CN109320748A - Waterproof system and preparation method thereof - Google Patents

Waterproof system and preparation method thereof Download PDF

Info

Publication number
CN109320748A
CN109320748A CN201811115994.6A CN201811115994A CN109320748A CN 109320748 A CN109320748 A CN 109320748A CN 201811115994 A CN201811115994 A CN 201811115994A CN 109320748 A CN109320748 A CN 109320748A
Authority
CN
China
Prior art keywords
parts
butadiene rubber
styrene butadiene
pitch
softening agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811115994.6A
Other languages
Chinese (zh)
Inventor
杨小林
任雯
徐天勇
肖立
黄飞
巫治国
曾心
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Yangshida Waterproof Material Co Ltd
Original Assignee
Sichuan Yangshida Waterproof Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan Yangshida Waterproof Material Co Ltd filed Critical Sichuan Yangshida Waterproof Material Co Ltd
Priority to CN201811115994.6A priority Critical patent/CN109320748A/en
Publication of CN109320748A publication Critical patent/CN109320748A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of waterproof systems and preparation method thereof, it is composed of uncured water-repellent paint and SBS modified asphalt waterproof coiled material two parts, in which: uncured water-repellent paint weight are as follows: 45-55 parts of 90# pitch, 6-10 parts of thermoplastic styrene butadiene rubber, 8-16 parts of powder styrene butadiene rubber, 6-10 parts of tackifying resin, 8-12 parts of softening agent, high temperature modified dose 1-4 parts, 10-16 parts of talcum powder；SBS modified asphalt waterproof coiled material weight are as follows: 25-35 parts of 90# pitch, 4-8 parts of softening agent, 3-6 parts of thermoplastic styrene butadiene rubber, 2-4 parts of PE reworked material, 30-36 parts of talcum powder.Whole system compatibility is good, so that having good adhesive property, perfectly fits together with base, effectively prevents channeling water.Hot melt material hot melt application is avoided, safety, environment are impacted.

