CN109267335A - A kind of production method of the fabric with the differential function in front and back sides - Google Patents
A kind of production method of the fabric with the differential function in front and back sides Download PDFInfo
- Publication number
- CN109267335A CN109267335A CN201811012852.7A CN201811012852A CN109267335A CN 109267335 A CN109267335 A CN 109267335A CN 201811012852 A CN201811012852 A CN 201811012852A CN 109267335 A CN109267335 A CN 109267335A
- Authority
- CN
- China
- Prior art keywords
- fabric
- parts
- sub
- drying
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to fabric printing technical fields, disclose a kind of production method of fabric with the differential function in front and back sides, include the following steps: A, dyeing and printing process fabric, obtain fabric color embryo；B, after handling the one side of the fabric color embryo with the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine, a sub-band liquid fabric is obtained；C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；D, the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric is obtained into two sub-band liquid fabrics after being handled on intaglio press or gravure printing machine with hydrophilic absorptive work liquid；E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.The present invention has the characteristics that low manufacture cost, simple using equipment, thickener, fabric front and back sides functional effect are good without adding.
Description
Technical field
The invention belongs to fabric printing technical fields, and in particular to a kind of fabric with the differential function in front and back sides
Production method.
Background technique
The production technology of existing fabric has following defects that 1, using cylinder or Flat screen printing method, is knitting respectively
The front of object stamps waterproofing agent to reach the function of waterproof water repellent.Hydrophilic agent is stamped in the reverse side of fabric to reach hydrophilic moisture absorption
Function.The significant deficiency of the technology is: must be added to thickener so that waterproofing agent or hydrophilic agent can become the slurry of printability.
And the addition of thickener can allow waterproof or hydrophilic effect to be significantly damaged, or even 50% effect is all unable to reach.Therefore,
This method is unable to get the unidirectional moisture conducting function fabric of high quality.
2, using the method for spray (spraying), reach the function of waterproof water repellent in the front spray waterproofing agent of fabric respectively
Energy.Reach the function of hydrophilic moisture absorption in the reverse side spray hydrophilic agent of fabric.The significant deficiency of the technology is: spraying apparatus can not
Obtain uniform fog partial size to get must not the very consistent droplet of size, then large-sized fog will penetrate into fabric
Another side.Therefore, this method is unable to get the unidirectional moisture conducting function fabric of high quality.
Summary of the invention
In order to solve the above problems existing in the present technology, it is an object of that present invention to provide one kind to have front and back sides differential
The production method of the fabric of function.
The technical scheme adopted by the invention is as follows:
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
Agent 1-30 parts, 0-5 parts of wetting agent, 0-3 parts of defoaming agent, 0-5 parts of crosslinking agent, 90-100 parts of water of reason.
Further, hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: hydrophilic finishing agent
1-30 parts, 0-5 parts of wetting agent, 0-3 parts of defoaming agent, 0-5 parts of crosslinking agent, 90-100 parts of water.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is -200 line of 60 line,
Penetration depth of the antifouling working solution of waterproof and oilproof on fabric color embryo is no more than the half of fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is -200 line of 60 line,
Penetration depth of the hydrophilic absorptive work liquid on single side processing fabric is no more than two points of single side processing fabric thickness
One of.
Further, the temperature of the drying of the step C is 140 DEG C -160 DEG C, drying time 1-5min.
Further, the temperature of the drying of the step E is 140 DEG C -160 DEG C, drying time 1-5min.
The invention has the benefit that a kind of producer of fabric with the differential function in front and back sides of the invention
Method, the equipment of use is simple, it is at low cost, realize two-sided processing to fabric；Pass through the use to each single side of fabric
Working solution penetration depth control on the fabric, and the accurate adjustment by matching to working solution, the present invention realize nothing
The differential function fabric fabric in front and back sides of high-quality is made in the auxiliary agent that additional thickener etc must be added, so as to avoid existing
There is defect present in technology, while production method is simple, is easy to implement industrialized production.
Specific embodiment
Further explaination is done to the present invention combined with specific embodiments below.
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
The present invention is by the line number of selection anilox roll and by controlling working solution to liquid speed control working solution in fabric side
Penetration degree on material, by the cooperation of line number and penetration degree so that, the working solution infiltration of the every one side of fabric uniformly, from
And the front and back sides of fabric is made to maintain the differential function of high-quality.At intaglio press (or gravure printing machine)
On, the specification of anilox roll is selected, depending on fabric specification, in order to which working solution is controlled to liquid measure to control working solution in fabric
On penetration depth subject to.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
Agent 1-30 parts, 0-5 parts of wetting agent, 0-3 parts of defoaming agent, 0-5 parts of crosslinking agent, 90-100 parts of water of reason.
