CN109233379A - A kind of high-elastic waterproof asphalt emulsion - Google Patents
A kind of high-elastic waterproof asphalt emulsion Download PDFInfo
- Publication number
- CN109233379A CN109233379A CN201811190237.5A CN201811190237A CN109233379A CN 109233379 A CN109233379 A CN 109233379A CN 201811190237 A CN201811190237 A CN 201811190237A CN 109233379 A CN109233379 A CN 109233379A
- Authority
- CN
- China
- Prior art keywords
- parts
- elastic waterproof
- asphalt emulsion
- waterproof asphalt
- emulsion according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of high-elastic waterproof asphalt emulsions for belonging to technical field of chemical paint.It is composed of the following parts by weight: 36-40 parts of water, 15-20 parts of styrene, 1-2 parts of molecular regulation agent, 1-3 parts of emulsifier, 35-40 parts of butyl acrylate, 2-4 parts of chelating agent, 0.2-0.3 parts of initiator, 0.1-0.2 parts of defoaming agent, 0.2-0.4 parts of thickener, 1-2 parts of colloid protective agent, 0.5-0.7 parts of multifunctional assistant, 0.1-0.3 parts of mould inhibitor.There is aqueous high-elastic waterproof asphalt emulsion provided by the invention excellent low temperature to extend efficiency, and tensile strength, fabulous with pitch compatibility, adhesive force is strong, and cracking resistance is freeze proof, antiseepage, water-tolerant.
Description
Technical field
The invention belongs to technical field of chemical paint, and in particular to a kind of high-elastic waterproof asphalt emulsion.
Background technique
Pitch for paving the way, roof waterproof and coating material, but there are some in terms of physical property for pure pitch
It is insufficient.Therefore, it is necessary to improve to it.Emulsified asphalt is by high temperature road asphalt, by mechanical stirring and chemically stable
Method is distributed in water and forms under room temperature that viscosity is very low, the good pavement construction material of mobility.Emulsified asphalt has section
Can, it is widely used, easy to use the features such as, be mainly used for the upgrading and maintenance of road pavement and road.With traditional heated bitumen phase
Than emulsified asphalt is safer, energy saving and environmentally friendly, and avoids noxious emission and reduce environmental pollution, reduces worker's burning
The risk of cold danger and open firing explosion.But after general emulsified asphalt construction, there are the elder generations that low temperature embrittlement, high temperature trickle
It is insufficient, the popularization restricted its application.Occur some asphalt emulsions on the market at present, is exactly its emulsifying effectiveness to pitch
Difference is less susceptible to emulsify.In addition, the solid content of these asphalt emulsions is not high, production efficiency is influenced.
Summary of the invention
Problem to solve the above-mentioned problems, the invention proposes a kind of high-elastic waterproof asphalt emulsions.
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 36-40 parts of water, styrene 15-20
Part, 1-2 parts of molecular regulation agent, 1-3 parts of emulsifier, 35-40 parts of butyl acrylate, 2-4 parts of chelating agent, 0.2-0.3 parts of initiator,
0.1-0.2 parts of defoaming agent, 0.2-0.4 parts of thickener, 1-2 parts of colloid protective agent, 0.5-0.7 parts of multifunctional assistant, mould inhibitor
0.1-0.3 parts.
The molecular regulation agent is 2,4- diphenyl -4-methyl-1-pentene, methyl styrene linear dimerization body or methylbenzene
One or two kinds of mixtures of ethylene dimerization object.
The emulsifier is polyoxyethylene alkylphenol ether, in alkylolamides, sodium sulfate of polyethenoxy ether of fatty alcohol
One or two kinds of mixtures.
The chelating agent be one of aminotrimethylenephosphonic acid, 1-hydroxy ethylidene-1,1-diphosphonic acid, hexapotassium or
Two kinds of mixture.
The initiator is sodium peroxydisulfate or ammonium persulfate.
The defoaming agent is dimethyl silicone polymer.
The thickener is sodium carboxymethylcellulose pyce.
The colloid protective agent is one or both of polyvinyl alcohol, polyvinyl acetate, Sodium Polyacrylate.
The multifunctional assistant be calcium chloride, magnesium chloride, one of calcium nitrate or more than one.
