CN109280442A - Excellent color art coatings of a kind of shell coloured silk piece and preparation method thereof - Google Patents

Excellent color art coatings of a kind of shell coloured silk piece and preparation method thereof Download PDF

Info

Publication number
CN109280442A
CN109280442A CN201811095134.0A CN201811095134A CN109280442A CN 109280442 A CN109280442 A CN 109280442A CN 201811095134 A CN201811095134 A CN 201811095134A CN 109280442 A CN109280442 A CN 109280442A
Authority
CN
China
Prior art keywords
parts
coloured silk
agent
silk piece
excellent color
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811095134.0A
Other languages
Chinese (zh)
Inventor
叶文思
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811095134.0A priority Critical patent/CN109280442A/en
Publication of CN109280442A publication Critical patent/CN109280442A/en
Pending legal-status Critical Current

Abstract

The present invention relates to excellent color art coatings of a kind of shell coloured silk piece and preparation method thereof, by weight include water: 20-22.5 parts, preservative: 1-3 parts, lotion: 60-80 parts, defoaming agent: 0.4-0.6 parts, coalescing agent: 2-4 parts, propylene glycol: 1-3 parts, multifunctional assistant: 0.2-0.3 parts, thickener: 0.8-1.2 parts, shell coloured silk piece: 90-110 parts, particle mixed liquor: 750-850 parts.The present invention does not influence public place business without noise by mane bruss brush coating;It and is not in waste caused by shell coloured silk piece largely falls on the ground, when construction is condensed to original three process to greatly simplify process together, is conducive to promote and apply.

Description

Excellent color art coatings of a kind of shell coloured silk piece and preparation method thereof
Technical field
The present invention relates to Material Fields, specially technical field of coatings, relate generally to a kind of excellent color art of shell coloured silk piece and apply Material and preparation method thereof.
Background technique
Art coatings are a kind of novel wall decoration Art materials, have product it is nontoxic, it is environmentally friendly, be provided simultaneously with waterproof, It is dust-proof, the functions such as fire-retardant, and high-quality art coatings can be scrubbed, for a long time often new feature of color, thus by building trade It is widely popularized.Art coatings are brushed on the wall, just as putty, are fused together completely with metope.Therefore, effect It can more natural, fitting;In addition, compared with other finishing materials, art coatings do not have flavescence, colour fading, cracking, blistering, mouldy The problems such as appearance, long service life.
Shell coloured silk piece coating is a kind of thick slurry texture coating of novel environment friendly, using dedicated painting tool, the effect made Fruit natural harmony, color is soft abundant, has excellent waterproofness and weatherability, hides with excellent adhesive force with perfect Gai Li persistently protects color.Moisture-proof sound-absorbing, texture is strong, and expressive force is abundant, can meet want to the three-dimensional art moulding of wall completely It asks.It is widely used in building inner-outer wall, luxurious hotel, garden villa, sculpture, mountain villa, karaoke halls and particular/special requirement moulding Occasion.However, existing coloured silk piece coating antifouling capacity is inadequate, and it is low to the adhesive force of substrate, it is easy to fall off.
