ether, DC365 wetting dispersing agent are added by formula rate
In device, it is uniformly mixed；
Step 2: PU65 auxiliary rheological agents are added in the mixture that the first step obtains, and stirring, speed of agitator 400rpm,
Mixing time is 1h, is uniformly mixed；
Step 3: 800 mesh glass flakes are added in the mixture that second step obtains, stir, speed of agitator is
1500rpm, mixing time 1h are uniformly mixed and obtain component A；
Step 4: BS901 polyamide curing agent, water after mixing, are obtained B component；
Step 5: the component A that the 4th step obtains is mixed with the B component that the 5th step obtains, stir evenly to get product,
Obtained properties of product are shown in Table 1.
Embodiment 2
The present embodiment 2 the difference from embodiment 1 is that, the variation of component, preparation method indifference.
Aqueous glass flake paint is characterized in that in the present embodiment: according to parts by weight include component A and B component:
Wherein component A includes: isopropanol and 6 parts of propylene glycol monomethyl ether mixture, 5 parts of DC828 auxiliary rheological agents, PU65 wetting point
1 part of powder, 60 parts of WPE-51-60 epoxy resin, 28 parts of 800 mesh glass flake；
Wherein B component include: aqueous polyamide curing agent BS901 be 50 parts, deionized water is 50 parts.
Obtained properties of product are shown in Table 1.
Embodiment 3
The present embodiment 3 and the difference of embodiment 1 and embodiment 2 be, the variation of component, preparation method indifference.
Aqueous glass flake paint is characterized in that in the present embodiment: according to parts by weight include component A and B component:
Wherein component A includes: 6 parts of isopropanol, 5 parts of DC828 auxiliary rheological agents, 1 part of BYK2055 wetting dispersing agent, WPE-51-
60 60 parts of epoxy resin, 28 parts of 800 mesh glass flake；
Wherein B component include: aqueous polyamide curing agent BS901 be 50 parts, deionized water is 50 parts.
Obtained properties of product are shown in Table 1.
Comparative example 1
This comparative example 1 the difference from embodiment 1 is that, the variation of component, preparation method indifference.
Coating is characterized in that in the present embodiment: according to parts by weight include component A and B component:
Wherein component A includes: 8 parts of propylene glycol monomethyl ether, 4 parts of PU65 auxiliary rheological agents, 1 part of DC365 wetting dispersing agent, WPE-
87 parts of 51-60 epoxy resin.
Wherein B component include: aqueous polyamide curing agent BS901 be 55 parts, deionized water is 45 parts.
Obtained properties of product are shown in Table 1.
Comparative example 2
This comparative example 2 the difference from example 2 is that, the variation of component, preparation method indifference.
Coating is characterized in that in the present embodiment: according to parts by weight include component A and B component:
Wherein component A includes: isopropanol and 6 parts of propylene glycol monomethyl ether mixture, 5 parts of DC828 auxiliary rheological agents, PU65 wetting point
1 part of powder, 88 parts of WPE-51-60 epoxy resin；
Wherein B component include: aqueous polyamide curing agent BS901 be 50 parts, deionized water is 50 parts.
Obtained properties of product are shown in Table 1.
Comparative example 3
This comparative example 3 is distinguished with embodiment 3 to be, the variation of component, preparation method indifference.
Aqueous glass flake paint is characterized in that in the present embodiment: according to parts by weight include component A and B component:
Wherein component A includes: 6 parts of isopropanol, 5 parts of DC828 auxiliary rheological agents, 1 part of BYK2055 wetting dispersing agent, WPE-51-
60 88 parts of epoxy resin；
Wherein B component include: aqueous polyamide curing agent BS901 be 50 parts, deionized water is 50 parts.
Obtained properties of product are shown in Table 1.
The performance test that table 1 is formulated
Through embodiment 1,2,3 as can be seen that in the case where other components variation, as long as the change of component of glass flake
Less, the performance of coating is stablized, and toughness is good, solidification is quick, environmental protection, without containing the heavy metal being harmful to the human body, meets production
It is required that.
Through comparative example 1,2,3 as can be seen that in the indeclinable situation of other components, as long as not adding glass flake,
The performance of coating is unstable, not tough and tensile, slow curing.
As described above, must not be explained although the present invention has been indicated and described referring to specific preferred embodiment
For the limitation to invention itself.It without prejudice to the spirit and scope of the invention as defined in the appended claims, can be right
Various changes can be made in the form and details for it.
Claims (9)
1. a kind of aqueous glass flake paint, it is characterised in that: according to parts by weight include component A and B component:
Wherein component A includes: one 5~10 parts of reactive diluent, 2~5 parts of auxiliary rheological agents, 1~2 part of wetting dispersing agent, asphalt mixtures modified by epoxy resin
50~60 parts of rouge, 5~30 parts of scale；
Wherein B component includes: 40~60 parts of polyamide curing agent, 40~60 parts of deionized water.
2. aqueous glass flake paint according to claim 1, it is characterised in that: the reactive diluent one is alcohol ester ten
Two, isopropanol, butyl glycol ether, one or more of propylene glycol monomethyl ether.
3. aqueous glass flake paint according to claim 1, it is characterised in that: the auxiliary rheological agents are DC828, PU65
One or more；The wetting dispersing agent is one or more of DC365, BYK2055, ELNT3660.
4. aqueous glass flake paint according to claim 1, it is characterised in that: the epoxy resin is WPE-51-60.
5. aqueous glass flake paint according to claim 1, it is characterised in that: the glass flake is 800 mesh glass
Scale.
6. aqueous glass flake paint according to claim 1, it is characterised in that: the polyamide curing agent be BS901,
One or more of AB-HGF-100, BS906.
7. aqueous glass flake paint according to claim 1, it is characterised in that: the curing agent BS901.
8. a kind of prepare the method such as the described in any item aqueous glass flake paints of claim 1-7, it is characterised in that: including
Following steps:
Step 1: epoxy resin, reactive diluent, wetting dispersing agent are added to the container by formula rate, it is uniformly mixed；
Step 2: auxiliary rheological agents are added in the mixture that the first step obtains, stir, is uniformly mixed；
Step 3: filler is added in the mixture that second step obtains, stir, is uniformly mixed and obtains component A；
Step 4: water mixes, and high-speed stirred obtains B component after mixing in proportion by aqueous polyamide curing agent；
Step 5: the component A that the 4th step obtains is mixed with the B component that the 5th step obtains, stir evenly to get product.
9. the preparation method of aqueous glass flake paint according to claim 8, it is characterised in that: the second step stirs
Mixing revolving speed is 400~600rpm, and mixing time is 0.5~1h；The speed of agitator of the third step is 1500~2000rpm, is stirred
Mixing the time is 0.5~1h.