CN109252417A - A kind of corrugation paper pulp and preparation method thereof with fire resistance characteristic - Google Patents
A kind of corrugation paper pulp and preparation method thereof with fire resistance characteristic Download PDFInfo
- Publication number
- CN109252417A CN109252417A CN201810983324.XA CN201810983324A CN109252417A CN 109252417 A CN109252417 A CN 109252417A CN 201810983324 A CN201810983324 A CN 201810983324A CN 109252417 A CN109252417 A CN 109252417A
- Authority
- CN
- China
- Prior art keywords
- parts
- paper pulp
- added
- blender
- pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of corrugation paper pulp and preparation method thereof with fire resistance characteristic, it in parts by weight include following components, 40-60 parts of wood pulp, cornstarch 10-15,5-15 parts of Lauxite, 10-20 parts of melamine resin, 5-10 parts of inorganic ceramic fiber, 3-8 parts of guar gum, 2-7 parts of bentonite and 2-5 parts of higher fatty acids sodium；The production method of the corrugation paper pulp are as follows: Lauxite, melamine resin and higher fatty acids sodium are heated to molten condition, is added in blender and is stirred；Inorganic ceramic fiber, guar gum and bentonite are added in the blender of a step to continue to stir；Wood pulp and cornstarch are added in blender, continue to stir；Mixture after stirring is taken out, die for molding is put into, obtains corrugated board.Operation of the present invention simple process, pulp beating performance is good, and the preparation of waterproof paper pulp is that waterproof material is directly added in paper pulp process, forms waterproofing slurry, simplifies process, further reduce costs.
Description
Technical field
The invention belongs to pulp technology for making paper, are in particular a kind of environment-friendly paper pulp with fire resistance characteristic and its production
Method.
Background technique
Corrugated case is a kind of most widely used packing articles, and dosage is always first of various packing articles.Generation more than half
Since discipline, corrugated case, which has gradually replaced the transportation and packing such as wooden case with its superior service performance and good processing performance, to be held
Device becomes the main force of transportation and packing.The waterproof and dampproof property of corrugated case is poor, is always the defect enduring market to the fullest extent and denouncing.Especially
It is that the cold chains such as chilled meat, fruits and vegetables, medicine packaging market scale is increasing in recent years, corrugation packaging industry urgent need fundamentally solves
After packed in cases of having determined dampness the problem of easy crush.
Summary of the invention
In view of the problems of the above-mentioned prior art, the purpose of the present invention is to propose to a kind of corrugated papers with fire resistance characteristic
Slurry and preparation method thereof.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of corrugation paper pulp with fire resistance characteristic, includes following components in parts by weight, and 40-60 parts of wood pulp, corn form sediment
Powder 10-15,5-15 parts of Lauxite, 10-20 parts of melamine resin, 5-10 parts of inorganic ceramic fiber, guar gum 3-8
Part, 2-7 parts of bentonite and 2-5 parts of higher fatty acids sodium.
Preferably, the corrugation paper pulp parts by weights number includes following components, 45 parts of wood pulp, cornstarch 12, ureaformaldehyde
11 parts of resin, 12 parts of melamine resin, 6 parts of inorganic ceramic fiber, 4 parts of guar gum, 5 parts of bentonite and higher aliphatic
5 parts of sour sodium.
Preferably, the production method of the corrugation paper pulp are as follows:
A: Lauxite, melamine resin and higher fatty acids sodium are heated to molten condition, are added to stirring
It is stirred in machine with the speed of 400-600r/min, mixing time 10-15min；
B: inorganic ceramic fiber, guar gum and bentonite is added in the blender of a step and continues to stir, keeps
Temperature is 50-70 DEG C, mixing speed 500-800r/min, mixing time 20-30min；
C: wood pulp and cornstarch are added in blender, continue to stir, temperature is maintained at 40-50 DEG C, mixing speed
For 800-1000r/min, mixing time 20-30min；
D: the mixture after stirring is taken out, die for molding is put into, obtains corrugated board.
Compared with prior art, beneficial effects of the present invention are as follows: operation of the present invention simple process, raw material pulping performance
Good, obtained pulp quality is good, and pulping yield is high, and fibrous binding force is high, provides excellent paper pulp raw material for production corrugated paper；And
And in the present invention waterproof paper pulp preparation method, be directly in paper pulp process addition Lauxite, melamino-formaldehyde
Resin waterproof material forms waterproofing slurry, can simplify process to avoid increasing by a procedure when processing carton more,
It further reduces costs.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
The example for closing specific embodiment is described in further details the present invention.