In the prior art, a variety of water-water coating, such as Chinese patent document are had studied to increase adhesive force CN108300047A discloses a kind of indoor anti-pollution water-water coating, including protective glue, color-mixed base paint and continuous phase, described Protective glue includes following components: protection rubber powder: 5-25 parts, deionized water: and 75-90 parts, thinner: 0-5 parts, mould inhibitor: 0.1- 4 parts, fungicide: 0.1-3 parts, pH adjusting agent: 0-1 parts;The color-mixed base paint includes following components: deionized water: 45-65 Part, mould inhibitor: 0.1-0.5 parts, dispersing agent: 0.1-1 parts, cellulose: 0.5-1 parts, antifreezing agent: 0.5-1.5 parts, filler: 5-20 Part, defoaming agent: 0.5-1.5 parts, pH adjusting agent: 0.1-0.8 parts, lotion: 15-45 parts, coalescing agent: 0.5-1.5 parts, sterilization Agent: 0.1-1 parts, wetting agent: 0.2-1 parts;Continuous phase includes following components: deionized water: 5.5-15 parts, Nano silica sol: 5- 10 parts, modified cellulose: 1-5 parts, lotion: 70-95 parts, coalescing agent: 3-10 parts, antifreezing agent: 2-10 parts, pH adjusting agent: 0.1-0.5 parts, thickener: 0.1-0.8 parts.And preparation method thereof for black body radiation material research it is very much.However, above-mentioned text In offering, has the effect of shell coloured silk piece to make, can only first brush both sides emulsion paint, then use when emulsion paint does not have completely dry Shell coloured silk piece is sprayed wall by machine, and so not only spraying noise is big, many shell coloured silk pieces can be also lost, due to shell coloured silk piece Metope cannot be bonded to rapidly and fall and in turn result in waste, meanwhile, above method process is more, the not dry upper wall of emulsion paint is taken advantage of, Difficulty is brought to large-area construction.
For construction is inconvenient, three-dimensional sense is not strong, work progress is easy in the excellent color art coatings of shell coloured silk piece in the prior art Wasting problem, need to be invented it is a kind of it is easy for construction, three-dimensional sense is strong, work progress will not wasting shell coloured silk piece it is excellent Color art coatings.
Summary of the invention
Therefore, technical problem to be solved by the present invention lies in technological deficiency in the prior art is overcome, to provide one It is kind easy for construction, three-dimensional sense is strong, work progress will not the excellent color art coatings of wasting shell coloured silk piece.
It by weight include water for this purpose, the present invention provides a kind of shell coloured silk piece excellent color art coatings: 20-22.5 part, prevent Rotten agent: 1-3 parts, lotion: 60-80 parts, defoaming agent: 0.4-0.6 parts, coalescing agent: 2-4 parts, propylene glycol: 1-3 parts, multifunctional assistant Agent: 0.2-0.3 parts, thickener: 0.8-1.2 parts, shell coloured silk piece: 90-110 parts, particle mixed liquor: 750-850 parts.
Preferably, the excellent color art coatings of the shell coloured silk piece, including water: 21.25 parts, preservative: 2 parts, lotion: 70 Part, defoaming agent: 0.5 part, coalescing agent: 3 parts, propylene glycol: 2 parts, multifunctional assistant: 0.25 part, thickener: 1 part, shell coloured silk Piece: 100 parts, particle mixed liquor: 800 parts.
It is preferred that the excellent color art coatings of the shell coloured silk piece, wherein particle mixed liquor include: glue 140-160 parts of protection, Basic colored paint 600-700 parts.
It is preferred that the excellent color art coatings of the shell coloured silk piece, wherein particle mixed liquor includes: 150 parts of glue of protection, basis 650 parts of colored paint.
It is preferred that the excellent color art coatings of the shell coloured silk piece, wherein protection glue includes 900-1000 parts of water, preservative 1-3 Part, rubber powder 45-50 parts of protection, preferably 950 parts of water, 2 parts of preservative, 48 parts of rubber powder of protection.
It is preferred that the excellent color art coatings of the shell coloured silk piece, wherein basic colored paint includes water: 600-650 parts, cellulose: 1- 3 parts, defoaming agent: 4-6 parts, dispersing agent: 1-3 parts, preservative: 1-3 parts, forming agent: 28-32 parts, multifunctional assistant: 6-8 parts, at Film auxiliary agent: 6-8 parts, propylene glycol: 4-6 parts, lotion: 120-140 parts, pearl powder: 180-200 parts.
