CN109247854A - A kind of bathing towel, constituent of bathing towel and preparation method thereof - Google Patents
A kind of bathing towel, constituent of bathing towel and preparation method thereof Download PDFInfo
- Publication number
- CN109247854A CN109247854A CN201811023488.4A CN201811023488A CN109247854A CN 109247854 A CN109247854 A CN 109247854A CN 201811023488 A CN201811023488 A CN 201811023488A CN 109247854 A CN109247854 A CN 109247854A
- Authority
- CN
- China
- Prior art keywords
- bathing towel
- yarn
- frosted layer
- warp thread
- bathing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of bathing towels, the constituent of bathing towel and preparation method thereof, including bathing towel base, the first frosted layer and the second frosted layer are respectively equipped on the two sides of the bathing towel base, the edge of bathing towel base, the first frosted layer and the second frosted layer is wound with reinforcement viscose;First frosted layer and the second frosted layer are by warp thread, weft yarn, reinforce yarn A and reinforces yarn B composition, warp thread and weft yarn are mutually perpendicular to, warp thread and the angle reinforced between yarn A are 45 °, bamboo fiber has good gas permeability, instant water absorption, the characteristics such as stronger wearability and good dyeability, natural antibacterial, it is antibacterial, anti-mite, deodorization and anti-ultraviolet function, moisture absorption is ventilative, bacteriostasis antibiosis, it is cool in summer and warm in winter, the features such as environmentally protective, not only there is outstanding warmth retention property, and soft pro-skin, improve the snugness of fit of wool fabric, using the sewing mode for being in rice font, reinforce the firmness of sewing.
Description
Technical field
The present invention relates to a kind of bathing towel, in particular to a kind of bathing towel, constituent of bathing towel and preparation method thereof.
Background technique
Bathing towel generally uses cotton material to make, and also has other be accepted and bathing towel industry is usual is used for certainly
The fiber of bathing towel.Because it will be exactly bathing towel quality for the standard of the industry and the demand in market with the particularity of skin contact
Want soft, in this way can be comfortable with skin contact, but exactly because making the soft friction of looped pile monomer quality in bathing towel terry loop layer in this way
Power is inadequate, and the effect that Rapid Cleaning goes out dirt can not be played when washing one's face and bathing chopping, and efficiency is very low.
With the development of society, people start to focus on the daily cleaning to itself in daily life, what many people had a bath
Frequency is more and more, or even respectively washes sooner or later once, and bathing can not only be played the role of cleaning human body, moreover it is possible to anti-disease.It gives a rubdown with a damp towel
Towel is widely used articles in people's daily life, helps to wash off the dirt for being attached to human body surface.It is existing to give a rubdown with a damp towel
The shapes such as bathing towel or gloves are made in the fiber product (such as nylon) that towel generally uses surface texturisation coarse, by user come
Wiping is returned to achieve the purpose that decontamination.However, investigation shows that existing wash towel forms the unreasonable structure of rough surface, matter is hard
And it is coarse, in use, the effect if decontamination is not achieved without firmly cleaning, but if firmly wiping or using the time
It is too long, it is possible to which that coup injury skin keeps cuticula impaired or strips off, causes subcutaneous hemorrhage, serious person causes Secondary bacterial
Infection, causes the skin diseases such as furuncle, epifolliculitis.
Summary of the invention
The purpose of the present invention is to provide a kind of bathing towel, the constituent of bathing towel and preparation method thereof, have washability and
The advantages of reliable broad-spectrum antimicrobial effect, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme: a kind of bathing towel, including bathing towel base, the bathing towel
It is respectively equipped with the first frosted layer and the second frosted layer on the two sides of base, bathing towel base, the first frosted layer and the second frosted layer
Edge is wound with reinforcement viscose;First frosted layer and the second frosted layer are by warp thread, weft yarn, reinforcement yarn A and reinforcement
Yarn B composition, warp thread and weft yarn are mutually perpendicular to, and warp thread and the angle reinforced between yarn A are 45 °, reinforce yarn A and reinforcement yarn B is mutual
In parallel, warp thread, weft yarn, reinforce yarn A and reinforce yarn B it is interlaced and sew on the top and bottom of bathing towel base.