The preparation of the antifouling working solution of waterproof and oilproof, which only needs in a conventional manner to mix above-mentioned several components, can be used.
Further, hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: hydrophilic finishing agent
1-30 parts, 0-5 parts of wetting agent, 0-3 parts of defoaming agent, 0-5 parts of crosslinking agent, 90-100 parts of water.
The preparation of hydrophilic absorptive work liquid, which only needs in a conventional manner to mix above-mentioned several components, can be used.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is -200 line of 60 line,
Penetration depth of the antifouling working solution of waterproof and oilproof on fabric color embryo is no more than the half of fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is -200 line of 60 line,
Penetration depth of the hydrophilic absorptive work liquid on single side processing fabric is no more than two points of single side processing fabric thickness
One of.
Further, the temperature of the drying of the step C is 140 DEG C -160 DEG C, drying time 1-5min.
Further, the temperature of the drying of the step E is 140 DEG C -160 DEG C, drying time 1-5min.
Embodiment 1
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；The specification of the anilox roll of the intaglio press or gravure printing machine of the step B is 60
Line, penetration depth of the antifouling working solution of waterproof and oilproof on fabric color embryo are no more than the half of fabric color flake thickness degree.Step B
The antifouling working solution of the waterproof and oilproof is grouped as by the group of following parts by weight: 1 part of three-proof finishing agent, 90 parts of water.
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
The temperature of the drying of the step C is 140 DEG C, drying time 1min.
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
The specification of the anilox roll of the intaglio press or gravure printing machine of the step D is 60 lines, hydrophilic absorptive work liquid
Penetration depth on single side processing fabric is no more than the half of single side processing fabric thickness.Described in step D
Hydrophilic absorptive work liquid be grouped as by the group of following parts by weight: 1 part of hydrophilic finishing agent, 90 parts of water.
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
The temperature of the drying of the step E is 140 DEG C, drying time 1min.
Embodiment 2
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
30 parts of agent, 100 parts of water of reason.
Hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: 30 parts of hydrophilic finishing agent, water
100 parts.
The specification of the anilox roll of the intaglio press or gravure printing machine of the step B is 200 lines, the antifouling work of waterproof and oilproof
Make the half that penetration depth of the liquid on fabric color embryo is no more than fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is 200 lines, hydrophilic
Penetration depth of the absorptive work liquid on single side processing fabric is no more than the half of single side processing fabric thickness.
Further, the temperature of the drying of the step C is 160 DEG C, drying time 5min.
Further, the temperature of the drying of the step E is 160 DEG C, drying time 5min.
Embodiment 3
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
15 parts of agent, 95 parts of water of reason.
Further, hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: hydrophilic finishing agent
15 parts, 92 parts of water.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is 100 lines, waterproof
Penetration depth of the grease proofing antifouling working solution on fabric color embryo is no more than the half of fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is 100 lines, hydrophilic
Penetration depth of the absorptive work liquid on single side processing fabric is no more than the half of single side processing fabric thickness.
Further, the temperature of the drying of the step C is 150 DEG C, drying time 2min.
Further, the temperature of the drying of the step E is 150 DEG C, drying time 2min.
Embodiment 4
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
1 part of agent, 1 part of wetting agent, 1 part of defoaming agent, 1 part of crosslinking agent, 93 parts of water of reason.
Further, hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: hydrophilic finishing agent
1 part, 1 part of wetting agent, 1 part of defoaming agent, 1 part of crosslinking agent, 92 parts of water.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is 80 lines, and waterproof is anti-
Penetration depth of the antifouling working solution of oil on fabric color embryo is no more than the half of fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is 80 lines, hydrophilic suction
Penetration depth of the wet working solution on single side processing fabric is no more than the half of single side processing fabric thickness.
Further, the temperature of the drying of the step C is 145 DEG C, drying time 3min.
Further, the temperature of the drying of the step E is 145 DEG C, drying time 3min.
Embodiment 5
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
15 parts of agent, 3 parts of wetting agent, 2 parts of defoaming agent, 2 parts of crosslinking agent, 94 parts of water of reason.
Further, hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: hydrophilic finishing agent
13 parts, 3 parts of wetting agent, 2 parts of defoaming agent, 3 parts of crosslinking agent, 95 parts of water.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is 110 lines, waterproof
Penetration depth of the grease proofing antifouling working solution on fabric color embryo is no more than the half of fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is 110 lines, hydrophilic
Penetration depth of the absorptive work liquid on single side processing fabric is no more than the half of single side processing fabric thickness.
Further, the temperature of the drying of the step C is 155 DEG C, drying time 4min.
Further, the temperature of the drying of the step E is 155 DEG C, drying time 4min.
Embodiment 6
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
20 parts of agent, 4 parts of wetting agent, 3 parts of defoaming agent, 5 parts of crosslinking agent, 92 parts of water of reason.