It is preferred that the excellent color art coatings of the shell coloured silk piece, wherein basic colored paint includes water: 620 parts, cellulose: 2 parts, disappear Infusion: 5 parts, dispersing agent: 2 parts, preservative: 2 parts, forming agent: 30 parts, AMP95:7 parts, coalescing agent: 7 parts, propylene glycol: 5 Part, lotion: 130 parts, pearl powder: 190 parts.
It is preferred that the excellent color art coatings of the shell coloured silk piece, wherein cellulose is hydroxyethyl cellulose HEC;Preservative is card Pine;Lotion is silicone acrylic emulsion;Defoaming agent is mineral oil antifoam agent;Coalescing agent is alcohol ester 12;Multifunctional assistant is AMP95; Thickener is ASE-60.
The present invention also provides the preparation methods of the excellent color art coatings of the shell coloured silk piece, by protection glue raw material to turn Fast 1500r/min is stirred evenly, and basic colored paint raw material high speed (usual 1800r/min) is dispersed 20-30min, reaches viscosity 130KU or more, it is spare;Glue and basic colored paint mixing granulation will be protected to obtain particle mixed liquor with three leaf dispersion impellers or pelletizer; The excellent color art coatings raw material low speed of shell coloured silk piece is dispersed into (usual 200r/min) 20-30min, reaches viscosity 130KU or more i.e. ?.
The present invention also provides the applications of the excellent color art coatings of the shell coloured silk piece, are mainly used for building external paint, water The a variety of materials surface such as mud wall face, stainless steel, metal aluminum sheet, plastic cement, glass, ceramic tile, EPS sheet, FRP, GRC.When construction, First to white primer on metope or it is tuned into shell coloured silk piece similar color priming paint.After parching, coloured silk excellent to shell is tempered into right amount Facilitate construction concentration, is slightly flattened when half-dried with special plastic scraper plate with wall in mane bruss crossing method mopping.Thoroughly Parch rear upper cover smooth surface oil, completion.
Shell coloured silk piece of the present invention excellent color art coatings are not influenced public by mane bruss brush without noise when constructing Place business;Simultaneously be not in the waste largely fallen on the ground, original three process is condensed to together, to simplify process. After previous excellent color art coatings construction, there are many blank spaces between color tablets and color tablets, the present invention is filled in the blanks place with shell coloured silk piece, It improves excellent color class and enriches color, effective upgrading has been carried out to excellent coloured silk.
In conclusion the excellent color art coatings of shell coloured silk piece of the present invention are mainly granulated by protection glue and basic colored paint, Particle mixed liquor is obtained, then makes shell coloured silk piece with paint.Coloured silk art coatings excellent to shell coloured silk piece of the present invention carry out performance detection, warp Its visible antifouling capacity and relatively strong for the adhesive force of substrate is detected, is easy to the advantages of constructing in addition, is suitble to be widely popularized and answer With.
Detailed description of the invention
With reference to the accompanying drawing, the content of the present invention will be explained in more detail.It should be appreciated that implementation of the invention is not limited to Following attached drawing, the accommodation in any form and/or change made to the present invention fall within the scope of the present invention.
Fig. 1 shows the art coatings effect after increasing color piece.
Fig. 2 shows the art coatings effect of the embodiment 1 after increasing color piece.
Specific embodiment
Below with reference to embodiment, the content of the present invention will be explained in more detail.It should be appreciated that implementation of the invention is not limited to In the following examples, the accommodation in any form and/or change made to the present invention fall within the scope of the present invention.
In the present invention, if not refering in particular to, all parts, percentage are unit of weight, and all equipment and raw material etc. are equal It is commercially available or the industry is common.Method in following embodiments is unless otherwise instructed the routine of this field Method.
Embodiment 1
Protective glue production: 950 parts of water, 2 parts of Kathon CG, 48 parts of rubber powder of protection add up to 1000 parts, equal with the stirring of 1500 revolving speeds It is even.