The mould inhibitor is one of parachlorophenol, 2- methylol ethyl alcohol, 2- methyl -2- methylol propyl alcohol
Or two kinds.
Beneficial effects of the present invention: high-elastic waterproof asphalt emulsion provided by the invention aims at modified pitch and designs, energy
There is a good compatibility with anion and cationic asphalt, it is very big the shortcomings that improving pitch heat sagging, to the cold embrittlement,
Extending efficiency with excellent low temperature, tensile strength, quick-drying, film forming, weatherability, adhesive force is strong, cracking resistance, freeze proof, antiseepage,
Water resistance is fabulous.
Specific embodiment
The present invention will be further described combined with specific embodiments below.
Embodiment 1
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 38 parts of water, 18 parts of styrene, 2,
4- diphenyl -1.5 parts of 4-methyl-1-pentene, 2 parts of alkylolamides, 38 parts of butyl acrylate, 3 parts of aminotrimethylenephosphonic acid, mistake
0.25 part of sodium sulphate, 0.15 part of dimethyl silicone polymer, 0.3 part of sodium carboxymethylcellulose pyce, 1.5 parts of polyvinyl alcohol, calcium chloride 0.6
Part, 0.2 part of 2- methylol ethyl alcohol.
Embodiment 2
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 36 parts of water, 15 parts of styrene, 2,
4- diphenyl -1 part of 4-methyl-1-pentene, 1 part of alkylolamides, 35 parts of butyl acrylate, 2 parts of aminotrimethylenephosphonic acid, over cure
0.2 part of sour sodium, 0.1 part of dimethyl silicone polymer, 0.2 part of sodium carboxymethylcellulose pyce, 1 part of polyvinyl alcohol, 0.5 part of magnesium chloride, 2- hydroxyl
0.1 part of methyl amino ethanol.
Embodiment 3
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 40 parts of water, 20 parts of styrene, 2,
4- diphenyl -2 parts of 4-methyl-1-pentene, 3 parts of alkylolamides, 40 parts of butyl acrylate, 4 parts of aminotrimethylenephosphonic acid, over cure
0.3 part of sour sodium, 0.2 part of dimethyl silicone polymer, 0.4 part of sodium carboxymethylcellulose pyce, 2 parts of polyvinyl alcohol, 0.7 part of calcium chloride, 2- hydroxyl
0.3 part of methyl amino ethanol.
Embodiment 4
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 38 parts of water, 18 parts of styrene, 2,
4- diphenyl -1.5 parts of 4-methyl-1-pentene, 2 parts of alkylolamides, 38 parts of butyl acrylate, 3 parts of aminotrimethylenephosphonic acid, mistake
0.25 part of sodium sulphate, 0.15 part of dimethyl silicone polymer, 0.3 part of sodium carboxymethylcellulose pyce, 1.5 parts of polyvinyl alcohol, calcium chloride 0.6
Part, 0.2 part of 2- methylol ethyl alcohol, 1 part of diethylstilbestrol bisphosphate.
Embodiment 5
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 38 parts of water, 18 parts of styrene, 2,
4- diphenyl -1.5 parts of 4-methyl-1-pentene, 2 parts of alkylolamides, 38 parts of butyl acrylate, 3 parts of aminotrimethylenephosphonic acid, mistake
0.25 part of sodium sulphate, 0.15 part of dimethyl silicone polymer, 0.3 part of sodium carboxymethylcellulose pyce, 1.5 parts of polyvinyl alcohol, calcium chloride 0.6
Part, 0.2 part of 2- methylol ethyl alcohol, 1 part of aluctyl.
Embodiment 6
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 38 parts of water, 18 parts of styrene, 2,
4- diphenyl -1.5 parts of 4-methyl-1-pentene, 2 parts of alkylolamides, 38 parts of butyl acrylate, 3 parts of aminotrimethylenephosphonic acid, mistake
0.25 part of sodium sulphate, 0.15 part of dimethyl silicone polymer, 0.3 part of sodium carboxymethylcellulose pyce, 1.5 parts of polyvinyl alcohol, calcium chloride 0.6
Part, 0.2 part of 2- methylol ethyl alcohol, 1 part of 1- chrloroanthracene.