Preferably, the bamboo fibre bathing towel that bathing towel base is produced using natural bamboo as raw material.
Another technical solution of the invention is to provide a kind of constituent of bathing towel, and warp thread and weft yarn are by wool, gather
Fragrant oxadiazoles fiber, sisal hemp and nylon is blended by mass percentage forms, wool proportion is 60%-80%, poly- virtue is disliked
Diazole fiber proportion is 20%-30%, sisal hemp proportion is 10%-20% and nylon proportion is 10%-20%,
Sisal hemp, nylon and poly- fragrant oxadiazoles fiber are intertwined and connected with wool side by side;Reinforcing yarn A and reinforcement yarn B with natural polymer is
Raw material, by chemical fiber wire, such as viscose, ammonia copper wire and the short velvet of cotton is one or more is made through chemical method.
Preferably, the short velvet of cotton is extracted in cellulosic material by chemical method.
Another technical solution of the invention is to provide a kind of preparation method of bathing towel, comprising the following steps:
S1: through boiling bamboo pulp at a high temperature of 80~90 DEG C, NaOH and 100 DEG C of condition of 2% concentration is poured into bamboo pulp
Under boil 100min after, when solution temperature is down to 70~80 DEG C, be added concentration be 5% hydrogen peroxide, continue heat 0.5h, protect
Temperature is held at 70~80 DEG C, is filtered later, filter residue to neutrality is sufficiently washed with distilled water and extracts cellulose, cellulose is heated up to
Polyvinyl alcohol 10kg is added at 50-60 DEG C, continues heating stirring, is warming up to 95-98 DEG C, melts polyvinyl alcohol all, it is permanent
Warm 30min cooling, temperature are down to 80 DEG C or so, enter completely reacted acrylamide gel while stirring plus such as, stir 5min, reaction
30min adds water 100kg, and polyacrylamide glue is added while stirring and carries out utilizing gel spinning after glue is cooling
Bathing towel base is ready to spare;
S2: it chosen on bathing towel knitting machine as needed by warp thread, weft yarn, reinforce the single cord that yarn A and reinforcement yarn B are made into
Or multi cord carries out the first frosted layer and the production of the second frosted layer in bathing towel base, warp thread, weft yarn reinforce yarn A and reinforce yarn B
It is woven respectively in four edges of bathing towel base using double thread weave is intersected, bathing towel is divided into multilayer, whole process temperature
Degree control is at 50 DEG C or less;
S3: the bathing towel weaved is placed on a platform, bathing towel base, the first frosted layer and the second frosted layer corner
Viscose, four corners that warp thread, weft yarn, reinforcement yarn A and reinforcement yarn B are connect by strong viscose with bathing towel base are reinforced in place's sewing
Cladding is got up;
S4: heat-shaping is carried out to its surface by non-contact thermal mode, heating temperature is 60 DEG C or more, will be formed
Bathing towel afterwards is packaged machine packaging.
Preferably, reinforce viscose in step S3 and extract pure alpha-cellulose by cellulosic material, with caustic soda, two
Nitric sulfid processing, obtains orange-yellow sodium cellulose xanthate, is re-dissolved in diluted sodium hydroxide solution, de- through filtering, maturation
After bubble, wet spinning is carried out, coagulating bath is made of sulfuric acid, sodium sulphate and zinc sulfate.
Compared with prior art, the beneficial effects of the present invention are:
This bathing towel, constituent of bathing towel and preparation method thereof, the bamboo that bathing towel base is produced using natural bamboo as raw material
Fiber bathing towel, bamboo fiber have good gas permeability, instant water absorption, stronger wearability and good dyeability etc. special
Property, natural antibacterial, antibacterial, anti-mite, deodorization and anti-ultraviolet function, moisture absorption is ventilative, bacteriostasis antibiosis, cool in summer and warm in winter, environmentally protective
The features such as, the shapes such as bathing towel or gloves are made in the fiber product that the first frosted layer and the second frosted layer use surface more soft
Shape is wiped by user back and forth to achieve the purpose that decontamination, and sisal hemp, nylon and poly- fragrant oxadiazoles fiber are wound with wool side by side
Connection not only has outstanding warmth retention property, but also soft pro-skin, improves the snugness of fit of wool fabric, has very
Good washability and reliable broad-spectrum antimicrobial effect, antibacterial in effect 95% or so, warp thread, weft yarn reinforce yarn A and reinforce yarn B
Interlaced and sewing, using the sewing mode for being in rice font, reinforces the secured of sewing on the top and bottom of bathing towel base
Degree.