Embodiment one
A kind of corrugation paper pulp with fire resistance characteristic includes following components, 47 parts of wood pulp, cornstarch in parts by weight
12,11 parts of Lauxite, 14 parts of melamine resin, 6 parts of inorganic ceramic fiber, 4 parts of guar gum, 3 parts of bentonite and
3 parts of higher fatty acids sodium.
In the above-mentioned technical solutions, the production method of the corrugation paper pulp are as follows:
A: Lauxite, melamine resin and higher fatty acids sodium are heated to molten condition, are added to stirring
It is stirred in machine with the speed of 600r/min, mixing time 15min；
B: inorganic ceramic fiber, guar gum and bentonite is added in the blender of a step and continues to stir, keeps
Temperature is 50-70 DEG C, mixing speed 800r/min, mixing time 30min；
C: wood pulp and cornstarch are added in blender, continue to stir, temperature is maintained at 40-50 DEG C, mixing speed
For 800r/min, mixing time 25min；
D: the mixture after stirring is taken out, die for molding is put into, obtains corrugated board.
Embodiment two
A kind of corrugation paper pulp with fire resistance characteristic includes following components, 45 parts of wood pulp, cornstarch in parts by weight
12,11 parts of Lauxite, 12 parts of melamine resin, 6 parts of inorganic ceramic fiber, 4 parts of guar gum, 5 parts of bentonite and
5 parts of higher fatty acids sodium.
Preferably, the production method of the corrugation paper pulp are as follows:
A: Lauxite, melamine resin and higher fatty acids sodium are heated to molten condition, are added to stirring
It is stirred in machine with the speed of 500r/min, mixing time 10min；
B: inorganic ceramic fiber, guar gum and bentonite is added in the blender of a step and continues to stir, keeps
Temperature is 50-70 DEG C, mixing speed 500r/min, mixing time 20min；
C: wood pulp and cornstarch are added in blender, continue to stir, temperature is maintained at 40-50 DEG C, mixing speed
For 800r/min, mixing time 20-30min；
D: the mixture after stirring is taken out, die for molding is put into, obtains corrugated board.
Obviously, various changes and modifications can be made to the invention without departing from essence of the invention by those skilled in the art
Mind and range.In this way, if these modifications and changes of the present invention belongs to the range of the claims in the present invention and its equivalent technologies
Within, then the present invention is also intended to include these modifications and variations.
Although the present invention and its advantage has been described in detail it should be appreciated that without departing from by the attached claims
Defined by can carry out various changes, substitution and transformation in the case where the spirit and scope of the present invention.Moreover, the model of the application
Enclose the specific embodiment for being not limited only to process, equipment described in specification, means, method and steps.In the art is common
Technical staff is from the disclosure it will be readily understood that execution and corresponding reality described herein can be used according to the present invention
Apply the essentially identical function of example or process that obtain the result essentially identical with it, that existing and future is to be developed, equipment,
Means, method or step.Therefore, the attached claims are intended in the range of them include such process, equipment, hand
Section, method or step.
Claims (3)
1. a kind of corrugation paper pulp with fire resistance characteristic, it is characterised in that: in parts by weight include following components, wood pulp 40-60
Part, cornstarch 10-15,5-15 parts of Lauxite, 10-20 parts of melamine resin, 5-10 parts of inorganic ceramic fiber, melon
3-8 parts of bean gum of that, 2-7 parts of bentonite and 2-5 parts of higher fatty acids sodium.
2. a kind of corrugation paper pulp with fire resistance characteristic according to claim 1, it is characterised in that: the corrugation paper pulp
Score by weight includes following components, 45 parts of wood pulp, cornstarch 12,11 parts of Lauxite, 12 parts of melamine resin,
6 parts of inorganic ceramic fiber, 4 parts of guar gum, 5 parts of bentonite and 5 parts of higher fatty acids sodium.
3. a kind of corrugation paper pulp with fire resistance characteristic according to claim 1, it is characterised in that: the corrugation paper pulp
Production method are as follows:
A: Lauxite, melamine resin and higher fatty acids sodium are heated to molten condition, are added in blender
It is stirred with the speed of 400-600r/min, mixing time 10-15min；
B: inorganic ceramic fiber, guar gum and bentonite is added in the blender of a step and continues to stir, keeps temperature
It is 50-70 DEG C, mixing speed 500-800r/min, mixing time 20-30min；
C: wood pulp and cornstarch are added in blender, continue to stir, temperature is maintained at 40-50 DEG C, and mixing speed is
800-1000r/min, mixing time 20-30min；
D: the mixture after stirring is taken out, die for molding is put into, obtains corrugated board.