Description

Waterproof system and preparation method thereof
Technical field
The invention belongs to construction waterproofing engineering fields, and in particular to a kind of waterproof system and preparation method thereof.
Background technique
In recent years, in construction waterproofing engineering, vibration, base's sedimentation and deformation, cracking of building etc. will lead to waterproof The destruction of layer, and then leak, it is in practical applications, general using empty laid process, point bonding construction, to alleviate base course crack change Destruction of the shape to waterproof layer, but this causes to be easy to phenomena such as localized seepage occurs and causes channeling water.Meanwhile in current policy Under, environmental protection is a primary requirement, is all using hot melt application for SBS modified asphalt waterproof coiled material traditional handicraft, this is right All it is one in the problems such as construction site safety, environmental protection greatly to test.
Summary of the invention
The technical problems to be solved by the invention are as follows: solution hot melt class waterproof roll channeling water because of empty laid process and caused by putting bonding Problem, and improve traditional construction to the hidden danger of environment and safety.
The technical solution of the present invention is as follows: a kind of waterproof system, by uncured water-repellent paint and SBS modified asphalt waterproof coiled material Two parts are composed, in which:
Uncured water-repellent paint weight are as follows: 45-55 parts of 90# pitch, 6-10 parts of thermoplastic styrene butadiene rubber, powder butylbenzene 8-16 parts of rubber, 6-10 parts of tackifying resin, 8-12 parts of softening agent, high temperature modified dose 1-4 parts, 10-16 parts of talcum powder；
SBS modified asphalt waterproof coiled material weight are as follows: 25-35 parts of 90# pitch, 4-8 parts of softening agent, thermoplastic styrene butadiene rubber 3-6 parts of glue, 2-4 parts of PE reworked material, 30-36 parts of talcum powder.
Further, the 90# pitch is the 90# pitch of middle extra large pitch (Sichuan) Co., Ltd.
Further, thermoplastic styrene butadiene rubber is the thermoplastic styrene butadiene rubber that Yueyang petrochemical industry trade mark is SBS1401-792.
Further, powder styrene butadiene rubber is the powder butylbenzene rubber that the Shandong Gao Shi Ke Gong Co., Ltd trade mark is SBR50% Glue.
Further, tackifying resin is the tackifying resin that the lily magnolia chemical industry trade mark is 8005.
Further, softening agent is that Chengdu steps this and opens up the softening agent that the new energy lubriation material Co., Ltd trade mark is 1#.
Further, high temperature modified dose of high temperature modified dose for husky rope (Sasol) Germany Co., Ltd.
Further, talcum powder is the talcum powder that the river river You Hua mining industry partial size is 200 mesh
Further, PE reworked material is Chengdu Nian Xin plastic cement Co., Ltd product.
The invention also discloses a kind of preparation methods of waterproof system, comprising the following steps:
(1) 190 DEG C are heated to by 45-55 parts and 6-10 parts of thermoplastic styrene butadiene rubber of 90# pitch, then sequentially add powder fourth 8-16 parts of benzene rubber, 6-10 parts of tackifying resin, 8-12 parts of softening agent, high temperature modified dose 1-4 parts, temperature are maintained at 190 DEG C of processes 2h continuously stir mixing after, be added talcum powder 10-16 part, be stirred for 1h discharge, uncured water-repellent paint is made；
(2) by 25-35 parts of 90# pitch, 4-8 parts of softening agent, 3-6 parts of thermoplastic styrene butadiene rubber, 190 DEG C are heated to, to thermoplastic Butadiene-styrene rubber completely with pitch after mixing, add 2-4 parts of PE reworked material, keep the temperature 190 DEG C, after stirring 2h, expected to PE After fully dissolved, talcum powder 30-36 parts, then uniform stirring 1h discharging is added, prepares 4mm thickness by asphalt felt production equipment Two-sided SBS modified asphalt waterproof coiled material；
(3) after needing waterproof position to carry out base treatment, uncured water-repellent paint made from squeegeeing step (1), then The modified asphalt waterproof coiled material that on uncured water-repellent paint prepared by paving step (2).
Compared with prior art, the invention has the following advantages:
1, the entire decorum has superpower self-healing property, pressure-sensitive and creep properties, and when waterproof layer is by destroying, breakdown point will not Expand, and breakage energy self-regeneration.
2, whole system compatibility is good, so that having good adhesive property, perfectly fits together with base, effectively Prevent channeling water.
3, good permeability can close base's pore, absorb base because of the stress of slight deformation cracking release, avoid answering Power is applied to waterproof layer, causes the destruction of waterproof layer.
4, excellent workability does not need curing time, carries out the next step after construction at once, and effect is 1+1 > 2.
5, hot melt material hot melt application is avoided, safety, environment are impacted.
Specific embodiment