Detailed description of the invention
Fig. 1 is overall structure figure of the invention.
Fig. 2 is whole sectional view of the invention.
Fig. 3 is frosted layer structure chart of the invention;
In figure: 1, bathing towel base;2, the first frosted layer;21, warp thread;22, weft yarn;23, reinforce yarn A;24, reinforce yarn B;3,
Second frosted layer;4, reinforce viscose.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear;It is complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments, is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
A kind of bathing towel referring to FIG. 1-2, including bathing towel base 1, what bathing towel base 1 was produced using natural bamboo as raw material
Bamboo fibre bathing towel, bamboo fiber have good gas permeability, instant water absorption, stronger wearability and good dyeability etc. special
Property, natural antibacterial, antibacterial, anti-mite, deodorization and anti-ultraviolet function have moisture absorption ventilative, bacteriostasis antibiosis, cool in summer and warm in winter, green
The features such as environmentally friendly, is respectively equipped with the first frosted layer 2 and the second frosted layer 3, the first frosted layer 2 and on the two sides of bathing towel base 1
The shapes such as bathing towel or gloves are made using the more soft fiber product in surface in two frosted layers 3, are wiped back and forth by user
To achieve the purpose that decontamination, the edge of bathing towel base 1, the first frosted layer 2 and the second frosted layer 3, which is wound with, reinforces viscose 4,
The corner of bathing towel base 1, the first frosted layer 2 and the second frosted layer 3 is carried out sewing and avoided in the process used by reinforcement viscose 4
In cause bifurcated;
Referring to Fig. 3, a kind of constituent of bathing towel, the first frosted layer 2 and the second frosted layer 3 are by warp thread 21, weft yarn
22, reinforce yarn A 23 and reinforce the composition of yarn B 24, warp thread 21 and weft yarn 22 are mutually perpendicular to, between warp thread 21 and reinforcement yarn A23
Angle is 45 °, and warp thread 21 and weft yarn 22 are mixed by mass percentage by wool, poly- fragrant oxadiazoles fiber, sisal hemp and nylon
It spins, wool proportion is 60%-80%, poly- fragrant oxadiazoles fiber proportion is 20%-30%, sisal hemp proportion
It is 10%-20% for 10%-20% and nylon proportion, sisal hemp, nylon and poly- fragrant oxadiazoles fiber are wound with wool side by side
Connection not only has outstanding warmth retention property, but also soft pro-skin, improves the snugness of fit of wool fabric, has very
Good washability and reliable broad-spectrum antimicrobial effect, it is antibacterial in effect 95% or so, reinforce yarn A 23 and reinforces yarn B 24 mutually
In parallel, reinforce yarn A 23 and reinforce yarn B 24 with natural polymer to be raw material, by chemical fiber wire, such as viscose, ammonia copper wire and cotton
Short velvet is one or more to be made through chemical method, and warp thread 21, weft yarn 22, reinforcement yarn A23 and reinforcement yarn B 24 are interlaced simultaneously
Sewing, using the sewing mode for being in rice font, reinforces the firmness of sewing on the top and bottom of bathing towel base 1, wherein on
The short velvet of the cotton stated is extracted in cellulosic material by chemical method.