The production of basic colored paint: 620 parts of water, 2 parts of hydroxyethyl cellulose, 5 parts of defoaming agent, 2 parts of dispersing agent, 2 parts of Kathon CG, at 30 parts of type agent, 7 parts of AMP95,12 parts of alcohol ester, 5 parts of propylene glycol, 130 parts of Ahmedabad Silicon-rich acrylic emulsion, 190 parts of pearl powder close Meter: 1000 parts, high speed 1800r/min dispersion 20-30 minutes spare, reaches viscosity 130KU or more.
Make color tablets i.e. particle mixed liquor: 150 parts of glue of protection, basic 650 parts of colored paint add up to 800 parts, with three leaf dispersion impellers Or pelletizer is granulated.
Shell coloured silk piece is with paint: 19 parts of water, 2 parts of Kathon CG, 70 parts of Ahmedabad Silicon-rich acrylic emulsion, 0.5 part of defoaming agent, alcohol ester 12 Part, 2 parts of propylene glycol, AMP950.25 parts, 1 part of ASE-60,2.25 parts of water (reconciliation thickener ASE-60 use), shell coloured silk piece 90 Part, 10 parts of pearl powder, 800 parts of particle mixed liquor add up to 1000 parts, and low speed 200r/min mixing, viscosity is in 130KU or more.
Embodiment 2
Protective glue production: 973 parts of water, 2 parts of Kathon CG, 25 parts of rubber powder of protection add up to 1000 parts, equal with the stirring of 1500 revolving speeds It is even.
The production of basic colored paint: 600 parts of water, 2 parts of hydroxyethyl cellulose, 4 parts of defoaming agent, 2 parts of dispersing agent, 2 parts of Kathon CG, at 32 parts of type agent, 6 parts of AMP95,12 parts of alcohol ester, 5 parts of propylene glycol, 140 parts of Ahmedabad Silicon-rich acrylic emulsion, 200 parts of pearl powder close Meter: 1000 parts, high speed 1800r/min dispersion 20-30 minutes spare, reaches viscosity 130KU or more.
Make color tablets i.e. particle mixed liquor: 150 parts of glue of protection, basic 650 parts of colored paint add up to 800 parts, with three leaf dispersion impellers Or pelletizer is granulated.
Shell coloured silk piece is with paint: 19 parts of water, 2.5 parts of Kathon CG, 70 parts of Ahmedabad Silicon-rich acrylic emulsion, 0.5 part of defoaming agent, alcohol ester ten 2 2.5 parts, 2 parts of propylene glycol, 0.25 part of AMP95,1 part of ASE-60,2.25 parts of water (reconciliation thickener ASE-60 use), shell 90 parts of color piece, 10 parts of pearl powder, 800 parts of particle mixed liquor add up to 1000 parts, and low speed 200r/min mixing, viscosity is in 130KU More than.
Comparative example 1
Protective glue production: 950 parts of water, 2 parts of Kathon CG, 48 parts of rubber powder of protection add up to 1000 parts, equal with the stirring of 1500 revolving speeds It is even.
The production of basic colored paint: 620 parts of water, 2 parts of hydroxyethyl cellulose, 5 parts of defoaming agent, 2 parts of dispersing agent, 2 parts of Kathon CG, at 30 parts of type agent, 7 parts of AMP95,12 parts of alcohol ester, 5 parts of propylene glycol, 130 parts of Ahmedabad Silicon-rich acrylic emulsion, 100 parts of titanium dioxide, kaolinite 90 parts of soil adds up to: 1000 parts, high speed 1800r/min dispersion 20-30 minutes spare, reaches viscosity 130KU or more.
Make color tablets i.e. particle mixed liquor: 150 parts of glue of protection, basic 650 parts of colored paint add up to 800 parts, with three leaf dispersion impellers Or pelletizer is granulated.