In following embodiment, 90# pitch is the 90# pitch of middle extra large pitch (Sichuan) Co., Ltd, and thermoplastic styrene butadiene rubber is Yueyang petrochemical industry trade mark is the thermoplastic styrene butadiene rubber of SBS1401-792, and powder styrene butadiene rubber is Shandong Gao Shi Ke Gong Co., Ltd board Number be SBR50% powder styrene butadiene rubber, tackifying resin is the tackifying resin that the lily magnolia chemical industry trade mark is 8005, and softening agent is Chengdu Mai Si opens up the softening agent that new energy lubriation material Co., Ltd's trade mark is 1#, and high temperature modified dose limited for husky rope (Sasol) Germany High temperature modified dose of company, PE reworked material are that PE reworked material is that Chengdu Nian Xin plastic cement Co., Ltd produces, and talcum powder is river oil China Mining industry partial size in river is the talcum powder of 200 mesh.Above-mentioned material is commercially available.
Embodiment 1
190 DEG C are heated to by 50 parts and 8 parts of thermoplastic styrene butadiene rubber of 90# pitch, then sequentially adds powder styrene butadiene rubber 12 Part, 8 parts of tackifying resin, 10 parts of softening agent, high temperature modified dose 2 parts, temperature are maintained at 190 DEG C and continuously stir mixing by 2h Afterwards, 10 parts of talcum powder are added, 1h discharging is stirred for, the uncured water-repellent paint of the present invention is made.
By 28 parts of pitch of 90# pitch 90#, 6 parts of softening agent, 4.5 parts of thermoplastic styrene butadiene rubber, 190 DEG C are heated to, to thermoplastic fourth Benzene rubber completely with pitch after mixing, add 2.5 parts of PE reworked material, keep the temperature 190 DEG C, it is complete to PE material after stirring 2h After dissolution, 32.5 parts of talcum powder, then uniform stirring 1h discharging is added.4mm thickness is prepared by asphalt felt production equipment SBS modified asphalt waterproof coiled material.
Application method: after needing waterproof position to carry out base treatment, uncured water-repellent paint is brushed, then uncured Paving modified asphalt waterproof coiled material on water-repellent paint.
Embodiment 2
190 DEG C are heated to by 45 parts and 6 parts of thermoplastic styrene butadiene rubber of 90# pitch, then sequentially adds powder styrene butadiene rubber 8 Part, 6 parts of tackifying resin, 8 parts of softening agent, high temperature modified dose 1 part, temperature be maintained at 190 DEG C by 2h continuously stir mixing after, 10 parts of talcum powder are added, 1h discharging is stirred for, uncured water-repellent paint is made；
By 25 parts of 90# pitch, 4 parts of softening agent, 3 parts of thermoplastic styrene butadiene rubber, 190 DEG C are heated to, it is complete to thermoplastic styrene butadiene rubber Entirely after mixing with pitch, 2 parts of PE reworked material are added, keeps the temperature 190 DEG C, after stirring 2h, after PE material is completely dissolved, is added 30 parts of talcum powder, then uniform stirring 1h discharging, the modified drip of the two-sided SBS of 4mm thickness is prepared by asphalt felt production equipment Green waterproof roll；
Application method: after needing waterproof position to carry out base treatment, uncured water-repellent paint is brushed, then uncured Paving modified asphalt waterproof coiled material on water-repellent paint.
Embodiment 3
190 DEG C are heated to by 55 parts and 10 parts of thermoplastic styrene butadiene rubber of 90# pitch, then sequentially adds powder styrene butadiene rubber 16 Part, 10 parts of tackifying resin, 12 parts of softening agent, high temperature modified dose 4 parts, temperature are maintained at 190 DEG C and continuously stir mixing by 2h Afterwards, 16 parts of talcum powder are added, 1h discharging is stirred for, uncured water-repellent paint is made；
By 35 parts of 90# pitch, 8 parts of softening agent, 6 parts of thermoplastic styrene butadiene rubber, 190 DEG C are heated to, it is complete to thermoplastic styrene butadiene rubber Entirely after mixing with pitch, 4 parts of PE reworked material are added, keeps the temperature 190 DEG C, after stirring 2h, after PE material is completely dissolved, is added 36 parts of talcum powder, then uniform stirring 1h discharging, the modified drip of the two-sided SBS of 4mm thickness is prepared by asphalt felt production equipment Green waterproof roll；
Application method: after needing waterproof position to carry out base treatment, uncured water-repellent paint is brushed, then uncured Paving modified asphalt waterproof coiled material on water-repellent paint.
Construction process:
The uncured water-repellent paint of base treatment → brushing → weak part extra play construction → positioning, check and correction, snap the line → paving It pastes SBS modified asphalt waterproof coiled material → warehouse, exhaust, compacting → overlap edge and receives head sealing → water-storing test → examination.
The performance indicator of uncured water-repellent paint and SBS modified asphalt waterproof coiled material is as shown in Table 1 and Table 2:
The uncured water-repellent paint index of table 1
2 SBS modified asphalt waterproof coiled material index of table
Detection project Survey index Examination criteria
Pulling force/(N/50mm) ≥800 GB 18242-2008
Maximum pull elongation/% ≥40 GB 18242-2008
Impermeability 0.3Mpa, 30min are waterproof GB 18242-2008
Heat resistance 105 DEG C, 2h non-displacement, trickling, drippage GB 18242-2008
Low temperature flexibility/DEG C - 25 DEG C, 1h flawless GB 18242-2008
Overlap edge peel strength ≥1.5 GB 18242-2008