Another technical solution of the invention is to provide a kind of preparation method of bathing towel, comprising the following steps:
Step 1: through boiling bamboo pulp at a high temperature of 80~90 DEG C, NaOH and 100 DEG C that 2% concentration is poured into bamboo pulp
Under the conditions of boil 100min after, when solution temperature is down to 70~80 DEG C, be added concentration be 5% hydrogen peroxide, continue to heat
0.5h maintains the temperature at 70~80 DEG C, filters later, and filter residue to neutrality is sufficiently washed with distilled water and extracts cellulose, cellulose
It is heated up to add polyvinyl alcohol 10kg at 50-60 DEG C, continues heating stirring, be warming up to 95-98 DEG C, melt polyvinyl alcohol all
To change, constant temperature 30min cooling, temperature is down to 80 DEG C or so, enters completely reacted acrylamide gel while stirring plus such as, 5min is stirred,
30min is reacted, 100kg is added water, polyacrylamide glue is added while stirring and carries out utilizing gel spinning etc. after glue is cooling
Step bathing towel base 1 is ready to spare;
Step 2: it chosen on bathing towel knitting machine as needed by warp thread 21, weft yarn 22, reinforce yarn A23 and reinforce yarn B24
The single cord or multi cord being made into carry out the first frosted layer 2 and the production of the second frosted layer 3, warp thread 21, weft yarn in bathing towel base 1
22, reinforce yarn A23 and reinforcement yarn B24 woven in the four of bathing towel base 1 edges using double thread weave is intersected respectively,
Bathing towel is divided into multilayer, and whole process temperature is controlled at 50 DEG C or less;
Step 3: the bathing towel weaved is placed on a platform, bathing towel base 1, the first frosted layer 2 and the second frosted layer
Viscose 4 is reinforced in 3 edge sewing, and strong viscose 4 is by warp thread 21, weft yarn 22, reinforcement yarn A23 and reinforces yarn B24 and bathing towel
Four corners cladding that base 1 connects is got up, and is reinforced viscose 4 and is extracted pure alpha-cellulose by cellulosic material, with burning
Alkali, carbon disulfide processing, obtain orange-yellow sodium cellulose xanthate, are re-dissolved in diluted sodium hydroxide solution, are filtered, is ripe
After deaeration, wet spinning is carried out, coagulating bath is made of sulfuric acid, sodium sulphate and zinc sulfate;
Step 4: heat-shaping is carried out to its surface by non-contact thermal mode, heating temperature is 60 DEG C or more, will
Bathing towel after sizing is packaged machine packaging.
In summary;This bathing towel, constituent of bathing towel and preparation method thereof, bathing towel base 1 is using natural bamboo as raw material
The bamboo fibre bathing towel produced, bamboo fiber have good gas permeability, instant water absorption, stronger wearability and good dye
The characteristics such as color, natural antibacterial, antibacterial, anti-mite, deodorization and anti-ultraviolet function, moisture absorption is ventilative, bacteriostasis antibiosis, it is cool in summer and warm in winter,
The features such as environmentally protective, the first frosted layer 2 and the second frosted layer 3 using the more soft fiber product in surface be made bathing towel or
The shapes such as gloves are wiped by user back and forth to achieve the purpose that decontamination, sisal hemp, nylon and poly- fragrant oxadiazoles fiber side by side with
Wool is intertwined and connected, and not only has outstanding warmth retention property, but also soft pro-skin, improves the comfortable and easy to wear of wool fabric
Property, there is good washability and reliable broad-spectrum antimicrobial effect, antibacterial in effect 95% or so, warp thread 21, is reinforced weft yarn 22
Yarn A 23 and reinforcement yarn B 24 is interlaced and sews on the top and bottom of bathing towel base 1, using the sewing for being in rice font
Mode reinforces the firmness of sewing.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art within the technical scope of the present disclosure, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of bathing towel, including bathing towel base (1), which is characterized in that be respectively equipped with first on the two sides of the bathing towel base (1)
Frosted layer (2) and the second frosted layer (3), the edge winding of bathing towel base (1), the first frosted layer (2) and the second frosted layer (3)
There are reinforcement viscose (4);First frosted layer (2) and the second frosted layer (3) are by warp thread (21), weft yarn (22), reinforcement yarn A
(23) and reinforce yarn B (24) composition, warp thread (21) and weft yarn (22) are mutually perpendicular to, between warp thread (21) and reinforcement yarn A (23)
Angle is 45 °, reinforces yarn A (23) and reinforcement yarn B (24) is parallel to each other, and warp thread (21), weft yarn (22) are reinforced yarn A (23) and added
Strong yarn B (24) is interlaced and sews on the top and bottom of bathing towel base (1).