Shell coloured silk piece is with paint: 19 parts of water, 2 parts of Kathon CG, 70 parts of Ahmedabad Silicon-rich acrylic emulsion, 0.5 part of defoaming agent, alcohol ester 12 Part, 2 parts of propylene glycol, AMP950.25 parts, 1 part of ASE-60,2.25 parts of water (reconciliation thickener ASE-60 use), shell coloured silk piece 90 Part, 10 parts of titanium dioxide, 800 parts of particle mixed liquor add up to 1000 parts, and low speed 200r/min mixing, viscosity is in 130KU or more.
Comparative example 2
A kind of indoor anti-pollution water-water preparation method for coating referring to disclosed in CN108300047A prepares coating, middle part Point raw material selected from type consistent in the application, cellulose is hydroxyethyl cellulose HEC;Mould inhibitor is Kathon CG;Lotion is bar Moral Silicon-rich acrylic emulsion, thickener ASE-60;Coalescing agent is alcohol ester 12;The raw material not occurred in remaining the application is all made of Common raw material in this field, while shell coloured silk piece is added.Including protective glue, color-mixed base paint and continuous phase, the protective glue packet Include following components: protection rubber powder: 20 parts, deionized water: 75 parts, thinner: 3 parts, mould inhibitor: 1 part, fungicide: 0.5 part, pH Regulator: 0.5 part;The color-mixed base paint includes following components: deionized water: 52 parts, mould inhibitor: and 0.5 part, dispersing agent: 1 Part, cellulose: 1 part, antifreezing agent: 0.5 part, filler: 15 parts, defoaming agent: 1 part, pH adjusting agent: 0.5 part, lotion: 25 parts, film forming Auxiliary agent: 1.5 parts, fungicide: 0.5 part, wetting agent: 1.5 parts;The continuous phase includes following components: deionized water: 7 parts, being received Rice silica solution: 5 parts, modified cellulose: 5 parts, lotion: 70 parts, coalescing agent: 5 parts, antifreezing agent: 7 parts, pH adjusting agent: 0.3 part, Thickener: 0.2 part, 10 parts of shell coloured silk piece.
According to the coating of embodiment 1-2 and comparative example 1-2, the design parameter of coating is measured, as shown by the following table 1.
Table 1,1 coating anti-pollution parameter of comparative example and steadiness parameter
Embodiment 1 Embodiment 2 Comparative example 1 Comparative example 2
Stain resistant 0 0 ≥2 ≥5
Pollution level It is pollution-free It is pollution-free Slightly pollute There is pollution
Perception color difference No color differnece No color differnece More apparent color difference More apparent color difference
Gray card grade 5 5 3 3
VOC ≤8 ≤8 130 190
Adhesive force grade ≤1 ≤1 3 5
Hot 55 DEG C of storages stability test in 30 days Pass through Pass through Thickening Thickening
Normal temperature storage stability test in 30 days Pass through Pass through Micro- thickening Thickening is obvious
Compared by each coating parameter it is found that the adhesive strength of embodiment 1-2 coating is apparently higher than the painting in comparative example 1-2 Material, and the stain resistant of embodiment 1-2 coating is substantially better than the stain resistant of the coating in comparative example 1-2, embodiment 1-2 coating Stability at the beginning of the test of coating steady heat storage and normal temperature storage stability test performance is also significantly better than the coating in comparative example 1-2 Stability.Importantly, the coating of embodiment 1-2 can be directly brushed through mane bruss to wall or other matrixes, it will not Generate waste caused by separately brushing in comparative example.
Compared with prior art, the beneficial effects of the present invention are: coating stain resistance of the present invention is good, adhesive force is high, simultaneously Property is stablized, and fills blank space between color tablets and color tablets with shell coloured silk piece, improves excellent color class and enriches color, to excellent coloured silk Effective upgrading is carried out.
Obviously, the specific type used in above-described embodiment is only intended to clearly illustrate example, and is not pair The restriction of embodiment.For those of ordinary skill in the art, it can also be made on the basis of the above description Its various forms of variation or variation.There is no necessity and possibility to exhaust all the enbodiments.And it thus extends out Obvious changes or variations it is still within the protection scope of the invention.