Claims (10)

1. a kind of waterproof system, which is characterized in that combined by uncured water-repellent paint and SBS modified asphalt waterproof coiled material two parts It forms, in which:
Uncured water-repellent paint weight are as follows: 45-55 parts of 90# pitch, 6-10 parts of thermoplastic styrene butadiene rubber, powder styrene butadiene rubber 8-16 parts, 6-10 parts of tackifying resin, 8-12 parts of softening agent, high temperature modified dose 1-4 parts, 10-16 parts of talcum powder；
SBS modified asphalt waterproof coiled material weight are as follows: 25-35 parts of 90# pitch, 4-8 parts of softening agent, thermoplastic styrene butadiene rubber 3- 6 parts, 2-4 parts of PE reworked material, 30-36 parts of talcum powder.
2. a kind of waterproof system shown according to claim 1, which is characterized in that the 90# pitch is middle extra large pitch (Sichuan) The 90# pitch of Co., Ltd.
3. a kind of waterproof system shown according to claim 1, which is characterized in that thermoplastic styrene butadiene rubber is that Yueyang petrochemical industry trade mark is The thermoplastic styrene butadiene rubber of SBS1401-792.
4. a kind of waterproof system shown according to claim 1, which is characterized in that powder styrene butadiene rubber is that Shandong Gao Shi section work has The limit company trade mark is the powder styrene butadiene rubber of SBR50%.
5. a kind of waterproof system shown according to claim 1, which is characterized in that tackifying resin is that the lily magnolia chemical industry trade mark is 8005 Tackifying resin.
6. a kind of waterproof system shown according to claim 1, which is characterized in that softening agent steps this for Chengdu and opens up new energy lubrication Materials Co., Ltd's trade mark is the softening agent of 1#.
7. a kind of waterproof system shown according to claim 1, which is characterized in that high temperature modified dose is husky rope (Sasol) Germany High temperature modified dose of Co., Ltd.
8. a kind of waterproof system shown according to claim 1, which is characterized in that talcum powder is that the river river You Hua mining industry partial size is The talcum powder of 200 mesh.
9. a kind of waterproof system shown according to claim 1, which is characterized in that PE reworked material is the prosperous limited public affairs of plastic cement in Chengdu year Department produces.
10. -9 described in any item a kind of preparation methods of waterproof system according to claim 1, which is characterized in that including following Step:
(1) 190 DEG C are heated to by 45-55 parts and 6-10 parts of thermoplastic styrene butadiene rubber of 90# pitch, then sequentially add powder butylbenzene rubber 8-16 parts of glue, 6-10 parts of tackifying resin, 8-12 parts of softening agent, high temperature modified dose 1-4 parts, temperature are maintained at 190 DEG C by 2h's After continuously stirring mixing, it is added talcum powder 10-16 parts, 1h discharging is stirred for, uncured water-repellent paint is made；
(2) by 25-35 parts of 90# pitch, 4-8 parts of softening agent, 3-6 parts of thermoplastic styrene butadiene rubber, 190 DEG C are heated to, to thermoplastic styrene butadiene Rubber completely with pitch after mixing, add 2-4 parts of PE reworked material, keep the temperature 190 DEG C, it is completely molten to PE material after stirring 2h Xie Hou is added talcum powder 30-36 parts, then uniform stirring 1h discharging, prepares 4mm thickness by asphalt felt production equipment SBS modified asphalt waterproof coiled material；
(3) after needing waterproof position to carry out base treatment, uncured water-repellent paint made from squeegeeing step (1), then non- Solidify the modified asphalt waterproof coiled material that on water-repellent paint prepared by paving step (2).
CN201811115994.6A 2018-09-25 2018-09-25 Waterproof system and preparation method thereof Pending CN109320748A (en)