2. a kind of bathing towel as described in claim 1, it is characterised in that: bathing towel base (1) produces by raw material of natural bamboo
Bamboo fibre bathing towel.
3. a kind of constituent of bathing towel, it is characterised in that: warp thread (21) and weft yarn (22) are by wool, gather fragrant oxadiazoles fibre
Dimension, sisal hemp and nylon is blended by mass percentage forms, wool proportion be 60%-80%, poly- virtue oxadiazoles fiber institute
Accounting example is 20%-30%, sisal hemp proportion is 10%-20% and nylon proportion is 10%-20%, sisal hemp, nylon
It is intertwined and connected side by side with wool with poly- fragrant oxadiazoles fiber;Reinforce yarn A (23) and reinforce yarn B (24) with natural polymer to be former
Material, by chemical fiber wire, such as viscose, ammonia copper wire and the short velvet of cotton is one or more is made through chemical method.
4. a kind of constituent of bathing towel as claimed in claim 3, it is characterised in that: the short velvet of cotton is by chemical method in fibre
It ties up and is extracted in plain substance.
5. a kind of preparation method of bathing towel, which comprises the following steps:
S1: it through boiling bamboo pulp at a high temperature of 80~90 DEG C, is boiled under the conditions of NaOH and 100 DEG C of 2% concentration is poured into bamboo pulp
After boiling 100min, when solution temperature is down to 70~80 DEG C, the hydrogen peroxide that concentration is 5% is added, continues to heat 0.5h, keeps temperature
Degree filters later at 70~80 DEG C, and filter residue to neutrality is sufficiently washed with distilled water and extracts cellulose, cellulose is heated up to 50-60
DEG C when add polyvinyl alcohol 10kg, continue heating stirring, be warming up to 95-98 DEG C, melt polyvinyl alcohol all, constant temperature
30min cooling, temperature are down to 80 DEG C or so, enter completely reacted acrylamide gel while stirring plus such as, stir 5min, reaction
30min adds water 100kg, and polyacrylamide glue is added while stirring and carries out utilizing gel spinning after glue is cooling
Bathing towel base (1) is ready to spare;
S2: it chosen on bathing towel knitting machine as needed by warp thread (21), weft yarn (22), reinforce yarn A (23) and reinforce yarn B (24)
The single cord or multi cord being made into carry out the first frosted layer (2) and the second frosted layer (3) production, warp thread on bathing towel base (1)
(21), weft yarn (22), reinforcement yarn A (23) and reinforcement yarn B (24) are double using intersecting in four edges of bathing towel base (1) respectively
Screw thread weave is woven, and bathing towel is divided into multilayer, and whole process temperature is controlled at 50 DEG C or less;
S3: the bathing towel weaved is placed on a platform, bathing towel base (1), the first frosted layer (2) and the second frosted layer (3)
Edge sewing reinforce viscose (4), strong viscose (4) by warp thread (21), weft yarn (22), reinforce yarn A (23) and reinforcement yarn B
(24) the four corners cladding being connect with bathing towel base (1);
S4: heat-shaping is carried out to its surface by non-contact thermal mode, heating temperature is 60 DEG C or more, after sizing
Bathing towel is packaged machine packaging.
6. a kind of preparation method of bathing towel as claimed in claim 5, it is characterised in that: reinforce in step S3 viscose (4) by
Cellulosic material extracts pure alpha-cellulose, with caustic soda, carbon disulfide processing, obtains orange-yellow cellulose xanthic acid
Sodium is re-dissolved in diluted sodium hydroxide solution, after filtering, maturation deaeration, carries out wet spinning, coagulating bath is by sulfuric acid, sulfuric acid
Sodium and zinc sulfate composition.