Claims (10)

1. a kind of excellent color art coatings of shell coloured silk piece, include by weight
Water: 20-22.5 parts, preservative: 1-3 parts, lotion: 60-80 parts, defoaming agent: 0.4-0.6 parts, coalescing agent: 2-4 parts, third Glycol: 1-3 parts, multifunctional assistant: 0.2-0.3 parts, thickener: 0.8-1.2 parts, shell coloured silk piece: 90-110 parts, particle mixing Liquid: 750-850 parts.
2. the excellent color art coatings of shell coloured silk piece according to claim 1, including
Water: 21.25 parts, preservative: 2 parts, lotion: 70 parts, defoaming agent: 0.5 part, coalescing agent: 3 parts, propylene glycol: 2 parts, more function Energy auxiliary agent: 0.25 part, thickener: 1 part, shell coloured silk piece: 100 parts, particle mixed liquor: 800 parts.
3. the excellent color art coatings of -2 described in any item shell coloured silk pieces according to claim 1, wherein particle mixed liquor includes: protection 140-160 parts of glue, basic 600-700 parts of colored paint.
4. the excellent color art coatings of shell coloured silk piece according to claim 1-3, wherein particle mixed liquor includes: protection 150 parts of glue, basic 650 parts of colored paint.
5. the excellent color art coatings of shell coloured silk piece according to claim 1-4, wherein protection glue includes water 900- 1000 parts, 1-3 parts of preservative, rubber powder 45-50 parts of protection, preferably 950 parts of water, 2 parts of preservative, 48 parts of rubber powder of protection.
6. the excellent color art coatings of shell coloured silk piece according to claim 1-5, wherein basic colored paint includes water: 600- 650 parts, cellulose: 1-3 parts, defoaming agent: 4-6 parts, dispersing agent: 1-3 parts, preservative: 1-3 parts, forming agent: 28-32 parts, more function Energy auxiliary agent: 6-8 parts, coalescing agent: 6-8 parts, propylene glycol: 4-6 parts, lotion: 120-140 parts, pearl powder: 180-200 parts.
7. the excellent color art coatings of shell coloured silk piece according to claim 1-5, wherein basic colored paint includes water: 620 Part, cellulose: 2 parts, defoaming agent: 5 parts, dispersing agent: 2 parts, preservative: 2 parts, forming agent: 30 parts, AMP95:7 part, form a film help Agent: 7 parts, propylene glycol: 5 parts, lotion: 130 parts, pearl powder: 190 parts.
8. the excellent color art coatings of shell coloured silk piece according to claim 1-7, wherein cellulose is hydroxy ethyl fiber Plain HEC;Preservative is Kathon CG;Lotion is silicone acrylic emulsion;Defoaming agent is mineral oil antifoam agent;Coalescing agent is alcohol ester 12;It is more Function additive is AMP95;Thickener is ASE-60.
9. the preparation method of the excellent color art coatings of shell coloured silk piece according to claim 1-7, former by protection glue Material is stirred evenly with revolving speed 1500r/min, by basic colored paint raw material high speed dispersion 20-30min, reaches viscosity 130KU or more, standby With;Glue and basic colored paint mixing granulation will be protected to obtain particle mixed liquor with three leaf dispersion impellers or pelletizer;Shell coloured silk piece is excellent Color art coatings raw material low speed disperses 20-30min, reaches viscosity 130KU or more to obtain the final product.
10. the application of the excellent color art coatings of any one of -9 shell coloured silk pieces according to claim 1, which is characterized in that for building The a variety of materials table such as exterior coating, cement wall surface, stainless steel, metal aluminum sheet, plastic cement, glass, ceramic tile, EPS sheet, FRP, GRC Face.
CN201811095134.0A 2018-09-19 2018-09-19 Excellent color art coatings of a kind of shell coloured silk piece and preparation method thereof Pending CN109280442A (en)