Comparative example 1
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 38 parts of water, 18 parts of styrene, alkane
2 parts of base alkylolamides, 38 parts of butyl acrylate, 3 parts of aminotrimethylenephosphonic acid, 0.25 part of sodium peroxydisulfate, dimethyl silicone polymer
0.15 part, 0.3 part of sodium carboxymethylcellulose pyce, 1.5 parts of polyvinyl alcohol, 0.6 part of calcium chloride, 0.2 part of 2- methylol ethyl alcohol.
Comparative example 2
A kind of high-elastic waterproof asphalt emulsion, is composed of the following parts by weight: 38 parts of water, 18 parts of styrene, 2,
4- diphenyl -1.5 parts of 4-methyl-1-pentene, 2 parts of alkylolamides, 38 parts of butyl acrylate, 3 parts of aminotrimethylenephosphonic acid, mistake
0.25 part of sodium sulphate, 0.15 part of dimethyl silicone polymer, 0.3 part of sodium carboxymethylcellulose pyce, 0.6 part of calcium chloride, 2- methylol
0.2 part of ethyl alcohol.
Experimental example 1:
The test of low temperature elongation percentage is carried out to the product of embodiment 1-6 and comparative example 1-2, test result is shown in Table 1:
Table 1
Note: * represents P < 0.05 compared with example 1 group.
As can be seen from Table 1, the high-elastic waterproof asphalt emulsion product low temperature elongation percentage of 1-3 of the embodiment of the present invention is higher than
630%, it is higher than commercial product, the product low temperature elongation percentage of embodiment 4-6 is higher than embodiment 1, and the product low temperature of comparative example 1-2
Elongation percentage is lower than embodiment 1.
Experimental example 2:
Immersion test test is carried out to the product of embodiment 1-6 and comparative example 1-2, is impregnated 96 hours and 200 hours respectively,
Test result is shown in Table 2:
Table 2
As can be seen from Table 2, the high-elastic waterproof asphalt emulsion product of 1-3 of the embodiment of the present invention impregnates 96 hours in water
It is without exception, 200 hours micro disperses are impregnated, the product of embodiment 4-6 impregnates without exception, comparative example 1-2 immersion 96 hours in 200 hours
Start to disperse.
Claims (10)
1. a kind of high-elastic waterproof asphalt emulsion, which is characterized in that be composed of the following parts by weight: 36-40 parts of water, benzene
15-20 parts of ethylene, 1-2 parts of molecular regulation agent, 1-3 parts of emulsifier, 35-40 parts of butyl acrylate, 2-4 parts of chelating agent, initiator
0.2-0.3 parts, 0.1-0.2 parts of defoaming agent, 0.2-0.4 parts of thickener, 1-2 parts of colloid protective agent, multifunctional assistant 0.5-0.7
Part, 0.1-0.3 parts of mould inhibitor.
2. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the molecular regulation agent is 2,
4- diphenyl -4-methyl-1-pentene, methyl styrene linear dimerization body or the one or two kinds of of methyl styrene dimer object mix
Close object.
3. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the emulsifier is alkylbenzene
The mixture of one or both of phenol polyethenoxy ether, alkylolamides, sodium sulfate of polyethenoxy ether of fatty alcohol.
4. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the chelating agent is amino three
The mixture of one or both of methylenephosphonic acid, 1-hydroxy ethylidene-1,1-diphosphonic acid, hexapotassium.
5. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the initiator is persulfuric acid
Sodium or ammonium persulfate.
6. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the defoaming agent is poly- diformazan
Radical siloxane.
7. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the thickener is that methyl is fine
Tie up plain sodium.
8. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the colloid protective agent is poly-
One or both of vinyl alcohol, polyvinyl acetate, Sodium Polyacrylate.
9. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the multifunctional assistant is chlorine
Change calcium, magnesium chloride, one of calcium nitrate or more than one.
10. a kind of high-elastic waterproof asphalt emulsion according to claim 1, which is characterized in that the mould inhibitor is to chlorine
One or both of phenol, 2- methylol ethyl alcohol, 2- methyl -2- methylol propyl alcohol.