Further, hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: hydrophilic finishing agent
20 parts, 3 parts of wetting agent, 2 parts of defoaming agent, 3 parts of crosslinking agent, 94 parts of water.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is 160 lines, waterproof
Penetration depth of the grease proofing antifouling working solution on fabric color embryo is no more than the half of fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is 160 lines, hydrophilic
Penetration depth of the absorptive work liquid on single side processing fabric is no more than the half of single side processing fabric thickness.
Further, the temperature of the drying of the step C is 153 DEG C, drying time 4min.
Further, the temperature of the drying of the step E is 155 DEG C, drying time 3min.
Embodiment 7
A kind of production method of the fabric with the differential function in front and back sides, includes the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is used to the antifouling working solution of waterproof and oilproof on intaglio press or gravure printing machine
After processing, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the one side without the antifouling working solution processing of waterproof and oilproof of the single-side fabric fabric, in intaglio press
Or after being handled on gravure printing machine with hydrophilic absorptive work liquid, obtain two sub-band liquid fabrics；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
Further, the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: three proofings are whole
30 parts of agent, 5 parts of wetting agent, 3 parts of defoaming agent, 5 parts of crosslinking agent, 100 parts of water of reason.
Further, hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: hydrophilic finishing agent
30 parts, 5 parts of wetting agent, 3 parts of defoaming agent, 5 parts of crosslinking agent, 100 parts of water.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is 140 lines, waterproof
Penetration depth of the grease proofing antifouling working solution on fabric color embryo is no more than the half of fabric color flake thickness degree.
Further, the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is 140 lines, hydrophilic
Penetration depth of the absorptive work liquid on single side processing fabric is no more than the half of single side processing fabric thickness.
Further, the temperature of the drying of the step C is 151 DEG C, drying time 3min.
Further, the temperature of the drying of the step E is 151 DEG C, drying time 3min.
The present invention is not limited to above-mentioned optional embodiment, anyone can show that other are each under the inspiration of the present invention
The product of kind form.Above-mentioned specific embodiment should not be understood the limitation of pairs of protection scope of the present invention, protection of the invention
Range should be subject to be defined in claims, and specification can be used for interpreting the claims.
Claims (7)
1. a kind of production method of the fabric with the differential function in front and back sides, characterized by the following steps:
A, dyeing and printing process fabric obtains fabric color embryo；
B, the one side of the fabric color embryo is handled on intaglio press or gravure printing machine with the antifouling working solution of waterproof and oilproof
Afterwards, a sub-band liquid fabric is obtained；
C, single side processing fabric will after the sub-band liquid fabric drying, be obtained；
D, by the single-side fabric fabric without the one side of the antifouling working solution processing of waterproof and oilproof, in intaglio press or recessed
After being handled on version printing machine with hydrophilic absorptive work liquid, two sub-band liquid fabrics are obtained；
E, by after the two sub-band liquid fabric drying, double treatment fabric is obtained.
2. a kind of production method of fabric with the differential function in front and back sides according to claim 1, feature
Be: the antifouling working solution of waterproof and oilproof described in step B is grouped as by the group of following parts by weight: 1-30 parts of three-proof finishing agent,
0-5 parts of wetting agent, 0-3 parts of defoaming agent, 0-5 parts of crosslinking agent, 90-100 parts of water.
3. a kind of production method of fabric with the differential function in front and back sides according to claim 2, feature
Be: hydrophilic absorptive work liquid described in step D is grouped as by the group of following parts by weight: 1-30 parts of hydrophilic finishing agent, wetting
0-5 parts of agent, 0-3 parts of defoaming agent, 0-5 parts of crosslinking agent, 90-100 parts of water.
4. a kind of production method of fabric with the differential function in front and back sides according to claim 3, feature
Be: the specification of the anilox roll of the intaglio press or gravure printing machine of the step B is -200 line of 60 line, and waterproof and oilproof is antifouling
Penetration depth of the working solution on fabric color embryo is no more than the half of fabric color flake thickness degree.
5. a kind of production method of fabric with the differential function in front and back sides according to claim 4, feature
Be: the specification of the anilox roll of the intaglio press or gravure printing machine of the step D is -200 line of 60 line, hydrophilic absorptive work
Penetration depth of the liquid on single side processing fabric is no more than the half of single side processing fabric thickness.
6. a kind of production method of fabric with the differential function in front and back sides according to claim 5, feature
Be: the temperature of the drying of the step C is 140 DEG C -160 DEG C, drying time 1-5min.
7. a kind of production method of fabric with the differential function in front and back sides according to claim 6, feature
Be: the temperature of the drying of the step E is 140 DEG C -160 DEG C, drying time 1-5min.